DOE OSTI2019

Integrated Two-Stage Alkaline-Oxidative Pretreatment of Hybrid Poplar. Part 1: Impact of Alkaline Pre-Extraction Conditions on Process Performance and Lignin Properties

We previously demonstrated that a two-stage pretreatment comprising of an alkaline pre-extraction followed by a Cu-catalyzed alkaline–oxidative treatment is effective at pretreating hardwoods under relatively mild reaction conditions. In this work, we focus on characterizing how biomass source and reaction conditions used during the alkaline pre-extraction impact the subsequent processing stages as well as lignin yields and properties. Specifically, three hybrid poplars were subjected to the first stage alkaline pre-extraction under various conditions including differences in time (15–300 min), temperature (95–155 °C), and alkali loadings (50–200 mg NaOH/g biomass), and the impact on total mass solubilization, lignin recovery, and lignin purity was determined. Empirical correlations were developed between reaction conditions and mass solubilization and lignin recovery during the pre-extraction stage. For select conditions, lignin properties were assessed and include β-O-4 content determined by 13C NMR, molecular mass distributions as determined by gel permeation chromatography, and susceptibility to depolymerization to aromatic monomers using thioacidolysis and formic acid catalyzed depolymerization. We found alkaline pre-extraction performed at higher temperatures generated lignins exhibiting lower contamination by polysaccharides, lower aromatic monomer yields from depolymerization, lower molar masses, and lower β-O-4 contents relative to the lower temperature pre-extractions. Lastly, the pre-extracted biomass from select conditions was assessed for its response to the subsequent Cu-catalyzed alkaline–oxidative treatment and enzymatic hydrolysis. It was demonstrated that minor differences in delignification during pre-extraction have quantifiable impacts on the subsequent efficacy of the second stage of pretreatment and enzymatic hydrolysis with improved lignin removal during the first pre-extraction stage resulting in improved hydrolysis yields.

09 BIOMASS FUELS↗
DOE OSTI2017

Position Assignment and Oxidation State Recognition of Fe and Co Centers in Heterometallic Mixed-Valent Molecular Precursors for the Low-Temperature Preparation of Target Spinel Oxide Materials

A series of mixed-valent, heterometallic (mixed-transition metal) diketonates that can be utilized as prospective volatile single-source precursors for the low-temperature preparation of M x M' 3–x O 4 spinel oxide materials is reported. Three iron–cobalt complexes with Fe/Co ratios of 1:1, 1:2, and 2:1 were synthesized by several methods using both solid-state and solution reactions. On the basis of nearly quantitative reaction yields, elemental analyses, and comparison of metal–oxygen bonds with those in homometallic analogues, heterometallic compounds were formulated as [Fe III (acac) 3 ][Co II (hfac) 2 ] (1), [Co II (hfac) 2 ][Fe III (acac) 3 ][Co II (hfac) 2 ] (2), and [Fe II (hfac) 2 ][Fe III (acac) 3 ][Co II (hfac) 2 ] (3). In the above heteroleptic complexes, the Lewis acidic, coordinatively unsaturated CoII/FeII centers chelated by two hexafluoroacetylacetonate (hfac) ligands maintain bridging interactions with oxygen atoms of acetylacetonate (acac) groups that chelate the neighboring Fe III metal ion. Preliminary assignment of Fe and Co positions/oxidation states in 1–3 drawn from X-ray structural investigation was corroborated by a number of complementary techniques. Single-crystal resonant synchrotron diffraction and neutron diffraction experiments unambiguously confirmed the location of Fe and Co sites in the molecules of dinuclear (1) and trinuclear (2) complexes, respectively. Direct analysis in real time mass spectrometry revealed the presence of Fe III - and Co II -based fragments in the gas phase upon evaporation of precursors 1 and 2 as well as of Fe III , Fe II , and Co II species for complex 3. Theoretical investigation of two possible “valent isomers”, [Fe II I(acac) 3 ][Co II (hfac) 2 ] (1) and [Co III (acac) 3 ][Fe II (hfac) 2 ] (1'), provided an additional support for the metal site/oxidation state assignment giving a preference of 6.48 kcal/mol for the experimentally observed molecule 1. Magnetic susceptibility measurements data are in agreement with the presence of high-spin FeIII and CoII magnetic centers with weak anti-ferromagnetic coupling between those in molecules of 1 and 2. Highly volatile heterometallic complexes 1–3 were found to act as effective single-source precursors for the low-temperature preparation of iron–cobalt spinel oxides Fe x Co 3–x O 4 known as important materials for diverse energy-related applications.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2017

Modulating Hole Transport in Multilayered Photocathodes with Derivatized p-Type Nickel Oxide and Molecular Assemblies for Solar-Driven Water Splitting

We report here a new photocathode composed of a bi-layered doped NiO film topped by a macro-mesoporous ITO (ioITO) layer with molecular assemblies attached to the ioITO surface. The NiO film containing a 2% K+ doped NiO inner layer and a 2% Cu2+ doped NiO outer layer provides sufficient driving force for hole transport after injection to NiO by the molecular assembly. The tri-layered oxide, NiK0.02O | NiCu0.02O | ioITO, sensitized by a ruthenium polypyridyl dye and functionalized with a nickel-based hydrogen evolution catalyst, outperforms its counterpart, NiO | NiO | ioITO, in photocatalytic hydrogen evolution from water over a period of several hours with a Faradaic yield of ~90%.

Shan, Bing↗
DOE OSTI2017

Interplay between Terminal and Bridging Diiron Hydrides in Neutral and Oxidized States

This study describes the structural, spectroscopic, and electrochemical properties of electronically unsymmetrical diiron hydrides. The terminal hydride Cp*Fe(pdt)Fe(dppe)(CO)H ([1(t-H)]0, Cp*– = Me5C5 –, pdt2– = CH2(CH2S–)2, dppe = Ph2PC2H4PPh2) was prepared by hydride reduction of [Cp*Fe(pdt)Fe(dppe)(CO)(NCMe)]+. As established by X-ray crystallography, [1(t- H)]0 features a terminal hydride ligand. Unlike previous examples of terminal diiron hydrides, [1(t-H)]0 does not isomerize to the bridging hydride [1(µ-H)]0. Oxidation of [1(t-H)]0 gives [1(t- H)]+, which was also characterized crystallographically as its BF4 – salt. Density functional theory (DFT) calculations indicate that [1(t-H)]+ is best described as containing an Cp*Fe(III) center. In solution, [1(t-H)]+ isomerizes to [1(µ-H)]+ as anticipated by DFT. Reduction of [1(µ- H)]+ by Cp2Co affords the diferrous bridging hydride [1(µ-H)]0. Electrochemical measurements and DFT calculations indicate that the couples [1(t-H)]+/0 and [1(µ-H)]+/0 differ by 210 mV. Qualitative measurements indicate that [1(t-H)]0 and [1(µ-H)]0 are close in free energy. Protonation of [1(t-H)]0 in MeCN solution affords H2 even with weak acids via hydride transfer.

Yu, Xin↗
DOE OSTI2018

Electrophilic Impact of High-Oxidation State Main-Group Metal and Ligands on Alkane C–H Activation and Functionalization Reactions

High-oxidation state main-group metal complexes are potential alternatives to transition metals for electrophilic alkane C–H functionalization reactions. Yet, there is little known about how selection of the p-block, main-group metal and ligand impact alkane C–H activation and functionalization thermodynamics and reactivity. This work reports density functional theory calculations used to determine qualitative and quantitative features of C–H activation and metal-methyl functionalization energy landscapes for reaction between high-oxidation state d 10 s 0 In III , Tl III , Sn IV , and Pb IV carboxylate complexes with methane. While the main-group metal influences the C–H activation barrier height in a periodic manner, the carboxylate ligand has a much larger quantitative impact on C–H activation with stabilized carboxylate anions inducing the lowest barriers. For metal-methyl reductive functionalization reactions, the main-group metal dramatically influences the barrier heights, which are correlated to reaction thermodynamics and bond heterolysis energies as a model for two-electron reduction energies. Generally, this work begins to outline which main-group metals and carboxylate ligands could be useful for alkane functionalization systems that utilize electrophilic C–H activation and metal-alkyl functionalization reactions.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2025

Feasibility of Metal Oxide Glasses and Polymer Membranes as Sorbents for Gaseous Oxidized Mercury

Mass spectrometry methods are currently under development by the atmospheric mercury (Hg) research community to elucidate the identity of atmospheric oxidized mercury (Hg II ) compounds. Due to high instrument detection limits, materials that can quantitatively preconcentrate atmospheric Hg II without facilitating compound-altering chemical reactions are needed to support these methods. Cation exchange membranes (CEM) and nylon membranes are currently used to preconcentrate ambient Hg II for concentration measurements and Hg II compound estimation, respectively. However, CEM and nylon membranes are poor candidates for observations by mass spectrometry methods due to release of interfering compounds upon heating; glasses do not have this problem. Here, three metal oxide glasses were explored as potential alternatives for Hg II preconcentration for future use with mass spectrometry methods: calcium phosphate (CaP), iron phosphate (FeP), and calcium aluminate (CaAl). The glasses demonstrated quantitative selective capture of HgBr 2 without capture of Hg 0 . Under ambient conditions, the CaP, FeP, and CaAl sorbed 36.4 ± 12.6% of the total HgII as the CEM. However, when Hg concentrations were normalized to surface area, CaP, FeP, and CaAl sorbed more HgBr 2 in the laboratory and ambient HgII compared to CEM. The CEM and CaP retained similar concentrations of HgBr 2 when preloaded samples were deployed in the field. Additionally, a permeation tube-based calibrator was used to load sorbents with HgBr 2 for investigation of HgII retention on CEM and thermal desorption profile changes on nylon membranes during active sampling. Nylon membranes were purchased from three vendors and used to compare HgBr 2 retention; a different HgBr 2 thermal desorption profile was achieved for each vendor’s nylon membrane.

Amides↗
DOE OSTI2015

Low-surface-area hard carbon anode for Na-ion batteries via graphene oxide as a dehydration agent

Na-ion batteries are emerging as one of the most promising energy storage technologies, particularly for grid-level applications. Among anode candidate materials, hard carbon is very attractive due to its high capacity and low cost. However, hard carbon anodes often suffer a low first-cycle Coulombic efficiency and fast capacity fading. In this study, we discover that doping graphene oxide into sucrose, the precursor for hard carbon, can effectively reduce the specific surface area of hard carbon to as low as 5.4 m²/g. We further reveal that such doping can effectively prevent foaming during caramelization of sucrose and extend the pyrolysis burn-off of sucrose caramel over a wider temperature range. Thus, the obtained low-surface-area hard carbon greatly improves the first-cycle Coulombic efficiency from 74% to 83% and delivers a very stable cyclic life with 95% of capacity retention after 200 cycles.

25 ENERGY STORAGE↗
DOE OSTI2017

Ammonia Oxidation by Abstraction of Three Hydrogen Atoms from a Mo–NH 3 Complex

We report ammonia oxidation by homolytic cleavage of all three H atoms from a Mo৶ 15 NH 3 complex using the 2,4,6-tri-tert-butylphenoxyl radical to afford a Mo-alkylimido (Mo৶ 15 NR) complex (R = 2,4,6-tri-t-butylcyclohexa-2,5-dien-1-one). Reductive cleavage of Mo৶15NR generates a terminal Mo৶N nitride, and a [Mo৶ 15 NH] + complex is formed by protonation. Computational analysis describes the energetic profile for the stepwise removal of three H atoms from the Mo৶ 15 NH 3 complex and the formation of Mo৶ 15 NR. Acknowledgment. This work was supported as part of the Center for Molecular Electrocatalysis, an Energy Frontier Re-search Center funded by the U.S. Department of Energy (U.S. DOE), Office of Science, Office of Basic Energy Sciences. EPR and mass spectrometry experiments were performed using EMSL, a national scientific user facility sponsored by the DOE’s Office of Biological and Environmental Research and located at PNNL. The authors thank Dr. Eric D. Walter and Dr. Rosalie Chu for assistance in performing EPR and mass spectroscopy analysis, respectively. Computational resources provided by the National Energy Re-search Scientific Computing Center (NERSC) at Lawrence Berkeley National Laboratory. Pacific North-west National Laboratory is operated by Battelle for the U.S. DOE.

Molybdenum, ammonia, phosphines, pendant amines, h↗
DOE OSTI2019

Directing Boron–Phosphorus Bonds in Crystalline Solid: Oxidative Polymerization of P=B=P Monomers into 1D Chains

Over 20 years after the last inorganic ternary B–P compound was reported, Na 2 BP 2 , a new compound containing one-dimensional B–P polyanionic chains has been synthesized. Common high-temperature synthetic methods required for the direct reaction of boron and phosphorus negate the possible formation of metastable or low temperature phases. In this study, oxidative elimination was used to successfully condense 0D BP 2 3– anionic monomers found in a Na 3 BP 2 precursor into unique 1D BP 2 2– chains consisting of five-member B 2 P 3 rings connected by bridging P atoms in the crystal structure of Na 2 BP 2 . In conclusion, the synthesis was guided by in situ X-ray powder diffraction studies, which revealed the metastable nature of the products of oxidative elimination reactions. Na 2 BP 2 is predicted to be an electron balanced semiconductor which was confirmed by UV–vis spectroscopy with the experimentally determined band gap of 1.1 eV.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2014

Revisiting Photoemission and Inverse Photoemission Spectra of Nickel Oxide from First Principles: Implications for Solar Energy Conversion

We use two different ab initio quantum mechanics methods, complete active space self-consistent field theory applied to electrostatically embedded clusters and periodic many-body G₀W₀ calculations, to reanalyze the states formed in nickel(II) oxide upon electron addition and ionization. In agreement with interpretations of earlier measurements, we find that the valence and conduction band edges consist of oxygen and nickel states, respectively. However, contrary to conventional wisdom, we find that the oxygen states of the valence band edge are localized whereas the nickel states at the conduction band edge are delocalized. We argue that these characteristics may lead to low electron-hole recombination and relatively efficient electron transport, which, coupled with band gap engineering, could produce higher solar energy conversion efficiency compared to that of other transition-metal oxides. Both methods find a photoemission/inverse-photoemission gap of 3.6-3.9 eV, in good agreement with the experimental range, lending credence to our analysis of the electronic structure of NiO.

Environmental Molecular Sciences Laboratory↗
DOE OSTI2014

Size- and Support-Dependent Evolution of the Oxidation State and Structure by Oxidation of Subnanometer Cobalt Clusters

Size-selected subnanometer cobalt clusters with 4, 7 and 27 cobalt atoms supported on amorphous alumina and ultrananocrystalline diamond (UNCD) surfaces were oxidized after exposure to ambient air. Grazing incidence X-ray absorption near edge spectroscopy (GIXANES) and near edge X-ray absorption fine structure (NEXAFS) used to characterize the clusters revealed a strong dependency of the oxidation state and structure of the clusters on the surface. A dominant Co2+ phase was identified in all samples. However, form XANES analysis, on UNCD about 10% fraction of Co0 phase was identified for all three cluster sizes and about 30% and 12% fraction of Co3+ phase in 4, 7 and 27 atoms, respectively. In the alumina-supported clusters, the dominating Co2+ component was attributed to cobalt aluminate, indicative of a very strong binding to the support. NEXAFS showed that in addition to strong binding of the clusters to alumina, their structure in great extent follows the tetrahedral morphology of the support. The supported clusters of all three sizes were found resistant to agglomeration when exposed to reactive gases at elevated temperatures and atmospheric pressure.

Yin, Chunrong↗
DOE OSTI2018

Combining CO 2 reduction with propane oxidative dehydrogenation over bimetallic catalysts

In this paper, the inherent variability and insufficiencies in the co-production of propylene from steam crackers has raised concerns regarding the global propylene production gap and has directed industry to develop more on-purpose propylene technologies. The oxidative dehydrogenation of propane by CO 2 (CO 2 -ODHP) can potentially fill this gap while consuming a greenhouse gas. Non-precious FeNi and precious NiPt catalysts supported on CeO 2 have been identified as promising catalysts for CO 2 -ODHP and dry reforming, respectively, in flow reactor studies conducted at 823 K. In-situ X-ray absorption spectroscopy measurements revealed the oxidation states of metals under reaction conditions and density functional theory calculations were utilized to identify the most favorable reaction pathways over the two types of catalysts.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗
DOE OSTI2021

Emergent properties at oxide interfaces controlled by ferroelectric polarization

Abstract Ferroelectric materials are characterized by the spontaneous polarization switchable by the applied fields, which can act as a “gate” to control various properties of ferroelectric/insulator interfaces. Here we review the recent studies on the modulation of oxide hetero-/homo-interfaces by ferroelectric polarization. We discuss the potential applications of recently developed four-dimensional scanning transmission electron microscopy and how it can provide insights into the fundamental understanding of ferroelectric polarization-induced phenomena and stimulate future computational studies. Finally, we give the outlook for the potentials, the challenges, and the opportunities for the contribution of materials computation to future progress in the area.

Chemistry↗
DOE OSTI2018

Nucleation of dislocations and their dynamics in layered oxide cathode materials during battery charging

Lithium-rich layered oxides (LRLO) are among the leading candidates for the next-generation cathode material for energy storage, delivering 50% excess capacity over commercially used compounds. Despite excellent prospects, voltage fade has prevented effective use of the excess capacity, and a major challenge has been a lack of understanding of the mechanisms underpinning the voltage fade. Here, using operando three-dimensional Bragg coherent diffractive imaging, we directly observe the nucleation of a mobile dislocation network in LRLO nanoparticles. The dislocations form more readily in LRLO as compared with a classical layered oxide, suggesting a link between the defects and voltage fade. We show microscopically how the formation of partial dislocations contributes to the voltage fade. The insights allow us to design and demonstrate an effective method to recover the original high-voltage functionality. Furthermore, our findings reveal that the voltage fade in LRLO is reversible and call for new paradigms for improved design of oxygen-redox active materials.

25 ENERGY STORAGE↗
DOE OSTI2022

A single-Pt-atom-on-Ru-nanoparticle electrocatalyst for CO-resilient methanol oxidation

Single Pt atom catalysts are key targets because a high exposure of Pt substantially enhances electrocatalytic activity. In addition, PtRu alloy nanoparticles are the most active catalysts for the methanol oxidation reaction. To combine the exceptional activity of single Pt atom catalysts with an active Ru support we must overcome the synthetic challenge of forming single Pt atoms on noble metal nanoparticles. In this report we demonstrate a process that grows and spreads Pt islands on Ru branched nanoparticles to create single-Pt-atom-on-Ru catalysts. By following the spreading process by in situ TEM, we found that the formation of a stable single atom structure is thermodynamically driven by the formation of strong Pt–Ru bonds and the lowering of the surface energy of the Pt islands. The stability of the single-Pt-atom-on-Ru structure and its resilience to CO poisoning result in a high current density and mass activity for the methanol oxidation reaction over time.