SEARCH · Engineering Papers

Results for “microstructural properties”

Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

SourceResearch connectionFrom yearThrough year

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

At least 127 records · Page 7

All sources NASA NTRS DOE OSTI

NASA NTRS1996

Effects of thermomechanical processing on the microstructure and mechanical properties of Nb-1Zr-C alloys

A systematic study to evaluate the effects of thermomechanical processing on the microstructure and mechanical properties of Nb-1Zr alloy sheet containing 0.06 and 0.1 wt.%C (PWC-11) was conducted and compared to the results of Nb-1Zr. Coarse orthorhombic Nb2C precipitates were present in all the cast, extruded and cold rolled Nb-Zr samples containing C. After high temperature (greater than 0.5 T(sub m)) exposure (with or without applied stress), the Nb2C transforms to very fine and extremely stable FCC (Zr, Nb)C dispersoid, resulting in a highly creep resistant material. Only ZrO2 precipitates were found in Nb-1Zr. The creep strength of the 0.06C and the 0.1C carbide strengthened alloys were much superior to Nb-1Zr. At 1350 K the strength of the 0.06C alloy was about three times that of Nb-1Zr, while the 0.1C alloy had about five times the creep stress capability of Nb-1Zr. The tensile strength, long term creep strength, and stability of the microstructure of the PWC-11 sheet appear to be independent of the number of 1900 K extrusions performed prior to cold rolling. The microhardness of these single, double and triple extnided PWC-11 sheets also were comparable. The tensile strength of PWC-11 and Nb-1Zr at room temperature and 1350 K were comparable.

Titran, Robert H.↗

NASA NTRS1992

Effect of braze processing on the microstructure and mechanical properties of SCS-6/beta21S titanium matrix composites

An investigation is conducted of the effects of braze processing on the microstructure and tensile properties of SiC fiber-reinforced Ti-15Mo-2.7Nb-3Al-0.25Si-matrix composite (TMC) laminates; the brazing alloy was the commercial Ti-15Cu-15Ni, in both its conventional and metglass forms. Tensile tests conducted at room temperature, 1200 F, and 1500 F showed that the braze processes (1) had little effect on tensile properties, and (2) appeared to degrade neither the reinforcing fibers not the fiber/matrix interfacial bondline.

Hoffman, Eric K.↗

NASA NTRSDate not supplied

Microstructure and Mechanical Properties of Additively Manufactured Haynes 282: A Comparative Analysis between L-PBF and LP-DED Technologies

This study compares the microstructure and tensile properties of Haynes 282 fabricated using laser powder bed fusion and laser powder directed energy deposition. Both sets underwent stress-relieving, followed by hot isostatic pressing, and the standard double aging heat treatment. Tensile testing was conducted at room temperature on specimens fabricated with both technologies to evaluate and compare their tensile behaviors. Results show that the ultimate tensile and yield strengths of laser powder bed fused specimens were 18% and 57% higher, respectively than those of laser powder directed energy deposited ones, whereas the elongation to failure was similar in both. The difference in strengths is attributed to the differences in the size of ɣ' precipitates and grains, i.e., those in the LP-DED specimens being larger, whereas similar elongation to failure is attributed to the carbide debonding dominating the fracture mechanism in both batches.

Additive manufacturing↗

NASA NTRS1998

Surface Chemistry, Microstructure, and Tribological Properties of Cubic Boron Nitride Films

This report deals with the surface chemistry, microstructure, bonding state, morphology, and friction and wear properties of cubic boron nitride (c-BN) films that were synthesized by magnetically enhanced plasma ion plating. Several analytical techniques - x-ray photoelectron spectroscopy, transmission electron microscopy and electron diffraction, Fourier transform infrared spectroscopy, atomic force microscopy, and surface profilometry - were used to characterize the films. Sliding friction experiments using a ball-on-disk configuration were conducted for the c-BN films in sliding contact with 440C stainless-steel balls at room temperature in ultrahigh vacuum (pressure, 10(exp -6), in ambient air, and under water lubrication. Results indicate that the boron-to-nitrogen ratio on the surface of the as-deposited c-BN film is greater than 1 and that not all the boron is present as boron nitride but a small percentage is present as an oxide. Both in air and under water lubrication, the c-BN film in sliding contact with steel showed a low wear rate, whereas a high wear rate was observed in vacuum. In air and under water lubrication, c-BN exhibited wear resistance superior to that of amorphous boron nitride, titanium nitride, and titanium carbide.

Watanabe, Shuichi↗

NASA NTRS1991

The effect of copper, chromium, and zirconium on the microstructure and mechanical properties of Al-Zn-Mg-Cu alloys

The present study evaluates the effect of the systematic variation of copper, chromium, and zirconium contents on the microstructure and mechanical properties of a 7000-type aluminum alloy. Fracture toughness and tensile properties are evaluated for each alloy in both the peak aging, T8, and the overaging, T73, conditions. Results show that dimpled rupture essentially characterize the fracture process in these alloys. In the T8 condition, a significant loss of toughness is observed for alloys containing 2.5 pct Cu due to the increase in the quantity of Al-Cu-Mg-rich S-phase particles. An examination of T8 alloys at constant Cu levels shows that Zr-bearing alloys exhibit higher strength and toughness than the Cr-bearing alloys. In the T73 condition, Cr-bearing alloys are inherently tougher than Zr-bearing alloys. A void nucleation and growth mechanism accounts for the loss of toughness in these alloys with increasing copper content.

Wagner, John A.↗

NASA NTRS1998

Microstructure and Mechanical Properties of Reaction-Formed Joints in Reaction Bonded Silicon Carbide Ceramics

A reaction-bonded silicon carbide (RB-SiC) ceramic material (Carborundum's Cerastar RB-SIC) has been joined using a reaction forming approach. Microstructure and mechanical properties of three types of reaction-formed joints (350 micron, 50-55 micron, and 20-25 micron thick) have been evaluated. Thick (approximately 350 micron) joints consist mainly of silicon with a small amount of silicon carbide. The flexural strength of thick joints is about 44 plus or minus 2 MPa, and fracture always occurs at the joints. The microscopic examination of fracture surfaces of specimens with thick joints tested at room temperature revealed the failure mode to be typically brittle. Thin joints (<50-55 micron) consist of silicon carbide and silicon phases. The room and high temperature flexural strengths of thin (<50-55 micron) reaction-formed joints have been found to be at least equal to that of the bulk Cerastar RB-SIC materials because the flexure bars fracture away from the joint regions. In this case, the fracture origins appear to be inhomogeneities inside the parent material. This was always found to be the case for thin joints tested at temperatures up to 1350C in air. This observation suggests that the strength of Cerastar RB-SIC material containing a thin joint is not limited by the joint strength but by the strength of the bulk (parent) materials.

Singh, M.↗

NASA NTRS1987

Effect of high-temperature annealing on the microstructure and thermoelectric properties of GaP doped SiGe

Annealing of GaP doped SiGe will significantly alter the thermoelectric properties of the material resulting in increased performance as measured by the figure of merit Z and the power factor P. The microstructures and corresponding thermoelectric properties after annealing in the 1100 to 1300 C temperature range have been examined to correlate performance improvement with annealing history. The figure of merit and power factor were both improved by homogenizing the material and limiting the amount of cross-doping. Annealing at 1215 C for 100 hr resulted in the best combination of thermoelectric properties with a resultant figure of merit exceeding 1x10 to the -3 deg C to the -1 and a power factor of 44 microW/cm/deg C sq for the temperature range of interest for space power: 400 to 1000 C.

Draper, Susan L.↗

NASA NTRS1987

The microstructure and tensile properties of extruded melt-spun ribbons of iron-rich B2 FeAl

The microstructure of extruded rods of iron-rich FeAl(B2-structure), as characterized by TEM, SEM, optical microscopy and x-ray diffractometry, consisted of elongated grains with a 111-line fibre texture containing a high dislocation density. Numerous oxide particles were found, mostly in lines which reflected the matrix flow during extrusion. In addition, some large inclusions were present. Tensile testing of annealed, relatively dislocation-free specimens as a function of increasing temperature found increasing ductility up to 900K, above which a ductility drop occurred accompanied by a change in fracture mode, from transgranular cleavage to intergranular fracture. The yield strength, which was independent of temperature up to 800K (at about 500MPa), also decreased rapidly as diffusion became more important. The predominant slip vector changed from 111-line to 100-line around 700K.

Baker, I.↗

NASA NTRS1978

Microstructure and mechanical properties of quenched and tempered 300M steel

Type 300M steel, which is being used for the landing gear on the space shuttle orbiter, was subjected to a wide range of quenched and tempered heat treatments. The plane-strain fracture toughness and the tensile ultimate and yield strengths were evaluated. Cryogenic mechanical properties were obtained for conventionally heat-treated steel. The microstructure of all heat-treated test coupons was studied both optically and by transmission electron microscopy. Fracture surfaces were studied by means of scanning electron microscopy. Results indicate that substantial improvement in toughness with no loss in strength can be accomplished in quenched and tempered steel by austenitizing at 1255 K or higher. Low fracture toughness in conventionally austenitized 300M steel (1144 K) appears to be caused by undissolved precipitates, seen both in the submicrostructure and on the fracture surface, which promote failure by quasi-cleavage. The precipitates appeared to dissolve in the range 1200 to 1255 K.

Youngblood, J. L.↗

NASA NTRS1980

Microstructure and mechanical properties of hip-consolidated Rene 95 powders

The effects of heat-treatments on the microstructure of P/M Rene 95 (a nickel-based powder metal), consolidated by the hot-isostatic pressing (HIP), were examined. The microstructure of as-HIP'd specimen was characterized by highly serrated grain boundaries. Mechanical tests and microstructural observations reveal that the serrated grain boundaries improved ductility at both room and elevated temperatures by retarding crack propagation along grain boundaries.

Shimanuki, Y.↗

NASA NTRS1989

Microstructure and tensile properties of Fe-40 at. pct Al alloys with C, Zr, Hf, and B additions

The influence of small additions of C, Zr, and Hf, alone or in combination with B, on the microstructure and tensile behavior of substoichiometric FeAl was investigated. Tensile properties were determined from 300 to 1100 K on powder which was consolidated by hot extrusion. All materials possessed some ductility at room temperature, although ternary additions generally reduced ductility compared to the binary alloy. Adding B to the C- and Zr-containing alloys changed the fracture mode from intergranular to transgranular and restored the ductility to approximately 5 percent elongation. Additions of Zr and Hf increased strength up to about 900 K. Fe6Al6Zr and Fe6Al6Hf precipitates, both with identical body-centered tetragonal structures, were identified as the principal second phase in these alloys. Strength decreased steadily as temperature increased above 700 K, as diffusion-assisted mechanisms became operative. Although all alloys had similar strengths at 1100 K, Hf additions significantly improved high-temperature ductility by suppressing cavitation.

Gaydosh, D. J.↗

NASA NTRS1997

Microstructure and Mechanical Properties of Vacuum Plasma Sprayed Cu-8Cr-4Nb

This paper compares the tensile properties of Cu-8Cr-4Nb material produced by VPS to material previously produced by extrusion. The microstructure of the VPS material is also presented. The combustion chamber liner of rocket motors represents an extreme materials application. The liner hot wall is exposed to a 2760 C (5000 F) flame while the cold side is exposed to cryogenic hydrogen liquid. Materials for use in the combustion chamber liner require a combination of high temperature strength, creep resistance, and low cycle fatigue resistance along with high thermal conductivity. The hot side is also subject to localized cycles between reducing and oxidizing environments that degrade the liner by a process called blanching. A new Cu-8 at.% Cr-4 at% Nb (Cu-8Cr-4Nb) alloy has been developed at NASA Lewis Research Center as a replacement for the currently used alloy, NARloy-z (Cu-3 wt.% Ag-0.5 wt.% Zr). The alloy is strengthened by a fine dispersion of Cr2Nb particles. The alloy has better mechanical properties than NARloy-Z while retaining most of the thermal conductivity of pure copper. The alloy has been successfully consolidated by extrusion and hot isostatic pressing (HIPing). However, vacuum plasma spraying (VPS) offers several advantages over prior consolidation methods. VPS can produce a near net shape piece with the profile of the liner. In addition, oxidation resistant and thermal barrier coatings can be incorporated as an integral part of the liner hot wall during the VPS deposition. The low oxygen VPS Cu-8Cr-4Nb exhibits a higher strength than Cu-8Cr-4Nb produced by extrusion at elevated temperatures and a comparable strength at room temperature. Moduli and ductility were not significantly different. However, the ability to produce parts to near-net shape and maintain the good elevated temperature tensile properties of the extruded Cu-8Cr-4Nb makes VPS an attractive processing method for fabricating rocket engine combustion liners.

Holmes, Richard↗

NASA NTRS1972

A study of the microstructure and optical properties of thin lead-dielectric cermet films

A transmission electron microscopy study involving direct and replicating techniques is directed to a definition of the microstructure of radio frequency-sputtered, thin lead-dielectric cermet films. Once defined, this microstructure is used to obtain theoretical film refractive indices. The Maxwell Garnett theory provides a basis for the theoretical results. Measurements of film transmission and reflectivity are used to obtain rough experimental values for film refractive indices by the Tekucheva method. More exact values are obtained via ellipsometry. The rough Tekucheva values are used to determine the range over which computer calculations interpreting the ellipsometric results must be made. This technique yields accurate values for the film refractive indices.

Owen, R. B.↗

NASA NTRS1995

Effect of Nb2O5 and V2O5 addition on the superconducting properties of YBa2Cu3O(y) thin films

The effect of Nb2O5 and V2O5 addition on the superconducting properties and microstructure of YBa2Cu3O(y) has been studied in thin films. Polycrystalline targets for laser ablation were prepared by mixing high purity V2O5 or Nb2O5 powders with a well characterized YBa2Cu3O(y) powder in the range 0 to 4 wt percent by solid state reaction method. Thin films (approximately 1500 A thickness) of the above targets were grown on (100) SrTiO3 (STO) and (100) LaAlO3 (LAO) substrates at 700 C temperature by pulsed laser deposition (PLD) technique. In the case of Nb2O5 addition we have noticed an increase in J(sub c) up to 0.5 wt percent and higher additive concentration (greater than 0.5 wt percent) have degraded the superconducting properties. However, in the case of V2O3 addition, there is an improvement in current density and microstructural properties up to 1 wt percent and the superconducting properties degrade for concentrations greater than 1 wt percent. The best J(sub c) for 0.5 wt percent of Nb2O5 added YBCO thin film is 1.6 x 10(exp 6) A/sq cm and for that of V2O5 added sample is 3.4 x 10(exp 6) A/sq cm at 77 K as compared to the pure YBa2Cu3O(y) (YBCO) film J(sub c) (1.2 x 10(exp 6) A/sq cm) observed on STO substrates. The reason for improvement in J(sub c) and microstructural properties in the case of V2O5 addition could be due to the low melting of V2O5 (690 C) which can act as a very good surfactant during deposition. Over all, we have realized that Nb2O5 addition or V2O5 addition to YBCO have shown significant improvement over the undoped YBa2Cu3O(7-x) films grown under identical conditions.

Srinivas, S.↗

NASA NTRSDate not supplied

3D Printed Ceramic Reinforced Polymer Composites Microstructure and Mechanical Properties

In Fused Filament Fabrication (FFF) 3D printing a part is made by extruding material layer by layer. Benefits of FFF are the ability to print complex shapes quickly and at a lower cost compared to other manufacturing methods. In this work, filaments composed of either silicon carbide (SiC) or zirconium silicate ceramic particulates in a polylactic-acid (PLA) matrix were used to print specimens for microstructural analysis and mechanical testing. Pure PLA samples were also printed and tested as a baseline for comparison. A Design of Experiments approach was used to test the interactions between three different parameters and their effect on ultimate strength, Young’s modulus, and yield strength. For compression test specimens, these parameters were infill percentage, number of shells, and print orientation angle. For tensile test specimens, the parameters were layer height, number of shells, and infill orientation angle. Pre- and post-compression test samples were evaluated by scanning electron microscopy for microstructural analysis. Infill percentage had the greatest effect on mechanical properties while number of shells and print orientation angle had minor effects. When changing the layer lines from perpendicular to parallel, relative to the loading direction, SiC-PLA had higher mechanical properties while pure PLA properties had decreased, and zirconium silicate-PLA had mix results.

Fused filament fabrication↗

NASA NTRS1999

The Effect of Microstructure on Mechanical Properties of Directionally Solidified Al2O3/ZrO2(Y2O3) Eutectic

The eutectic architecture of a continuous reinforcing phase within a higher volume fraction phase or matrix can be described as a naturally occurring in-situ composite. Here we report the results of experiments aimed at identifying the sources of high temperature creep resistance and high levels of strength in a two phase Al2O3/ZrO2(Y2O3) system. The mechanical properties of two phase Al2O3/ZrO2(Y2O3) eutectic are superior to those of either constituent alone due to strong constraining effects provided by the coherent interfaces and microstructure. The AlO3/ZrO2(Y2O3) eutectic maintains a low energy interface resulting from directional solidification and can produce strong and stable reinforcing phase/matrix bonding. The phases comprising a eutectic are thermodynamically compatible at higher homologous temperatures than man-made composites and as such offer the potential for superior high temperature properties.

Sayir, Ali↗

NASA NTRS1991

Microstructure and mechanical properties of a single crystal NiAl alloy with Zr or Hf rich G-phase precipitates

The possibility of producing NiAl reinforced with the G-phase (Ni16X6Si7), where X is Zr or Hf, has been investigated. The microstructure of these NiAl alloys have been characterized in the as-cast and annealed conditions. The G-phases are present as fine cuboidal precipitates (10 to 40 nm) and have lattice parameters almost four times that of NiAl. They are coherent with the matrix and fairly resistant to coarsening during annealing heat treatments. Segregation and nonuniform precipitate distribution observed in as-cast materials were eliminated by homogenization at temperatures near 1600 K. Slow cooling from these temperatures resulted in large plate shaped precipitates, denuded zones, and a loss of coherency in some of the large particles. Faster cooling produced a homogeneous fine distribution of cuboidal G-phase particles in the matrix. Preliminary mechanical properties for the Zr-doped alloy are presented and compared to binary single crystal NiAl. The presence of these precipitates appears to have an important strengthening effect at temperatures not less than 1000 K compared to binary NiAl single crystals.

Locci, I. E.↗

NASA NTRS1992

Influence of Processing on the Microstructure and Mechanical Properties of a NbAl3-Base Alloy

Induction melting and rapid solidification processing, followed by grinding to 75-micron powder and P/M consolidation, have been used to produce a multiphase, NbAl3-based, oxidation-resistant alloy of Nb-67Al-7Cr-0.5Y-0.25W composition whose strength and ductility are significantly higher than those of the induction-melted alloy at test temperatures of up to 1200 K. Attention is given to the beneficial role of microstructural refinement; the major second phase, AlNbCr, improves both oxidation resistance and mechanical properties.

Hebsur, Mohan G.↗