NASA NTRS1993

Growth experiment of narrow band-gap semiconductor PbSnTe single crystals in space (M-1)

An experiment on crystal growth of Pb(1-x)Sn(x)Te in microgravity is planned. This material is an alloy of the compound semiconductors PbTe and SnTe. It is a promising material for infrared diode lasers and detectors in the wavelength region between 6 and 30 micron. Since the electrical properties of Pb(1-x)Sn(x)Te depend greatly on the Pb/Sn ratio and crystalline defects as well as impurity concentration, homogeneous, defect-free, high-quality crystals are anticipated. Although many growth methods, such as the pulling method, the Bridgman method, the vapor growth method, etc., have been applied to the growth of Pb(1-x)Sn(x)Te, large, homogeneous, low-defect-density crystals have not yet been grown on Earth. The unsuccessful results were caused by buoyancy-driven convection in the fluids induced by the specific gravity difference between heated and cooled fluids on Earth. A crystal is grown by cooling the melt from one end of the ampoule. In crystal growth from the melt, about 30 percent of the SnTe in the melt is rejected at the solid-liquid interface during solidification. On Earth, the rejected SnTe is completely mixed with the remaining melt by convection in the melt. Therefore, SnTe concentration in the melt, and accordingly in the crystal, increases as the crystal grows. In the microgravity environment, buoyancy-driven convection is suppressed because the specific gravity difference is negligible. In that case, the rejected SnTe remains at the solid-liquid interface and its concentration increases only at the interface. If the growth rate is higher than the PbTe-SnTe interdiffusion rate, the amount of SnTe which diffuses from the interface into the melt increases as SnTe piles up at the interface, and finally it balances the amount of rejected SnTe during solidification, resulting in steady-state SnTe transportation at the interface. By using this principle, compositionally homogeneous crystals can be grown. Furthermore, low-defect-density crystals will be grown in microgravity, because convection causes crystalline defects by mising hot and cold fluids and generating temperature fluctuations in them.

Yamada, Tomoaki↗

NASA NTRS2006

Microwave Signatures of Snow on Sea Ice: Observations

Part of the Earth Observing System Aqua Advanced Microwave Scanning Radiometer (AMSR-E) Arctic sea ice validation campaign in March 2003 was dedicated to the validation of snow depth on sea ice and ice temperature products. The difficulty with validating these two variables is that neither can currently be measured other than in situ. For this reason, two aircraft flights on March 13 and 19,2003, were dedicated to these products, and flight lines were coordinated with in situ measurements of snow and sea ice physical properties. One flight was in the vicinity of Barrow, AK, covering Elson Lagoon and the adjacent Chukchi and Beaufort Seas. The other flight was farther north in the Beaufort Sea (about 73 N, 147.5 W) and was coordinated with a Navy ice camp. The results confirm the AMSR-E snow depth algorithm and its coefficients for first-year ice when it is relatively smooth. For rough first-year ice and for multiyear ice, there is still a relationship between the spectral gradient ratio of 19 and 37 GHz, but a different set of algorithm coefficients is necessary. Comparisons using other AMSR-E channels did not provide a clear signature of sea ice characteristics and, hence, could not provide guidance for the choice of algorithm coefficients. The limited comparison of in situ snow-ice interface and surface temperatures with 6-GHz brightness temperatures, which are used for the retrieval of ice temperature, shows that the 6-GHz temperature is correlated with the snow-ice interface temperature to only a limited extent. For strong temperature gradients within the snow layer, it is clear that the 6-GHz temperature is a weighted average of the entire snow layer.

Markus, Thorsten↗

NASA NTRS2001

Use of a Multiwavelength Pyrometer in Several Elevated Temperature Aerospace Applications

A multiwavelength pyrometer was developed for applications unique to aerospace environments. It was shown to be a useful and versatile technique for measuring temperature, even when the emissivity is unknown. It has also been used to measure the surface temperatures of ceramic zircomia thermal barrier coatings and alumina. The close agreement between pyrometer and thin film thermocouple temperatures provided an independent check. Other applications of the multiwavelength pyrometer are simultaneous surface and bulk temperature measurements of a transparent material, and combustion gas temperature measurement using a special probe interfaced to the multiwavelength pyrometer via an optical fiber. The multiwavelength pyrometer determined temperature by transforming the radiation spectrum in a broad wavelength region to produce a straight line (in a certain spectral region), whose intercept in the vertical axis gives the temperature. Implicit in a two-color pyrometer is the assumption of wavelength independent emissivity. Though the two data points of a two-color pyrometer similarly processed would result immediately in a similar straight line to give the unknown temperature, the two-color pyrometer lacks the greater data redundancy of the multiwavelength pyrometer, which enables it to do so with improved accuracy. It also confirms that emissivity is indeed wavelength independent, as evidenced by a multitude of the data lying on a simple straight line. The multiwavelength pyrometer was also used to study the optical transmission properties of a nanostructured material from which a quadratic exponential functional frequency dependence of its spectral transmission was determined. Finally, by operating the multiwavelength pyrometer in a very wide field of view mode, the surface temperature distribution of a large hot surface was obtained through measurement of just a single radiation spectrum.

Ng, Daniel↗

NASA NTRS1994

The effect of various metallurgical parameters on the flow and fracture behavior of polycrystalline NiAl near the brittle-to-ductile transition

An investigation of the effect of various metallurgical parameters such as interfaces, allowing additions, test temperature, and strain rate on the flow and fracture behavior of polycrystalline NiAl is summarized. From this study, a more complete understanding of the deformation and fracture behavior of polycrystalline NiAl near the brittle-to-ductile transition temperature has been developed. A mechanism for the BDTT is proposed that is based on the operation of localized dislocation climb processes that operate within the vicinity of the grain boundaries and provide the additional deformation mechanisms necessary for grain-to-grain compatibility during plastic deformation. Finally, methods for improving the low temperature mechanical behavior of NiAl were considered and reviewed within the context of the present knowledge of NiAl-based materials and the operative deformation and fracture mechanisms determined in this study. Special emphasis was placed on the use of second phases for improving low temperature properties.

Noebe, Ronald D.↗

NASA NTRS2015

Core Analysis Combining MT (TIPPER) and Dielectric Sensors (Sans EC) in Earth and Space

On terrestrial planets and moons of our solar system cores reveal details about a geological structure's formation, content, and history. The strategy for the search for life is focused first on finding water which serves as a universal solvent, and identifying the rocks which such solvent act upon to release the constituent salts, minerals, ferrites, and organic compounds and chemicals necessary for life. Dielectric spectroscopy measures the dielectric properties of a medium as a function of frequency. Reflection measurements in the frequency range from 300 kHz to 300 MHz were carried out using RF and microwave network analyzers interrogating SansEC Sensors placed on clean geological core samples. These were conducted to prove the concept feasibility of a new geology instrument useful in the field and laboratory. The results show that unique complex frequency spectra can be acquired for a variety of rock core samples. Using a combination of dielectric spectroscopy and computer simulation techniques the magnitude and phase information of the frequency spectra can be converted to dielectric spectra. These low-frequency dielectric properties of natural rock are unique, easily determined, and useful in characterizing geology. TIPPER is an Electro-Magnetic Passive-Source Geophysical Method for Detecting and Mapping Geothermal Reservoirs and Mineral Resources. This geophysical method uses distant lightning and solar wind activity as its energy source. The most interesting deflections are caused by the funneling of electrons into more electrically conductive areas like mineralized faults, water or geothermal reservoirs. We propose TIPPER to be used with SansEC for determining terrain/ocean chemistry, ocean depth, geomorphology of fracture structures, and other subsurface topography characteristics below the ice crust of Jovian moons. NASA envisions lander concepts for exploration of these extraterrestrial icy surfaces and the oceans beneath. One such concept would use a nuclear powered heated tip for melting through the ice sheath of Europa and inserting a down hole SansEC with TIPPER interface. NASA's Juno space probe already on the way to Jupiter as part of the Exploration New Frontiers Program and the planned Europa mission will conduct detailed reconnaissance of Jupiter's moon Europa and investigate whether the icy moon could harbor conditions suitable for life. It has already been observed that Jovian moons have auroras that may serve as naturally occurring active energy sources for a TIPPER instrument.

Mound, Michael C.↗

NASA NTRS2003

The Interaction Between an Insoluble Particle and an Advancing Solid/Liquid Interface: Micro-Gravity Experiments and Theoretical Developments

The interaction of an insoluble particle with an advancing solid/liquid interface (SLI) has been a subject of investigation for the past four decades. While the original interest stemmed from geology applications (e.g., frost heaving in soil), researchers soon realized that the complex science associated with such an interaction is relevant to many other scientific fields encompassing metal matrix composites (MMCs), high temperature superconductors, inclusion management in steel, growth of monotectics, and preservation of biological cells. During solidification of a liquid containing an insoluble particle, three distinct interaction phenomena have been experimentally observed: instantaneous engulfment of the particle, continuous pushing, and particle pushing followed by engulfment. It was also observed that for given experimental conditions and particle size there is a critical solidification velocity, V(sub cr), above which a particle is engulfed. During solidification of MMCs pushing leads to particle agglomeration at the grain boundaries and this has detrimental effects on mechanical properties of the casting. Consequently, the process must be designed for instantaneous engulfment to occur. This implies the development of accurate theoretical models to predict V(sub cr), and perform benchmark experiments to test the validity of such models. Although considerable progress has been made in understanding the pushing/engulfment phenomenon (PEP), its quantification in terms of the material and processing parameters remains a focus of research. Since natural convection currents occurring during terrestrial solidification experiments complicate the study of PEP, execution of experiments on the International Space Station (ISS) has been approved and funded by NASA. Extensive terrestrial (1g) experiments and preliminary micro-gravity (mu g) experiments on two space shuttle missions have been conducted in preparation for future experiments on the ISS. The investigated systems included metal-ceramic particles (pure aluminum - zirconia particles) and transparent organic - non-reactive particles (succinonitrile - polystyrene and biphenyl - glass). This paper will discuss the experimental results obtained in both lg and pg conditions and the influence of the natural convection on V(sub cr). A summary of past mathematical models and our recent theoretical developments will also be presented to explain the experimentally observed particle/SLI interaction.

Catalina, Adrian V.↗

NASA NTRS1990

Characterization of unnotched SCS-6/Ti-15-3 metal matrix composites at 650 C

Ti-15-3 reinforced with SCS-6 silicon carbide fibers, in five different layups, was tested at 650 C to determine monotonic and fatigue strengths, basic mechanical properties, and damage initiation and progression. The elevated temperature results were compared to those obtained at room temperature. Analytical predictions were made of the monotonic stress-strain response as well as cyclic stress-strain hysteresis. The fiber reinforcement was found to significantly increase the static and fatigue strengths of the laminates over that of the matrix material at elevated temperature while the increase was insignificant at room temperature. Initial damage, in either the fibers or the matrix, was partitioned as a function of the life and applied strain range in the constituents. High strains and short lives resulted in multiple fiber failure with no signs of matrix fatigue cracking. Low strains and long lives resulted in extensive matrix cracking and no fiber breaks away from the fracture surface. At 650 C the matrix was too weak to cause fiber-matrix interface failure prior to matrix yielding. Laminate fatigue lives were hypothesized to be a function of the 0 deg fiber stress. More scatter was found in the 0 deg fiber stress vs. high temperature fatigue life data than for the room temperature data. An initial unloading modulus that was greater than the initial loading modulus was observed in the elevated temperature fatigue tests.

Pollock, W. D.↗

NASA NTRS1992

Characterization of unnotched SCS-6/Ti-15-3 metal matrix composites at 650 C

Ti-15-3 reinforced with SCS-6 silicon carbide fibers, in five different layups, was tested at 650 C to determine monotonic and fatigue strengths, basic mechanical properties, and damage initiation and progression. The elevated temperature results were compared to those obtained at room temperature. Analytical predictions were made of the monotonic stress-strain response as well as cyclic stress-strain hysteresis. The fiber reinforcement was found to significantly increase the static and fatigue strengths of the laminates over that of the matrix material at elevated temperature while the increase was insignificant at room temperature. Initial damage, in either the fibers or the matrix, was partitioned as a function of the life and applied strain range in the constituents. High strains and short lives resulted in multiple fiber failure with no signs of matrix fatigue cracking. Low strains and long lives resulted in extensive matrix cracking and no fiber breaks away from the fracture surface. At 650 C the matrix was too weak to cause fiber-matrix interface failure prior to matrix yielding. Laminate fatigue lives were hypothesized to be a function of the 0 deg fiber stress. More scatter was found in the 0 deg fiber stress vs. high temperature fatigue life data than for the room temperature data. An initial unloading modulus that was greater than the initial loading modulus was observed in the elevated temperature fatigue tests.

Pollock, William D.↗

NASA NTRS2004

Modeling the interaction Between Ethylene Diamine and Water Films on the Surface of a Carbon Nanotube

It has been observed that a carbon nanotube (CNT) AFM tip coated with ethylene diamine (EDA) penetrates the liquid water-air interface more easily than an uncoated nanotube tip. The EDA coating remains intact through repeated cycles of dipping and removal. In order to understand the physical basis for this observation, we use ab initio quantum chemistry calculations to study the EDA-CNT-water interaction and to parameterize a force field describing this system. Molecular dynamics (MD) simulations are carried out for EDA-water mixtures and an EDA-coated carbon nanotube immmed in water. These simulations are similar to our earlier MD study that characterized the CNT-water interface. The attractive CNT-EDA and CNT-water interactions arise primarily from van der Waals forces, and the EDA-EDA, EDA-water and water-water interactions are mainly due to hydrogen bond formation. The binding energ of single EDA molecule to the nanotube is nearly three times larger than the corresponding value found for water (4.3 versus 1.5 kcal mol, respectively). The EDA molecules readily stick to and diffuse along the CNT surface. As a resulf mixing of the EDA and water films does not occur on the timescale of the MD simulations. The EDA film reduces the hydrophobicity of the nanotube surface and acts like a prototypical surfactant in stabilizing the suspension of carbon nanotubes in water. For this presentation, we use the MD simulations to determine how the presence of the carbon nanotube surface perturbs the properties of EDA-water mixtures.

Jaffe, Richard L.↗

NASA NTRS2012

Equilibrium Limit of Boundary Scattering in Carbon Nanostructures: Molecular Dynamics Calculations of Thermal Transport

It is widely known that graphene and many of its derivative nanostructures have exceedingly high reported thermal conductivities (up to 4000 W/mK at 300 K). Such attractive thermal properties beg the use of these structures in practical devices; however, to implement these materials while preserving transport quality, the influence of structure on thermal conductivity should be thoroughly understood. For graphene nanostructures, having average phonon mean free paths on the order of one micron, a primary concern is how size influences the potential for heat conduction. To investigate this, we employ a novel technique to evaluate the lattice thermal conductivity from the Green-Kubo relations and equilibrium molecular dynamics in systems where phonon-boundary scattering dominates heat flow. Specifically, the thermal conductivities of graphene nanoribbons and carbon nanotubes are calculated in sizes up to 3 microns, and the relative influence of boundary scattering on thermal transport is determined to be dominant at sizes less than 1 micron, after which the thermal transport largely depends on the quality of the nanostructure interface. The method is also extended to carbon nanostructures (fullerenes) where phonon confinement, as opposed to boundary scattering, dominates, and general trends related to the influence of curvature on thermal transport in these materials are discussed.

Haskins, Justin↗

NASA NTRS1982

Thermal degradation of the tensile properties of undirectionally reinforced FP-AI203/EZ 33 magnesium composites

The effects of isothermal and cyclic exposure on the room temperature axial and transverse tensile strength and dynamic flexural modulus of 35 volume percent and 55 volume percent FP-Al2O3/EZ 33 magnesium composites were studied. The composite specimens were continuously heated in a sand bath maintained at 350 C for up to 150 hours or thermally cycled between 50 and 250 C or 50 and 350 C for up to 3000 cycles. Each thermal cycle lasted for a total of six minutes with a hold time of two minutes at the maximum temperature. Results indicate to significant loss in the room temperature axial tensile strength and dynamic flexural modulus of composites thermally cycled between 50 and 250 C or of composites isothermally heated at 350 C for up to 150 hours from the strength and modulus data for the untreated, as fabricated composites. In contrast, thermal cycling between 50 and 350 C caused considerable loss in both room temperature strength and modulus. Fractographic analysis and measurement of composite transverse strength and matrix hardness of thermally cycled and isothermally heated composites indicated matrix softening and fiber/matrix debonding due to void growth at the interface and matrix cracking as the likely causes of the strength and modulus loss behavior.

Bhatt, R. T.↗

NASA NTRSDate not supplied

Surface Instability of Liquid Propellants in Microgravity During Pulsed Settling Operations

Pulsing reaction control system (RCS) thrusters, vent valves, or other propulsion devices can preserve propellant resources in space, but this operation also effectively introduces a vibration to the vehicle. When the vibration is perpendicular to the liquid propellant surface, Faraday waves may be generated at the liquid-vapor interface. These Faraday instabilities can perturb or break up the liquid surface of cryogenic tanks, leading to inefficiencies in thermal management or even ullage collapse. Drawing from theory and experiments, an engineering model defining the allowable design regions for pulsed settling in microgravity was assembled and verified with computational fluid dynamics (CFD) simulations. A traditional settling metric, the Bond number, was also overlaid in the model to indicate which duty cycles were insufficient to overcome surface tension and aggregate propellant. Mission planners and engineers can consult the tool to rapidly evaluate the stability of a liquid-vapor interface given the pulse frequency and the excitation acceleration. Expressions developed for Faraday waves induced by a sinusoidal forcing input at standard gravity were found to provide excellent predictive capabilities for pulsed, or rectangular, waveforms in the absence of a consistent gravitational acceleration. This study extends the usage of these equations to an alternative forcing function and microgravity environments for the purpose of estimating natural frequencies, surface mode shapes, surface wave amplitudes, and the onset of droplet ejection. CFD simulations with the Loci/STREAM-VoF (Volume of Fluid) solver were initially validated against experimental results in standard gravity. Discrete points on the design map were then investigated with CFD and confirmed that the engineering model reliably indicates surface stability and most Faraday wave characteristics without requiring higher-fidelity tools. The engineering model is highly extensible and can be adapted for various propellant fill fractions, fluid properties, and tank sizes.

Faraday Waves↗

NASA NTRSDate not supplied

Surface Instability of Liquid Propellants in Microgravity During Pulsed Settling Operations

Pulsing reaction control system (RCS) thrusters, vent valves, or other propulsion devices can preserve propellant resources in space, but this operation also effectively introduces a vibration to the vehicle. When the vibration is perpendicular to the liquid propellant surface, Faraday waves may be generated at the liquid-vapor interface. These Faraday instabilities can perturb or break up the liquid surface of cryogenic tanks, leading to inefficiencies in thermal management or even ullage collapse. Drawing from theory and experiments, an engineering model defining the allowable design regions for pulsed settling in microgravity was assembled and verified with computational fluid dynamics (CFD) simulations. A traditional settling metric, the Bond number, was also overlaid in the model to indicate which duty cycles were insufficient to overcome surface tension and aggregate propellant. Mission planners and engineers can consult the tool to rapidly evaluate the stability of a liquid-vapor interface given the pulse frequency and the excitation acceleration. Expressions developed for Faraday waves induced by a sinusoidal forcing input at standard gravity were found to provide excellent predictive capabilities for pulsed, or rectangular, waveforms in the absence of a consistent gravitational acceleration. This study extends the usage of these equations to an alternative forcing function and microgravity environments for the purpose of estimating natural frequencies, surface mode shapes, surface wave amplitudes, and the onset of droplet ejection. CFD simulations with the Loci/STREAM-VoF (Volume of Fluid) solver were initially validated against experimental results in standard gravity. Discrete points on the design map were then investigated with CFD and confirmed that the engineering model reliably indicates surface stability and most Faraday wave characteristics without requiring higher-fidelity tools. The engineering model is highly extensible and can be adapted for various propellant fill fractions, fluid properties, and tank sizes.

Faraday Waves↗

NASA NTRS1983

Thermal degradation of the tensile properties of undirectionally reinforced FP-Al2O3/EZ 33 magnesium composites

The effects of isothermal and cyclic exposure on the room temperature axial and transverse tensile strength and dynamic flexural modulus of 35 volume percent and 55 volume percent FP-Al203/EZ 33 magnesium composites were studied. The composite specimens were continuously heated in a sand bath maintained at 350 C for up to 150 hours or thermally cycled between 50 and 250 C or 50 and 350 C for up to 3000 cycles. Each thermal cycle lasted for a total of six minutes with a hold time of two minutes at the maximum temperature. Results indicate no significant loss in the room temperature axial tensile strength and dynamic flexural modulus of composites thermally cycled between 50 and 250 C or of composites isothermally heated at 350 C for up to 150 hours from the strength and modulus data for the untreated, as-fabricated composites. In contrast, thermal cycling between 50 and 350 C caused considerable loss in both room temperature strength and modulus. Fractographic analysis and measurement of composite transverse strength and matrix hardness of thermally cycled and isothermally heated composites indicated matrix softening and fiber/matrix debonding due to void growth at the interface and matrix cracking as the likely causes of the strength and modulus loss behavior. Previously announced in STAR as N82-21260

Bhatt, R.T.↗

NASA NTRS1994

Thermomechanical Fatigue Damage/Failure Mechanisms in SCS-6/Timetal 21S [0/90](Sub S) Composite

The thermomechanical fatigue (TMF) deformation, damage, and life behaviors of SCS6/Timetal 21S (0/90)s were investigated under zero-tension conditions. In-phase (IP) and out-of-phase (OP) loadings were investigated with a temperature cycle from 150 to 650 deg C. An advanced TMF test technique was used to quantify mechanically damage progression. The technique incorporated explicit measurements of the macroscopic (1) isothermal static moduli at the temperature extremes of the TMF cycle and (2) coefficient of thermal expansion (CTE) as functions of the TMF cycles. The importance of thermal property degradation and its relevance to accurate post-test data analysis and interpretation is briefly addressed. Extensive fractography and metallography were conducted on specimens from failed and interrupted tests to characterize the extent of damage at the microstructure level. Fatigue life results indicated trends analogous to those established for similar unidirectional(0) reinforced titanium matrix composite systems. High stress IP and mid to low stress OP loading conditions were life-limiting in comparison to maximum temperature isothermal conditions. Dominant damage mechanisms changed with cycle type. Damage resulting from IP TMF conditions produced measurable decreases in static moduli but only minimal changes in the CTE. Metallography on interrupted and failed specimens revealed extensive (0) fiber cracking with sparse matrix damage. No surface initiated matrix cracks were present. Comparable OP TMF conditions initiated environment enhanced surface cracking and matrix cracking initiated at (90) fiber/matrix (F/M) interfaces. Notable static moduli and CTE degradations were measured. Fractography and metallography revealed that the transverse cracks originating from the surface and (90) F/M interfaces tended to converge and coalesce at the (0) fibers.

Castelli, Michael G.↗

NASA NTRS1988

Properties of silicon carbide fiber-reinforced silicon nitride matrix composites

The mechanical properties of NASA Lewis developed SiC/RBSN composites and their thermal and environmental stability havd been studied. The composites consist of nearly 30 vol pct of aligned 142 micron diameter chemically vapor-deposited SiC fibers in a relatively porous silicon nitride matrix. In the as-fabricated condition, the unidirectional and 2-D composites exhibited metal-like stress-strain behavior, graceful failure, and showed improved properties when compared with unreinforced matrix of comparable density. Furthermore, the measured room temperature tensile properties were relativley independent of tested volume and were unaffected by artifical notches normal to the loading direction or by thermal shocking from temperatures up to 800 C. The four-point bend strength data measured as a function of temperature to 1400 C in air showed that as-fabricated strength was maintained to 1200 C. At 1400 C, however, nearly 15 pct loss in strength was observed. Measurement of room temperature tensile strength after 100 hr exposure at temperatures to 1400 C in a nitrogen environment indicated no loss from the as-fabricated composite strength. On the other hand, after 100 hr exposure in flowing oxygen at 1200 and 1400 C, the composites showed approximately 40 pct loss from their as-fabricated ultimate tensile strength. Those exposed between 400 to 1200 C showed nearly 60 pct strength loss. Oxidation of the fiber/matrix interface as well as internal oxidation of the porous Si3N4 matrix are likely mechanisms for strength degradation. The excellent strength reproducibility, notch insensitivity, and high temperature strength of the composite makes it an ideal candidate for advanced heat engine applications provided coating or densification methods are developed to avoid internal oxidation attack.

Bhatt, Ramakrishna T.↗

NASA NTRS1988

Coastal Zone Color Scanner

The Coastal Zone Color Scanner (CZCS) spacecraft ocean color instrument is capable of measuring and mapping global ocean surface chlorophyll concentration. It is a scanning radiometer with multiband capability. With new electronics and some mechanical, and optical re-work, it probably can be made flight worthy. Some additional components of a second flight model are also available. An engineering study and further tests are necessary to determine exactly what effort is required to properly prepare the instrument for spaceflight and the nature of interfaces to prospective spacecraft. The CZCS provides operational instrument capability for monitoring of ocean productivity and currents. It could be a simple, low cost alternative to developing new instruments for ocean color imaging. Researchers have determined that with global ocean color data they can: specify quantitatively the role of oceans in the global carbon cycle and other major biogeochemical cycles; determine the magnitude and variability of annual primary production by marine phytoplankton on a global scale; understand the fate of fluvial nutrients and their possible affect on carbon budgets; elucidate the coupling mechanism between upwelling and large scale patterns in ocean basins; answer questions concerning the large scale distribution and timing of spring blooms in the global ocean; acquire a better understanding of the processes associated with mixing along the edge of eddies, coastal currents, western boundary currents, etc., and acquire global data on marine optical properties.

Johnson, B.↗

NASA NTRS2013

Crystal Growth of ZnSe and Related Ternary Compound Semiconductors by Vapor Transport in Low Gravity

Crystals of ZnSe and related ternary compounds, such as ZnSeS and ZnSeTe, will be grown by physical vapor transport in the Material Science Research Rack (MSRR) on International Space Station (ISS). The objective of the project is to determine the relative contributions of gravity-driven fluid flows to the compositional distribution, incorporation of impurities and defects, and deviation from stoichiometry observed in the crystals grown by vapor transport as results of buoyance-driven convection and growth interface fluctuations caused by irregular fluid-flows on Earth. The investigation consists of extensive ground-based experimental and theoretical research efforts and concurrent flight experimentation. The objectives of the ground-based studies are (1) obtain the experimental data and conduct the analyses required to define the optimum growth parameters for the flight experiments, (2) perfect various characterization techniques to establish the standard procedure for material characterization, (3) quantitatively establish the characteristics of the crystals grown on Earth as a basis for subsequent comparative evaluations of the crystals grown in a low-gravity environment and (4) develop theoretical and analytical methods required for such evaluations. ZnSe and related ternary compounds have been grown by vapor transport technique with real time in-situ non-invasive monitoring techniques. The grown crystals have been characterized extensively by various techniques to correlate the grown crystal properties with the growth conditions.

Su, Ching-Hua↗