A Multi-Parameter Approach for Calculating Crack Instability

An accurate fracture control analysis of spacecraft pressure systems, boosters, rocket hardware and other critical low-cycle fatigue cases where the fracture toughness highly impacts cycles to failure requires accurate knowledge of the material fracture toughness. However, applicability of the measured fracture toughness values using standard specimens and transferability of the values to crack instability analysis of the realistically complex structures is refutable. The commonly used single parameter Linear Elastic Fracture Mechanics (LEFM) approach which relies on the key assumption that the fracture toughness is a material property would result in inaccurate crack instability predictions. In the past years extensive studies have been conducted to improve the single parameter (K-controlled) LEFM by introducing parameters accounting for the geometry or in-plane constraint effects]. Despite the importance of the thickness (out-of-plane constraint) effects in fracture control problems, the literature is mainly limited to some empirical equations for scaling the fracture toughness data] and only few theoretically based developments can be found. In aerospace hardware where the structure might have only one life cycle and weight reduction is crucial, reducing the design margin of safety by decreasing the uncertainty involved in fracture toughness evaluations would result in lighter hardware. In such conditions LEFM would not suffice and an elastic-plastic analysis would be vital. Multi-parameter elastic plastic crack tip field quantifying developments combined with statistical methods] have been shown to have the potential to be used as a powerful tool for tackling such problems. However, these approaches have not been comprehensively scrutinized using experimental tests. Therefore, in this paper a multi-parameter elastic-plastic approach has been used to study the crack instability problem and the transferability issue by considering the effects of geometrical constraints as well as the thickness. The feasibility of the approach has been examined using a wide range of specimen geometries and thicknesses manufactured from 7075-T7351 aluminum alloy.

Zanganeh, M.↗

Enhanced composites via selective interfacial modification

A laminate comprising a first ply, a second ply, and a third ply which sandwiching the second ply between the first ply and the third ply. The laminate further includes a first plurality of interfacial modifiers arranged between opposing faces of the first ply and the second ply. The first plurality of interfacial modifiers are arranged in a first pattern. The laminate includes a second plurality of interfacial modifiers arranged between opposing faces of the second ply and the third ply such that the first plurality of interfacial modifiers and the second plurality of interfacial modifiers are arranged on opposite faces of the second ply. The second plurality of interfacial modifiers are arranged in a second pattern. The first pattern and the second pattern are configured to increase crack growth resistance of the laminate by selectively toughening portions of the laminate to control propagation of interfacial cracks within the laminate.

Sills, Ryan B.↗

Application of two creep fatigue life models for the prediction of elevated temperature crack initiation of a nickel base alloy

Cyclic Damage Accumulation (CDA) and Total Strain-Strain Range Partitioning (TS-SRP) models for predicting the creep-fatigue crack initiation life of high temperature alloys are presented. The models differ in their fundamental assumptions regarding the controlling parameters for fatigue crack initiation and in the amount of data required to determine model constants. The CDA model represents a ductility exhaustion approach and uses stress quantities to calculate the cyclic fatigue damage. The TS-SRP model is based on the use of total mechanical strain and earlier concepts of the Strain Range Partitioning Method. Both models were applied to a well controlled fatigue data set at a high temperature nickel base alloy, B1900 + Hf, tested at 1600 F and 1800 F. The tests were divided into a baseline data set required to determine model constants and a verification data set for evaluation of the predictive capability of the models. Both models correlated the baseline data set to within factors of two in life, and predicted the verification data set to within a factor of three or better. In addition, sample calculations to demonstrate the application of each model and discusions of the predictive capabilities and areas requiring further development are presented.

Moreno, V.↗

Effect of Control Mode and Test Rate on the Measured Fracture Toughness of Advanced Ceramics

The effects of control mode and test rate on the measured fracture toughness of ceramics were evaluated by using chevron-notched flexure specimens in accordance with ASTM C1421. The use of stroke control gave consistent results with about 2% (statistically insignificant) variation in measured fracture toughness for a very wide range of rates (0.005 to 0.5 mm/min). Use of strain or crack mouth opening displacement (CMOD) control gave approx. 5% (statistically significant) variation over a very wide range of rates (1 to 80 μm/m/s), with the measurements being a function of rate. However, the rate effect was eliminated by use of dry nitrogen, implying a stress corrosion effect rather than a stability effect. With the use of a nitrogen environment during strain controlled tests, fracture toughness values were within about 1% over a wide range of rates (1 to 80 micons/m/s). CMOD or strain control did allow stable crack extension well past maximum force, and thus is preferred for energy calculations. The effort is being used to confirm recommendations in ASTM Test Method C1421 on fracture toughness measurement.

silicon nitride↗

Repairing High γ’ Hot Section Gas Turbine Components Using Advanced Manufacturing

This article describes the ability to use laser-blown powder deposition to repair high γ' IN-100 superalloy gas turbine components. The influence of various process conditions on the ability to make crack-free IN-100 deposits over surrogate high γ' alloys was investigated to identify cracking mechanisms in the deposit and heat-affected zones (HAZs). The various crack formation mechanisms, such as solidification cracking and liquation cracking, were evaluated using multiscale characterization and numerical simulation. The cracking in the deposit region was predominantly solidification cracking, while those observed in the HAZ were liquation cracking. The results showed that controlling thermally induced residual stresses is the key to eliminating cracking, and the optimum preheat temperature was determined. In conclusion, the results were then contrasted with those in published literature and an approach to effectively repair hot section parts was presented.

36 MATERIALS SCIENCE↗

Impact of polymer additives on crack mitigation of rod-coated fuel cell cathode catalyst layers

Cracks in catalyst layers (CLs) are a potential source of long-term failure in a fuel cell membrane electrode assembly (MEA). While modifications to the CL ink formulation can affect the degree of cracking, these changes may lead to lower initial performance than their cracked analogues due to the established link between formulation and performance. In this work, we explored the use of polymeric additives to mitigate CL cracks. Small quantities of poly (acrylic acid), poly (ethylene oxide), poly (methyl methacrylate), or poly (vinyl alcohol) - 5 wt% relative to ionomer mass - were added to the ink prior to its final mixing. Poly (vinyl alcohol) resulted in crack-free CLs, whereas the other polymers resulted in CLs with similar crack percentages as the control CL. Through a combination of transmission electron microscopy, X-ray computed tomography, and infrared spectroscopy, we ascribed the crack-mitigating mechanism of poly (vinyl alcohol) to its ability to hydrogen-bond with Nafion, the ion conducting polymer binder in the catalyst ink. Initial performance of this non-cracked electrode exhibited nearly identical electrochemical behavior to its cracked counterpart, demonstrating that PVA additives successfully reduce cracks while maintaining cell initial performance.

30 DIRECT ENERGY CONVERSION↗

Test program to provide confidence in liquid oxygen cooling of hydrocarbon fueled rocket thrust chambers

An experimental program has been planned at the NASA Lewis Research Center to build confidence in the feasibility of liquid oxygen cooling for hydrocarbon fueled rocket engines. Although liquid oxygen cooling has previously been incorporated in test hardware, more runtime is necessary to gain confidence in this concept. In the previous tests, small oxygen leaks developed at the throat of the thrust chamber and film cooled the hot-gas side of the chamber wall without resulting in catastrophic failure. However, more testing is necessary to demonstrate that a catastrophic failure would not occur if cracks developed further upstream between the injector and the throat, where the boundary layer has not been established. Since under normal conditions cracks are expected to form in the throat region of the thrust chamber, cracks must be initiated artificially in order to control their location. Several methods of crack initiation are discussed in this report. Four thrust chambers, three with cracks and one without, should be tested. The axial location of the cracks should be varied parametrically. Each chamber should be instrumented to determine the effects of the cracks, as well as the overall performance and durability of the chambers.

Armstrong, E. S.↗

Test program to provide confidence in liquid oxygen cooling of hydrocarbon fueled rocket thrust chambers

In previous tests of liquid oxygen cooling of hydrocarbon fueled rocket engines, small oxygen leaks developed at the throat of the thrust chamber and film cooled the hot gas side of the chamber wall without resulting in catastrophic failure. However, more testing is necessary to demonstrate that a catastropic failure would not occur if cracks developed further upstream between the injector and the throat, where the boundary layer has not been established. Since under normal conditions cracks are expected to form in the throat region of the thrust chamber, cracks must be initiated artificially in order to control their location. Several methods of crack initiation are discussed here.

Armstrong, Elizabeth S.↗

Elevated temperature crack growth in aluminum alloys: Tensile deformation of 2618 and FVS0812 aluminum alloys

Understanding the damage tolerance of aluminum alloys at elevated temperatures is essential for safe applications of advanced materials. The objective of this project is to investigate the time dependent subcritical cracking behavior of powder metallurgy FVS0812 and ingot metallurgy 2618 aluminum alloys at elevated temperatures. The fracture mechanics approach was applied. Sidegrooved compact tension specimens were tested at 175, 250, and 316 C under constant load. Subcritical crack growth occurred in each alloy at applied stress intensity levels (K) of between about 14 and 25 MPa/m, well below K (sub IC). Measured load, crack opening displacement and displacement rate, and crack length and growth rate (da/dt) were analyzed with several continuum fracture parameters including, the C-integral, C (sub t), and K. Elevated temperature growth rate data suggest that K is a controlling parameter during time dependent cracking. For FVS0812, da/dt is highest at 175 C when rates are expressed as a function of K. While crack growth rate is not controlled by C (sub t) at 175 C, da/dt appears to better correlate with C (sub t) at higher temperatures. Creep brittle cracking at intermediate temperatures, and perhaps related to strain aging, is augmented by time dependent transient creep plasticity at higher temperatures. The C (sub t) analysis is, however, complicated by the necessity to measure small differences in the elastic crack growth and creep contributions to the crack opening displacement rate. A microstructural study indicates that 2618 and FVS0812 are likely to be creep brittle materials, consistent with the results obtained from the fracture mechanics study. Time dependent crack growth of 2618 at 175 C is characterized by mixed transgranular and intergranular fracture. Delamination along the ribbon powder particle boundaries occurs in FVS0812 at all temperatures. The fracture mode of FVS0812 changes with temperature. At 175 C, it is characterized as dimpled rupture, and at 316 C as mixed matrix superplastic rupture and matrix-dipersoid debonding.

Leng, Yang↗

The effect of heat treatment and test parameters on the aqueous stress corrosion cracking of D6AC steel

The crack growth behavior of D6AC steel as a function of stress intensity, stress and corrosion history and test technique, under sustained load in natural seawater, 3.3 percent NaCl solution, distilled water, and high humidity air was investigated. Reported investigations of D6AC were considered with emphasis on thermal treatment, specimen configuration, fracture toughness, crack-growth rates, initiation period, threshold, and the extension of corrosion fatigue data to sustained load conditions. Stress history effects were found to be most important in that they controlled incubation period, initial crack growth rates, and apparent threshold.

Gilbreath, W. P.↗

Preliminary criteria for the fracture control of space shuttle structures

The complex and multidisciplinary factors are presented which relate to the prevention of structural failure due to the initiation or propagation of cracks or crack-like defects. The fracture control criteria are applicable to space shuttle components which are: (1) susceptible to cracking or fracture on the basis of anticipated loads and environment, and (2) critical to either crew safety or system performance. The criteria define the design, fabrication, environmental control, inspection, maintenance, repair, and verification procedures required for adequate fracture control.

Source record↗

Interaction of Cracks Between Two Adjacent Indents in Glass

Experimental observations of the interaction behavior of cracks between two adjacent indents were made using an indentation technique in soda-lime glass. It was specifically demonstrated how one indent crack initiates and propagates in the vicinity of another indent crack. Several types of crack interactions were examined by changing the orientation and distance of one indent relative to the other. It was found that the residual stress field produced by elastic/plastic indentation has a significant influence on controlling the mode of crack interaction. The interaction of an indent crack with a free surface was also investigated for glass and ceramic specimens.

Choi, S. R.↗

Characterization of Two-Dimensionally Braided Composites Subject to Static and Fatigue Loading

This paper presents a characterization of damage processes in four different two-dimensionally braided architectures consisting of graphite fibers in an epoxy matrix, subjected to both static and fatigue loading. Both notched and unnotched specimens were tested from each architecture. Damage mechanisms in static compression testing were found to range from matrix cracking in an architecture controlled by shearing characteristics of the matrix to axial fiber bundle kinking and splitting in architectures controlled by unidirectional fiber bundles. In both static tension and tension-tension fatigue testing, it was found that all architectures sustained the same basic damage types and progression sequences. The first types of damage to occur were splits in the braider bundles and cracks in the resin rich areas. Once a sufficient density of this type of damage had occurred, the axial bundles began to disbond from the surrounding constituents, and continued to do so until ultimate failure. One architecture sustained an additional mode of failure, which involved splitting of the axial bundles along their length. Varied degrees of notch sensitivity were found among the different architectures. In one architecture, this was attributed to differences found in the stacking of the individual plys of the braided architecture. As the density of axial bundles adjacent to the notch increased, the rate of stiffness loss increased and the life decreased.

Burr, Scott T.↗

Kink bands promote exceptional fracture resistance in a NbTaTiHf refractory medium-entropy alloy

Single-phase body-centered cubic (bcc) refractory medium- or high-entropy alloys can retain compressive strength at elevated temperatures but suffer from extremely low tensile ductility and fracture toughness. We examined the strength and fracture toughness of a bcc refractory alloy, NbTaTiHf, from 77 to 1473 kelvin. This alloy’s behavior differed from that of comparable systems by having fracture toughness over 253 MPa·m 1/2 , which we attribute to a dynamic competition between screw and edge dislocations in controlling the plasticity at a crack tip. Whereas the glide and intersection of screw and mixed dislocations promotes strain hardening controlling uniform deformation, the coordinated slip of <111> edge dislocations with {110} and {112} glide planes prolongs nonuniform strain through formation of kink bands. These bands suppress strain hardening by reorienting microscale bands of the crystal along directions of higher resolved shear stress and continually nucleate to accommodate localized strain and distribute damage away from a crack tip.

36 MATERIALS SCIENCE↗

Effect of Control Mode and Load Rate on Fracture Toughness of Brittle Ceramics

The effects of control mode and rate on the fracture toughness of ceramics were measured by using chevron-notched flexure specimen in accordance with ASTM C1421. The use of stroke control gave consistent results with about 2% variation in measured fracture toughness for a very wide range of rates (0.005 to 0.5 mm/min). Use of strain or CMOD control gave an approximately 5% variation over a very wide range of rates, with the measurements being a function of rate. However, the effect was eliminated by use of dry nitrogen, implying a stress corrosion effect rather than a stability effect. With the use of nitrogen for strain control, fracture toughness values were within about 1% over a wide range of rates (1 to 80 micro-epsilon/sec.). CMOD or strain control did allow stable crack extension well past maximum load, and thus is preferred for energy calculations. The effort is being used to confirm recommendations in ASTM International standard C1421 on fracture toughness measurement.

control mode↗

Effect of Control Mode and Test Rate on Fracture Toughness of Advanced Ceramics

The effects of control mode and rate on the fracture toughness of ceramics were measured by using chevron-notched flexure specimen in accordance with ASTM C1421. The use of stroke control gave consistent results with about 2% variation in measured fracture toughness for a very wide range of rates (0.005 to 0.5 mm/min). Use of strain or CMOD control gave ~5% variation over a very wide range of rates, with the measurements being a function of rate. However, the effect was eliminated by use of dry nitrogen, implying a stress corrosion effect rather than a stability effect. With the use of nitrogen for strain control, fracture toughness values were within about 1% over a wide range of rates (1 to 80 /s). CMOD or strain control did allow stable crack extension well past maximum load, and thus is preferred for energy calculations. The effort is being used to confirm recommendations in ASTM International standard C1421 on fracture toughness measurement.

fracture toughness↗

International Conference on Advances in Communication and Control Systems, 1st, Washington, DC, June 18-20, 1987, Proceedings

Theoretical models of communication and control systems are discussed in reviews and reports. Topics addressed include smoothing and identification for random fields, the information and coding capacities of mismatched Gaussian channels, recursive least-squares estimation and Kalman filtering by systolic arrays, Kemp echo digital filters, a periodic test-scheduling scheme for communication and queuing processes, and receivers for direct-sequence systems. Consideration is given to a distributed-parameter model for detecting cracks in rotors, active control of aeroelastic systems governed by functional differential equations, robust multivariable control of large space structures, finite-rank relatively bounded perturbations of semigroup generators, and sensitivity analysis of convex optimal-control problems.

Declaris, Nicholas↗

Multiscale modeling of hydrogenolysis of ethane and propane on Ru(0001): Implications for plastics recycling

Plastic waste presents an environmental threat. Chemical recycling via hydrogenolysis can convert plastic waste into waxes, lubricants, and fuels. Among catalysts, Ru stands out for its superior activity and selectivity. The chemistry of light alkane hydrogenolysis can help understanding plastics deconstruction. Here, we perform first-principles calculations, develop descriptor-based relations, and conduct microkinetic modeling and analysis on ethane and propane. Predictions are in excellent agreement with experimental data. We identify a similar cracking pattern for both hydrocarbons entailing a deeply dehydrogenated species with the removal of four hydrogen atoms: CHCH*+* → 2CH* for ethane and CH 3 CCH*+2* → CH 3 C* + CH* for propane. We find that the rate-determining step is the C-C cracking for ethane and the first dehydrogenation from the terminal carbon (CH 3 CH 2 CH 3 *+* → CH 3 CH 2 CH 2 *+H*) for propane. The vinyl species CH 2 CH* produced from propane cracking is responsible for whether a single or multiple cracking events occur and effectively controls the selectivity. Specifically, ethane formation in propane hydrogenolysis is suppressed at elevated temperatures due to over-cracking via multiple (two here) cracking events being preferred over hydrogenation and desorption of ethane from the catalyst. Our workflow and models provide a baseline for future studies on heavier hydrocarbons. Insights into recent experimental studies of polyethylene over Ru-based catalysts are discussed.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗