NASA NTRSDate not supplied

Characterizing the Effects of Thermal Profile and Gas Environment on the Heat Treatment of JSC-1A Lunar Simulant Using Combined Thermogravimetry and Mass Spectroscopy

As NASA strives towards a long duration presence on the Moon, it has become increasingly important to learn how to better utilize resources from the lunar surface for everything from habitats, vehicle infrastructure, and chemical extraction. To that end, a variety of lunar simulants have been sourced from terrestrially available volcanic minerals and glass as Apollo regolith is a finite resource unavailable for experimentation needing large masses. However, while mineralogy and chemical composition can approach that of lunar material in these simulants, there are still distinct non-lunar phases such as hydrates, carbonates, sulfates, and clays that can cause simulants to behave distinctly non-lunar in a variety of processing conditions that would ideally be applied to lunar material. Notably, severe glassy bubbling has been documented in a variety of vacuum sintering experiments on JSC-1A lunar Maria simulant heated via microwaves. The origins of this outgassing have not been well understood, but are normally attributed to the decomposition of non-lunar contaminates intrinsic to virtually all terrestrially sourced simulants. As such, a series of controlled environmental tests were performed to ascertain the origins of the high temperature outgassing and to develop heat treatments that can drive JSC-1A closer to lunar composition and behavior. It was found that in JSC-1A that distinct gas evolutions of water, carbon dioxide, and sulfur dioxide occur in both inert gas and vacuum. Additionally, the presence of hydrogen during heat treatments was shown to dramatically change gas evolutions, leading to distinctly more lunar-like composition and behavior from JSC-1A simulant.

sinter↗
NASA NTRSDate not supplied

Characterizing the Effects of Thermal Profile and Gas Environment on the Heat Treatment of JSC-1A Lunar Simulant Using Combined Thermogravimetry and Mass Spectroscopy

As NASA strives towards a long duration presence on the Moon, it has become increasingly important to learn how to better utilize resources from the lunar surface for everything from habitats, vehicle infrastructure, and chemical extraction. To that end, a variety of lunar simulants have been sourced from terrestrially available volcanic minerals and glass as Apollo regolith is a finite resource unavailable for experimentation needing large masses. However, while mineralogy and chemical composition can approach that of lunar material in these simulants, there are still distinct non-lunar phases such as hydrates, carbonates, sulfates, and clays that can cause simulants to behave distinctly non-lunar in a variety of processing conditions that would ideally be applied to lunar material. Notably, severe glassy bubbling has been documented in a variety of vacuum sintering experiments on JSC-1A lunar Maria simulant heated via microwaves. The origins of this outgassing have not been well understood, but are normally attributed to the decomposition of non-lunar contaminates intrinsic to virtually all terrestrially sourced simulants. As such, a series of controlled environmental tests were performed to ascertain the origins of the high temperature outgassing and to develop heat treatments that can drive JSC-1A closer to lunar composition and behavior. It was found that in JSC-1A that distinct gas evolutions of water, carbon dioxide, and sulfur dioxide occur in both inert gas and vacuum. Additionally, the presence of hydrogen during heat treatments was shown to dramatically change gas evolutions, leading to distinctly more lunar-like composition and behavior from JSC-1A simulant.

sinter↗
NASA NTRS1993

Improved Heat Treatment Of Steel Alloy 4340

New process takes significantly less time than prior heat-treatment processes. Involves placing steel plate directly in furnace and heat-treating. Plate then quenched in slowly moving oil to reduce stresses. Any deflection then pressed out. Possible uses of 4340 steel include new and improved bulletproof vests for military and police personnel and armor for bulletproof automobiles for military, police, diplomatic, and private users. Also used in other military land vehicles as tanks and in both military and civilian aircraft. Lighter armorplate enables land vehicles and aircraft to attain greater speed and maneuverability, consume less fuel, and afford better protection from snipers or terrorists.

Cooper, Lawrence B.↗
NASA NTRS2016

Impact Toughness and Heat Treatment for Cast Aluminum

A method for transforming a cast component made of modified aluminum alloy by increasing the impact toughness coefficient using minimal heat and energy. The aluminum alloy is modified to contain 0.55%-0.60% magnesium, 0.10%-0.15% titanium or zirconium, less than 0.07% iron, a silicon-tomagnesium product ratio of 4.0, and less than 0.15% total impurities. The shortened heat treatment requires an initial heating at 1,000deg F. for up to I hour followed by a water quench and a second heating at 350deg F. to 390deg F. for up to I hour. An optional short bake paint cycle or powder coating process further increase.

Lee, Jonathan A↗
DOE OSTI2025

Effect of post-weld heat treatment on microstructure and mechanical properties of rotary inertia friction welded dissimilar 422-4140 martensitic steel piston joints

The study investigated how post‐weld heat treatment (PWHT) temperature affects the microstructure and localized deformation/fracture during bend testing of rotary inertia friction welds (RIFW) between AISI 422 stainless steel and AISI 4140 steel. RIFW produced a fully martensitic interface with approximately 550 HV hardness in both the thermo-mechanically affected (TMAZ) and heat‐affected zones (HAZ). Due to differences in temper resistance, the 4140 TMAZ/HAZ softened progressively under PWHT temperatures from 525 °C to 700 °C, while the 422 TMAZ unexpectedly maintained about 550 HV up to 600 °C before significantly softening at temperatures ≥625 °C. This asymmetric softening generated steep hardness gradients across the interface at temperatures ≤600 °C. Furthermore, carbon migration across the interface was minimal up to 600 °C, moderate at 625 °C, and by 700 °C produced a carbide‐rich eutectoid layer in the 422 TMAZ alongside a carbon‐depleted soft ferrite layer in the 4140 TMAZ. Strain during bending was PWHT‐dependent, concentrating on the 4140 side; in as-welded joints, the high hardness led to deformation and crack initiation in the base metals, whereas in PWHT samples, cracking initiated in the softened 4140 TMAZ near the interface. The intermediate PWHT temperature of 625 °C offered the best balance of limited carbon diffusion across the interface, relatively low peak weld hardness and minimized hardness gradients across the interface, more homogenous deformation, and good bend test performance.

4140 low-alloy steel↗
NASA NTRS1972

Changes in some physical properties induced by vacuum heat treatment

A method is proposed for reducing or eliminating outgassing of materials by heat treating them in vacuum prior to use. This may be performed on the raw material prior to manufacturing and installation or after fabrication of parts. Processing of a fabricated part can be performed only on relatively small parts and on assemblies containing no components which are affected by the required temperatures and pressures. Processing conditions of temperature and time are dependent on the particular application and the materials involved. Silicone-coated fiber glass cloth was vacuum-heat treated for 100 hrs at 400 + or - 25 F at pressures of 0.001 torr or less. The materials were tested in terms of tensile strength and tear properties in both the smooth and several creased configurations. Data obtained on one side silicone coated fiber glass showed large reductions in these properties as a result of the vacuum-heat treatment. The problem was alleviated by coating both sides of the fiber glass.

Hultquist, A. E.↗
NASA NTRS2018

Location-Specific Microstructure and the Effect of Heat Treatment on Electron-Beam Melted Ni-Based Superalloy LSHR

Examine set-to-set variability with 4 build sets with the same layout Establish the effect of solutioning heat treatments (HT) on as-fabricated grain structure and microstructure – (gamma)’-solvus= 1156 ºC (1) As-fabricated (2) 2 hour subsolvus HT(-15 ºC) + conventional 2-step aging (3, 4, 5) 0.5 hour, 2 hours, 4 hours supersolvus HT (+18 ºC) + 2 step aging Gain insight into location-specific microstructure to correlate later to mechanical properties (tensile, creep, LCF behavior)

heat treatment↗
DOE OSTI2021

Temperature and time effects of post-weld heat treatments on tensile properties and microstructure of Zircaloy-4

Opportunities exist to expand the application of Zircaloy-4 (Zry-4) into lower-temperature (<100°C) applications. Welded areas within these structures are potential failure points and post-weld heat treatments (PWHTs) are not yet standardized for application in this temperature range. Zry-4 tungsten inert gas (TIG) welds were given PWHTs from 450-900°C with hold times from 0.5-48 hours to investigate changes to tensile properties and microstructure. Treatment of 800°C for 1 hour was found to produce the most ductile material, measured by total elongation of the tensile bar (16.5%). Furthermore, both PWHT time and temperature were observed to increase total elongation, except in extreme (>800°C or >18hours) cases, but the effect of temperature was stronger. The second order cumulative annealing parameter shows a trend with tensile properties. Average grain sizes in the fusion zone and heat affected zone did not change under any of the PWHTs until the development of an undesirable blocky-alpha phase, which was only observed to form in the heat affected zones for hold times greater than 18hr at 800°C.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Microstructural effects on the rotating bending fatigue behavior of Ti–6Al–4V produced via laser powder bed fusion with novel heat treatments

The rotating bending fatigue (RBF) behavior (fully reversed, R = -1) of additively manufactured (AM) Ti–6Al–4V alloy produced via laser powder bed fusion (PBF-L) was investigated with respect to different microstructures achieved through novel heat treatments. The investigation herein seeks to elucidate the effect of microstructure by controlling variables that can affect fatigue behavior in Ti–6Al–4V, such as chemistry, porosity, and surface roughness. In order to control these variables, different hot isostatic pressing (HIP) treatments at 800 °C, 920 °C, and 1050 °C with a 920 °C temper were applied to three sets of Ti–6Al–4V cylinders that originated from the same PBF-L build, such that there were 30 tests per condition. After HIP treatment, the specimens were machined and tested. The highest runout stress was achieved after sub-β transus HIP at 800 °C for 2 h at 200 MPa of pressure. A significant drop in fatigue strength was attributed to large prior-β grains and grain boundary α resulting from super-β transus HIP treated specimens. In conclusion, for the sub-β transus HIP specimens, differences in fatigue strength were attributed to α lath thickness, relative dislocation density, and dislocation boundary strengthening.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Effect of post-extrusion heat treatment on mechanical property of aluminum alloy 2024 tube produced using Shear Assisted Processing and Extrusion (ShAPE)

The present work deals with the Shear Assisted Processing and Extrusion (ShAPE) of aluminum alloy 2024 tubes and mechanical property optimization via post extrusion heat treatments (T3510 and T8510). The ShAPE process enables extruding AA2024 at an extrusion speed of 7.4 m/min and extrusion temperature of 480 °C, which is otherwise beyond the extrudability limit of this alloy using conventional extrusion techniques. The ultimate tensile strength reaches 466 MPa for ShAPE+T3510 condition and 503 MPa for ShAPE+T8510 condition, both of which exceed the corresponding ASTM/ASM (minimum/typical) values for the studied tube geometry. The yield strength reaches 382 MPa for ShAPE+T3510 condition and 481 MPa for ShAPE+T8510 condition, both of which surpass any reported values in the literature or the highest industrial values. In addition, the ductility of AA2024 tube fabricated from ShAPE+T3510 or ShAPE+T8510 are evidently improved by the grain size refinement, second phase refinement, and enhanced uniformity in second phase distribution due to the severe plastic deformation of ShAPE process.

Shear Assisted Processing and Extrusions (ShAPE), ↗
NASA NTRS1978

Fluxless Brazing and Heat Treatment of a Plate-Fin Sandwich Actively Cooled Panel

The processes and techniques used to fabricate plate-fin sandwich actively cooled panels are presented. The materials were 6061 aluminum alloy and brazing sheet having clad brazing alloy. The panels consisted of small scale specimens, fatigue specimens, and a large 0.61 m by 1.22 m test panel. All panels were fluxless brazed in retorts in heated platen presses while exerting external pressure to assure intimate contact of details. Distortion and damage normally associated with that heat treatment were minimized by heat treating without fixtures and solution quenching in an organic polymer solution. The test panel is the largest fluxless brazed and heat treated panel of its configuration known to exist.

Beuyukian, C. S.↗
DOE OSTI2025

The effect of heat treatment on the defect evolution in LPBF 316H stainless steel

This work investigates the effect of processing and heat treatment on defect evolution and irradiation response of laser powder bed fusion (LPBF) 316H stainless steel, with comparisons to LPBF 316L and wrought 316L/316H. Using in-situ and ex-situ ion irradiations across a wide parameter space—temperature (300–675 °C), dose (0.2–25 dpa), dose rate (10 -3 –10 -5 dpa/s), and helium co-implantation (20–2500 appm)—we correlated void swelling, dislocation loop evolution, and segregation behavior with pre-irradiation microstructures (as-built, stress-relieved, solution-annealed, and cold-worked). Results show that swelling is strongly controlled by dislocation density: intermediate densities maximize swelling, while solution annealing or cold working reduce susceptibility to levels comparable to wrought alloys. Low dose rates and helium both promote cavity nucleation and lower the incubation barrier, with helium suppressing the role of dislocation density and driving swelling behavior toward wrought-like response. Loop evolution in SA LPBF 316H resembles wrought 316L but shows localized denuded zones near low-angle grain boundaries. STEM-EDS mapping further revealed Ni segregation at voids and sparse Al-rich oxides, without evidence of Ni–Si precipitates. Collectively, these findings identify dislocation density, helium content, and dose rate as the factors governing swelling in LPBF 316H and provide mechanistic datasets for model validation, supporting LAIN and the qualification of AM austenitic steels for nuclear service.

316 stainless steel↗