Controlled synthesis of nickel ferrite nanocrystals with tunable properties using a novel induction thermal plasma method
Nickel ferrite spinel nanopowders were synthesised using a solution spray radio-frequency inductively coupled plasma reactor over a wide range of compositions (Ni{sub x}Fe{sub 3-x}O{sub 4}, x ≤ 1), with metastable powders produced for x = 0, 0.25, and 0.5. X-ray fluorescence and X-ray diffraction coupled to Rietveld refinement show that this synthesis technique offers an excellent level of control over both the chemical and crystallographic composition of the nanopowder through the control of the input Fe/Ni ratio. The technique produces highly crystalline nanopowders without the need for post-synthesis annealing. A bulk Fe/Ni ratio ≥2 yields a pure spinel Ni{sub x}Fe{sub 3-x}O{sub 4} phase, whereas Fe/Ni ratio <2 results in the excess Ni partitioning to a secondary bunsenite (Ni{sub x},Fe{sub 1-x})O phase. Morphological analysis using transmission electron microscopy shows that two types of particles are produced in different parts of the reactor: a highly faceted powder with the truncated octahedron morphology and a smaller-sized random agglomerate. The faceted particles have a log-normal particle size distribution, with an average size of about 30 nm while the agglomerates have a characteristic length of ∼3–5 nm.