A method to produce sintered silicon carbide ceramics in which powdery carbonaceous components with a dispersant are mixed with silicon carbide powder, shaped as required with or without drying, and fired in nonoxidation atmosphere is described. Carbon black is used as the carbonaceous component.
The history of research into the microstructure and properties of ceramic ware is discussed; methods of producing ceramics with particular characteristics are investigated. Bubbles, sintering, cracks, and electron microscopy are discussed.
A mother alloy of 10% Cr and 90% Cu was prepared by sintering. This was alloyed with the Cu melt and Cu-Cr alloys containing about 0.5% Cr was obtained. These alloys could be deformed easily in both the hot and cold states. By measuring the hardness change, age-hardening properties of cast alloys were studied, which were quenched from 950 deg and aged at 300 to 700 deg for 1 hour. The maximum hardness was obtained with the tempering temperature of 500 deg. For the temperature of solution-treatment, 950 deg was insufficient and that above 1000 deg necessary. For the tempering time, a treatment at 500 deg for 1 hr. or at 450 deg for 3 hrs. yielded the maximum hardness. As for the properties for electrical conductors, 3 kinds of wires (diam. 2 mm.) were made: (1) after cold-drawn to 2 mm., solution-treated, quenched, and then tempered (500 deg, 1 hr.); (2) after quenching, cold-drawn (75% reduction) to 2 mm. and tempered (500 deg, 1 hr.); and (3) after quenching, cold-drawn (81%) to intermediate diameter, tempered (500 deg, 1 hr.) and then cold-drawn (88%) again. Properties obtained for the 3 kinds, respectively, were as follows: conductivity 91, 90, and 86%. Tensile strength and strength for electrical conductivity are given.
Ni hydroxide sintered electrodes which are filled electrochemically are superior to chemically treated electrodes. In the electrochemical process, the hydroxide grows on the Ni grains and possesses a well-defined porous structure. Diffusion and conducting mechanisms are therefore facilitated.
Radiographic, ultrasonic, and scanning laser acoustic microscopy (SLAM) techniques were used to characterize silicon nitride and silicon carbide MOR bars in various stages of fabrication. Conventional and microfocus x-ray techniques were found capable of detecting minute high density inclusions in as-received powders, green compacts, and fully densified specimens. Significant density gradients in sintered bars were observed by radiography, ultrasonic velocity, and SLAM. Ultrasonic attenuation was found sensitive to microstructural variations due to grain and void morphology and distribution. SLAM was also capable of detecting voids, inclusions, and cracks in finished test bars. It was determined that thermoacoustic microscopy techniques have promise for application to green and densified ceramics.
A statistically designed experiment was conducted to determine optimum conditions for ball milling alpha-SiC in water. The influence of pH adjustment, volume percent solids loading, and mill rotational speed on grinding effectiveness was examined. An equation defining the effect of those milling variables on specific surface area was obtained. The volume percent solids loading of the slurry had the greatest influence on the grinding effectiveness in terms of increase in specific surface area. As grinding effectiveness improved, mill and media wear also increased. Contamination was minimized by use of sintered alpha-SiC milling hardware.
This report describes the results of a program designed to evaluate the breakaway friction and dynamic friction/wear characteristics of materials having potential for use as load bearing components in a high-performance high-temperature heavy duty diesel engine. Ten candidate materials were selected, six of which were evaluated under all possible material combinations as both stationary as well as moving breakaway specimens. The remaining materials were evaluated either in the static mode against themselves and all other materials, or against themselves only. Experiments were performed at five temperatures up to 650 C (1200 F) and unit pressures of 700 kPa (100 lb/sq in.), 3500 kPa (500 lb/sq in.), and 7000 kPa (1000 lb/sq in.). Experimental results indicate that under dynamic conditions, four of the ten materials exhibited good to excellent friction/wear characteristics in various material combinations. These materials were: titanium carbide, silicon nitride, silicon carbide (reaction sintered), and Refel (SiC).
Sintered alpha-SiC was examined in both oxidation and hot corrosion with a burner rig at 400 kPa (4 atm) and 1000 C with a flow velocity of 310 ft/sec. Oxidation tests for times to 46 hr produced virtually no attack, whereas tests with 4 ppm Na produced extensive corrosion in 13-1/2 hr. Thick glassy layers composed primarily of sodium silicate formed in the salt corrosion tests. This corrosion attack caused severe pitting of the silicon carbide substrate which led to a 32 percent strength decrease below the as-received material. Parallel furnace tests of Na2SO4/air induced attacked yielded basically similar results with some slight product composition differences. The differences are explained in terms of the continuous sulfate deposition which occurs in a burner rig.
Sintered alpha SiC was corroded by thin films of Na2SO4 and Na2CO3 molten salts at 1000%. This hot corrosion attack reduced room temperature strengths by as much as 50%. Strength degradation was porportional to the degree and uniformity of corrosion pitting attack as controlled by the chemistry of the molten salt. Extensive fractography identified corrosion pits as the most prevalent source of failure. A fracture mechanics treatment of the strength/pit depth relationship produced an average K sub IC equal to 2.6 MPa sub m 1/2, which is consistent with published values.
Studies on a number of types of nickel electrodes after cycle failure in a Ni/H2 cell showed that the failure is due to the loss of high rate discharge capability rather than an absolute capacity loss. The failure mechanism is speculated to be a combination of migration of the active material away from the current collecting nickel sinter, increased porosity of the active material caused by cycling, and an electrical isolation process of the active material during discharge.
To avoid metallic impurities normally introduced by milling ceramic powders in conventional steel hardware, an attrition mill (high-energy stirred ball mill) was constructed with the wearing parts (mill body, stirring arms, and media) made from silicon nitride. Commercial silicon and Si3N4 powders were milled to fine uniform particles with only minimal contamination - primarily from wear of the sintered Si3N4 media.
The chemical compatibility of lithium with tows of carbon and aramid fibers and silicon carbide and boron monofilaments was investigated by encapsulating the fibers in liquid lithium and also by sintering. The lithium did not readily wet the various fibers. In particular, very little lithium infiltration into the carbon and aramid tows was achieved and the strength of the tows was seriously degraded. The strength of the boron and silicon carbide monofilaments, however, was not affected by the liquid lithium. Therefore lithium is not feasible as a matrix for carbon and aramid fibers, but a composite containing boron or silicon carbide fibers in a lithium matrix may be feasible for specialized applications.
The plastic flow of plasma-sprayed ZrO2-8Y2O3 ceramic has been measured at temperatures up to 1250 C and compared to the plastic flow of pressed and sintered ZrO2-8Y2O3. Plasma spraying of binary oxide ceramics is found to result in a metastable state which is inelastic at high temperature but can also be stabilized or devitrified through heat treating so as to decrease plastic properties. The mechanical properties of the as-plasma sprayed and devitrified ceramic sheet material was measured. An improved algorithm that incorporates the inherently nonlinear thermomechanical field equations was used to determine the influence of inelastic material behavior on the thermomechanical response of ceramic coated seal components. Significant creep was found during the thermal shock and steady heating periods with insufficient time during thermal quench to reverse the process, thereby inducing significant residual stresses into the components.
In a brief study of the feasibility of welding sintered alpha-SiC, solid-state welding and brazing were investigated. Joint quality was determined solely by microstructural examination. Hot-pressure welding was shown to be feasible at 1950 C. Diffusion welding and brazing were also successful under hot isostatic pressure at 1950 C when boride, carbide, and silicide interlayers were used. Furnace brazing was accomplished at 1750 C when a TiSi2 interlayer was introduced.
Small supported metal particles have become a popular area of intense research interest, and important contributions to the considered problems are being made from the fields of uhv technology, thin film physics surface science, and surface and thin film instrumentation. Attention is given to insulating supports, particulate metal deposits and their properties, metal/support interactions and gas exposures, and integrated experimental approaches. It is concluded that major contributions to the field of model catalysis should be forthcoming in the near future from uhv-based methods of research. Catalysis and catalysis-related problem areas expected to benefit from advanced model studies include catalyst preparation processing, sintering mechanisms for metals and alloys, separation of initial and final state effects for supported clusters, and the influence of particle and/or support morphologies.
Refractory fibers more than double strength of coating. Impact strengths of ceramic coatings increase with increasing whisker content. Silicon carbide whiskers clearly produce largest increase, and improvement grows even more with high-temperature sintering. Coating also improves thermal and mechanical properties of electromagnetic components, mirrors, furnace linings, and ceramic parts of advanced internal-combustion engines.
Metals, ceramics, and glasses just some of possible raw materials. Key components of equipment for new microballoon fabrication process nozzle, crucible assembly, and drop tube. Recessed, conical inner orifice aids in producing uniform, symmetrical microballoons. All-graphite crucible assembly resistant to misalinement and cracks. Drop tube ensures timely solidification of microballoons used in fluidized-bed heat exchangers; as containers for hazardous materials; catalysts in chemical and pharmaceutical processes; solid fuel for rockets; fuel containers for fusion power experiments; shock-wave dampers; and starting materials for high-strength, low-density sintered alloys and ceramics.
Reactants released by crushing or puncturing. Agglomerated gas-filled spheres hexagonally close packed and sintered or glued together into rods strung together at ends. Rods fed into crushing machine to release material in spheres as needed.