Results for “fracture behavior”

Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

SourceResearch connectionFrom yearThrough year

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

At least 145 records · Page 8

All sources NASA NTRS DOE OSTI

NASA NTRS1980

Notched graphite polymimide composites at room and notched graphite polymide composites at room and elevated temperatures

The fracture behavior in graphite/polyimide (Gr/PI) Celion 6000/PMR-15 composites was characterized. Emphasis was placed on the correlation between the observed failure modes and the deformation characteristics of center-notched Gr/Pl laminates. Crack tip damage growth, fracture strength and notch sensitivity, and the associated characterization methods were also examined. Special attention was given to nondestructive evaluation of internal damage and damage growth, techniques such as acoustic emission, X-ray radiography, and ultrasonic C-scan. Microstructural studies using scanning electron microscopy, photomicrography, and the pulsed nuclear magnetic resonance technique were employed as well. All experimental procedures and techniques are described and a summary of representative results for Gr/Pl laminates is given.

Awerbuch, J.↗

NASA NTRS1991

Elevated temperature fracture of RS/PM aluminum alloy 8009

The fracture behavior of advanced powder metallurgy Al-Fe-V-Si alloy 8009 (previously called FVS0812) is being characterized under monotonic loads, as a function of temperature. Particular attention is focused on contributions to the fracture mechanism from the fine grained dispersoid strengthened microstructure, dissolved solute from rapid solidification, and the moist air environment. Time-dependent crack growth is characterized in advanced aluminum alloys at elevated temperatures with the fracture mechanics approach, and cracking mechanisms are examined with a metallurgical approach. Specific tasks were to obtain standard load crack growth experimental information from a refined testing system; to correlate crack growth kinetics with the j-integral and time dependent C(sub t)(t); and to investigate the intermediate temperature embrittlement of 8009 alloy in order to understand crack growth mechanisms.

Porr, William C., Jr.↗

NASA NTRS1985

Fracture and crack growth in orthotropic laminates

A mathematical model based on the classical shear-lag assumptions is used to study the residual strength and fracture behavior of composite laminates with symmetrically placed buffer strips. The laminate is loaded by a uniform remote longitudinal tensile strain and has initial damage in the form of a transverse crack in the parent laminate between buffer strips. The crack growth behavior as a function of material properties, number of buffer-strip plies, spacing, width of buffer strips, longitudinal matrix splitting, and debonding at the interface is studied. Buffer-strip laminates are shown to arrest fracture and increase the residual strengths significantly over those of one material laminates, with S-glass being a more effective buffer strip material than Kevlar in increasing the damage tolerance of graphite/epoxy panels. For a typical graphite/epoxy laminate with S-glass buffer-strips, the residual strength is about 2.4 times the residual strength of an all graphite/epoxy panel with the same crack length. Approximately 50% of this increase is due to the S-glass/epoxy buffer-strips, 40% due to longitudinal splitting of the buffer strip interface and 10% due to bonding.

Goree, James G.↗

NASA NTRS1987

A fractographic investigation of the influence of stacking sequence on the strength of notched laminated composites

The fracture behavior of T300/5208 CFRP laminate panels with 12 different combinations of ply orientation and stacking sequence is investigated experimentally, using optical microscopy, SEM, and X-ray radiography to characterize the notch-tip damage zones and fracture surfaces of center-cracked tension specimens subjected to tensile loading at constant crosshead displacement rate 20 micron/s. The results are presented graphically and analyzed in detail. Significant differences in notched strength are found for different ply fiber orientations and stacking sequences; the laminates with few major delaminations had a greater percentage of fracture due to broken fibers and also higher notched strength.

Harris, Charles E.↗

NASA NTRS1999

Experimental Verification of Computational Models for Laminated Composites

The objective of the research reported herein is to develop a progressive damage methodology capable of predicting the residual strength of continuous fiber-reinforced, laminated, polymer matrix composites with through-penetration damage. The fracture behavior of center-notch tension panels with thin crack-like slits was studied. Since fibers are the major load-carrying constituent in polymer matrix composites, predicting the residual strength of a laminate requires a criterion for fiber fracture. The effects on fiber strain due to other damage mechanisms such as matrix cracking and delaminations must also be modeled. Therefore, the research herein examines the damage mechanisms involved in translaminate fracture and identifies the toughening mechanisms responsible for damage growth resistance in brittle epoxy matrix systems. The mechanics of matrix cracking and fiber fracture are discussed as is the mathematical framework for the progressive damage model developed by the authors. The progressive damage analysis algorithms have been implemented into a general purpose finite element code developed by NASA, the Computational Structural Mechanics Testbed (COMET). Damage growth is numerically simulated and the analytical residual strength predictions are compared to experimental results for a variety of notched panel configurations and materials systems.

Harris, Charles E.↗

NASA NTRS2019

Myco-Architecture off Planet: Growing Surface Structures at Destination

Our work focused on filling major select key technical knowledge gaps, and technical aspects to be addressed in a Phase II proposal were identified such as the secretion of glues or plastics by the fungi or bacteria to form biocomposites. Specifically, we raised the technical TRL by assessing the growth of in-house mycelial-producing strains on potential food substrates and analyzed the advantages and disadvantages to their use off planet. Growth of the mycelia on sawdust and powdered nutrients including dried, powdered algae, was used as a baseline. We measured growth as a function of temperature, tested the relevant material properties of the mycelia products produced, and measured the mass of input and output volume for production per volume of material. Mycotecture was produced in a bag simulating the proposed mission implementation. Post-production such as heat treatment (as is done with terrestrial mycotecture)was assessed.The material properties of the dried, frozen and baked mycelial outputs included density, strength,thermal insulation and flame retardation. Tensile/compression testing on biocomposite material specimens was performed to obtain three-dimensional elastic constants, as well as to examine deformation and fracture behavior. These mechanical tests were performed on both dormant and activated samples to understand the evolution of the structural material. In addition, experimental data obtained from the mechanical testing was used to build a failure prediction model that accounts for material anisotropy. This aided in future structural design through a quantitative understanding of the mechanical limits of the material. To examine the texture, defects, fracture surfaces of the material, high-resolution microstructural imaging was utilized before and after the mechanical tests. This microstructural analysis informed us about the macro-structural behavior and influenced structural design. Thermal decomposition analysis was also performed tounderstand the thermal limits.

Biocomposites↗

NASA NTRS1971

Friction, wear, and lubrication in vacuum

A review of studies and observations on the friction, wear, and lubrication behavior of materials in a vacuum environment is presented. The factors that determine and influence friction and wear are discussed. They include topographical, physical, mechanical, and the chemical nature of the surface. The effects of bulk properties such as deformation characteristics, fracture behavior, and structure are included.

Buckley, D. H.↗

NASA NTRS1985

Fracture of thick graphite/epoxy laminates with part-through surface flaws

Fracture behavior of tensile specimens containing through-the-thickness flaws and part-through semi-elliptic surface flaws was investigated. The material was T300/5208 graphite/epoxy, with a stacking sequence 0/+ or - 45/90 sub ns. Laminate thicknesses ranged from 8 to 120 plies. Fracture toughness for specimens with through-the-thickness flaws was a function of laminate thickness. Fracture toughness was also independent of crack size. Fracture toughness for the thick laminates was also independent of specimen geometry (center-cracked tension specimen, compact tension specimen, and three-point bend specimen). Using the asymptotic value of facture toughness and linear elastic isotropic fracture mechanics, the notched strength of tensile specimens with semi-elliptic surface flaws was predicted. The strength ratio is a function of the flaw depth (a/t) and flaw aspect (a/c) ratios. Comparisons between predicted and experimental strengths are good for large values of a/t. The notched strength of filament wound graphite/epoxy tensile specimens with part-through surface flaws was also predicted.

Morris, D. H.↗

NASA NTRS1986

Fracture of thick graphite/epoxy laminates with part-through surface flaws

Fracture behavior of tensile specimens containing through-the-thickness flaws and part-through semi-elliptic surface flaws was investigated. The material was T300/5208 graphite/epoxy, with a stacking sequence 0/+ or - 45/90 sub ns. Laminate thicknesses ranged from 8 to 120 plies. Fracture toughness for specimens with through-the-thickness flaws was a function of laminate thickness. Fracture toughness was also independent of crack size. Fracture toughness for the thick laminates was also independent of specimen geometry (center-cracked tension specimen, compact tension specimen, and three-point bend specimen). Using the asymptotic value of fracture toughness and linear elastic isotropic fracture mechanics, the notched strength of tensile specimens with semi-elliptic surface flaws was predicted. The strength ratio is a function of the flaw depth (a/t) and flaw aspect (a/c) ratios. Comparisons between predicted and experimental strengths are good for large values of a/t. The notched strength of filament wound graphite/epoxy tensile specimens with part-through surface flaws was also predicted.

Harris, C. E.↗

NASA NTRS2015

Mechanical Properties of Air Plasma Sprayed Environmental Barrier Coating (EBC) Materials

Development work in Environmental Barrier Coatings (EBCs) for Ceramic Matrix Composites (CMCs) has focused considerably on the identification of materials systems and coating architectures to meet application needs. The evolution of these systems has occurred so quickly that modeling efforts and requisite data for modeling lag considerably behind development. Materials property data exists for many systems in the bulk form, but the effects of deposition on the critical properties of strength and fracture behavior are not well studied. We have plasma sprayed bulk samples of baseline EBC materials (silicon, ytterbium disilicate) and tested the mechanical properties of these materials to elicit differences in strength and toughness. We have also endeavored to assess the mixed-mode fracture resistance, Gc, of silicon in a baseline EBC applied to SiCSiC CMC via four point bend test. These results are compared to previously determined properties of the comparable bulk material.

Ceramic Matrix Composites (CMC's)↗

NASA NTRS1975

Hot tensile properties and deformation response of a gamma/Ni/-gamma prime/Ni3Al/-delta/Ni3Nb/ eutectic composite

Three distinct regions of tensile, deformation and fracture behavior were observed in a 2.5 wt. per cent Al gamma/gamma prime-delta eutectic alloy as the testing temperature was varied. The major finding was an extraordinary ductility maximum at about 550 C. It was shown that this phenomenon is caused by the deflection of transverse cracks at the eutectic grain boundaries when yielding occurs. This delamination between eutectics grains caused by fracture of a gamma prime eutectic grain boundary film leads to a distinctly different 'wood-like' fracture surface morphology. Above 690 C to 926 C, yield and tensile strength values decrease while ductility increase slightly. Cooperative twinning of both phases develops giving rise to block-like deformation of the microstructure quite in parallel to the behavior observed previously in the gamma-delta system.

Bertorello, H. R.↗

NASA NTRS2003

Advances in Structural Integrity Analysis Methods for Aging Metallic Airframe Structures with Local Damage

Analysis methodologies for predicting fatigue-crack growth from rivet holes in panels subjected to cyclic loads and for predicting the residual strength of aluminum fuselage structures with cracks and subjected to combined internal pressure and mechanical loads are described. The fatigue-crack growth analysis methodology is based on small-crack theory and a plasticity induced crack-closure model, and the effect of a corrosive environment on crack-growth rate is included. The residual strength analysis methodology is based on the critical crack-tip-opening-angle fracture criterion that characterizes the fracture behavior of a material of interest, and a geometric and material nonlinear finite element shell analysis code that performs the structural analysis of the fuselage structure of interest. The methodologies have been verified experimentally for structures ranging from laboratory coupons to full-scale structural components. Analytical and experimental results based on these methodologies are described and compared for laboratory coupons and flat panels, small-scale pressurized shells, and full-scale curved stiffened panels. The residual strength analysis methodology is sufficiently general to include the effects of multiple-site damage on structural behavior.

fatigue-crack growth↗

NASA NTRS1980

Anisotropic Tribological Properties of Silicon Carbide

The anisotropic friction, deformation and fracture behavior of single crystal silicon carbide surfaces were investigated in two categories. The categories were called adhesive and abrasive wear processes, respectively. In the adhesive wear process, the adhesion, friction and wear of silicon carbide were markedly dependent on crystallographic orientation. The force to reestablish the shearing fracture of adhesive bond at the interface between silicon carbide and metal was the lowest in the preferred orientation of silicon carbide slip system. The fracturing of silicon carbide occurred near the adhesive bond to metal and it was due to primary cleavages of both prismatic (10(-1)0) and basal (0001) planes.

Miyoshi, K.↗

NASA NTRSDate not supplied

Interlaminar R-Curve Effects in Thermoplastic Composites: Experiments and Model Correlations

The interlaminar fracture behavior of thermoplastic composites under Mode-I and Mode-II static loading is investigated in this research. The material system under consideration is a carbon fiber reinforced low melt semi-crystalline resin TC1225 LMPAEK T700G (T700/LMPAEK)†. Characterization experiments were conducted to measure the load-displacement response, peak load, and propagation of delamination from a pre-implanted Kapton® insert. The Mode-I response was characterized using a double cantilever beam (DCB) test according to the ASTM D5528-22 standard. It was observed that the propagation exhibited significant resistance to delamination growth, i.e., an R-Curve effect. The test data indicated that the steady-state fracture toughness, G SS I , was approximately twice the mean initiation fracture toughness, G Ic . The Mode-II response of an end notch flexure (ENF) specimen tested according to the ASTM D7905-19 standard exhibited an unexpected stable behavior upon attaining peak load. Prior to attaining peak load, the Mode-II response exhibited some non-linearity, which may be attributed to nonlinear bulk material response, e.g., hyper-elasticity, viscoelasticity, plasticity, etc., and potentially friction at the load/support rollers and R-Curve effects. Finite element models based on the Cohesive Zone Method (CZM) and the Virtual Crack Closure Technique (VCCT) were used to predict the DCB and ENF specimen responses. DCB analysis results obtained using G SS I predicted propagation consistent with experimental data. However, results obtained with the as characterized G Ic were inaccurate in predicting delamination growth onset and peak load. ENF analysis results obtained with the as-characterized Mode-II fracture toughness, G IIc , were inaccurate in predicting the peak load and propagation. Hence, R-Curve effects were included in both DCB and ENF simulations, which enabled improved predictions. The experimentally determined Mode-I R-Curve was used for the DCB simulations, whereas an R-Curve was derived for Mode-II assuming that the change in compliance of the specimen was associated with crack growth only.

Prabhakar M Rao↗

NASA NTRSDate not supplied

Interlaminar R-Curve Effects in Thermoplastic Composites: Experiments and Model Correlations

Prabhakar Rao↗

NASA NTRS2013

Applications of Automation Methods for Nonlinear Fracture Test Analysis

As fracture mechanics material testing evolves, the governing test standards continue to be refined to better reflect the latest understanding of the physics of the fracture processes involved. The traditional format of ASTM fracture testing standards, utilizing equations expressed directly in the text of the standard to assess the experimental result, is self-limiting in the complexity that can be reasonably captured. The use of automated analysis techniques to draw upon a rich, detailed solution database for assessing fracture mechanics tests provides a foundation for a new approach to testing standards that enables routine users to obtain highly reliable assessments of tests involving complex, non-linear fracture behavior. Herein, the case for automating the analysis of tests of surface cracks in tension in the elastic-plastic regime is utilized as an example of how such a database can be generated and implemented for use in the ASTM standards framework. The presented approach forms a bridge between the equation-based fracture testing standards of today and the next generation of standards solving complex problems through analysis automation.

Allen, Phillip A.↗

NASA NTRS1985

Influence of voids on the strength of wrought materials

Three-dimensional voids, which are present in most materials, may be satisfactorily modelled by two-dimensional holes (i.e., cylindrical voids) in sheet metal. In this study, the influence of certain orientations and shapes of voids upon the mechanical properties and fracture behavior of certain ductile materials has been studied. The presence of voids is found to exert a negligible influence on the ultimate tensile strength, owing to plastic flow neutralizing the stress intensification present before yielding occurs. The shape and orientation of the defects, however, are seen to play an important role relative to strain at fracture. The maximum intensified tensile stress criterion which holds for brittle materials is found to apply to ductile materials as well.

Shaw, M. C.↗

NASA NTRS1991

Combined mode I-mode III fracture toughness of a particulate reinforced metal-matrix composite

The aim of this investigation was to determine the fracture behavior of a particulate reinfored aluminum alloy composite under combined mode I-mode III loading conditions. A modified three-point bend specimen was used to carry out these tests. It was found that the mode I loading condition was energetically most favorable. Addition of mode III components to the system seems to increase the amount of redundant work during fracture without affecting the critical fracture criterion.

Manoharan, M.↗