Work was conducted that could lead to a high energy density electrochemical capacitor, completely free of liquid electrolyte. A three-dimensional RuO sub x-ionomer composite structure has been successfully formed and appears to provide an ionomer ionic linkage throughout the composite structure. Capacitance values of approximately 0.6 F/sq cm were obtained compared with 1 F/sq cm when a liquid electrolyte is used with the same configuration.
Poly-4-vinylpyridinebisulfate (P4VPBS) is a polymeric salt that has shown promise as a water-free proton-conducting material (solid electrolyte) suitable for use in membrane/electrode assemblies in fuel cells. Heretofore, proton-conducting membranes in fuel cells have been made from perfluorinated ionomers that cannot conduct protons in the absence of water and, consequently, cannot function at temperatures >100 C. In addition, the stability of perfluorinated ionomers at temperatures >100 C is questionable. However, the performances of fuel cells of the power systems of which they are parts could be improved if operating temperatures could be raised above 140 C. What is needed to make this possible is a solid-electrolyte material, such as P4VPBS, that can be cast into membranes and that both retains proton conductivity and remains stable in the desired higher operating temperature range. A family of solid-electrolyte materials different from P4VPBS was described in Anhydrous Proton-Conducting Membranes for Fuel Cells (NPO-30493), NASA Tech Briefs, Vol. 29, No. 8 (August 2005), page 48. Those materials notably include polymeric quaternized amine salts. If molecules of such a polymeric salt could be endowed with flexible chain structures, it would be possible to overcome the deficiencies of simple organic amine salts that must melt before being able to conduct protons. However, no polymeric quaternized amine salts have yet shown to be useful in this respect. The present solid electrolyte is made by quaternizing the linear polymer poly- 4-vinylpyridine (P4VP) to obtain P4VPBS. It is important to start with P4VP having a molecular weight of 160,000 daltons because P4VPBS made from lower-molecular-weight P4VP yields brittle membranes. In an experimental synthesis, P4VP was dissolved in methanol and then reacted with an excess of sulfuric acid to precipitate P4VPBS. The precipitate was recovered, washed several times with methanol to remove traces of acid, and dried to a white granular solid. In another synthesis, nanoparticles of silica rich with surface hydroxyl groups were added to P4VP in methanol solution, which was then reacted with excess sulfuric acid to precipitate granules of a composite that most probably had the composition (P4VPBS)-SiO2-SiO(HSO4)2. The granular P4VPBS produced in the first-mentioned synthesis was dissolved in water to make a glue-like, turbid solution; the granular P4VPBS/silica composite produced in the second-mentioned synthesis was mixed with water to make a turbid, glue-like suspension. The proportions of polymer salt to water in such preparations can be varied; it was found that approximately equal parts of water and polymer salt yield a solution or suspension amenable to further processing.
Herein, ionomer-free amorphous iridium oxide (IrO x ) thin electrodes are first developed as highly active anodes for proton exchange membrane electrolyzer cells (PEMECs) via low-cost, environmentally friendly, and easily scalable electrodeposition at room temperature. Combined with a Nafion 117 membrane, the IrO x -integrated electrode with an ultralow loading of 0.075 mg cm –2 delivers a high cell efficiency of about 90%, achieving more than 96% catalyst savings and 42-fold higher catalyst utilization compared to commercial catalyst-coated membrane (2 mg cm –2 ). Additionally, the IrO x electrode demonstrates superior performance, higher catalyst utilization and significantly simplified fabrication with easy scalability compared with the most previously reported anodes. Notably, the remarkable performance could be mainly due to the amorphous phase property, sufficient Ir 3+ content, and rich surface hydroxide groups in catalysts. Overall, due to the high activity, high cell efficiency, an economical, greatly simplified and easily scalable fabrication process, and ultrahigh material utilization, the IrO x electrode shows great potential to be applied in industry and accelerates the commercialization of PEMECs and renewable energy evolution.
Anion-exchange membrane fuel cells represent a promising and scalable approach for hydrogen energy utilization. However, their development is hindered by the weak bonding between metal catalysts and carbon supports, along with challenges in fabricating electronically/ionically conductive electrodes. Here, we report a composite cathode of Nb-doped brookite TiO 2 nanorods that have robust stability when combined with Pt nanoscale catalysts in an alkaline fuel cell. The composite cathode, fabricated without the addition of an ionomer, delivers a power density of 419 mW cm −2 at a current density of 650 mA cm −2 and a voltage retention of 81% at 100 mA cm −2 after 25 h, substantially outperforming a cathode fabricated from commercial Pt/C. Further investigations of the chemical structure, anion exchange capacity, and mass transfer resistance reveal that a solvent residue derived from N-methylpyrrolidone plays an important role in charge transfer and mass transport in the alkaline fuel cell.
The C–H functionalization of commodity polymers could be a promising approach for upcycling plastic waste into advanced materials, which can alter the properties of the original materials through the introduction of different functionalities onto the existing backbone structures. In this study, waste polystyrene (PS) was modified by Friedel–Crafts acylation using 4-chlorobutyryl chloride (4-CBC) followed by reaction with N-alkylimidazoles to form cationic polyelectrolytes. These methods provide access to what are essentially poly(ionic liquid) (poly(IL)) materials with properties that are distinctly different from those of the PS from which they were formed. In one notable example, the glass transition temperature (T g ) of imidazolium-functionalized PS was ∼16 °C, which is a nearly 90 °C reduction from PS. This is also evidenced by macroscopic mechanical properties where the poly(IL) product is highly elastic in stark contrast to brittle PS. Moreover, the resulting ionomers showed self-healing behaviors in the presence of a “free” IL further contributing to the utility of the materials. Here, the methods in this work can open opportunities to utilize waste PS to obtain a vast array of poly(IL) materials with highly tailored structures and properties.
Commercial membrane electrolyzers rely on acidic fluorocarbon membranes and ionomers, requiring the use of expensive IrO x -based oxygen-evolution catalysts. Anion-exchange-membrane water electrolyzers (AEMWEs) operate in an alkaline environment, enabling the use of non-precious-metal catalysts. Here, we study and engineer CoO x -based catalyst-coated anodes deposited via hydrothermal synthesis directly onto porous transport layers both with and without thermal annealing. The self-supported, nanoneedle-structured Co3O4 anode, formed by annealing the as-synthesized cobalt carbonate hydroxide, Co(CO3) x (OH) y , outperforms the baseline Co3O4 nanoparticle ink-based anode in pure-water-fed AEMWE due to the improved catalyst-layer continuity and thus number of electroactive Co species. The as-synthesized and unannealed Co(CO3) x (OH) y , however, appears to undergo substantial conversion to a more-active CoO x (OH) y phase predominantly at the surface, with nominal Co3+ present and higher electrical conductivity, lowering the cell voltage to ∼200 mV at 1.0 A·cm–2 in pure-water-fed AEMWE compared to the conventional Co3O4 nanoparticle anodes. We analyze the differences in electrode electrochemical response between pure-water and KOH feed modes, finding distinct activation and degradation modes. The Co(CO3) x (OH) y anode shows significant activation and slower degradation linked to the conversion to oxyhydroxide. We propose catalyst layer designs that promote both hydroxide and electron transport, alongside interfacial engineering strategies to obtain high performance while mitigating anode degradation.
A catalyst-coated membrane (CCM) approach to electrode fabrication for high pH water electrolysis offers enhanced interfacial contact between the catalyst layer and the membrane surface in comparison to the catalyst-coated substrate (CCS) electrode configuration. The CCM facilitates enhanced ionic and water transport between the cathode and the anion exchange membrane (AEM). This advantage is particularly significant with AEM water electrolysis (compared to proton exchange membrane water electrolysis) because the cathode typically operates under dry conditions and relies solely on diffusive water transport across the AEM from the liquid-fed anode. This study presents a direct performance comparison between CCS and CCM cathode configurations using identical hydrogen evolution reaction (HER) catalysts and other components. The use of a pseudo-reference electrode integrated into the membrane electrode assembly enabled detailed analysis of the CCM cathode polarization behavior. Surface characterization provided insight into the degradation mechanisms associated with the CCM configuration. Optimization of the cathode ionomer cross-link density improved both the cathode polarization performance and the electrolysis device durability. Further optimization of the HER catalyst loading in the CCM cathode resulted in additional gains in the electrolysis efficiency. Collectively, these findings offer valuable guidance for the design and fabrication of high-performance, durable AEM electrolysis CCMs.
The stringent cost and performance requirements of renewable hydrogen production systems dictate that electrolyzers benefit from the use of nonprecious catalysts only if they deliver the same level of activity and durability as their precious metal counterparts. Here we report on recent work to understand interrelationships between the intrinsic activity of Ni- and Pt-based electrolyzer cathode catalysts and their performance in zero-gap alkaline water electrolyzer assemblies. Our results suggest that nanoparticulate Ni–Mo exhibits HER activity that is roughly 10-fold lower than Pt–Ru on the basis of turnover frequency under low (≤100 mV) polarization conditions. We further found that the HER activity of Ni–Mo/C cathodes is inhibited by aryl piperidinium anionexchange ionomers bearing bicarbonate counter-anions. After addressing this poisoning effect, we produced electrolyzer assemblies based on Ni–Mo/C cathodes that delivered indistinguishable current density vs cell potential relationships compared to otherwise identical assemblies with Pt–Ru cathodes. This result indicates that the contribution of the cathode to the total cell polarization is small, even for the less active Ni–Mo/C catalyst, and further implies that Pt-based cathodes can indeed be replaced by nonprecious alternatives with no loss in performance.
Segmented cells are a class of advanced diagnostic devices that enable the measurement of current distribution within the active area of an electrochemical cell, allowing for the evaluation of localized impacts from operating conditions, flow fields and component inhomogeneities. Segmented cell devices have been applied to support R&D efforts for the advancement of polymer electrolyte membrane fuel cell technologies and more recently proton exchange membrane water electrolysis (PEMWE). Beyond current density distributions, segmented cells have been successfully deployed to collect the distribution of other relevant parameters such as high frequency resistance and electrode potentials. Very recently, a promising impedance method has been reported for water electrolysis where a one-dimensional segmented cell is coupled to a multichannel potentiostat, to enable the measurement of local cell impedances, further expanding the diagnostic capabilities of the segmented cell. In this study, we will present recent efforts to accurately measure local impedance characteristics for a PEMWE cell using a two-dimensional segmented cell device coupled with a multichannel potentiostat. The distribution of local resistances, i.e. high frequency, charge transfer, mass transport and catalyst layer, and iR-free overpotentials were successfully measured after eliminating sources of random and systematic error. We will discuss the application of this diagnostic on a cell containing a 1 cm feature simulating an ionomer skin. The results from these tests give insights if such an irregularity needs to be classified as a defect, and highlight the usefulness of coupling impedance spectroscopy with segmented cells for holistic spatial diagnostics of electrochemical devices.
The water balance in hydroxide-exchange-membrane fuel cells (HEMFCs) is a key challenge for improved performance and durability, intimately linked with the various interfaces and coupled phenomena. For every 4 electrons produced, 4 water molecules are generated in the anode and 2 consumed in the cathode, while electroosmosis transports water across the HEM from the cathode to the anode. Consequently, a concentration gradient drives water back, from anode to cathode. Ineffective water management could lead to cathode dry-out, limiting reaction rate and causing ionomer degradation, or to anode flooding. To address these concerns, it is critical to measure the water transport operando . Herein, a home-built water-flux station is used to measure total water flux during cell operation with different inlet relative humidities and back pressures. Increasing the HEM thickness fourfold decreases the water flux at high current density, and utilizing microporous layers on both the anode and cathode decreases the water flux from the anode to the cathode. However, the most significant variable in changing the water flux was found by increasing the anode back pressure. Furthermore, humidity cycling significantly changed electrochemical performance without affecting the overall water fluxes. These findings can be translated to other devices utilizing an HEM.
A study of various compositions of anodes for proton exchange membrane water electrolysis aimed at reducing precious metal content and system costs without compromising performance and durability is presented. A key challenge in current water electrolysis technologies is the reliance on high iridium loadings to ensure sufficient catalytic activity, electronic conductivity, and durability for the oxygen evolution reaction. To address this, catalyst layers based on the stable but kinetically limited rutile phase of iridium oxide are combined with platinum nanoparticles and carbon-based additives to improve structural properties and ink processability. By systematically varying the volume ratios of carbon to precious metals and ionomer to solids, compositional trends have been identified, and significant performance improvements have been achieved. Structural and elemental analysis confirms improved dispersion of platinum and iridium can be achieved, as well as electronic conductivity improvements within the catalyst layer. Polarization curve analysis has shown the ability of added Pt and C to significantly increase catalytic activity. These results highlight the potential positive impact of Pt and C on anode structure, composition, and cell performance.
The loss of platinum (Pt) electrochemically active surface area (ECSA) is a critical degradation mode that often becomes a limiting factor for heavy-duty proton exchange membrane fuel cell vehicles. High surface area carbon supports have been shown to improve Pt dispersion and limit detrimental ionomer-electrocatalyst interactions due to their large interior pore volume. Here, in this work, using automated scanning transmission electron tomography, the degradation of nanoparticles located on the interior versus exterior surfaces of the carbon support is compared following a catalyst-specific accelerated stress test (AST) of 90,000 voltage cycles between 0.6 V to 0.95 V. The results reveal a notable increase in median particle size for both interior and exterior Pt catalyst particles, with a slightly higher increase in particle size distribution and loss of specific surface area for the particles located on the exterior carbon surface. The fraction of Pt nanoparticles that reside within the interior of the carbon support also increased following the AST test, accompanied by evidence of an increase in average carbon mesopore size. Here, the results shed light on the degradation mechanisms affecting electrochemical properties and the enhanced particle accessibility at lower relative humidity.
Abstract Carbon‐based materials are extensively used in fuel cell applications due to their crucial role in maintaining high performance. Particularly, carbon black (CB) stands out as a preferred electrode material for fuel cells, owing to its high electrical conductivity and large surface area. This review focuses on the functionalization of CB and its use as a support for Pt‐based catalysts in proton exchange membrane fuel cells. Functionalization strategies include oxidation, covalent functionalization, as well as polymer grafting or impregnation. Various approaches to functionalize the CB surface are discussed that effectively tailor the surface properties of electrodes, leading to improved fuel cell performance. The improvements are seen in enhanced dispersibility of catalyst particles, better ionomer distribution, increased catalyst stability, and reduced carbon corrosion. This review provides an overview of various modifications applied to CB to enhance their structural and electrochemical properties, thereby boosting fuel cell performance.
Greenhouse gas emissions present a significant challenge to humanity, and utilizing renewable electricity to convert emitted CO 2 into value-added products offers a promising solution; however, traditional CO 2 capture and regeneration processes remain energy-intensive, restricting the overall system efficiency and decarbonization efficacy. In this study, an advanced direct reduction of captured CO 2 with large current densities for formate electrosynthesis was demonstrated without the need for CO 2 regeneration or compression. The bismuth nanosheet (DRM-BiNS) was synthesized by direct reduction of a Bi-based MOF, representing a new class of catalytic materials with a large surface area and interconnected pores, suitable for the direct reduction of captured CO 2 . By seamlessly combining experimentation and simulation, insights into the structure-parameter-performance relation were acquired in a flow cell setting, including critical membrane-electrode distance, cell orientation, and pumping flow rate. Important flow-cell components, such as catholyte volume, electrode substrate, membrane choice, and ionomer type, were also carefully examined to enhance the cell performance. In sharp contrast to prior studies limited to current densities below 20 mA/cm 2 in bicarbonate-based captured CO 2 solutions, this work demonstrates a remarkable current density of 300 mA/cm 2 with an FE to formate comparable to the case with gas-fed CO 2 reduction. Moreover, the process sustained an FE above 50% at a high current density of 500 mA/cm 2 . The DRM-BiNS catalyst exhibited outstanding selectivity, activity, and stability, significantly outperforming oxide-derived bismuth nanosheets (OD-BiNS) in captured CO 2 reduction. Furthermore, these findings offer critical insights into the development of sustainable and scalable CO 2 utilization technologies.
Polymer electrolyte membrane fuel cells (PEMFCs) are promising power sources for heavy-duty vehicles (HDVs) owing to cleanliness and efficiency. However, the degradation of membrane electrode assemblies (MEAs) under HDV conditions remains a huge challenge. Here, this work investigated MEA durability under HDV conditions using a US Department of Energy standard accelerated stress test for 180,000 cycles (equivalent to 1 million miles of HDV operation). Effects of catalyst Pt content on MEA durability were examined using homemade 30% Pt/C (H-Pt/C) and commercial 46% Pt/C (C-Pt/C) catalysts. Both MEAs experienced H 2 /air and H 2 /O 2 performance loss over cycles. Analysis with scanning transmission electron microscopy, X-ray diffraction, inductively coupled plasma mass spectrometry, and mercury intrusion porosimetry revealed severe degradation of Pt nanoparticles (NPs), support structures, and the catalyst layer. Two degradation stages for NPs were proposed: Ostwald ripening dominated the initial 60,000 cycles, followed by combined Ostwald ripening and particle migration. Measurements with ion chromatography, high-frequency resistance, and oxygen-diffusion resistance revealed degradation of membrane and ionomer, respectively.
Distribution of relaxation time (DRT) is used to interpret electrochemical impedance spectroscopy (EIS) for proton exchange membrane (PEM) water electrolyzers, with an attempt to separate overlapped relaxation processes in Nyquist plots. By varying operating conditions and catalyst loadings, four main relaxation peaks arising from EIS can be identified and successfully separated from low to high frequencies as (P1) mass transport, (P2) oxygen evolution reaction kinetics, (P3) reaction kinetics (with faster time constant than P2), and (P4) ionic transport. Here, the shape, height, and frequency of the DRT peaks change with different membrane electrode assembly (MEA) configurations. Electron microscopy reveals distinct features from the cross-sectioned MEAs which verify critical DRT results in that increasing the iridium (Ir)-anode loading from 0.2 mgIr/cm 2 to 1.5 mgIr/cm 2 reduces kinetic losses due to higher site-access; a thick and compacted anode, however, also triggers higher ohmic resistances from membrane/catalyst layer hydration and increases transport losses due to longer ionomer pathways. DRT provides higher resolution to EIS for deconvoluting processes with different relaxation times and the quantification of DRT peaks improves the accounting of total losses from each process.
In several recent studies, it has been proposed that the fundamental understanding of penetrant transport in dense polymer membranes occurring via the solution-diffusion model, which has been the generally accepted theoretical framework for describing penetrant transport in such materials for the past several decades, is flawed. An alternate mechanistic framework based on the idea of two-phase flow in a porous medium (i.e., pore-flow) has been broadly advanced instead, with proponents of this approach claiming that the pore-flow theoretical framework provides the necessary mechanistic insight to design novel polymeric membrane materials for emerging applications. In this study, we show experimental results for hydraulic permeation of water that are entirely consistent with the solution-diffusion theory, without modification, for three dense polymeric membranes: crosslinked poly(ethylene glycol diacrylate) (XLPEGDA), Nafion 117 ionomer in the sodium counterion form (Nafion 117-Na), and cellulose acetate (CA). By measuring water flux at transmembrane pressures up to 240 bar, we observe a nonlinear relationship between the transmembrane pressure (TMP) and water flux, J w , for XLPEGDA and Nafion 117-Na, while this relationship is linear for CA. We demonstrate that the behavior of these three materials is described via the solution-diffusion model. According to the solution-diffusion model, flux is, to a good approximation, proportional to the transmembrane concentration difference induced by the pressure difference across the membrane, rather than to TMP itself. Water sorption isotherms are reported for all three materials. They further justify the nonlinear relationship between TMP and J w observed in XLPEGDA and Nafion 117-Na, emphasizing that the nonlinearity in the flux/TMP relationship stems from nonlinearities in the sorption isotherm with pressure. Additionally, the relationship between water flux and TMP can be predicted, a priori, with no adjustable parameters when a predictive model for the diffusion coefficient of water is employed in conjunction with the experimental water sorption isotherms in the solution-diffusion model. Furthermore, our results demonstrate the validity of the solution-diffusion model to describe transport of penetrants in dense polymer membranes, while highlighting the sensitivity of the solution-diffusion model to the many physical and mathematical simplifications commonly applied to the theory in literature.
Hydrocarbon-based polymers offer several advantages, including lower environmental impacts, cost effectiveness, and the ability to finely tune properties. Here, we have developed trifluoromethanesulfonimide (TFSI)-functionalized poly(norbornene) (PNB) polymers utilizing a specifically designed oxa-Michael addition of a vinyl TFSI anion to an alcohol. Our results reveal that PNB-TFSI derivatives exhibit superior thermal stability and mechanical robustness compared with Nafion. The optimized PNB-TFSI-H-48 polymer (IEC 1.86 mmol/g) exhibits equivalent performance to Nafion as an anode ionomer in a proton exchange membrane fuel cell. Exchanging the counter ion to Li + enables PNB-TFSI to be used for Li-ion battery applications. Propylene carbonate plasticized PNB-TFSI derivatives achieve an Li-ion conductivity of over 10 −5 S/cm at 30°C. This Li polymer electrolyte exhibits excellent electrochemical stability (5 V vs. Li + /Li) and good cycling in a Li symmetric cell. These results highlight the potential and rational design of PNB-TFSI polymers for next-generation energy storage and conversion technologies.