Correlation between grain boundary misorientation and M{sub 23}C{sub 6} precipitation behaviors in a wrought Ni-based superalloy
The correlation between the grain boundary misorientation and the precipitation behaviors of intergranular M{sub 23}C{sub 6} carbides in a wrought Ni–Cr–W superalloy was investigated by using the electron backscattered diffraction (EBSD) technique. It was observed that the grain boundaries with a misorientation angle less than 20°, as well as all coincidence site lattice (CSL) boundaries, are immune to precipitation of the M{sub 23}C{sub 6} carbides; in contrast, the random high-angle grain boundaries with a misorientation angle of 20°–40° provide preferential precipitation sites of the M{sub 23}C{sub 6} carbides at the random high-angle grain boundaries with a higher misorientation angle of 55°–60°/[2 2 3] turn to retard precipitation of M{sub 23}C{sub 6} carbides owing to their nature like the Σ3 grain boundaries and retard the precipitation of M{sub 23}C{sub 6} carbides. The low-angle and certain random grain boundary segments induced by twins were found to interrupt the precipitation of the M{sub 23}C{sub 6} carbides along the high-angle grain boundaries. - Highlights: ► The low angle grain boundaries and CSL boundaries are immune to precipitation. ► M23C6 precipitate preferentially at random grain boundaries within 20°–40°. ► Some certain random grain boundary segments interrupt M23C6 precipitation.