A General Overview of Cathodic Protection in Reinforced Concrete
Corrosion of reinforcement steel in concrete is a prevalent issue in infrastructures worldwide, with the direct costs of repair estimated to be $1 trillion annually. Treatment options are complicated by the concrete’s role in the corrosion process. Ordinary, modern-day cement is so alkaline that it maintains a thick passive layer on the steel surface, reducing corrosion to inconsequential rates. However, environmental contaminants in the form of carbon dioxide or chlorides may cause a breakdown in the passive layer, exposing the steel surface to corrosion. Galvanic cells will be free to form due to potential differences along the rebar, and anode sites will create dissolved iron ions that cannot travel far through the still concrete. Thus, rust products will accumulate directly onto the steel/concrete interface. Iron oxides have a much higher volume relative to steel, and even a miniscule amount of rust can produce enough volumetric stress to cause cracking, spalling and delamination of the surrounding concrete, increasing the risk of structural failure. Safeguards and inhibiting technology exist to limit the chances of corrosion initiation by either species, but cracking of the concrete cover and gradual accumulation of contaminants means that corrosion is unavoidable in certain environments and will initiate, given enough time.