Mn(Pt 1–x Pd x ) 5 P: Isovalent tuning of Mn-sublattice magnetic order
Here, e report the growth and characterization of MnPd 5 P, a rare-earth-free ferromagnet, with T C ≈ 295 K and planar anisotropy, and conduct a substitutional study with its antiferromagnetic analogue MnPt 5 P. We provide a solution route to grow large single crystals of MnPd 5 P and the series Mn(Pt 1–x Pd x ) 5 P by adding Mn into Pd-P and (Pt 1–x Pd x )-P based melts. All compounds in the family adopt the layered anti-CeCoIn5 type structure with the space group P4/mmm, and EDS and X-ray diffraction results indicate that MnPt 5 P and MnPd 5 P form a complete solid solution. Based on measurements of the temperature- and field-dependent magnetization and resistance, we construct a temperature-composition (T-x) phase diagram for Mn(Pt 1–x Pd x ) 5 P and demonstrate that the initial antiferromagnetic order found in MnPt 5 P is extraordinarily sensitive to Pd substitution. At low Pd fractions (x < 0.010), the single antiferromagnetic transition in pure MnPt 5 P splits into a higher temperature ferromagnetic transition followed first, upon cooling, by a lower temperature ferromagnetic to antiferromagnetic transition and then by a re-entrant antiferromagnetic to ferromagnetic transition at even lower temperatures. The antiferromagnetic region makes up a bubble phase that persists up to x ≈ 0.008-0.009 for T ≈ 150 K, with all samples x < 0.008 recovering their initial ferromagnetic state upon further cooling to base temperature. Over the same low substitution range we find a non-monotonic change in the room temperature value of the unit cell volume, further suggesting that pure MnPt 5 P is very close to an instability. Once x > 0.010, Mn(Pt 1–x Pd x ) 5 P undergoes a only single transition into the ferromagnetic phase. The Curie temperature initially increases rapidly with x, rising from T C ≈ 197 K at x = 0.013 to a maximum of T C ≈ 312 K for x ≈ 0.62, and then falling back to T C ≈ 295 K for pure MnPd 5 P (x = 1.00). Given that Pt and Pd are isoelectronic, this work raises questions as to the origin of the extreme sensitivity of the magnetic ground state in MnPt 5 P upon introducing Pd.