Composition, response to pressure, and negative thermal expansion in M II B IV F 6 (M = Ca, Mg; B = Zr, Nb) [Composition, response to pressure, and negative thermal expansion in A II B IV F 6 ; A - Ca, Mg, B - Zr, Nb]
CaZrF 6 has recently been shown to combine strong negative thermal expansion (NTE) over a very wide temperature range (at least 10–1000 K) with optical transparency from mid-IR into the UV range. Variable-temperature and high-pressure diffraction has been used to determine how the replacement of calcium by magnesium and zirconium by niobium(IV) modifies the phase behavior and physical properties of the compound. Similar to CaZrF 6 , CaNbF 6 retains a cubic ReO 3 -type structure down to 10 K and displays NTE up until at least 900 K. It undergoes a reconstructive phase transition upon compression to ~400 MPa at room temperature and pressure-induced amorphization above ~4 GPa. Prior to the first transition, it displays very strong pressure-induced softening. MgZrF 6 adopts a cubic ( Fm$\bar{3}$m ) structure at 300 K and undergoes a symmetry-lowering phase transition involving octahedral tilts at ~100 K. Immediately above this transition, it shows modest NTE. Its’ thermal expansion increases upon heating, crossing through zero at ~500 K. Unlike CaZrF 6 and CaNbF 6 , it undergoes an octahedral tilting transition upon compression (~370 MPa) prior to a reconstructive transition at ~1 GPa. Cubic MgZrF 6 displays both pressure-induced softening and stiffening upon heating. MgNbF 6 is cubic ( Fm$\bar{3}$m ) at room temperature, but it undergoes a symmetry-lowering octahedral tilting transition at ~280 K. It does not display NTE within the investigated temperature range (100–950 K). Furthermore the replacement of Zr(IV) by Nb(IV) leads to minor changes in phase behavior and properties, the replacement of the calcium by the smaller and more polarizing magnesium leads to large changes in both phase behavior and thermal expansion.