DOE OSTI2021

Transformations of Ti-5Al-5V-5Cr-3Mo powder due to reuse in laser powder bed fusion: A surface analytical approach

Reactive Ti-5Al-5 V-5Cr-3Mo (Ti5553) alloy feedstock powder is used in laser powder-bed fusion (LPBF). Due to the large quantity of powder necessary for LPBF, powder is reused numerous times under oxidizing environments. Transformations to the powder’s native surface oxide may impact the LPBF process and lead to deviations from expected behavior of printed parts. In this work, we present a multimodal characterization of new and reused powder by combining X-ray photoelectron spectroscopy (XPS), time-of-flight secondary ion mass spectrometry (ToF-SIMS), and transmission electron microscopy (TEM) of focused ion beam (FIB)-prepared cross sections of individual powder particles to understand how the surface oxide composition changes, grows, and becomes hydroxylated and hydrated due to reuse. We show that the native oxide film of Ti5553 powder is a hydroxylated mixed oxide composed of TiO 2 and Al 2 O 3 that grows from 5.6 +/- 0.7 nm to 8.3 +/- 1.1 nm due to reuse. Al oxide regions of the surface oxide become more hydroxylated during reuse in comparison to Ti oxide regions. This indicates that an outer oxide of pure TiO 2 may enhance recyclability of Ti5553 powder while the presence of Al oxides may decrease recyclability. Further characterization of surface transformations due to recyclability may eliminate unnecessary variation in LPBF.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Height-resolved emission spectroscopy and high-speed imaging of the TiAl6V4 vapor plume under laser powder bed fusion conditions

Optical emission spectroscopy is increasingly used as an in situ monitoring technique during laser powder bed fusion (LPBF) because plume emission holds elemental information not found in other in situ sensing techniques. This work explores the shape, stability, and temperature of the emission plume above the melt pool of Ti6Al4 V undergoing laser scans under LPBF-like processing conditions, using high-speed video and height-resolved spectroscopy to study the details of plume dynamics. Optical emission spectroscopy is conducted in the 480 nm to 525 nm region, where Ti emission is strong, with 0.3 mm vertical resolution above the baseplate. The Boltzmann plot method is used to determine temperature at each probed elevation, which indicates that the hottest location of the plume is occasionally elevated 0.3 mm to 0.6 mm above the scanning surface. The results show that the plume shape, stability, temperature, and spectra are highly dependent on the processing conditions. We highlight some of the complexities of optical emission spectroscopy and discuss potential challenges for implementing optical emission spectroscopy across an entire build.

36 MATERIALS SCIENCE↗
DOE OSTI2023

A framework for forming thermoset polymer networks during laser powder bed fusion additive manufacturing

It is commonly reported that the limited availability of material types is a major barrier to widespread adoption for polymer laser powder bed fusion (PBF/L) additive manufacturing (AM). A deeper understanding of the physico-chemical relationships between AM process stimuli and polymer responsive behavior is needed to make data-driven decisions for PBF/L specific material development and formulation. Many researchers have cumulatively built the current state of PBF/L “science-based manufacturing” framework where an initial guess for process parameter values can be determined from measured polymer properties and the first-principles of physics. However, published literature has focused on developing this framework for thermoplastic processing of polymers omitting many specific concerns unique to processing thermosetting materials. The authors consider in the present work the implications of many specific aspects unique to thermosetting polymers during PBF/L manufacturing. These aspects are contextually discussed according to the five sub-functions of PBF/L and are described mathematically where appropriate alongside example data from thermosetting materials commercially available in powder form. Further, this expansion of the prevailing material development framework to include thermosetting polymers paves the way for the unique performance properties offered by that class to be manifest through AM’s geometric freedom.

36 MATERIALS SCIENCE↗
DOE OSTI2026

A LASER POWDER BED FUSION ADDITIVE MANUFACTURING CHARACTERIZATION APPROACH AND DATASET HIGHLIGHTING IMPLICATIONS FOR CROSS-PLATFORM PERFORMANCE CONSISTENCY

Additive Manufacturing (AM) has remained a rapidly growing technology over the past decade, which affords many benefits. However, there is one main hinderance to widespread adoption: Products produced on one Laser Powder Bed Fusion (LPBF) AM system can vary in mechanical performance from those produced on another system. This is due to the fact that while LPBF AM system is producing a product’s shape, it is also producing the product’s material. Due to the complex and dynamic nature of LPBF, items fabricated on one system can be different in terms of dimensions, microstructure and quality compared to items fabricated on a different make or model system. This lack of cross-platform performance consistency makes widespread adoption challenging. This work was created to help understand the variation between different Laser Powder Bed Fusion (LPBF) Additive Manufacturing (AM) systems across different manufacturers, models, and users, and to provide insight into how to ensure product consistency regardless of system selection.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Effect of processing parameters and strut dimensions on the microstructures and hardness of stainless steel 316L lattice-emulating structures made by powder bed fusion

In this study, we present the effects of input processing parameters and strut thickness (in square struts) on microstructure and properties in laser powder bed fusion additively manufactured stainless steel 316L lattice-emulating structures. Lattice-emulating X-structures with square cross-sections of 1.5, 1.0, and 0.5 mm were fabricated using three different parameter sets with varying power, speed, and therefore, linear energy density. Grain size and morphology were shown to be dictated by epitaxial growth, which was dependent on weld pool morphology. Additionally, grain size and morphology were shown to change across the thickness direction of the struts (from the bottom inclined surface to the top inclined surface). The spatial variation in grain size was reflected by changes in hardness through the thickness of each strut. The 0.5 mm struts exhibited more significant grain elongation in the strut direction and larger sub-grain solidification cell diameters than their thicker counterparts. The larger sub-grain solidification cell diameters in the 0.5 mm samples resulted in correspondingly lower hardness values when compared to samples of higher thicknesses.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Laser Powder Bed Fusion Additive Manufacture Nb1Zr Development

Next generation fission and fusion nuclear reactors require materials that can withstand operating temperatures greater than 500 °C, neutron irradiation doses of up to 200 displacements per atom (dpa), and potentially corrosive coolants such as the alkali liquid metals sodium, lithium, and NaK (Na33K eutectic alloy). Refractory alloys, such as Nb1Zr (Nb-1wt%Zr) and Molybdenum alloy TZM (Mo-0.5wt%Ti-0.08wt%Zr) have been traditionally considered viable candidates for advanced fission and fusion reactor concepts. However, it is relatively difficult to generate complex geometries of interest from these alloys using traditional manufacturing methods. In addition, there needs to be a concentrated effort to address refractory metal challenges at elevated temperature operation. In order to generate complex geometries of interest, modern manufacturing techniques are considered to increase the technological readiness level (TRL), cost-effectiveness, and schedule savings. This work focused on the continued development of laser powder bed fusion (L-PBF) additive manufacturing (AM) to improve both design flexibility, evaluate microstructure and properties, and ultimately accelerate the TRL and qualification of these processes and alloys for components to potentially be put into service. Niobium alloy Nb1Zr was identified through a down-selection process outlined in previous reports as a candidate to develop in L-PBF AM. Historically, Nb1Zr had been explored for high temperature fast spectrum fission reactors for both terrestrial and space applications. Molybdenum alloy TZM has also been considered for these reactor concepts due to exceptional high-temperature strength, creep resistance, and stability under irradiation. L-PBF AM of TZM has previously been investigated at LANL under the Microreactor program, NASA, ORNL, and in academia. However, due to the crack prone nature of TZM, L-PBF AM of TZM resulted in significant microcracking and additional development is required to pursue viable maturation. Other AM methods have been found to be more successful in printing TZM, and those alternatives approaches are discussed in this effort. The efforts detailed in this report focused on continued development of Nb1Zr through L-PBF and development of TZM via L-PBF and electron powder bed fusion (E-PBF). The objective of this work was to further the development of these AM techniques for the chosen refractory alloys, elucidating and addressing associated challenges through characterization of several demonstration builds. At LANL, Nb1Zr builds were completed using an EOS M290 and M400 machines, and a refractory alloy-dedicated L-PBF system, the Xact Metal XM200G, was installed. The XM200G primary purpose was to do the Nb1Zr parameter development process; however, due to difficulties associated with the machine installation and qualification process, it was decided to pivot development to the larger M400 and M290 machines. Although the supply of Nb1Zr powder was limited, it was sufficient to generate sub-scale metallographic specimens for the purpose of parameter development. This was first accomplished on the EOS M400 then the M290 due to machine schedule availability. Further development of TZM has been initiated at the University of Texas El Paso (UTEP) under contract with LANL to use both a heated build envelope L-PBF machine and E-PBF machine that have been found in the literature to mitigate microcracking. UTEP was provided with TZM powder and build plates to support parallel TZM parameter development across both machines. As part of the contract, UTEP will also be conducting microstructural characterization once optimized process parameters have been identified. The optimized process parameters for each machine will be used to generate a series of metallographic, mechanical, and surface finish specimens for subsequent characterization and testing. In the next section, we provide a detailed discussion of the methodology used for investigating the feasibility of leveraging these alloys for use in advanced reactor applications.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Quantification of solution annealing effects on microstructure and property in a laser powder bed fusion 316H stainless steel

Solution annealing (SA) is an effective way to mitigate microstructural heterogeneity and to optimize mechanical performance of alloys manufactured by laser powder bed fusion (LPBF). In this study, a comprehensive and quantitative understanding of the recovery and recrystallization processes in the SA temperature range of LPBF 316H stainless steel is provided using results from analytical electron microscopy and in-situ high-energy synchrotron x-ray scattering. The profound effect of dislocation structures and secondary phase particles on mechanical performance, particularly under tension and creep conditions, is rationalized using deformation models that incorporate microstructural inputs. This study, for the first time, quantifies the broad effect of nano oxide inclusions on dislocation recovery kinetics, on grain growth and recrystallization kinetics, and on tension strength and creep resistance. The fundamental differences between the LPBF and the conventional wrought materials are revealed. The findings address critical questions in post-build processing of AM materials and pave the way for their rapid qualification for high temperature applications.

In-situ X-ray diffraction↗
DOE OSTI2023

A review on experimentally observed mechanical and microstructural characteristics of interfaces in multi-material laser powder bed fusion

Additive manufacturing (AM) is a revolutionary technology. One of the key AM categories, metal powder-based fusion processes, has many advantages compared to conventional methods for fabricating structural materials, such as permitting increased geometric complexity. While single material metal powder AM has advanced significantly in the past decade, multi-material AM is gradually attracting more attention owing to the recent breakthrough in multi-material feedstock delivery and the growing interest of fabricating functionally graded components. Multi-material AM offers an alternative route for applications that require location dependent material properties and high geometrical complexity. The AM community has invented several ways to achieve compositional gradients and discrete boundaries in two and three dimensions using mechanical spreading, nozzle-based, electrophotographic, and hybrid techniques. This article reviews the current state of laser powder bed fusion based multi-material AM of metals with focuses on the characteristics of the material interface as well as the properties and performance of the AM built functionally graded materials. We show the common challenges and issues related to material transitions, such as defects, segregation, phase separation, and the efficacy of some potential solutions including material and process optimizations. Additionally, this study evaluates the applicability and limitations of the existing testing standards and methods for measuring mechanical performance of functionally graded materials. Finally, we discuss mechanical testing development opportunities, which can help multi-material AM move towards higher technological maturity. In general, we find that the link between gradient microstructure and mechanical properties is not well understood or studied and suggest several mechanical tests that may better inform this knowledge gap.

42 ENGINEERING↗
DOE OSTI2026

Microstructural evolution, defect mitigation, and precipitation behavior in AA6061 via laser powder bed fusion with high-temperature substrate heating

Defects, particularly solidification cracking, remain persistent challenges in the laser powder bed fusion (LPBF) processing of AA6061 aluminum alloy. This study systematically investigates defect mitigation, microstructural evolution, and mechanical properties associated with high-temperature substrate preheating at 500 °C. Comprehensive microstructural analyses, including characterization of defects, grain structures, and precipitation behavior, were performed on samples in both as-built and T6 heat-treated states. Elevated preheating substantially reduced solidification cracking across a wide processing window, while demonstrating decreased crack sensitivity to laser parameters. Columnar cracks along the build direction were observed despite substrate preheating. Lack-of-fusion and keyhole porosity were effectively eliminated, though gas-induced microporosity persisted at higher powers. In-depth characterization of two distinct laser power and speed conditions confirmed the formation of micron-sized, non-coherent Mg 2 Si precipitates under heated substrate conditions, alongside α-AlFeCrMnSi intermetallic phases indicative of in-situ thermal effects during fabrication. Subsequent T6 heat treatment revealed the formation of fine, coherent needle-shaped β″ strengthening precipitates. Despite substantial differences in processing parameters, comparable mechanical properties were measured in the as-built samples (∼52 MPa yield strength, ∼130 MPa tensile strength), primarily due to reduced strain hardening effects and consistent precipitation characteristics. Meanwhile, the T6 heat treatment led to significant improvement in properties, enhancing yield strength by over 400%, aligning closely with the performance of conventional wrought AA6061-T6. These findings underscore that high-temperature substrate preheating offers an effective means to suppress cracks, control precipitation, and enhance mechanical performance in LPBF-processed AA6061.

36 MATERIALS SCIENCE↗
DOE OSTI2026

Nondestructive Modular Leak Detection in 3D Printed 316L Stainless Steel Pipes via Laser Powder Bed Fusion

This research investigates the leak detection features of 316L Stainless Steel pipe structures manufactured via Laser Powder Bed Fusion (LPBF). This work involves the design of a modular sensor system integrating nondestructive evaluation (NDE) methods, including thermal imaging and ultrasonic frequency detection to detect and characterize leaks in components. This aims to improve leak detection sensitivity within medium-pressure gas systems, during continuous operation without halting flow or introducing safety risks. The system could be adaptable for use on unmanned aerial vehicles (UAVs), enabling remote leak detection in active environments. A custom pneumatic system incorporating temperature and pressure sensors was assembled to detect leaks in LPBF-printed 316L SS tee pipes. Experimental results and simulations confirm the system’s effectiveness in leak detection and material evaluation. This research program also integrated a Python-based image recognition platform based on a metallography and optical microscopy to assess the porosity and complement the leak detection data on the printed structures. This allows a detailed analysis of pore distribution and internal leak paths, which could compromise structural integrity, critical for quality control during manufacturing. Findings suggest that the investigated approach holds potential for enhancing leak detection technologies and adapt them for advanced manufactured parts.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Comparison of powder bed fusion and directed energy deposition for tailoring mechanical properties of traditionally brittle alloys

The mechanical performance of an Fe-Co intermetallic alloy processed by laser powder bed fusion (L-PBF) and laser directed energy deposition (L-DED) additive manufacturing is compared. L-PBF material was characterized by high strength (500–550 MPa) and high ductility (35%) in tension, corresponding to a ~250% increase in strength and an order-of-magnitude improvement in ductility relative to conventional material. Conversely, L-DED material exhibited similarly poor tensile properties to the conventional wrought alloy, with low strength (200–300 MPa) and low ductility (0–2.7%). Finally, the disparity in properties between L-PBF and L-DED material is discussed in the context of the fundamental differences between manufacturing methods.

36 MATERIALS SCIENCE↗
NASA NTRSDate not supplied

In-Situ Process Monitoring, Synchronization, and Mapping Laser Powder Bed Fusion Builds of Ti6Al4V

The use of in-situ process monitoring is of interest to lower the cost of inspection for the qualification of laser powder bed fusion (LPBF) parts. Precise monitoring of the LPBF-AM build process constitutes a multi-scale and multi-discipline task. There are several significant challenges to the in-situ approach: the synchronization of sensor signals to process steps, the physical interpretation and classification of sensor signals, managing very large datasets, and comparing the inputs with the observed monitoring signals. At NASA Langley Research Center, a configurable architecture additive testbed has been developed to monitor the build process with synchronized sensors. The philosophy and method adopted for the synchronization of the cameras with laser power & position Ti-6Al-4V LPBF are described. The synchronized in-situ monitoring signals are compared with ex-situ nondestructive inspection and optical microscopy observations. Such comparisons permit a better understanding of how the sequential process actions of LPBF-AM can affect build quality.

Laser Powder Bed Fusion↗
DOE OSTI2021

Optimization of direct aging temperature of Ti free grade 300 maraging steel manufactured using laser powder bed fusion (LPBF)

Maraging steels are of interest to the tool and die industry owing to their high strength, toughness and machinability. Additive manufacturing technologies like laser powder bed fusion (LPBF) can result in a paradigm shift in the design of maraging steel tools. Here, the lack of precipitates, in combination with solute segregation and non-equilibrium microstructure in Grade 300 maraging steel fabricated via LPBF makes the steel amenable to strengthening via direct aging post fabrication instead of the conventional solution treatment and aging. In this study we have focused on optimizing the direct aging temperature for a Ti-free Grade 300 maraging steel fabricated via LPBF for two different aging times. Through strain hardening analysis and detailed microstructural characterization, we show that direct aging at a temperature of 440 °C for 6 h resulted in the best strength-ductility combination. Aging samples at a lower temperature or shorter time resulted in no strain hardening prior to necking as a result of lower fraction of reverted austenite, whereas aging samples at a higher temperature resulted in extensive recrystallization of martensite, coarsening of precipitates, and extensive austenite reversion, resulting in softening of the fabricated parts.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Microstructural effects on the rotating bending fatigue behavior of Ti–6Al–4V produced via laser powder bed fusion with novel heat treatments

The rotating bending fatigue (RBF) behavior (fully reversed, R = -1) of additively manufactured (AM) Ti–6Al–4V alloy produced via laser powder bed fusion (PBF-L) was investigated with respect to different microstructures achieved through novel heat treatments. The investigation herein seeks to elucidate the effect of microstructure by controlling variables that can affect fatigue behavior in Ti–6Al–4V, such as chemistry, porosity, and surface roughness. In order to control these variables, different hot isostatic pressing (HIP) treatments at 800 °C, 920 °C, and 1050 °C with a 920 °C temper were applied to three sets of Ti–6Al–4V cylinders that originated from the same PBF-L build, such that there were 30 tests per condition. After HIP treatment, the specimens were machined and tested. The highest runout stress was achieved after sub-β transus HIP at 800 °C for 2 h at 200 MPa of pressure. A significant drop in fatigue strength was attributed to large prior-β grains and grain boundary α resulting from super-β transus HIP treated specimens. In conclusion, for the sub-β transus HIP specimens, differences in fatigue strength were attributed to α lath thickness, relative dislocation density, and dislocation boundary strengthening.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Hypereutectic Al-Ce-X (X=Mn, Cr, V, Mo, W) alloys fabricated by laser powder-bed fusion

Here, we characterize the microstructures and high-temperature mechanical properties of Al-2Ce and ternary Al-2Ce-1X (at.%) alloys fabricated by laser powder-bed fusion (LPBF), where X = Mn, Cr, V, Mo, and W are slow-diffusing transition metals. All ternary alloys show a hypereutectic microstructure in the as-LPBF state, containing an interconnected network of eutectic Al 11 Ce 3 phases (~10 vol.%) and an additional population of submicron, equiaxed Al 20 CeX 2 primary precipitates (~10 vol.%) which are isomorphous among these five alloys. Similar microstructures are present in arc-melted rods and atomized powders but are coarser due to the slower cooling rates in these processes. The hardness of the as-LPBF ternary Al-Ce-X alloys (1300–1400 MPa) is higher than that of the binary Al-Ce alloy (~1100 MPa) due to the higher volume fraction of strengthening phases. Furthermore, during exposure at 400 °C for up to three months, greater hardness retention is achieved in the ternary Al-Ce-X alloys (65–75%) than in the binary Al-Ce alloy (~55%), which is attributed to the extreme coarsening resistance of the Al 20 CeX 2 precipitates imparted by the very slow-diffusing ternary solute. These coarsening-resistant Al 20 CeX 2 precipitates also substantially improve alloy creep resistance, increasing the threshold stress for dislocation creep at 300°C from ~32 MPa for the binary Al-Ce alloy to ~77–100 MPa for the ternary Al-Ce-X alloys, and at 400°C from <10 MPa for the binary Al-Ce alloy to >40 MPa for the ternary Al-Ce-V alloy.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Laser pre-sintering for denudation reduction in the laser powder bed fusion additive manufacturing of Ti-6Al-4V alloy

As a fundamentally different process for creation of complex parts, laser powder bed fusion (LPBF) additive manufacturing exhibits complex behavior at the melt pool that has a direct influence on the macroscopic properties of the final material. Powder denudation, a previously studied deleterious phenomenon, is the displacement of powder due to entrainment in a jet of rapidly vaporized metal created by the process laser. To minimize the effect of denudation and inspired by methods in adjacent fields, a laser pre-sintering (LPS) method was studied in an effort to reduce denudation. LPS was found to be most effective in the 1–4 J/mm3 volumetric energy density processing regimes, minimizing the common experimentally observed problems with the LPBF process. Scanning electron microscopy of the LPS-treated powder bed revealed insight into the accelerating effect morphological irregularities along the powder particle surface have in the pre-sintering process. To further understand the process, an estimation of the sintered neck sizes necessary to eliminate denudation in LPS is made, qualitatively affirming the low energy densities needed to prevent denudation. Here, the results presented in this work represent an initial step towards understanding and implementing LPS as a quality-enhancing step in LPBF.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Leveraging Solute Segregation in Laser Powder Bed Fusion to Achieve Superior Strength and Ductility Via Single-Step Heat Treatment in Ti-Free Grade 300 Maraging Steel

Maraging steels are Fe-Ni precipitation-strengthened steels that can be heat treated for achieving high strength with an accompanying loss in ductility, a trend common to most metals. Here, we show that the segregation of Ni during laser powder bed fusion, commonly considered a nuisance that is dealt with via solutionizing heat treatments, can be leveraged via direct aging to achieve higher strength and ductility simultaneously, compared to a solutionized and aged condition. The high dislocation density in combination with solute segregation in the as-fabricated material promotes the precipitation of Mo-rich intermetallic phases that are responsible for the high strength, and the Ni segregated regions facilitate austenite reversion during direct aging. The reverted austenite enhances the elongation via transformation-induced plasticity. While overcoming the strength–ductility conundrum, direct aging can significantly reduce the energy and emissions associated with multistep heat treatments, especially in the global tool and die industry, while laser powder bed fusion (LPBF) can enable tools with integrated cooling channels for increased downstream production efficiency.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Microstructure and strengthening of Al-6Ce-3Ni-0.7Fe (wt%) alloy manufactured by laser powder-bed fusion

In this study, an Al-6Ce-3Ni-0.7Fe (wt%) alloy was fabricated via laser powder-bed fusion and its microstructure, thermal stability, tensile properties, and creep properties are investigated for two rapid-solidification rates with different eutectic spacings. For both faster- and slower-cooled states, the as-fabricated alloy mostly shows elongated grains with very fine eutectic networks (~40 nm lamellar width) comprising a high-volume fraction (~18 %) of intermetallic phases. Faster-cooled samples, however, display a less continuous eutectic network with finer spacing (~100 nm), leading to higher Orowan strengthening and therefore superior microhardness and yield stress up to ~350 °C. Upon aging (300 - 450 °C), micron-size Al 9 (Ni,Fe) 2 needle-like precipitates form within grains, and the Al 11 Ce 3 eutectic network spheroidizes, while retaining a submicron width and spacing, resulting in 33–37 % drop in microhardness after 144 h aging at 400 °C. Limited tensile ductility (~6 %) and creep ductility (~1-2 %) are measured for both faster- and slower-cooled alloys due to an inhomogeneous microstructure, where cavitation preferentially initiates at melt-pool boundaries, precipitate-free zones, and/or denuded zones, eventually leading to local fracture. Denuded zones, induced by stress, form due to diffusional flow with stress-dependent orientations, and are identified as microstructurally weak regions leading to strain localization. The present alloy does not show a significant difference in 300 °C creep resistance between: (i) tensile and compressive loading, (ii) faster- and slower-cooled samples, and (iii) continuous and spheroidized eutectics. Creep resistance at 300 °C is comparable to that of a Ce-richer Al-10.5Ce-3.1Ni-1.2Mn (wt%) alloy, despite the formation of denuded zones and needle-like Al 9 (Ni,Fe) 2 precipitates.

36 MATERIALS SCIENCE↗