Origin of proton irradiation-induced deep acceptors in Al 0.70 Ga 0.30 N
Deep level defect introduction and carrier removal were characterized using steady-state photocapacitance (SSPC), deep level transient spectroscopy (DLTS) and lighted capacitance–voltage for proton irradiated n-type Al 0.70 Ga 0.30 N Schottky diodes grown by metal-organic vapor phase epitaxy on AlN-on-sapphire templates. SSPC observed deep levels in the as-grown diode with zero-phonon transition energies of 2.20, 2.65, 3.10, 3.40, and 4.65 eV relative to the conduction band minimum (E c ), and an additional deep level emerged at 1.20 eV with irradiation. Lighted capacitance–voltage measurements quantified the deep level concentration (N t ) of states detected by SSPC, and it was observed that N t increased with proton fluence only for the 1.2 and 4.65 eV levels. Carrier removal was much larger than the increase in N t of the 1.2 and 4.65 eV deep levels, suggesting that radiation-induced deep level compensators existed beyond what was detected with SSPC. DLTS detected additional, proton-induced deep acceptors at E c —0.55, 0.82, and 1.16 eV, the latter of which is likely the same 1.20 eV deep state observed by SSPC. The concentration of the E c —0.82 eV defect state was large enough to reconcile carrier removal with total deep level introduction. Comparing the E c —0.82 and 1.16 eV deep acceptor levels to previous experimental and theoretical reports suggests that their atomistic origins could be the nitrogen vacancy (V N ) and oxygen substituting on the nitrogen sub-lattice (O N ), respectively. This defect behavior contrasts starkly with GaN, where V N and O N are shallow donors, and demonstrates that the electronic properties of defects can evolve drastically within the AlGaN alloy system ranging from wide bandgap GaN to ultra-wide bandgap AlN.