New High-Strength Ni-based Alloys for High Temperature Service in Liquid Fluoride Salt Environments
The ever-increasing demand for higher system thermal efficiency necessitates the operation of power generation cycles and heat conversion systems for chemical processes at progressively higher temperatures. As the system operating temperature increases, fewer and fewer materials are available with the required mechanical properties and environmental compatibility. This dearth of materials is particularly acute in structural applications at temperatures above 700°C in liquid Fluoride Salt Cooled High-Temperature Reactors (FHRs) and Concentrated Solar Power (CSP) systems where liquid fluoride and/or liquid chloride salts are used for their high thermal capacity and low thermal conductivity to store and transport heat. It has been shown that fluorides and chlorides can degrade the properties of the material used for storage and transport due to corrosive effects thus affecting the performance and lifetime characteristics. Thus, materials used for storage and transport for fluoride/chloride-salt must at the minimum have good compatibility with the salt by exhibiting low corrosion rates at the required temperatures. In addition, since many of the components will be subject to stresses in service, they need to have sufficient strength to resist plastic deformation, and the resistance to time dependent creep deformation at these temperatures, and stress levels. Achieving the combination of these properties required for higher temperatures is particularly challenging considering traditionally, the expected lifetime of some of the components used in these systems are from 30 years (CSP) to 80 years (FHRs). Although 316 stainless steel and associated redox corrosion reduction techniques are being considered for use in the first generational systems, use of 316SS is limited to operating temperatures up to ~ 650°C, thereby resulting in lower reactor efficiencies. Hastelloy ® N, developed at ORNL in the 1950s-60s for molten salt service is currently the leading candidate FHR structural alloy but has inadequate creep properties at high temperatures. Using a computationally-guided approach, Oak Ridge National Laboratory had developed new high strength alloys strengthened by γ’ precipitates (about 2X the strength of Hastelloy ® N) in small laboratory-scale heats that show good resistance to corrosion by fluorides and improved creep rupture life at temperatures up to 850°C (U.S. Patent Application No. 13/833,357 entitled “High Strength Alloys for High Temperature Service in Liquid-Salt Cooled Energy Systems”- granted U. S. Patent No. 9,540,714).