DOE OSTI2023
There is a gap in our understanding of the behavior of fused and molten fuel salts containing unavoidable contamination, such as those due to fabrication, handling, or storage. Therefore, this work used calorimetry to investigate the change in liquidus temperature of PuCl 3 , having an unknown purity and that had been in storage for several decades. Further research was performed by additions of NaCl, making several compositions within the binary system, and summarizing the resulting changes, if any, to the phase diagram. The melting temperature of the PuCl 3 was determined to be 746.5°C, approximately 20°C lower than literature reported values, most likely due to an excess of Pu metal in the PuCl 3 either due to the presence of metallic plutonium remaining from incomplete chlorination or due to the solubility of Pu in PuCl 3 . From the melting temperature, it was determined that the PuCl 3 contained between 5.9 to 6.2mol% Pu metal. Analysis of the NaCl-PuCl 3 samples showed that using the Pu rich PuCl 3 resulted in significant changes to the NaCl-PuCl 3 phase diagram. Most notably an unreported phase transition occurring at approximately 406°C and a new eutectic composition of 52.7mol% NaCl–38.7mol% PuCl 3 –2.5mol% Pu which melted at 449.3°C. Additionally, an increase in the liquidus temperatures was seen for NaCl rich compositions while lower liquidus temperatures were seen for PuCl 3 rich compositions. It can therefore be concluded that changes will occur in the NaCl-PuCl 3 binary system when using PuCl 3 with excess Pu metal. However, melting temperature analysis can provide valuable insight into the composition of the PuCl 3 and therefore the NaCl-PuCl 3 system.
11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗