NASA NTRS2005

Mechanical Behavior of Gamma-Met PX under Uniaxial Loading at Elevated Temperatures and High Strain Rates

Gamma titanium aluminides have received considerable attention over the last decade. These alloys are known to have low density, good high temperature strength retention and good oxidation and corrosion resistance. However, poor ductility and low fracture toughness have been the key limiting factors in the full utilization of these alloys. More recently, a new generation of gamma titanium aluminide alloys, commonly referred to as Gamma-met PX, has been developed by GKSS, Germany. These alloys have been observed to have superior strength and better oxidation resistance at elevated temperatures when compared with conventional gamma titanium aluminides. The present paper discusses results of a study to understand the uniaxial mechanical behavior in both compression and tension of Gamma-Met PX at elevated temperatures and high strain rates. The compression and tensile tests are conducted using a modified split-Hopkinson bar apparatus at test temperatures ranging from room temperature to 900 C and strain rates of up to 3500/s. Under uniaxial compression, in the temperature range from room to 600 C, the flow stress is observed to be nearly independent of test temperature. However, at temperatures higher than 600 C thermal softening is observed at all strain rates with the rate of thermal softening increasing dramatically between 800 C and 900 C. The room temperature tensile tests show negligible strain-rate dependence on both yield stress and flow stress. With an increase in test temperature from room to 900 C the material shows a drop in both yield and flow stress at all levels of plastic strain. However, the measured flow stress is still higher when compared to nickel based super-alloys and other gamma titanium aluminides under similar test conditions. Also, no anomaly in yield stress is observed up to 900 C.

Shazly, Mostafa↗
NASA NTRS1991

1000 to 1200 K time-dependent compressive deformation of single-crystalline and polycrystalline B2 Ni-40Al

The 1000-K and 1200-K time-dependent deformation of 100-line-oriented and non-100-line-oriented single crystals of Ni-40Al (made by a modified Bridgman technique) was examined over a large range of strain rates (from 0.1 to 10 to the -7th per sec). The results were compared with those for polycrystalline Ni-40Al made by hot pressing XD synthesized powder. The results from measurements of slow-plastic-strain-rate properties of the two materials show that single crystals offer no strength advantage over polycrystalline material. Both forms were found to deform via a dislocation climb mechanism.

Whittenberger, J. D.↗
NASA NTRS1986

Simplified cyclic structural analyses of SSME turbine blades

Anisotropic high-temperature alloys are used to meet the safety and durability requirements of turbine blades for high-pressure turbopumps in reusable space propulsion systems. The applicability to anisotropic components of a simplified inelastic structural analysis procedure developed at the NASA Lewis Research Center is assessed. The procedure uses as input the history of the total strain at the critical crack initiation location computed from elastic finite-element analyses. Cyclic heat transfer and structural analyses are performed for the first stage high-pressure fuel turbopump blade of the space shuttle main engine. The blade alloy is directionally solidified MAR-M 246 (nickel base). The analyses are based on a typical test stand engine cycle. Stress-strain histories for the airfoil critical location are computed using both the MARC nonlinear finite-element computer code and the simplified procedure. Additional cases are analyzed in which the material yield strength is arbitrarily reduced to increase the plastic strains and, therefore, the severity of the problem. Good agreement is shown between the predicted stress-strain solutions from the two methods. The simplified analysis uses about 0.02 percent (5 percent with the required elastic finite-element analyses) of the CPU time used by the nonlinear finite element analysis.

Kaufman, A.↗
NASA NTRS1997

Parallel adaptive mesh refinement techniques for plasticity problems

The accurate modeling of the nonlinear properties of materials can be computationally expensive. Parallel computing offers an attractive way for solving such problems; however, the efficient use of these systems requires the vertical integration of a number of very different software components, we explore the solution of two- and three-dimensional, small-strain plasticity problems. We consider a finite-element formulation of the problem with adaptive refinement of an unstructured mesh to accurately model plastic transition zones. We present a framework for the parallel implementation of such complex algorithms. This framework, using libraries from the SUMAA3d project, allows a user to build a parallel finite-element application without writing any parallel code. To demonstrate the effectiveness of this approach on widely varying parallel architectures, we present experimental results from an IBM SP parallel computer and an ATM-connected network of Sun UltraSparc workstations. The results detail the parallel performance of the computational phases of the application during the process while the material is incrementally loaded.

Barry, W. J.↗
DOE OSTI2020

A phase-field model for non-isothermal phase transformation and plasticity in polycrystalline yttria-stabilized tetragonal zirconia

Here we propose an elastoplastic phase-field (PF) model to investigate the mechanics of tetragonal-to-monoclinic phase transformation (TMPT) and elastoplastic deformation of polycrystalline yttria-stabilized tetragonal zirconia (YSTZ). A Landau polynomial with non-vanishing chemical energy at the equilibrium temperature is introduced to account for the actual formation energies of the phases. The effects of different grain orientations, latent heat, and temperature on TMPT and deformation mechanisms are considered. The suppressive transformation effects of the grain boundaries (GBs) is modeled using an inhomogeneous kinetic coefficient in the bulk and GBs. The simulation results for single crystals demonstrate the capability of the model to reproduce the orientation-dependent compressive deformation of YSTZ similar to atomistic simulations and micropillar experiments. The single crystal with [100] crystallographic orientation along the loading direction (SC[100]) displays both TMPT and plasticity, SC[101] experiences only phase transformation, while SC[001] undergoes only plastic yielding. The TMPT induced by compressive loading exhibits shape memory effect (SME) below the equilibrium transformation temperature and pseudoelasticity above it, while the critical transformation stress increases with increasing loading temperature. The irrecoverable plastic strain is found to trap a part of the monoclinic phase, which prevents a complete reverse transformation. The polycrystalline cases also display SME and PE at low and high temperatures, respectively. Due to the orientation differences between grains and the stress concentrations at geometric nonlinearities, plastic deformation occurs in polycrystalline YSTZ for an applied load less than the yield stress. The results suggest a possible limitation of plasticity and an improvement of the shape recovery of YSTZ if one can control the orientation of the grains and/or increase the density of stacking faults at the GBs during material processing.

36 MATERIALS SCIENCE↗
NASA NTRS1988

Life prediction modeling based on strainrange partitioning

Strainrange partitioning (SRP) is an integrated low-cycle-fatigue life predicting system. It was created specifically for calculating cyclic crack initiation life under severe high-temperature fatigue conditions. The key feature of the SRP system is its recognition of the interacting mechanisms of cyclic inelastic deformation that govern cyclic life at high temperatures. The SRP system bridges the gap between the mechanistic level of understanding that breeds new and better materials and the phenomenological level wherein workable engineering life prediction methods are in great demand. The system was recently expanded to address engineering fatigue problems in the low-strain, long-life, nominally elastic regime. This breakthrough, along with other advances in material behavior and testing technology, has permitted the system to also encompass low-strain thermomechanical loading conditions. Other important refinements of the originally proposed method include procedures for dealing with life-reducing effects of multiaxial loading, ratcheting, mean stresses, nonrepetitive (cumulative loading) loading, and environmental and long-time exposure. Procedure were also developed for partitioning creep and plastic strain and for estimating strainrange versus life relations from tensile and creep rupture properties. Each of the important engineering features of the SRP system are discussed and examples shown of how they help toward predicting high-temperature fatigue life under practical, although complex, loading conditions.

Halford, Gary R.↗
DOE OSTI2021

Role of deformation twinning in fatigue of CrCoNi medium-entropy alloy at room temperature

Here cylindrical specimens of CrCoNi alloy with electropolished surfaces were subjected to constant total strain amplitude low cycle fatigue. The alloy exhibited an initial period of cyclic hardening followed by cyclic softening until failure occurred. At the end of hardening stage at the peak of cyclic stress, well-developed persistent slip markings (PSMs) consisting of extrusions and intrusions were associated with thin deformation twins. A sophisticated experimental workflow was designed to extract information from the surface and the bulk of tested material. A combination of SEM, EBSD, ECCI, FIB and HR-STEM was used to study the internal structure and the surface profiles around the deformation twins, which were produced during the initial period of cyclic loading. Furthermore, localized cyclic plastic strain and stress concentrations near deformation twins led not only to early, well-developed PSMs, but also to the activation of TWIP and TRIP plasticity even at low macroscopic stress amplitudes.

36 MATERIALS SCIENCE↗
NASA NTRS1993

Importance of expansion and contraction in the formation of tectonic features on the Moon

The lack of globally distributed tectonic features on the lunar surface has been used to argue against significant changes in the radius of the Moon since the formation of the presently observed surface, which dates to the end of heavy bombardment about 3.9 Ga. This observation has been used previously to limit the maximum stresses to approximately 100 MPa that could be supported by the lunar lithosphere without the formation of globally distributed tectonic features, which in turn limits the maximum radius changes to plus or minus 1 km for a purely elastic lithosphere. In a previous abstract, limits on the elastic expansion or contraction of the Moon were reexamined with respect to realistic failure stresses necessary to produce actual lunar tectonic features. In addition, limits on the permanent (plastic) strain that could be accommodated by non-mascon grabens and wrinkle ridges were considered with more severe constraints placed on the total reasonable expansion and contraction of the Moon since 3.9 Ga. In this abstract, considerations of the distribution and mechanisms of formation due to a planetary radius change or their accommodating much permanent plastic planetary expansion or contraction.

Golombek, M. P.↗
DOE OSTI2024

Role of slip in hydrogen-assisted crack initiation in Ni-based alloy 725

We conduct in situ tensile straining experiments to investigate the role of hydrogen and slip in crack initiation in nickel-based alloy 725. Our experiments reveal no tendency for hydrogen to enhance localized slip and no necessity of slip for crack initiation. We use electrochemical charging to introduce hydrogen into samples, melt extraction to measure hydrogen content, and digital image correlation to analyze localized plastic strains during in situ tensile tests in a scanning electron microscope. Cracks initiate both in regions with and without nearby localized slip. Moreover, the fraction of cracks initiating with no nearby slip is greater at higher hydrogen content. Slip-assisted crack initiation generally occurs at locations where intergranular slip is arrested, especially at intersections of slipping coherent twin boundaries with thin twin lamellae. Cracks that initiate without nearby slip occur at a wider variety of microstructural features, including inclusions, triple junctions, and surface flaws.

36 MATERIALS SCIENCE↗
DOE OSTI2026

Part-scale evolution of fine-scale microstructural heterogeneity in solid-state additive manufacturing

Current solid-state additive manufacturing methods, refined through costly and time-consuming trial and error, have spurred interest in computational models that replicate material behavior under typical thermomechanical conditions (e.g., strain-rate ~ 102 s−1). These models, however, struggle to capture time-dependent microstructural evolution. In this work, Additive Friction-Stir Deposition (AFSD) is used as a representative case study for part-scale quantification of microstructure evolution at a fine spatial resolution (200 μm) by examining a liquid-nitrogen-cooled stop-action build via energy-dispersive X-ray diffraction coupled with a multi-channel detector. These results inform modeling efforts by linking process asymmetry to stored plastic strain, residual elastic strain, and texture development, and unlike current state-of-the-art characterization methods (e.g., EBSD or neutron diffraction), this approach provides both the spatial resolution and collection efficiency necessary to quantify fine-scale microstructural heterogeneity over large component volumes. As such, this technique provides essential validation data for computational models, e.g., crystal plasticity, enabling future prediction of heterogeneous behavior in AFSD and other additive manufacturing processes.

Franz, Cole [ORNL] (ORCID:0000000213465881)↗
NASA NTRS1975

Separation of the strain components for use in strainrange partitioning

Two methods are presented for separating the inelastic strain components of a complex hysteresis loop so that strainrange partitioning formulas can be applied to accurately determine cyclic life at elevated temperatures. These methods are required only if lower bounds established by strainrange partitioning concepts have been deemed inadequate in the establishment of expected lifetime. In one method, rapid loading and unloading is applied in the tensile and compressive half to isolate the plastic strain. In the second method, the creep is measured at a discrete number of points along the hysteresis loop by combining load-control tests into the general pattern of strain cycling under arbitrary temperature. Both methods are shown to give good results.

Manson, S. S.↗
NASA NTRS1975

Separation of the strain components for use in Strainrange Partitioning

Two methods are presented for separating the inelastic strain components of a complex hysteresis loop so that Strainrange Partitioning formulas can be applied to accurately determine cyclic life at elevated temperatures. These methods are required only if lower bounds established by Strainrange Partitioning concepts have been deemed inadequate in the establishment of expected lifetime. In one method rapid loading and unloading is applied in the tensile and compressive half to isolate the plastic strain. In the second method the 'creep' is measured at a discrete number of points along the hysteresis loop by combining load-control tests into the general pattern of strain cycling under arbitrary temperature. Both methods are shown to give good results.

Manson, S. S.↗
NASA NTRS1976

Application of strainrange partitioning to the prediction of MPC creep-fatigue data for 2 1/4 Cr-1 Mo steel

Creep-fatigue tests were conducted on annealed 2.25Cr-1Mo steel in air at 538 C involving interspersion of rapid strain cycles (0 to 22 cycles) between constant tensile stress-hold periods (23 or 47 hours). Life predictions were made on the basis of the strain range-life relations obtained from short-time material characterization tests on tubular specimens taken from the same heat as the specimens for the creep-fatigue tests. The creep-fatigue tests lasted from about 500 to 5000 hours, while the short-time tests used as the prediction basis lasted from 0.1 to 100 hours. By partitioning the creep and plastic strains within every cycle and summing the damage on a cycle-by-cycle basis, the predicted lives agreed with the observed ones within factors of two.

Saltsman, J. F.↗
NASA NTRS2001

Durability and Damage Development in Woven Ceramic Matrix Composites

Damage development in woven SiC/SiNC ceramic matrix composites (CMC's) under tensile and cyclic loading both at room and elevated temperatures have been investigated for the exhaust nozzle of high-efficient turbine engines. The ultimate strength, failure strain, proportional limit and modulus data at a temperature range of 23 to 1250 C are generated. The tensile strength of SiC/SiNC woven composites have been observed to increase with increased temperatures up to 1000 C. The stress/strain plot shows a pseudo-yield point at 25 percent of the failure strain (epsilon(sub r)) which indicates damage initiation in the form of matrix cracking. The evolution of damage beyond 0.25 epsilon(sub f), both at room and elevated temperature comprises multiple matrix cracking, interfacial debonding, and fiber pullout. Although the nature of the stress/strain plot shows damage-tolerant behavior under static loading both at room and elevated temperature, the life expectancy of SiC/SiNC composites degrades significantly under cyclic loading at elevated temperature. This is mostly due to the interactions of fatigue damage caused by the mechanically induced plastic strain and the damage developed by the creep strain. The in situ damage evolutions are monitored by acoustic event parameters, ultrasonic C-scan and stiffness degradation. Rate equations for modulus degradation and fatigue life prediction of ceramic matrix composites both at room and elevated temperatures are developed. These rate equations are observed to show reasonable agreement with experimental results.

Haque, A.↗
NASA NTRS1973

Thermal fatigue behavior of T-111 and ASTAR 811C in ultrahigh vacuum

The thermal fatigue behavior of the tantalum alloys T-111 (Ta-8W-2Hf) and ASTAR 811C (Ta-8W-1Re-0.7Hf-0.025C) has been evaluated using completely reversed push-pull fatigue tests conducted in ultrahigh vacuum with independently programmed temperature and strain cycles. Test results showed that cycling of the test temperature simultaneously with the mechanical strain in most cases significantly reduced the cycles to failure of both alloys compared to isothermal testing. Notched specimens had reduced lives under isothermal conditions, but the presence of a notch or use of a 1-h holdtime provided only a small further decrease in life for the temperature cycled tests. Compressive stress at the maximum temperature produced longer lives than tensile stress. ASTAR 811C was more fatigue resistant than T-111 isothermally and did not have as great a decrease in life with thermal cycling. Results are analyzed by partition of plastic strains into creep and creep-independent components and considering where each component was active in the hysteresis cycle.

Sheffler, K. D.↗
DOE OSTI2021

Understanding and quantifying electron beam effects during in situ TEM nanomechanical tensile testing on metal thin films

Transmission electron microscopy (TEM) imaging relies on high energy electrons for atomic scale resolution, however, the electrons themselves interact with and may alter the material being imaged. Using an in situ TEM MEMS-based nanomechanical testing technique, the effect of the electron beam (e-beam) on the deformation behavior of nanocrystalline Al and ultrafine-grained Au is investigated and quantified. We show that the e-beam enhances plastic deformation, leading to an increase in plastic strain rate and a decrease in true activation volume V* in Al (28 to 21b 3 , with b being the Burgers vector length). The e-beam has a much weaker effect on Au. The e-beam effect is not caused by knock-on damage, but rather an effective temperature increase due to additional atomic fluctuations provided by the e-beam. The effective temperature increase is larger for Al than Au. This e-beam effect does not change the deformation mechanisms, but instead accelerates the stress-driven, thermally activated plastic deformation. These experiments provide insight into the effects of the e-beam on plastic deformation in different metals and underscore the importance of understanding and quantifying these effects for proper interpretation of measured mechanical properties during in situ TEM experiments.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Effect of grain size on iron-boride nanoglasses

Metallic nanoglasses are made of amorphous grains that are separated by lower-density amorphous boundaries, which have been proposed to enhance plasticity through the deflection of cracks and shear bands at interfaces. It has been difficult to experimentally control grain size and interfacial structure to understand their roles in plastic deformation. Here, we fabricate bulk nanoglasses via compaction and sintering of colloidally synthesized amorphous iron-boride nanoparticles. These nanoglasses have amorphous grains with diameters from 116nm to 576nm and were tested using nanoindentation and micropillar compressions. The nanoglass with a grain size of 576 nm shows the highest elastic modulus and hardness of 101 GPa and 7.4GPa, respectively. Transmission electron microscopy reveals that nanocrystals form within the nanoglasses during compaction. Higher nanocrystal density correlates with higher nanoparticle crystallization enthalpy, an increase in plasticity, and a decrease in yield strength. Plastic strain of 5.0%, yield strength of 3.8GPa, and ultimate compressive strength of 2.7–3.8GPa were achieved. Here we show that the compaction of colloidal metallic glass nanoparticles results in robust bulk samples, with mechanical properties similar to that of other iron-based bulk metallic glasses.

36 MATERIALS SCIENCE↗