Concepts developed in study of SiO2/Si interface applied to analysis of native oxide/GaAs interface. High-resolution X-ray photoelectron spectroscopy (XPS) has been combined with precise chemical-profiling technique and resolution-enhancement methods to study stoichiometry of transitional layer. Results are presented in report now available.
Friction and wear experiments were conducted with elemental iron exposed to various corrosive media including two acids, base, and a salt. Studies involved various concentrations of nitric and sulfuric acids, sodium hydroxide, and sodium chloride. Load and reciprocating sliding speed were kept constant. With the base NaOH an increase in normality beyond 0.01 N resulted in a decrease in both friction and wear. X-ray photoelectron spectroscopy (XPS) analysis of the surface showed a decreasing concentration of ferric oxide (Fe2O3) on the iron surface with increasing NaOH concentration. With nitric acid (HNO3) friction decreased in solutions to 0.05 N, beyond which no further change in friction was observed. The concentration of Fe2O3 on the surface continued to increase with increasing normality. XPS analysis revealed the presence of sulfates in addition of Fe2O3 on surfaces exposed to sulfuric acid and iron chlorides but no sodium on surfaces exposed to NaCl.
X-ray photoelectron spectroscopy analyses and hardness experiments were conducted with cleaved magnesium oxide /001/ surfaces. The magnesium oxide bulk crystals were cleaved into specimens along the /001/ surface, and indentations were made on the cleaved surface in laboratory air, in nitrogen gas, or in degassed mineral oil with and without an additive while not exposing specimen surface to any other environment. The various additives examined contained sulfur, phosphorus, chlorine, or oleic acid. The sulfur-containing additive exhibited the highest hardness and smallest dislocation patterns evidencing plastic deformation; the chlorine-containing additive exhibited the lowest hardness and largest dislocation patterns evidencing plastic deformation. Hydrocarbon and chloride (MgCl2) films formed on the magnesium oxide surface. A chloride film was responsible for the lowest measured hardness.
The friction properties of some ferrous-base metallic glasses were measured both in argon and in vacuum to a temperature of 350 C. The alloy surfaces were also analyzed with X-ray photoelectron spectroscopy to identify the compounds and elements present on the surface. The results of the investigation indicate that even when the surfaces of the amorphous alloys, or metallic glasses, are atomically clean, bulk contaminants such as boric oxide and silicon dioxide diffuse to the surfaces. Friction measurements in both argon and vacuum indicate that the alloys exhibit higher coefficients of friction in the crystalline state than they do in the amorphous state.
X-ray photoelectron spectroscopy analysis, transmission electron microscopy, diffraction studies, and sliding friction experiments were conducted with ferrous-base metallic glasses in sliding contact with aluminum oxide at temperatures from room to 750 C in a vacuum of 30 nPa. The results indicate that there is a significant temperature influence on the friction properties, surface chemistry, and microstructure of metallic glasses. The relative concentrations of the various constituents at the surface of the sputtered specimens were very different from the normal bulk compositions. Contaminants can come from the bulk of the material to the surface upon heating and impart boric oxide and silicon oxide at 350 C and boron nitride above 500 C. The coefficient of friction increased with increasing temperature to 350 C. Above 500 C the coefficient of friction decreased rapidly. The segregation of contaminants may be responsible for the friction behavior.
Tribological studies and X-ray photoelectron spectroscopy analyses were conducted with sintered polycrystalline and single crystal silicon carbide surfaces in sliding contact with iron at various temperatures to 1500 C in a vacuum of 30 nPa. The results indicate that there is a significant temperature influence on both the friction properties and the surface chemistry of silicon carbide. The main contaminants on the as received sintered polycrystalline silicon carbide surfaces are adsorbed carbon, oxygen, graphite, and silicon dioxide. The surface revealed a low coefficient of friction. This is due to the presence of the graphite on the surface. At temperatures of 400 to 600 C graphite and copious amount of silicon dioxide were observed on the polycrystalline silicon carbide surface in addition to silicon carbide. At 800 C, the amount of the silicon dioxide decreased rapidly and the silicon carbide type silicon and carbon peaks were at a maximum intensity in the XPS spectra. The coefficients of friction were high in the temperature range 400 to 800 C. Small amounts of carbon and oxygen contaminants were observed on the as received single crystal silicon carbide surface below 250 C. Silicon carbide type silicon and carbon peaks were seen on the silicon carbide in addition to very small amount of graphite and silicon dioxide at temperatures of 450 to 800 C.
X-ray photoelectron spectroscopy analyses and hardness experiments were conducted on cleaved magnesium oxide /001/ surfaces. The magnesium oxide bulk crystals were cleaved to specimen size along the /001/ surface, and indentations were made on the cleaved surface in corrosive solutions containing HCl, NaOH, or HNO3 and in water without exposing the specimen to any other environment. The results indicated that chloride (such as MgCl2) and sodium films are formed on the magnesium oxide surface as a result of interactions between an HCl-containing solution and a cleaved magnesium oxide surface. The chloride films soften the magnesium oxide surface. In this case microhardness is strongly influenced by the pH value of the solution. The lower the pH, the lower the microhardness. Sodium films, which are formed on the magnesium oxide surface exposed to an NaOH containing solution, do not soften the magnesium oxide surface.
The effect of implanted oxygen impurities on the Ni/Ni2Si interface is investigated using X-ray photoelectron spectroscopy, He-4(+) backscattering and O(d, alpha)-16 N-14 nuclear reactions. Oxygen dosages corresponding to concentrations of 1, 2, and 3 atomic percent were implanted into Ni films evaporated on Si substrates. The oxygen, nickel, and silicon core lines were monitored as a function of time during in situ growth of the Ni silicide to determine the chemical nature of the diffusion barrier which forms in the presence of oxygen impurities. Analysis of the Ni, Si, and O core levels demonstrates that the formation of SiO2 is responsible for the Ni diffusion barrier rather than Ni oxide or mixed oxides, such as Ni2SiO4. It is determined that 2.2 x 10 to the 16th O/qu cm is sufficient to prevent Ni diffusion under UHV annealing conditions.
The valence level spectra of the Ni/Si and Pd/Si systems have been investigated using high resolution X-ray photoelectron spectroscopy. Temperature dependence studies for Ni deposited on thin thermal SiO2 demonstrate the importance of metal aggregation effects in the interpretation of binding energies as chemical shifts. Temperature studies for the Ni/Si system indicate that substantial chemical interaction occurs at the interface at temperatures as low as 100 K. These studies also show the presence of Ni in interstitial voids in the Si near the interface. A comparative study of the core and valence band features for the Ni and Pd silicides provides many valuable insights and a self-consistent picture of the attendent valence charge redistribution and its influence on the observed chemical shifts.
Silicon carbide surfaces were heated to 1500 C in a vacuum and analyzed at room temperature with X-ray photoelectron spectroscopy (XPS) and Auger electron spectroscopy (AES). The basic unit of the surfaces was considered as a plane of a tetrahedron of either SiC4 and CSi4 composition. AES spectra were obtained from 250-1500 C, with an analysis depth of 1 nm revealed the presence of little Si and mostly graphite. XPS analysis depth was 2 nm or less, and Si was found in the second 1 nm. Sliding friction tests with single-crystal silicon carbide in contact with iron in a vacuum were characterized by a stock-slip value. The coefficient of friction increased with increasing temperature up to 400 C, then decreased with increasing temperature from 400-600 C. Reheating surfaces to 800 C after preheating them to that temperature produced no changes in AES readings. It is concluded that the maximum density of silicon and silicon-carbide is at 800 C, and the higher the sliding temperature, the more metal that is transferred.
The considered investigation shows that the adhesion of evaporated Ni on polytetrafluoroethylene (PTFE) is enhanced by irradiating the PTFE surface prior to evaporation. Evidence obtained with the aid of X-ray photoelectron spectroscopy is presented concerning the association of the enhanced adhesion with an interfacial chemical reaction. Evaporated Ni clearly adheres better to the X-ray damaged PTFE surface than to the undamaged surface. There is evidence that the improved adhesion is not related to the Ni-C bond, but rather to the NiF2. A possible mechanism which may be consistent with the data is the formation of a F-Ni-C complex, where C is a member of the polymer chain.
The use of scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS) in the analysis of Ti 6-4 adherend surfaces is described. Differences in Ti 6-4 surface composition as determined by XPS after different chemical pretreatments are detailed. Analysis of fractured surfaces by SEM/XPS is used to establish the failure mode. The surface acidity of Ti 6-4 coupons can be established by reflectance visible spectroscopy using indicator dyes.
Using synchrotron radiation as a continuum background, the absorption spectrum of CO in the 380-470 A range was taken by using a double ion chamber. A Rydberg series in the 450 A (27.5 eV) region has been observed to converge to the F 2Pi, a two-electron excited state of CO(+). The series limit determined at 28.11 eV is in excellent agreement with the vertical ionization potential of the F 2Pi state measured by the high resolution photoelectron spectroscopy. A few dissociation processes leading to the productions of atomic ions and excited atomic fragments are also discussed.
A loaded spherical aluminum oxider rider was made to slide, while in various solutions, on a flat iron or nickel surface reciprocate a distance of 1 cm. Time of experiments was 1 hr during which the rider passed over the rider passed over the center section of the track 540 times. Coefficients of friction were measured throughout the experiments. Wear was measured by scanning the track with a profilometer. Analysis of some of the wear tracks included use of the SEM (scanning electron microscrope) and XPS (X-ray photoelectron spectroscopy). Investigated were the effect of various concentractions of NaOH and of water. On iron, increasing NaOH concentration above 0.01 N caused the friction and wear to decrease. This decrease is accompanied by a decrease in surface concentration of ferric oxide (Fe2O3) while more complex iron-oxygen compounds, not clearly identified, also form. At low concentrations of NaOH, such as 0.01 N, where the friction is high, the wear track is badely torn up and the surface is broken. At high concentration, such as 10 N, where the friction is low, the wear track is smooth. The general conclusion is that NaOH forms a protective, low friction film on iron which is destroyed by wear at low concentrations but remains intact at high concentrations of NaOH. Nickel behaves differently than iron in that only a little NaOH gives a low coefficient of friction and a surface which, although roughened in the wear track, remains intact.
The role of the interfacial region in determining the bond strength and durability of composite bonds is discussed. The characterization of a variety of carbon fibers including Celion 6000 using both scanning electron microscopy and X-ray photoelectron spectroscopy is discussed. The emphasis is on composite bonding, that is, the adhesive bonding between composites in contrast to fiber-matrix interaction. The primary objective of the research is the characterization of composite surfaces before adhesive bonding and after fracture of bonded specimens. Work done on the analysis of composite samples pretreated in a number of ways prior to bonding is detailed.
A pin-on-disk tribometer equipped with an induction heater was used to study the coefficient of friction as a function of temperature for tricresylphosphate (TCP) on continuous vacuum melted (CVM) M-50 tool steel when the TCP was present in a liquid reservoir (bulk lubrication), and when it was applied as a liquid layer directly to the disk (limited lubrication). Under limited lubrication conditions, experiments were performed in dry ( 100 ppm H2O) air, dry ( 20 ppm H2O) nitrogen, dry nitrogen with the disks heated to 700 C then cooled to room temperature before the TCP was applied and the measurements made (preheated disks), and moist nitrogen using preheated disks. When the coefficient of friction was plotted as a function of the disk temperature, the friction decreased at a characteristic temperature, T sub r whose observed values were 265 C for bulk lubrication conditions in dry air, 225 C for limited lubrication conditions in dry air, and 215 C for limited lubrication conditions in dry nitrogen. No decrease in friction was observed with preheated disks; instead a sharp failure temperature was observed at 218 C, which was taken as the temperature about which the behavior of TCP should be judged, X-ray photoelectron spectroscopy confirmed the presence of phosphate on the surface of the iron pins used in the tribometer under TCP lubrication. Depth profile studies support the idea that a chemical reaction occurs between the TCP and the metal surface at T sub r.
Sliding friction experiments, X-ray photoelectron spectroscopy (XPS) analysis, and electron microscopy and diffraction studies were conducted with ferrous base metallic glasses (amorphous alloys) in contact with aluminum oxide at temperatures to 750 C in a vacuum. Sliding friction experiments were also conducted in argon and air atmospheres. The results of the investigation indicate that the coefficient of friction increases with increasing temperature to 350 C in vacuum. The increase in friction is due to an increase in adhesion resulting from surface segregation of boric oxide and/or silicon oxide to the surface of the foil. Above 500 C the coefficient of friction decreased rapidly. The decrease correlates with the segregation of boron nitride to the surface. Contaminants can come from the bulk of the material to the surface upon heating and impart boric oxide and/or silicon oxide at 350 C and boron nitride above 500 C. The segregation of contaminants is responsible for the friction behavior. The amorphous alloys have superior wear resistance to crystalline 304 stainless steel. The relative concentrations of the various constituents at the surfaces of the amorphous alloys are very different from the nominal bulk compositions.
Because tricresyl-phosphate (TCP) is a common antiwear additive in lubricants, there is great interest in its interactions with metal substrates. The TCP was allowed to adsorb on polycrystalline iron and gold at room temperature. X-ray photoelectron spectroscopy (XPS) was used to analyze the adsorbed species. The substrate was then heated in steps to 330 C, and the changes in the adsorbate were analyzed after each step. On both substrates saturation adsorption occurred at about one monolayer, but the sticking coefficient was less on gold than on iron. Comparison of the XPS spectra of TCP on each substrate with the spectrum from condensed TCP indicated nondissociative adsorption on gold, possibly by dipole-induced dipole interaction. On iron, there was apparently additional interaction between the substrate and the tolyl groups on the TCP molecule. TCP began to desorb molecularly from gold as soon as the gold was heated above room temperature. The desorption was complete by 200 C. However, when the iron substrate was heated, TCP did not desorb but decomposed between 150 and 250 C.