Results for “Powder metallurgy”

Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

SourceResearch connectionFrom yearThrough year

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

At least 163 records · Page 9

All sources NASA NTRS DOE OSTI

NASA NTRS2003

Realistic Subscale Evaluations of the Mechanical Properties of Advanced Disk Superalloys

A series of experimental powder metallurgy disk alloys were evaluated for their processing characteristics and high temperature mechanical properties. Powder of each alloy was hot compacted, extruded, and isothermally forged into subscale disks. Disks were subsolvus and supersolvus heat treated, then quenched using procedures designed to reproduce the cooling paths expected in large-scale disks. Mechanical tests were then performed at 538, 704, and 815 C. Several alloys had superior tensile and creep properties at 704 C and higher temperatures, but were difficult to process and prone to quench cracking, chiefly due to their high gamma prime solvus temperature. Several other alloys had more favorable processing characteristics due to their lower gamma prime solvus temperature and balanced time-dependent properties at 704 C. Results indicate an experimental low solvus, high refractory alloy can build upon the best attributes of all these alloys, giving exceptional tensile and creep properties at high temperatures with good processing characteristics due to a low gamma prime solvus.

Gabb, Timothy P.↗

NASA NTRS2014

Development Status of a CVD System to Deposit Tungsten onto UO2 Powder via the WCI6 Process

Nuclear Thermal Propulsion (NTP) is under development for deep space exploration. NTP's high specific impulse (> 850 second) enables a large range of destinations, shorter trip durations, and improved reliability. W-60vol%UO2 CERMET fuel development efforts emphasize fabrication, performance testing and process optimization to meet service life requirements. Fuel elements must be able to survive operation in excess of 2850 K, exposure to flowing hydrogen (H2), vibration, acoustic, and radiation conditions. CTE mismatch between W and UO2 result in high thermal stresses and lead to mechanical failure as a result UO2 reduction by hot hydrogen (H2) [1]. Improved powder metallurgy fabrication process control and mitigated fuel loss can be attained by coating UO2 starting powders within a layer of high density tungsten [2]. This paper discusses the advances of a fluidized bed chemical vapor deposition (CVD) system that utilizes the H2-WCl6 reduction process.

Mireles, O. R.↗

NASA NTRS1982

Oxide dispersion hardened mechanically alloyed materials for high temperatures

The procedure of mechanical alloying makes it possible to obtain, with the aid of powder-metallurgy techniques, alloys that consist of a metallic matrix in which very fine oxide particles are dispersed. Mechanically alloyed compound powders can be used for making either forged or hot-rolled semifinished products. For these products, dispersion strengthening and precipitation hardening has been combined. At high temperatures, the strength characteristics of the alloy are determined by both dispersion hardening and by precipitation hardening processes. The effect produced by each process is independent of that due to the other. Attention is given to the principle of mechanical alloying developed by Benjamin (1970, 1976), the strength characteristics of mechanically alloyed materials, the corrosion resistance of mechanically alloyed material at high temperatures, and the preparation and characteristics of the alloy MA 6000 E.

Benjamin, J. S.↗

NASA NTRS1987

Effect of composition and grain size on slow plastic flow properties of NiAl between 1200 and 1400 K

A series of about 15-micron diameter polycrystalline B2 crystal structure NiAl alloys ranging in composition from 43.9 to 52.7 Al (at. pct) have been compression tested at constant velocities in air between 1200 and 1400 K. All materials were fabricated via powder metallurgy techniques with hot extrusion as the densification process. Seven intermediate compositions were produced by blending various amounts of two master heats of prealloyed powder; in addition, a tenth alloy of identical composition, 48.25 Al, as one of the blended materials, was produced from a third master heat. Comparison of the flow stress-strain rate behavior for the two 48.25 Al alloys revealed that their properties were identical. The creep strength of materials for Al/Ni not above 1.03 was essentially equal, and deformation could be described by a single stress exponent and activation energy. Creep at low temperatures and faster strain rates is independent of grain sizes and appears to be controlled by a subgrain mechanism. However, at higher temperatures and slower strain rates, diffusional creep seems to contribute to the overall deformation rate.

Whittenberger, J. Daniel↗

NASA NTRS2001

Aerospace Structural Materials Handbook Supplement GRCop-84

GRCop-84 is a high strength-high conductivity copper-based alloy developed at NASA Glenn Research Center for combustion chamber liners of regeneratively cooled rocket engines. It also has promise for other high heat flux applications operating at temperatures up to 700 C (1292 F) and potentially higher. The alloy must be made by powder metallurgy techniques such as gas atomization. Slower cooling rates such as those experienced during casting do not develop a proper microstructure. Once made into powder, the alloy exhibits excellent processability using conventional consolidation and forming techniques, e.g., extrusion and rolling. GRCop-84 is strengthened by a combination of dispersion and precipitation strengthening by fine (50-500 nanometer (2-20 microinch)) Cr2Nb particles and Hall-Petch strengthening from a fine copper grain size. The presence of a high volume fraction of particles prevents grain boundary sliding at high temperatures and contributes to the alloy's overall good high temperature mechanical properties. Maximum thermal conductivity is obtained by using two alloying elements (Cr, Nb) with limited solubility in solid Cu that form a high temperature intermetallic compound with an even lower solid solubility. The resulting matrix of the alloy is nearly pure copper. The limited solubility also minimizes Cr2Nb particle coarsening at elevated temperatures and enhances microstructural and mechanical property stability. Further enhancement of the microstructural stability is obtained by using a high volume fraction (approx. 14 vol.%) of Cr2Nb particles that effectively pin grain growth.

Ellis, David L.↗

NASA NTRS1986

Ultrasonic characterization of microstructure in powder metal alloy

The ultrasonic wave propagation characteristics were measured for IN-100, a powder metallurgy alloy used for aircraft engine components. This material was as a model system for testing the feasibility of characterizing the microstructure of a variety of inhomogeneous media including powder metals, ceramics, castings and components. The data were obtained for a frequency range from about 2 to 20 MHz and were statistically averaged over numerous volume elements of the samples. Micrographical examination provided size and number distributions for grain and pore structure. The results showed that the predominant source for the ultrasonic attenuation and backscatter was a dense (approx. 100/cubic mm) distribution of small micropores (approx. 10 micron radius). Two samples with different micropore densities were studied in detail to test the feasibility of calculating from observed microstructural parameters the frequency dependence of the microstructural backscatter in the regime for which the wavelength is much larger than the size of the individual scattering centers. Excellent agreement was found between predicted and observed values so as to demonstrate the feasibility of solving the forward problem. The results suggest a way towards the nondestructive detection and characterization of anomalous distributions of micropores when conventional ultrasonic imaging is difficult. The findings are potentially significant toward the application of the early detection of porosity during the materials fabrication process and after manufacturing of potential sites for stress induced void coalescence leading to crack initiation and subsequent failure.

Tittmann, B. R.↗

NASA NTRS1990

A laboratory means to produce tough aluminum sheet from powder

The rapid solidification of aluminum alloys as powder and the subsequent fabrication processes can be used to develop and tailor alloys to satisfy specific aerospace design requirements, including high strength and toughness. Laboratory procedures to produce aluminum powder-metallurgy (PM) materials are efficient but require evidence that the laboratory methods used can produce a product with superior properties. This paper describes laboratory equipment and procedures which can be used to produce tough aluminum PM sheet. The processing of a 2124 + 0.9 percent Zr aluminum alloy powder is used as an example. The fully hardened sheet product is evaluated in terms of properties and microstructure. The key features of the vacuum hot press pressing operation used to consolidate the powder are described. The 2124 + 0.9 percent Zr - T8 temper aluminum sheet produced was both strong (460-490 MPa yield strength) and tough (Kahn Tear unit-propagation- energy values over three times those typical for ingot metallurgy 2024-T81). Both the longitudinal and longitudinal-transverse directions of the sheet were tested. The microstructure was well refined with subgrains of one or two micrometers. Fine dispersoids of Al3Zr in the precipitate free regions adjacent to boundaries are believed to contribute to the improved toughness.

Singleton, O. R.↗

DOE OSTI2025

Additive manufacturing of amorphous metal soft magnetic composites

Soft magnet alloys are used as magnetic cores for electric motors, transformers, wind turbines and other power generation systems. Soft magnetic cores are expensive and time consuming to manufacture in the complex shapes required for next-generation devices using conventional press and sinter powder metallurgy. The objective of this effort is to additively manufacture high performance soft magnets, with reduced cost and reduced material waste and 10x lower energy (core) loss at the high operating frequencies of many electric machines. Laser powder bed fusion additive manufacturing is used as the fabrication method. Electrical steel and amorphous alloys atomized powders are used as a feedstock materials. Magnetic cores are printed in topology optimized structures such as the Hilbert curve because this has been shown to reduce energy losses by minimizing the eddy currents that circulate within the magnet at high frequencies. In our project, we succeed in printing FeSi 3.5wt% and FeSi 6.5wt% electrical steels, and iron-based soft magnetic amorphous alloys in the shape of Hilbert and Peano curve topology optimized structures. We found that the Peano curve has a higher cut-off frequency than the Hilbert curve, and that amorphous alloys have high cut-off frequencies and higher mechanical hardness than electrical steels. Processing conditions such as laser power, scan speed, and hatching pattern were optimized to achieve high density prints, and optimize magnetic performance. We find that the printing of amorphous alloy soft magnetic cores may be technoeconomically feasible for large scale applications such as transformers, for which supply chain issues and the labor costs of manual fabrication of magnetic cores is prohibitive in some cases.

36 MATERIALS SCIENCE↗

NASA NTRS1996

Testing of electroformed deposited iridium/powder metallurgy rhenium rockets

High-temperature, oxidation-resistant chamber materials offer the thermal margin for high performance and extended lifetimes for radiation-cooled rockets. Rhenium (Re) coated with iridium (Ir) allow hours of operation at 2200 C on Earth-storable propellants. One process for manufacturing Ir/Re rocket chambers is the fabrication of Re substrates by powder metallurgy (PM) and the application of Ir coatings by using electroformed deposition (ED). ED Ir coatings, however, have been found to be porous and poorly adherent. The integrity of ED Ir coatings could be improved by densification after the electroforming process. This report summarizes the testing of two 22-N, ED Ir/PM Re rocket chambers that were subjected to post-deposition treatments in an effort to densify the Ir coating. One chamber was vacuum annealed, while the other chamber was subjected to hot isostatic pressure (HIP). The chambers were tested on gaseous oxygen/gaseous hydrogen propellants, at mixture ratios that simulated the oxidizing environments of Earth-storable propellants. ne annealed ED Ir/PM Re chamber was tested for a total of 24 firings and 4.58 hr at a mixture ratio of 4.2. After only 9 firings, the annealed ED Ir coating began to blister and spall upstream of the throat. The blistering and spalling were similar to what had been experienced with unannealed, as-deposited ED Ir coatings. The HIP ED Ir/PM Re chamber was tested for a total of 91 firings and 11.45 hr at mixture ratios of 3.2 and 4.2. The HIP ED Ir coating remained adherent to the Re substrate throughout testing; there were no visible signs of coating degradation. Metallography revealed, however, thinning of the HIP Ir coating and occasional pores in the Re layer upstream of the throat. Pinholes in the Ir coating may have provided a path for oxidation of the Re substrate at these locations. The HIP ED Ir coating proved to be more effective than vacuum annealed and as-deposited ED Ir. Further densification is still required to match the integrity of chemically vapor deposited Ir coatings. Despite this, the successful long duration testing of the HIP ED Ir chamber, in an oxidizing environment comparable to Earth-storable propellants, demonstrated the viability of this Ir/Re rocket fabrication process.

Reed, Brian D.↗

NASA NTRS1984

Effects of long-time elevated temperature exposures on hot-isostatically-pressed power-metallurgy Udimet 700 alloys with reduced cobalt contents

Because almost the entire U.S. consumption of cobalt depends on imports, this metal has been designated "strategic'. The role and effectiveness of cobalt is being evaluated in commercial nickel-base superalloys. Udiment 700 type alloys in which the cobalt content was reduced from the normal 17% down to 12.7%, 8.5%, 4.3%, and 0% were prepared by standard powder metallurgy techniques and hot isostatically pressed into billets. Mechanical testing and microstructural investigations were performed. The mechanical properties of alloys with reduced cobalt contents which were heat-treated identically were equal or better than those of the standard alloy, except that creep rates tended to increase as cobalt was reduced. The effects of long time exposures at 760 C on mechanical properties and at 760 C and 845 C on microstructures were determined. Decreased tensile properties and shorter rupture lives with increased creep rates were observed in alloy modifications. The exposures caused gamma prime particle coarsening and formation of sigma phase in the alloys with higher cobalt contents. Exposure at 845 C also reduced the amount of MC carbides.

Hart, F. H.↗

NASA NTRS2023

Additive Manufacturing of Oxide Dispersion Strengthened Multi Principle Element Alloys for Future Aerospace Applications

Oxide Dispersion Strengthened (ODS) materials have long been of interest for their high temperature applications, and additive manufacturing enables their manufacturing viability. The ODS multi-principle element alloy NiCoCr was prepared using powder metallurgy techniques, additively manufactured, and evaluated for its processingmicrostructure-property relationships. The high temperature foundations of nickel-base superalloys and ODS materials were combined with the manufacturing advantages of 3D printing and the chemical simplicity of NiCoCr to inspire this work, which was divided into powder and printed material assessments. The project was achieved through multiple iterative project loops to assess the processing parameters’ impact on the microstructure and mechanical properties of the feedstock powder and printed material. The powder investigations (Chapter 3) focused on understanding the oxide coating that formed on the metal powder following acoustic mixing. Time of Flight Secondary Ion Mass Spectrometry was used to semi-quantitatively assess the amount of yttrium on the surface of the mixed powders, and indicated that a combination of higher mixing condition energy and moderate mixing time resulted in the most oxide coating on the NiCoCr powder. The results were supported by a qualitative assessment of scanning electron images of coated powder particles. Following mixing, the ODS NiCoCr was consolidated by Laser Powder Bed Fusion. The evaluations of the printed material (Chapter 4) frst considered screening experiments including Archimedes’ density, porosity, and grain size and number metrics from electron backscatter diffraction data. After the ideal additive manufacturing parameters were identifed, both the oxide homogeneity and yield strength were discussed for the idealized printed material. Overall, the project suggests that the combined use of qualitative or semi-quantitative powder surface analysis with Archimedes’ density analyses can be a valid high-throughput technique which can lead to process optimization of Laser Powder Bed Fusion additively manufactured ODS material.

Laura G Wilson↗

DOE OSTI2025

Pressureless Sintering of Pre-Alloyed Nanostructured Bainitic Steel Powders

A recent study shows that powder metallurgy and pressureless sintering are a viable pathway to realize full-density bulk components of nanostructure bainitic steels. A scalable, pressureless supersolidus liquid phase sintering (SLPS) approach to process nanostructured bainitic steel is evaluated. Furthermore, to address the oxidation issues associated with the mechanical alloying of elemental powders, powder atomization is used to produce pre-alloyed nanostructured bainitic steel powders.

mechanical alloying↗

NASA NTRS1991

The PM-200 lubrication system

Plasma sprayed composite coating of metal-bonded chromium carbide with additions of silver and thermochemically stable fluorides were previously reported to be lubricative in pin on desk bench tests from room temperature to 900 C. An early coating formulation of this type, designated as PS-200, was successfully tested as a cylinder coating in a Stirling engine at a TRRT of 760 C in a hydrogen atmosphere, and as a backup lubricant for gas bearings to 650 C. A subsequent optimization program has shown that tribological properties are further improved by increasing the solid lubricant content. The improved coating is designated as PS-212. The same powder formulation was used to make free-standing powder metallurgy (PM-212) parts by sintering or hot isostatic pressing. The process is very attractive for making parts that cannot be readily plasma sprayed such as bushings and cylinders that have small bore diameters and/or high length to diameter ratios. The properties of coatings and free-standing parts fabricated from these powders are reviewed.

Sliney, Harold E.↗

DOE OSTI2025

Amorphous complexion-aided sintering enables scalable processing of bulk nanocrystalline Cu-Zr with high strength and compressive plasticity

Nanocrystalline alloys can have exceptional strengths, yet due to limited microstructural stability it is difficult to fabricate bulk pieces through traditional processing routes that retain nanosized grains. In this study, centimeter-sized Cu-Zr alloy pellets were fabricated via a simple and improved powder metallurgy processing route. Different consolidation temperatures and times were employed to investigate the effect of amorphous grain boundary complexions on densification and the resulting mechanical properties. Bulk compression tests were carried out, with the samples that were hot pressed at 900 °C for 10 h exhibiting an excellent combination of average yield strength of 722 ± 45 MPa and average failure strain of 25.3 ± 2.4 %. Furthermore, we find that a powder processing route which enables amorphous complexion-assisted sintering leads to samples that (1) reach full density without requiring quenching treatments or other complex processing, (2) demonstrate appreciable plasticity, and (3) have strength that competes with commercially available high-strength Cu alloys.

Bulk nanocrystalline alloy↗

NASA NTRS2013

Copper-Multiwall Carbon Nanotubes and Copper-Diamond Composites for Advanced Rocket Engines

This paper reports on the research effort to improve the thermal conductivity of the copper-based alloy NARloy-Z (Cu-3 wt.%Ag-0.5 wt.% Zr), the state-of-the-art alloy used to make combustion chamber liners in regeneratively-cooled liquid rocket engines, using nanotechnology. The approach was to embed high thermal conductivity multiwall carbon nanotubes (MWCNTs) and diamond (D) particles in the NARloy-Z matrix using powder metallurgy techniques. The thermal conductivity of MWCNTs and D have been reported to be 5 to 10 times that of NARloy-Z. Hence, 10 to 20 vol. % MWCNT finely dispersed in NARloy-Z matrix could nearly double the thermal conductivity, provided there is a good thermal bond between MWCNTs and copper matrix. Quantum mechanics-based modeling showed that zirconium (Zr) in NARloy-Z should form ZrC at the MWCNT-Cu interface and provide a good thermal bond. In this study, NARloy-Z powder was blended with MWCNTs in a ball mill, and the resulting mixture was consolidated under high pressure and temperature using Field Assisted Sintering Technology (FAST). Microstructural analysis showed that the MWCNTs, which were provided as tangles of MWCNTs by the manufacturer, did not detangle well during blending and formed clumps at the prior particle boundaries. The composites made form these powders showed lower thermal conductivity than the base NARloy-Z. To eliminate the observed physical agglomeration, tangled multiwall MWCNTs were separated by acid treatment and electroless plated with a thin layer of chromium to keep them separated during further processing. Separately, the thermal conductivities of MWCNTs used in this work were measured, and the results showed very low values, a major factor in the low thermal conductivity of the composite. On the other hand, D particles embedded in NARloy-Z matrix showed much improved thermal conductivity. Elemental analysis showed migration of Zr to the NARloy-Z-D interface to form ZrC, which appeared to provide a low contact thermal resistance. These results are consistent with the quantum mechanics-based model predictions. NARloy-Z-D composites have relatively high thermal conductivities and are promising for further development.

Bhat, Biliyar N.↗

NASA NTRS2013

Copper Multiwall Carbon Nanotubes and Copper-Diamond Composites for Advanced Rocket Engines

Bhat, Biliyar N.↗

NASA NTRS2007

Powder Processing of High Temperature Cermets and Carbides at Marshall Space Flight Center

The Materials and Processing Laboratory at NASA Marshall Space Flight Center is developing Powder Metallurgy (PM) processing techniques for high temperature cermet and carbide material consolidation. These new group of materials would be utilized in the nuclear core for Nuclear Thermal Rockets (NTR). Cermet materials offer several advantages for NTR such as retention of fission products and fuels, better thermal shock resistance, hydrogen compatibility, high thermal conductivity, and high strength. Carbide materials offer the highest operating temperatures but are sensitive to thermal stresses and are difficult to process. To support the effort, a new facility has been setup to process refractory metal, ceramic, carbides and depleted uranium-based powders. The facility inciudes inert atmosphere glove boxes for the handling of reactive powders, a high temperature furnace, and powder processing equipment used for blending, milling, and sieving. The effort is focused on basic research to identify the most promising compositions and processing techniques. Several PM processing methods including Cold and Hot Isostatic Pressing are being evaluated to fabricate samples for characterization and hot hydrogen testing.

Salvail, Pat↗

DOE OSTI2025

A comparison of plastic and visco-plastic constitutive models for accurate predictions in PM-HIP

Powder metallurgy hot isostatic pressing (PM-HIP) is an advanced manufacturing process that can efficiently produce near net shape parts with high material utilization and uniform microstructures. While the PM-HIP process is used frequently to produce small-scale components, its application to large-scale components is still limited due to inadequate understanding of its complex processes that cause unpredictable post-HIP shape distortions. A computational model can be a cost-effective alternative to exhaustive experimentation required to understand the PM-HIP process fully. Therefore, we present a comparison of plastic and visco-plastic models that are frequently used to model the PM-HIP process. We show that the predictions of powder densification behavior and shape distortions obtained from both the models are similar under most conditions and agree well with experimental observations.

Sarkar, Subrato [ORNL]↗