NASA NTRS1993

Results of the second Round Robin on opening-load measurement conducted by ASTM Task Group E24.04.04 on crack closure measurement and analysis

A second experimental Round Robin on the measurement of the crack opening load in fatigue crack growth tests has been completed by the ASTM Task Group E24.04.04 on Crack Closure Measurement and Analysis. Fourteen laboratories participated in the testing of aluminum alloy compact tension specimens. Opening-load measurements were made at three crack lengths during constant Delta K, constant stress ratio tests by most of the participants. Four participants made opening-load measurements during threshold tests. All opening-load measurements were based on the analysis of specimens compliance behavior, where the displacement/strain was measured either at the crack mouth or the mid-height back face location. The Round Robin data were analyzed for opening load using two non-subjective analysis methods: the compliance offset and the correlation coefficient methods. The scatter in the opening load results was significantly reduced when some of the results were excluded from the analysis population based on an accept/reject criterion for raw data quality. The compliance offset and correlation coefficient opening load analysis methods produced similar results for data populations that had been screened to eliminate poor quality data.

Phillips, E. P.↗
NASA NTRS1994

An artifical corrosion protocol for lap-splices in aircraft skin

This paper reviews the progress to date to formulate an artificial corrosion protocol for the Tinker AFB C/KC-135 Corrosion Fatigue Round Robin Test Program. The project has provided new test methods to faithfully reproduce the corrosion damage within a lap-splice by accelerated means, the rationale for a new laboratory test environment, and a means for corrosion damage quantification. The approach is pragmatic and the resulting artificial corrosion protocol lays the foundation for future research in the assessment of aerospace alloys. The general means for quantification of corrosion damage has been presented in a form which can be directly applied to structural integrity calculations.

Shaw, Bevil J.↗
NASA NTRS1994

Fatigue crack growth under variable amplitude loading

Fatigue crack growth tests were conducted on an Fe 510 E C-Mn steel and a submerged arc welded joint from the same material under constant, variable, and random loading amplitudes. Paris-Erdogan's crack growth rate law was tested for the evaluation of m and C using the stress intensity factor K, the J-integral, the effective stress intensity factor K(sub eff), and the root mean square stress intensity factor K(sub rms) fracture mechanics concepts. The effect of retardation and residual stresses resulting from welding was also considered. It was found that all concepts gave good life predictions in all cases.

Sidawi, Jihad A.↗
NASA NTRS1995

An Experimental and Analytical Investigation of Stirling Space Power Converter Heater Head

NASA has identified the Stirling power converter as a prime candidate for the next generation power system for space applications requiring 60000 hr of operation. To meet this long-term goal, several critical components of the power converter have been analyzed using advanced structural assessment methods. Perhaps the most critical component, because of its geometric complexity and operating environment, is the power converter's heater head. This report describes the life assessment of the heater head which includes the characterization of a viscoplastic material model, the thermal and structural analyses of the heater head, and the interpolation of fatigue and creep test results of a nickel-base superalloy, Udimet 720 LI (Low Inclusions), at several elevated temperatures for life prediction purposes.

Abdul-Aziz, Ali↗
NASA NTRS2003

Near-Threshold Fatigue Crack Growth Behavior of Fine-Grain Nickel-Based Alloys

Constant-Kmax fatigue crack growth tests were performed on two finegrain nickel-base alloys Inconel 718 (DA) and Ren 95 to determine if these alloys exhibit near-threshold time-dependent crack growth behavior observed for fine-grain aluminum alloys in room-temperature laboratory air. Test results showed that increases in K(sub max) values resulted in increased crack growth rates, but no evidence of time-dependent crack growth was observed for either nickel-base alloy at room temperature.

Newman, John A.↗
NASA NTRS2002

Power Law Versus Exponential Form of Slow Crack Growth of Advanced Structural Ceramics: Dynamic Fatigue

The life prediction analysis based on an exponential crack velocity formulation was examined using a variety of experimental data on glass and advanced structural ceramics in constant stress-rate ("dynamic fatigue") and preload testing at ambient and elevated temperatures. The data fit to the strength versus In (stress rate) relation was found to be very reasonable for most of the materials. It was also found that preloading technique was equally applicable for the case of slow crack growth (SCG) parameter n > 30. The major limitation in the exponential crack velocity formulation, however, was that an inert strength of a material must be known priori to evaluate the important SCG parameter n, a significant drawback as compared to the conventional power-law crack velocity formulation.

Choi, Sung R.↗
NASA NTRS2008

The Effects of Heat Treatment and Microstructure Variations on Disk Superalloy Properties at High Temperature

The effects of heat treatment and resulting microstructure variations on high temperature mechanical properties were assessed for a powder metallurgy disk superalloy LSHR. Blanks were consistently supersolvus solution heat treated and quenched at two cooling rates, than aged at varying temperatures and times. Tensile, creep, and dwell fatigue crack growth tests were then performed at 704 C. Gamma' precipitate microstructures were quantified. Relationships between heat treatment-microstructure, heat treatment-mechanical properties, and microstructure-mechanical properties were assessed.

Gabb, Timothy P.↗
NASA NTRS2011

Resilient and Corrosion-Proof Rolling Element Bearings Made from Superelastic Ni-Ti Alloys for Aerospace Mechanism Applications

Mechanical components (bearings, gears, mechanisms) typically utilize hard materials to minimize wear and attain long life. In such components, heavily loaded contact points (e.g., meshing gear teeth, bearing ball-raceway contacts) experience high contact stresses. The combination of high hardness, heavy loads and high elastic modulus often leads to damaging contact stress. In addition, mechanical component materials, such as tool steel or silicon nitride exhibit limited recoverable strain (typically less than 1 percent). These material attributes can lead to Brinell damage (e.g., denting) particularly during transient overload events such as shock impacts that occur during the launching of space vehicles or the landing of aircraft. In this paper, a superelastic alloy, 60NiTi, is considered for rolling element bearing applications. A series of Rockwell and Brinell hardness, compressive strength, fatigue and tribology tests are conducted and reported. The combination of high hardness, moderate elastic modulus, large recoverable strain, low density, and intrinsic corrosion immunity provide a path to bearings largely impervious to shock load damage. It is anticipated that bearings and components made from alloys with such attributes can alleviate many problems encountered in advanced aerospace applications.

DellaCorte, Christopher↗
NASA NTRS2012

Comparison of an Inductance In-Line Oil Debris Sensor and Magnetic Plug Oil Debris Sensor

The objective of this research was to compare the performance of an inductance in-line oil debris sensor and magnetic plug oil debris sensor when detecting transmission component health in the same system under the same operating conditions. Both sensors were installed in series in the NASA Glenn Spiral Bevel Gear Fatigue Rig during tests performed on 5 gear sets (pinion/gear) when different levels of damage occurred on the gear teeth. Results of this analysis found both the inductance in-line oil debris sensor and magnetic plug oil debris sensor have benefits and limitations when detecting gearbox component damage.

Dempsey, Paula J.↗
NASA NTRS2014

Mass Reduction: The Weighty Challenge for Exploration Space Flight

Meeting nutritional and acceptability requirements is critical for the food system for an exploration class space mission. However, this must be achieved within the constraints of available resources such as water, crew time, stowage volume, launch mass and power availability.  Due to resource constraints, exploration class missions are not expected to have refrigerators or freezers for food storage, and current per person food mass must be reduced to improve mission feasibility.  The Packaged Food Mass Reduction Trade Study (Stoklosa, 2009) concluded that the mass of the current space food system can be effectively reduced by decreasing water content of certain foods and offering nutrient dense substitutes, such as meal replacement bars and beverages. Target nutrient ranges were established based on the nutritional content of the current breakfast and lunch meals in the ISS standard menu. A market survey of available commercial products produced no viable options for meal replacement bar or beverage products. New prototypes for both categories were formulated to meet target nutrient ranges. Samples of prototype products were packaged in high barrier packaging currently used for ISS and underwent an accelerated shelf life study at 31 degC and 41 degC (50% RH) for 24 weeks. Samples were assessed at the following time points: Initial, 6 weeks, 12 weeks, and 24 weeks. Testing at each time point included the following: color, texture, water activity, acceptability, and hexanal analysis (for food bars only). Proof of concept prototypes demonstrated that meal replacement food bars and beverages can deliver a comparable macronutrient profile while reducing the overall mass when compared to the ISS Standard Menu. Future work suggestions for meal replacement bars: Reformulation to include ingredients that reduce hardness and reduce browning to increase shelf life. Micronutrient analysis and potential fortification. Sensory evaluation studies including satiety tests and menu fatigue. Water Intake Analysis: The water in thermostabilized foods is considered as part of a crewmember's daily water intake. Extensive meal replacement would require further analyses to determine if additional water provisioning would be required per crewmember negating some of the mass savings.

Kloeris, Vickie L.↗
NASA NTRSDate not supplied

Impact of Powder Supply Variation on Mechanical Properties for Additive Manufacture of Alloy 718

The Additive Manufacturing Structural Integrity Initiative (AMSII) examined how a number of different Alloy 718 powder lots can create variation in microstructure and mechanical properties in parts fabricated using Laser Powder Bed Fusion. Being a common alloy, Alloy 718 powder can be found in a variety of compositions, fabrication techniques, and powder size distribution. Sixteen virgin powders, and three recycled powders were used to build samples for microstructure analysis, fatigue and tensile testing. The major impacts of the different powders manifested in variations in the microstructure, such as minor phases and grain size variation. There were corresponding variations in mechanical properties. A down-selection of powders were chosen for additional analysis, and a powder recyclability study was completed to look at the effect of reused powder.

Alloy 718↗
DOE OSTI2024

Structural Characterization of Deployed Thermoplastic and Thermoset Composite Tidal Turbine Blades

The National Renewable Energy Laboratory worked with Verdant Power to manufacture, and characterize, novel thermoplastic composite blades on their Gen5d 5 m diameter turbines at the Roosevelt Island Tidal Energy (RITE) site in the East River in N.Y. to demonstrate a low-cost manufacturing process for marine energy structures. Verdant had designed, manufactured, and deployed epoxy thermoset composite blades on three Gen5d turbines in October 2020. At a maintenance cycle in May 2021, a Gen5d turbine equipped with the NREL thermoplastic blades was deployed and retrieved in October 2021. Modal, static and fatigue structural characterization was performed on both blade types before and after the deployment. The static and modal test results showed that the thermoplastic blades were slightly stiffer than the epoxy blades both dry and after the deployment. The epoxy blades had about 8% increase in strain at the applied load after the deployment, whereas the thermoplastic blade strains were not changed significantly. Ultimately the thermoplastic blade failed during fatigue testing due to a crack which is thought to have initiated between the internal foam and the laminate at the location of the internal instrumentation. The Verdant Power Gen5d epoxy blades did not have this internal instrumentation and did not have this failure, performing adequately through the operational period. A lack of design information and fatigue data for both the thermoplastic laminates and the adhesive used means that further work is needed to fully understand his failure and the root cause analysis is ongoing. This paper provides details on the thermoplastic blade manufacturing, materials, test methodology and results.

17 WIND ENERGY↗
NASA NTRS1961

Residual Static Strength of ALuminum-Alloy Beams Containing Fatigue Cracks in the Tension Covers

Static tests were performed on 31 box beams containing fatigue cracks in order to determine their residual static strengths. The beams were constructed of 7075 and 2024 aluminum alloy according to several designs and employed stringers that were either bonded, riveted, or an integral part of the skin. skin (both aaterials) had the highest residual static strengths, whereas 7075 beams with integrally stiffened covers had the lowest residual static strengths. Except for the integrally stiffened beams, the skin material did not contribute to the residual static strength of the beams because the crack propagated across the skin before maximum load was reached. For the integrally stiffened beams, crack propagation and failure were synonymous. The test results are compared with predictions of the residual static strength. Fair agreement between predicted strength and actual strength was obtained for all beams tested.

Leybold, Herbert A.↗
NASA NTRS1978

Effect of wall thickness and material on flexural fatigue of hollow rolling elements

Hollow cylindrical bars were tested in a rolling-contact fatigue tester to determine the effects of material and outside diameter to inside diameter (OD/ID) ratios on fatigue failure mode and subsequent failure propagation. The range of applied loads with OD/ID ratios of 2.0, 1.6, 1.4, and 1.2 resulted in maximum tangential tensile stresses ranging from 165 to 655 MPa at the bore surface. Flexural failures of the hollow test bars occurred when this bore stress was 490 MPa or greater with AISI 52100 hollow bars and 338 MPa or greater with AISI M-50 hollow bars. Good correlation was obtained in relating the failures of these hollow bars with flexural failures of drilled balls from full-scale bearing test published previously.

Bamberger, E. N.↗
NASA NTRS1976

Flexural fatigue of hollow rolling elements

Hollow cylindrical bars were tested in the rolling-contact fatigue tester to determine the effects of material and outside diameter to inside diameter (OD/ID) ratios of 2.0, 1.6, 1.4, and 1.2 on fatigue failure mode and subsequent failure propagation. The range of applied loads with these OD/ID ratios resulted in maximum tangential tensile stresses ranging from 165 to 655 megapascals (24,000 to 95,000 psi) at the bore surface. Flexural failures of the hollow test bars occurred when this bore stress was 490 megapascals (71,000 psi) or greater with AISI 52100 hollow bars and 338 megapascals (49,000 psi) or greater with AISI M-50 hollow bars. Good correlation was obtained in relating the failures of these hollow bars with flexural failures of drilled balls from previously published full scale bearing tests.

Bamberger, E. N.↗
DOE OSTI2024

The Grain Boundary Relaxation (GBR) Approach for Manufacturing High Strength Nanocrystalline Lightweight Metals

The overarching goal of the project was to conduct research and development work as proposed in the Statement of Project Objective (SOPO) of the award document DE-FE-0009116. The project had 4 tasks and 12 milestones. All the milestone deliverables were completed. The accomplishments of the project objectives and technical discussions are described in Sections 3 and 4, respectively. The modeling and simulation work indicated that to increase the strength and stability of nanocrystalline aluminum (Al), selection of dopants, such as Mg, is necessary. It was predicted that the crystallite size should be less than 50 nm to give high strength. On the basis of modeling, cryo-milling of Al was conducted with the addition of Mg as a function of different times. The crystallite size of the cryo-milled powders was determined by XRD and TEM. Both measurements showed that the actual crystallite size of the grain was <40 nm. The thermal stability of the grain size was established as a function of temperature. It was established that the grain size was < 50 nm up to 500C. The crystallite size of the bulk sample prepared by spark plasma sintering (SPS) and cold spray (CS) additive manufacturing was less than <40 nm. The mechanical properties of the bulk samples prepared by SPS and CS, showed excellent microhardness, good tensile properties (>200 MPa) with moderate ductility and improved fatigue performance. Adding yttria stabilized zirconia (YSZ) improved the build thick of the CS sample, however the YSZ was getting embedded into the sample. A highly dense SPS samples sent for 3rd party testing to the Innovation Testing Services showed a minimum hardness of 180 HV with an average tensile strength of 512.5 MPa. The high cycle fatigue tests also showed an endurance limit of 179.5 MPa. The Energy cost evaluations showed an overall energy cost of around $\$$17.05 for the cryomilling and SPS processes and the total manufacturing cost calculations of $\$$78.14 for 1 kg of sample. The energy cost to prepare a Kg of CS sample is $\$$17.60 and the overall manufacturing cost is $\$$86.85.

36 MATERIALS SCIENCE↗
NASA NTRS1994

Fatigue resistance of unnotched and post impact(+/- 30 deg/0 deg) 3-D braided composites

The fatigue resistance of a multiaxial braided (3-D) graphite/expoxy composite in both unnotched and post impacted conditions has been evaluated. The material tested is a (+/- 30/0 deg) multiaxial braid constructed from AS4/12K tow graphite fibers and British Petroleum E905L epoxy resin. These materials were braided as dry preforms and the epoxy was added using a resin transfer molding process (RTM). The unnotched and post-impact specimens were tested in compression-compression fatigue at 10 Hz with a stress ratio of R=10. The unnotched tension-tension fatigue specimens were tested at S Hz with a stress ration of R=0.1. Damage initiation and growth was documented through the application of radiography and ultrasonic through transmission (C-scans). Visible inspection of surface and edge damage was also noted to describe the initiation and progression of damage in these materials. The mechanisms leading to damage initiation were established and failure modes were determined. Stiffness and strength degradation were measured as a function of applied cycles. These 3-D braided composite results were compared to strain levels currently used to design primary structure in commercial aircraft composite components made from prepreg tape and autoclave cured.

Portanova, Marc A.↗