CARES/Life Ceramics Durability Evaluation Software Enhanced for Cyclic Fatigue

The CARES/Life computer program predicts the probability of a monolithic ceramic component's failure as a function of time in service. The program has many features and options for materials evaluation and component design. It couples commercial finite element programs--which resolve a component's temperature and stress distribution--to reliability evaluation and fracture mechanics routines for modeling strength-limiting defects. The capability, flexibility, and uniqueness of CARES/Life have attracted many users representing a broad range of interests and has resulted in numerous awards for technological achievements and technology transfer. Recent work with CARES/Life was directed at enhancing the program s capabilities with regards to cyclic fatigue. Only in the last few years have ceramics been recognized to be susceptible to enhanced degradation from cyclic loading. To account for cyclic loads, researchers at the NASA Lewis Research Center developed a crack growth model that combines the Power Law (time-dependent) and the Walker Law (cycle-dependent) crack growth models. This combined model has the characteristics of Power Law behavior (decreased damage) at high R ratios (minimum load/maximum load) and of Walker law behavior (increased damage) at low R ratios. In addition, a parameter estimation methodology for constant-amplitude, steady-state cyclic fatigue experiments was developed using nonlinear least squares and a modified Levenberg-Marquardt algorithm. This methodology is used to give best estimates of parameter values from cyclic fatigue specimen rupture data (usually tensile or flexure bar specimens) for a relatively small number of specimens. Methodology to account for runout data (unfailed specimens over the duration of the experiment) was also included.

Nemeth, Noel N.↗

Large-displacement structural durability analyses of simple bend specimen emulating rocket nozzle liners

Large-displacement elastic and elastic-plastic, finite-element stress-strain analyses of an oxygen-tree high-conductivity (OFHC) copper plate specimen were performed using an updated Lagrangian formulation. The plate specimen is intended for low-cost experiments that emulate the most important thermomechanical loading and failure modes of a more complex rocket nozzle. The plate, which is loaded in bending at 593 C, contains a centrally located and internally pressurized channel. The cyclic crack initiation lives were estimated using the results from the analyses and isothermal strain-controlled low-cycle fatigue data for OFHC copper. A comparison of the predicted and experimental cyclic lives showed that an elastic analysis predicts a longer cyclic life than that observed in experiments by a factor greater than 4. The results from elastic-plastic analysis for the plate bend specimen, however, predicted a cyclic life in close agreement with experiment, thus justifying the need for the more rigorous stress-strain analysis.

Arya, Vinod K.↗

Distribution of Inclusion-Initiated Fatigue Cracking in Powder Metallurgy Udimet 720 Characterized

In the absence of extrinsic surface damage, the fatigue life of metals is often dictated by the distribution of intrinsic defects. In powder metallurgy (PM) alloys, relatively large defects occur rarely enough that a typical characterization with a limited number of small volume fatigue test specimens will not adequately sample inclusion-initiated damage. Counterintuitively, inclusion-initiated failure has a greater impact on the distribution in PM alloy fatigue lives because they tend to have fewer defects than their cast and wrought counterparts. Although the relative paucity of defects in PM alloys leads to higher mean fatigue lives, the distribution in observed lives tends to be broader. In order to study this important failure initiation mechanism without expending an inordinate number of specimens, a study was undertaken at the NASA Glenn Research Center where known populations of artificial inclusions (seeds) were introduced to production powder. Fatigue specimens were machined from forgings produced from the seeded powder. Considerable effort has been expended in characterizing the crack growth rate from inclusion-initiated cracks in seeded PM alloys. A rotating and translating positioning system, with associated software, was devised to map the surface inclusions in low-cycle fatigue (LCF) test bars and to monitor the crack growth from these inclusions. The preceding graph illustrates the measured extension in fatigue cracks from inclusions on a seeded LCF test bar subjected to cyclic loading at a strain range of 0.8 percent and a strain ratio (max/min) of zero. Notice that the observed inclusions fall into three categories: some do not propagate at all (arrest), some propagate with a decreasing crack growth rate, and a few propagate at increasing rates that can be modeled by fracture mechanics. The following graph shows the measured inclusion-initiated crack growth rates from 10 interrupted LCF tests plotted against stress intensities calculated for semi-elliptical cracks with the observed surface lengths. The expected scatter in the crack growth rates for stress intensity ranges near threshold is observed. These data will be used to help determine the distribution in growth rates of cracks emanating from inclusions as well as the proportion of cracks that arrest under various loading conditions.

Bonacuse, Peter J.↗

Crack tip field and fatigue crack growth in general yielding and low cycle fatigue

Fatigue life consists of crack nucleation and crack propagation periods. Fatigue crack nucleation period is shorter relative to the propagation period at higher stresses. Crack nucleation period of low cycle fatigue might even be shortened by material and fabrication defects and by environmental attack. In these cases, fatigue life is largely crack propagation period. The characteristic crack tip field was studied by the finite element method, and the crack tip field is related to the far field parameters: the deformation work density, and the product of applied stress and applied strain. The cyclic carck growth rates in specimens in general yielding as measured by Solomon are analyzed in terms of J-integral. A generalized crack behavior in terms of delta is developed. The relations between J and the far field parameters and the relation for the general cyclic crack growth behavior are used to analyze fatigue lives of specimens under general-yielding cyclic-load. Fatigue life is related to the applied stress and strain ranges, the deformation work density, crack nucleus size, fracture toughness, fatigue crack growth threshold, Young's modulus, and the cyclic yield stress and strain. The fatigue lives of two aluminum alloys correlate well with the deformation work density as depicted by the derived theory. The general relation is reduced to Coffin-Manson low cycle fatigue law in the high strain region.

Minzhong, Z.↗

Thermomechanical fatigue resistance of low temperature solder for multiwire interconnects in photovoltaic modules

Novel interconnect technologies leveraging low melting temperature solders, such as multiwire interconnects, are being deployed in photovoltaic (PV) modules for improved reliability through interconnect redundancy and lower thermal loads during interconnection and lamination. However, the equivalency of standardized accelerated testing to field conditions has not yet been established for these emerging technologies. In this study, the thermomechanical fatigue resistance of low temperature solder alloys is investigated and compared to that of conventional SnPb to assess the acceleration behavior of these alloys. While InSn is shown to have sufficient thermomechanical fatigue resistance on the order of that of SnPb, these results indicate Sn–Bi alloys may have poor thermomechanical fatigue resistance at field conditions. The results also show that Sn–Bi alloys have thermal cycling acceleration factors of less than one. This indicates that the standardized accelerated thermal cycling test, such as that in IEC 61215, will produce misleading results for Sn–Bi alloys and that unique testing is required for this PV module architecture. Though accelerated thermal cycling may be a meaningful qualification test for SnPb solder joints, these results suggest that mechanical loading may be a more appropriate test for Sn–Bi multiwire interconnects. This is due to the distinct processing and geometry of multiwire interconnects which may allow for mechanical, rather than strictly metallurgical interconnections.

14 SOLAR ENERGY↗

Fatigue, Creep-Fatigue, and Thermomechanical Fatigue Life Testing of Alloys

The fatigue crack initiation resistance of an alloy is determined by conducting a series of tests over a range of values of stress amplitude or strain range. The observed number of cycles to failure is plotted against the stress amplitude or strain range to obtain a fatigue curve. The fatigue properties quoted for an alloy are typically the constants used in the equation(s) that describe the fatigue curve. Fatigue lives of interest may be as low as 10(exp 2) or higher than 10(exp 9) cycles. Because of the enormous scatter associated with fatigue, dozens of tests may be needed to confidently establish a fatigue curve, and the cost may run into several thousands of dollars. To further establish the effects on fatigue life of the test temperature, environment, alloy condition, mean stress effects, creep-fatigue effects, thermomechanical cycling, etc. requires an extraordinarily large and usually very costly test matrix. The total effort required to establish the fatigue resistance of an alloy should not be taken lightly. Fatigue crack initiation tests are conducted on relatively small and presumed to be initially crack-free, samples of an alloy that are intended to be representative of the alloy's metallurgical and physical condition. Generally, samples are smooth and have uniformly polished surfaces within the test section. Some may have intentionally machined notches of well-controlled geometry, but the surface at the root of the notch is usually not polished. The purpose of polishing is to attain a reproducible surface finish. This is to eliminate surface finish as an uncontrolled variable. Representative test specimen geometries will be discussed later. Test specimens are cyclically loaded until macroscopically observable cracks initiate and eventually grow to failure. Normally, the fatigue failure life of a specimen is defined as the number of cycles to separation of the specimen into two pieces. Alternative definitions are becoming more common, particularly for low-cycle fatigue testing, wherein some prescribed indication of impending failure due to cracking is adopted. Specific criteria will be described later. As a rule, cracks that develop during testing are not measured nor are the test parameters intentionally altered owing to the presence of cracking.

Halford, Gary R.↗

Predictive analysis of metal fatigue in the high cyclic life range

This report summarizes various aspects of predictive approaches in high cycle fatigue, hcf. The distinction between hcf and low cycle fatigue, lcf, is discussed in relation to the transition life and strainrange, and curves are presented to establish regions wherein each range predominates depending on the properties of any material of interest. The role of loading order on hcf in cumulative damage analysis is also discussed, together with mean stress effects and their relaxation. Also briefly discussed are high temperature fatigue and ultra-high cycle fatigue.

Manson, S. S.↗

Creep fatigue life prediction for engine hot section materials (isotropic)

The first two years of a two-phase program aimed at improving the high temperature crack initiation life prediction technology for gas turbine hot section components are discussed. In Phase 1 (baseline) effort, low cycle fatigue (LCF) models, using a data base generated for a cast nickel base gas turbine hot section alloy (B1900+Hf), were evaluated for their ability to predict the crack initiation life for relevant creep-fatigue loading conditions and to define data required for determination of model constants. The variables included strain range and rate, mean strain, strain hold times and temperature. None of the models predicted all of the life trends within reasonable data requirements. A Cycle Damage Accumulation (CDA) was therefore developed which follows an exhaustion of material ductility approach. Material ductility is estimated based on observed similarities of deformation structure between fatigue, tensile and creep tests. The cycle damage function is based on total strain range, maximum stress and stress amplitude and includes both time independent and time dependent components. The CDA model accurately predicts all of the trends in creep-fatigue life with loading conditions. In addition, all of the CDA model constants are determinable from rapid cycle, fully reversed fatigue tests and monotonic tensile and/or creep data.

Moreno, Vito↗

Digital Twin Model for Advanced Manufacture of a Rotating Detonation Engine Injector

A digital twin material model (DTMM) of an additive manufacturing (AM) process was created to advance the state of the art in rotating detonation engine (RDE) injector design. Current RDE injectors are designed with large pressure drops, enabling a stable and repeatable combustion process. However, this comes at the cost of system efficiency. For the technology to transition to commercial fossil-based power generation, it is important to develop injectors with reduced flow losses. Low-loss injectors are difficult to design and manufacture with conventional manufacturing techniques. AM enables new design options, but the AM manufacturing process must be thoroughly understood to result in a robust design. A DTMM provides the necessary insight by defining the cause-effect relationships between process parameters, microstructure features, and properties. Therefore, a DTMM to support the design and manufacturing process was developed and applied to the design of a new additively manufactured low-loss injector. The injector combustion behavior was characterized through hot-fire tests, and mechanical performance was compared to the DTMM predictions. The two project goals were the successful development of the DTMM and the demonstration of an improved RDE injector design. The RDE injector design and DTMM developments occurred on parallel but dependent paths. The injector was designed to reduce pressure drop by increasing the cross-sectional flow area ratio between the injector air passages and the combustor annulus. This resulted in less structural material, raising the concern that thin members would be susceptible to high-cycle fatigue (HCF) under the periodic loading inherent to an RDE. It was most important for the DTMM to predict behavior in these features; therefore, the injector design concept guided the material thicknesses used in fatigue tests. The DTMM development started by manufacturing a series of coupons over the range of possible AM process variations. A design-of-experiment approach was used to select which process variable combinations gave the most efficient coverage relevant to the injector design space. The microstructure in each of these coupons was characterized, and then computational methods were used to create a numerical model of the correlation between process variables and microstructure. Next, a set of HCF samples were tested to calibrate existing models that map microstructure to HCF performance. Together, these two links formed the DTMM that calculates HCF behavior from AM process variables. Two injector prototypes were additively manufactured. The first injector design strategy aggressively pursued low-loss performance by substantially increasing the oxidizer flow area. The combination of manufacturing lead times and the fatigue testing schedule meant that the DTMM was not available when building this first prototype. Therefore, its process parameters were chosen based on a manual review of the available coupon data. This prototype was built successfully and evaluated in 58 combustion tests. Sustained detonation was achieved with remarkably reduced pressure loss, and some tests even displayed pressure loss characteristics similar to conventional gas turbine combustors. This achieved the project goal of improving RDE injector design. The second injector was manufactured according to the optimized parameters predicted by the DTMM. The flow area modifications of this injector were less aggressive than the first injector since demonstrating low pressure loss was not an objective of the second hot-fire test series. Rather, the test objective was to cause high cycle fatigue failure in the part due to periodic loading from the rotating detonation wave. The observed number of cycles to failure was to be compared to the number predicted by the DTMM and thereby assess the utility of the DTMM in component design. However, the required level of vibration was not obtained during combustion. Therefore, high cycle fatigue was not experienced in the hot-fire tests of the second injector. Fatigue data was obtained by further testing the second injector in a conventional HCF test apparatus. The injector demonstrated HCF strength above the DTMM prediction. In fact, it did not fail and testing was only discontinued due to reaching the end of the period of performance. This points to some success in the project’s primary goal of successfully developing and applying the DTMM to a component design. Implementing the DTMM recommendations for optimal processing parameters led to a part with acceptable properties. The DTMM was also shown to be an efficient correlator of data and to provide insight into the relationship between process settings, microstructure, and property performance. However, the failure of the DTMM prediction to match the experimental result of the injector fatigue test also points to the need to include significantly more data in the model development. In this project, coupons made with identical processing parameters exhibited drastically different properties from each other and from the injector part, which clearly influences the accuracy of a model that predicts performance based on parameters. Uncertainties in the build process must be quantified to develop more robust models. A denser and broader matrix of coupon process and geometry variations, several repeated builds of every point, more in-situ build process measurements, and direct observation of tensile and HCF sample microstructure (as opposed to separate microstructure specimens) are recommendations to improve future AM modeling efforts.

20 FOSSIL-FUELED POWER PLANTS↗

Microstructural Model for Creep-Fatigue Interaction in Grade 91 Steel

This report describes the completion of a crystal plasticity finite element simulation framework for creep-fatigue deformation and damage in Grade 91 steel. In addition to a description of the framework and a set of verification calculations, the report details an initial set of simulations applying the framework to examine low cycle fatigue and creep-fatigue interaction in Grade 91 at 600° C. Grade 91 is a likely material for future advanced microreactors and creep-fatigue will be a limiting structural damage mechanism, particularly for mobile reactors or load following systems. The framework described here could provide a better understanding of creep-fatigue damage mechanisms and directly examine creep, fatigue, and creep-fatigue interaction for Grade 91 at realistic component service conditions. This in turn could lead to improved design methods and component life estimation approaches, leading to more efficient and economical component designs.

36 MATERIALS SCIENCE↗

Factors Influencing Dwell Fatigue Cracking in Notches of Powder Metallurgy Superalloys

The influences of heat treatment and cyclic dwells on the notch fatigue resistance of powder metallurgy disk superalloys were investigated for low solvus high refractory (LSHR) and ME3 disk alloys. Disks were processed to produce material conditions with varied microstructures and associated mechanical properties. Notched specimens were first subjected to baseline dwell fatigue cycles having a dwell at maximum load, as well as tensile, stress relaxation, creep rupture, and dwell fatigue crack growth tests at 704 C. Several material heat treatments displayed a bimodal distribution of fatigue life with the lives varying by two orders-of-magnitude, while others had more consistent fatigue lives. This response was compared to other mechanical properties, in search of correlations. The wide scatter in baseline dwell fatigue life was observed only for material conditions resistant to stress relaxation. For selected materials and conditions, additional tests were then performed with the dwells shifted in part or in total to minimum tensile load. The tests performed with dwells at minimum load exhibited lower fatigue lives than max dwell tests, and also exhibited early crack initiation and a substantial increase in the number of initiation sites. These results could be explained in part by modeling evolution of peak stresses in the notch with continued dwell fatigue cycling. Fatigue-environment interactions were determined to limit life for the fatigue cycles with dwells.

Gabb, T. P.↗

Low-cycle thermal fatigue

A state-of-the-art review is presented of the field of thermal fatigue. Following a brief historical review, the concept is developed that thermal fatigue can be viewed as processes of unbalanced deformation and cracking. The unbalances refer to dissimilar mechanisms occurring in opposing halves of thermal fatigue loading and unloading cycles. Extensive data summaries are presented and results are interpreted in terms of the unbalanced processes involved. Both crack initiation and crack propagation results are summarized. Testing techniques are reviewed, and considerable discussion is given to a technique for thermal fatigue simulation, known as the bithermal fatigue test. Attention is given to the use of isothermal life prediction methods for the prediction of thermal fatigue lives. Shortcomings of isothermally-based life prediction methods are pointed out. Several examples of analyses and thermal fatigue life predictions of high technology structural components are presented. Finally, numerous dos and don'ts relative to design against thermal fatigue are presented.

Halford, G. R.↗

The high temperature deformation in cyclic loading of a single crystal nickel-base superalloy

The high temperature cyclic stress softening response of the single crystal nickel-base superalloy PWA 1480 was investigated. Specimens oriented near the 001- and 111-lines were tested at 1050 C in low-cycle fatigue and then microstructurally evaluated. The 001- and 111-line specimens had dissimilar flow behavior in monotonic tensile tests, but comparable softening in low-cycle fatigue. This softening was accompanied by rapid generation of dislocation networks at the gamma-gamma-prime interfaces and by a slower time-dependent coarsening of gamma-prime precipitates. Due to the rapid formation of a dislocation substructure at the gamma-gamma-prime interfaces, the cyclic stress softening could be modeled with an existing theory which related cyclic stress to the evolving microstructure and dislocation structure.

Gabb, T. P.↗

Fatigue Performance of an Improved Creep Strength 10%Cr Steel

The deployment of 9-12% Cr steels for elevated temperature applications up to 650 °C presents a cost-effective alternative to more expensive nickel-based alloys in steam turbine power generation. To enhance creep resistance at this temperature range, a novel ferritic-martensitic steel, designated CPJ7, was developed and fabricated at the National Energy Technology Laboratory. The alloy design aimed to mitigate the transformation of strengthening carbides into deleterious phases that degrade creep performance. Results have demonstrated that CPJ7 exhibits favorable creep and oxidation resistance at 650 °C. However, its fatigue performance remains unexplored. This study builds upon prior research by evaluating the low cycle fatigue behavior of CPJ7 and verifying that modifications beneficial to creep performance were not detrimental to the fatigue performance. The alloy was tested at both 650 °C and ambient temperature under fully reversed bending conditions (R = − 1) and a load ratio of 0.05. Furthermore, the alloy exhibits cyclic softening, a behavior consistent with other 9-10 wt.% Cr steels. Analysis of the microstructure and hysteresis loops further corroborate cyclic softening mechanisms typical of ferritic-martensitic steels. Overall, the fatigue performance of CPJ7 meets or exceeds that of P91 steel, demonstrating its potential for high-temperature structural applications.

9% Cr ferritic-martensitic steel↗

Additive Manufacturing Flaw Assessment Methodology

An evolution fatigue data and flaw tolerance of components produced using the Powder Bed Fusion (PBF) Additive Manufacturing (AM) process is documented in this report. Initial differences in fatigue data for AM components compared to smooth bar fatigue data indicated a need for a more detailed analysis of AM data available in technical literature. The investigation was initiated to support the development of a fatigue analysis methodology for AM components to support the of codification of AM technology for pressure equipment. The project was initiated to collect and analyze stainless steel 304L and 316L AM fatigue test data and corresponding process and quality information to develop S-N and E-N based fatigue data representation. Additional AM fatigue test data including Inconel Ti-6-4 and aluminum alloys were also considered for comparison purposes Metallic AM parts tend to contain various forms of defects distributed throughout the part. If an AM part is subjected to fatigue loading in service, a fatigue analysis needs to be performed during the design process to ensure an acceptable service life for the part. Post-process machining and polishing do not to improve fatigue resistance in any significant degree. The low cycle fatigue regime is of particular interest to this project in support of flaw acceptance criteria currently under development by ASME’s BPTCS/BNCS. Internal defects become exposed as external surface defects during machining for the machining of the AM part to final dimensions. This implies that as long as inherent AM defects are within a controlled limit in terms of both size and distribution characteristics, the corresponding fatigue test data in terms of either S-N (stress life) or E-N (strain life) can be investigated and characterized to establish fatigue properties of AM parts for design and fatigue evaluation purposes. The resulting S-N or E-N curves and their scatter bands can be used to derive fatigue design allowable stress values by capturing the effects of distributed discontinuities within an acceptable limit.

36 MATERIALS SCIENCE↗

High Fidelity Simulations of Unsteady Flow through Turbopumps and Flowliners

High fidelity computations were carried out to analyze the orbiter LH2 feedline flowliner. Computations were performed on the Columbia platform which is a 10,240-processor supercluster consisting of 20 Altix nodes with 512 processor each. Various computational models were used to characterize the unsteady flow features in the turbopump, including the orbiter Low-Pressure-Fuel-Turbopump (LPFTP) inducer, the orbiter manifold and a test article used to represent the manifold. Unsteady flow originating from the orbiter LPFTP inducer is one of the major contributors to the high frequency cyclic loading that results in high cycle fatigue damage to the gimbal flowliners just upstream of the LPFTP. The flow fields for the orbiter manifold and representative test article are computed and analyzed for similarities and differences. The incompressible Navier-Stokes flow solver INS3D, based on the artificial compressibility method, was used to compute the flow of liquid hydrogen in each test article.

Kiris, Cetin C.↗

High Fidelity Simulations for Unsteady Flow Through the Orbiter LH2 Feedline Flowliner

High fidelity computations were carried out to analyze the orbiter M2 feedline flowliner. Various computational models were used to characterize the unsteady flow features in the turbopump, including the orbiter Low-Pressure-Fuel-Turbopump (LPFTP) inducer, the orbiter manifold and a test article used to represent the manifold. Unsteady flow originating from the orbiter LPFTP inducer is one of the major contributors to the high frequency cyclic loading that results in high cycle fatigue damage to the gimbal flowliners just upstream of the LPFTP. The flow fields for the orbiter manifold and representative test article are computed and analyzed for similarities and differences. An incompressible Navier-Stokes flow solver INS3D, based on the artificial compressibility method, was used to compute the flow of liquid hydrogen in each test article.