DOE OSTI2020

In-situ observation of nano-oxide and defect evolution in 14YWT alloys

Nanostructured ferritic alloys (NFAs) are considered as candidates for structural components in advanced nuclear reactors due to their excellent radiation resistance as a result of a high density of nano-oxides (NOs) in the microstructure. Therefore, gaining an understanding on the stability of NOs under irradiation is crucial. In this study, we have investigated the evolution of defects and NOs in 14YWT NFAs under in-situ Kr ion irradiation at room temperature (RT) and 450°C up to 10 dpa. It has been found that irradiations at 450°C do not create any changes in the NOs, similar to the bulk irradiations. On the other hand, elemental mapping indicates that NOs dissolve mostly after 10 dpa irradiations at RT. Thus, while defects are both annihilated and pinned by NOs at low doses (before the dissolution of NOs), glissile loops start to escape to the foil surface at high doses (after the dissolution of NOs), justifying the significantly low fraction of (111) loops compared to the literature values. Furthermore, high resolution transmission electron microscopy analysis has shown that the NOs are mostly coherent Y 2 Ti 2 O 7 particles with pyrochlore crystal structure after both RT and 450°C irradiations, similar to those observed before irradiation.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Radiation induced hardening of beryllium during low temperature He implantation

The effect of ion irradiation on evolution of microstructure and hardening of beryllium with different impurity levels was investigated using TEM and nanoindentation. High purity S-65 grade and less-pure S-200-F grade were implanted by helium ions at temperatures of 50°C and 200°C. 11 different energies were used, so as to create a quasi-homogeneous 3 µm irradiated layer with average radiation damage of 0.1 dpa and average He content of 2000 appm.Nanoindentation experiments demonstrated that before irradiation, the S-200-F and S-65 grades have an average hardness of 3.7$\pm$0.8 GPa and 3.4$\pm$0.8 GPa correspondently. After implantation the hardness of both grades increased by about 60% for the 200°C irradiation and 100% for the 50°C irradiation. The crystallographic analysis of indented grains demonstrated that in the as-received materials the hardness is about 2.5 times higher when the indentation direction is close to the [0001] c-axis of beryllium compared to indentation perpendicular to [0001]. Hardness anisotropy significantly decreased after irradiation: the “soft orientation” was most sensitive to irradiation-induced hardening, with hardness increasing by about 140% after irradiation at 50°C and 100% after irradiation at 200°C, compared to about 15 - 20% for the “hard” orientation at both irradiation temperatures. The higher purity grade had smaller increase of the “soft orientation” hardness: 2.5$\pm$0.3 GPa for the S-65 and 2.9$\pm$0.2 GPa for the S-200-F.At both temperatures in both grades, under TEM investigation the radiation damage appears as “black dots” which are likely to be small dislocation loops with the number density of ~ 10 22 m -3 . No bubbles were observed by TEM inside grains and at grain boundaries. Analysis of the possible hardening contribution demonstrated that the observed “black dots” could be responsible for up to half of the measured hardening, while the rest of the hardening should originate from helium bubbles with the size below the TEM resolution (at or below 1.5 nm).

36 MATERIALS SCIENCE↗

DOE OSTI2024

Influence of high-strain-rate compression and subsequent heat treatment on (TiNbZr) 89 (AlTa) 11 refractory high-entropy alloys: Dynamic-mechanical behavior and microstructural changes

This study explored the dynamic-mechanical behavior of a novel low-density (TiNbZr) 89 (AlTa) 11 refractory high-entropy alloy (RHEA) across strain rates ranging from 1.0×10 3 to 3.5×10 3 s –1 . A significant increase in the yield and ultimate compressive strengths with rising strain rates up to 3.0×10 3 s –1 was observed and attributed to enhanced dislocation activities and stress-induced microstructural transformations. The formation of the B2 phase and Zr 5 Al 3 precipitates was found to be crucial in bolstering the alloy strength at high strain rates. Beyond strain rates of 3.0×10 3 s –1 , a decrease in strength occurred due to thermal softening and strain localization. Microstructural analyses at 3.5×10 3 s –1 revealed grain refinement, the development of micro shear bands, and dislocation tangles, which were indicative of dynamic recrystallization. Besides, the findings also revealed that the post-dynamic compression heat treatment further enhanced the hardness and microstructural stability of the alloy. These results highlight the potential of the (TiNbZr) 89 (AlTa) 11 RHEA for applications requiring materials with high strength-to-weight ratios, particularly in dynamically loaded environments. It is expected that the results of this study will further advance our fundamental understanding of the behavior of RHEAs under extreme conditions, thereby opening new avenues for material innovation.

36 MATERIALS SCIENCE↗