Fracture Analysis of Cohesive Zone Models for Modeling Residual Stress Induced Delamination in Composite Structures
A fracture study of coupon-scale composite cylinders with embedded defects was conducted with an objective to assess and validate a modeling approach using two available cohesive material models. The study included experimental and simulation evaluations of initiation of crack growth and progression. Interrupted thermal experiments used acoustic emissions monitoring to identify the onset of crack progression during each cooling interval and ultrasonic scanning provided images of defect growth. Verification, validation, and uncertainty quantification (VVUQ) processes were performed in the assessment of the simulation predicted temperature at which crack propagation begins (quantity of interest). The Sobol sensitivity analysis identified the hoop direction elastic modulus in the carbon fiber reinforced polymer (CFRP) plies as the most influential parameter for simulations using both cohesive models, accounting for at least 70% of the variation in the temperature at crack propagation. The UQ temperature range for the Tvergaard-Hutchinson model was higher (more conservative) than the experimental acoustic measurement indicators of crack progression, while the temperature range for the Thouless-Parmigiani model enveloped the experimental data points for the primary defect size of 0.75 x 1 in. The simulations could not capture the stable crack growth indicated in the experiments. This is likely due to the models’ inability to represent anisotropic fracture toughness attributed to the structure of the orthotropic fiber weave in a woven composite laminate.