Advanced single crystal for SSME turbopumps

The objective of this program was to evaluate the influence of high thermal gradient casting, hot isostatic pressing (HIP) and alternate heat treatments on the microstructure and mechanical properties of a single crystal nickel base superalloy. The alloy chosen for the study was PWA 1480, a well characterized, commercial alloy which had previously been chosen as a candidate for the Space Shuttle Main Engine high pressure turbopump turbine blades. Microstructural characterization evaluated the influence of casting thermal gradient on dendrite arm spacing, casting porosity distribution and alloy homogeneity. Hot isostatic pressing was evaluated as a means of eliminating porosity as a preferred fatigue crack initiation site. The alternate heat treatment was chosen to improve hydrogen environment embrittlement resistance and for potential fatigue life improvement. Mechanical property evaluation was aimed primarily at determining improvements in low cycle and high cycle fatigue life due to the advanced processing methods. Statistically significant numbers of tests were conducted to quantitatively demonstrate life differences. High thermal gradient casting improves as-cast homogeneity, which facilitates solution heat treatment of PWA 1480 and provides a decrease in internal pore size, leading to increases in low cycle and high cycle fatigue lives.

Fritzemeier, L. G.↗

Preliminary Study on Fatigue Strengths of Fretted Ti-48Al-2Cr-2Nb

The fatigue behavior (stress-life curve) of gamma titanium aluminide (Ti-48Al-2Cr-2Nb, atomic percent) was examined by conducting two tests: first, a fretting wear test with a fatigue specimen in contact with a typical nickel-based superalloy contact pad in air at temperatures of 296 and 823 K and second, a high-cycle fatigue test of the prefretted Ti-48Al-2Cr-2Nb fatigue specimen at 923 K. Reference high-cycle fatigue tests were also conducted with unfretted Ti-48Al-2Cr-2Nb specimens at 923 K. All Ti-48Al-2Cr-2Nb fatigue specimens were machined from cast slabs. The results indicate that the stress-life results for the fretted Ti-48Al-2Cr-2Nb specimens exhibited a behavior similar to those of the unfretted Ti-48Al-2Cr-2Nb specimens. The values of maximum stress and life for the fretted specimens were almost the same as those for the unfretted specimens. The resultant stress-life curve for the unfretted fatigue specimens was very flat. The flat appearance in the stress-life curve of the unfretted specimens is attributed to the presence of a high density of casting pores. The fatigue strengths of both the fretted and unfretted specimens can be significantly affected by the presence of this porosity, which can decrease the fatigue life of Ti-48Al-2Cr-2Nb. The presence of the porosity made discerning the effect of fretting damage on fatigue strength and life of the specimens difficult.

Miyoshi, Kazuhisa↗

Digital Twin Model for Advanced Manufacture of a Rotating Detonation Engine Injector

A digital twin material model (DTMM) of an additive manufacturing (AM) process was created to advance the state of the art in rotating detonation engine (RDE) injector design. Current RDE injectors are designed with large pressure drops, enabling a stable and repeatable combustion process. However, this comes at the cost of system efficiency. For the technology to transition to commercial fossil-based power generation, it is important to develop injectors with reduced flow losses. Low-loss injectors are difficult to design and manufacture with conventional manufacturing techniques. AM enables new design options, but the AM manufacturing process must be thoroughly understood to result in a robust design. A DTMM provides the necessary insight by defining the cause-effect relationships between process parameters, microstructure features, and properties. Therefore, a DTMM to support the design and manufacturing process was developed and applied to the design of a new additively manufactured low-loss injector. The injector combustion behavior was characterized through hot-fire tests, and mechanical performance was compared to the DTMM predictions. The two project goals were the successful development of the DTMM and the demonstration of an improved RDE injector design. The RDE injector design and DTMM developments occurred on parallel but dependent paths. The injector was designed to reduce pressure drop by increasing the cross-sectional flow area ratio between the injector air passages and the combustor annulus. This resulted in less structural material, raising the concern that thin members would be susceptible to high-cycle fatigue (HCF) under the periodic loading inherent to an RDE. It was most important for the DTMM to predict behavior in these features; therefore, the injector design concept guided the material thicknesses used in fatigue tests. The DTMM development started by manufacturing a series of coupons over the range of possible AM process variations. A design-of-experiment approach was used to select which process variable combinations gave the most efficient coverage relevant to the injector design space. The microstructure in each of these coupons was characterized, and then computational methods were used to create a numerical model of the correlation between process variables and microstructure. Next, a set of HCF samples were tested to calibrate existing models that map microstructure to HCF performance. Together, these two links formed the DTMM that calculates HCF behavior from AM process variables. Two injector prototypes were additively manufactured. The first injector design strategy aggressively pursued low-loss performance by substantially increasing the oxidizer flow area. The combination of manufacturing lead times and the fatigue testing schedule meant that the DTMM was not available when building this first prototype. Therefore, its process parameters were chosen based on a manual review of the available coupon data. This prototype was built successfully and evaluated in 58 combustion tests. Sustained detonation was achieved with remarkably reduced pressure loss, and some tests even displayed pressure loss characteristics similar to conventional gas turbine combustors. This achieved the project goal of improving RDE injector design. The second injector was manufactured according to the optimized parameters predicted by the DTMM. The flow area modifications of this injector were less aggressive than the first injector since demonstrating low pressure loss was not an objective of the second hot-fire test series. Rather, the test objective was to cause high cycle fatigue failure in the part due to periodic loading from the rotating detonation wave. The observed number of cycles to failure was to be compared to the number predicted by the DTMM and thereby assess the utility of the DTMM in component design. However, the required level of vibration was not obtained during combustion. Therefore, high cycle fatigue was not experienced in the hot-fire tests of the second injector. Fatigue data was obtained by further testing the second injector in a conventional HCF test apparatus. The injector demonstrated HCF strength above the DTMM prediction. In fact, it did not fail and testing was only discontinued due to reaching the end of the period of performance. This points to some success in the project’s primary goal of successfully developing and applying the DTMM to a component design. Implementing the DTMM recommendations for optimal processing parameters led to a part with acceptable properties. The DTMM was also shown to be an efficient correlator of data and to provide insight into the relationship between process settings, microstructure, and property performance. However, the failure of the DTMM prediction to match the experimental result of the injector fatigue test also points to the need to include significantly more data in the model development. In this project, coupons made with identical processing parameters exhibited drastically different properties from each other and from the injector part, which clearly influences the accuracy of a model that predicts performance based on parameters. Uncertainties in the build process must be quantified to develop more robust models. A denser and broader matrix of coupon process and geometry variations, several repeated builds of every point, more in-situ build process measurements, and direct observation of tensile and HCF sample microstructure (as opposed to separate microstructure specimens) are recommendations to improve future AM modeling efforts.

20 FOSSIL-FUELED POWER PLANTS↗

The role of creep in high temperature low cycle fatigue.

The significance of the role that creep can play in governing high-temperature, low-cycle fatigue resistance is investigated by conducting strain cycling tests on two high-temperature stainless steel alloys and making concurrent measurements of stress, temperature, and strain at various frequencies. The results are then analyzed in terms of damage imposed by creep and fatigue components. It is shown that creep can play an important and sometimes dominant role in low cycle fatigue at high temperatures. The results of the study include the findings that: (1) the simple life-fraction theory described is adequate for calculating creep damage when the cyclic creep rupture curve is used as a basis for analysis; (2) a method of universal slopes originally developed for room temperature use is sufficiently accurate at high temperature to be used to calculate pure fatigue damage; and (3) a linear creep-fatigue damage rule can explain the transitions observed from one failure mode to another.

Manson, S. S.↗

Additively manufacturing high-temperature aluminum alloy for automotive engine pistons

The purpose of the project was to evaluate DuAlumin-3D, an ORNL designed Al alloy, for additive manufacturing of high-performance automotive components. The project consisted of additively manufacturing a cylindrical block of representative material which was then heat treated before machining into test coupons. Testing included tensile tests as a function of temperature, high-cycle fatigue testing as a function of temperature, density and elastic modulus measurements, and thermophysical property measurements. Fractography was also performed on failed high-cycle fatigue specimens. The results were compared against benchmark AM Al alloys and current high-performance conventionally manufactured alloys. Overall, the DuAlumin-3D material outperformed the incumbent materials in mechanical properties, especially at elevated temperatures, while maintaining broadly similar thermophysical properties. The results of this study support further maturation of the material for additive manufacturing of high-performance automotive components.

36 MATERIALS SCIENCE↗

Additively manufactured Al-Ce-Ni-Mn alloy with improved elevated-temperature fatigue resistance

Here, the high cycle fatigue behavior of an additively manufactured (AM) Al-10.5Ce-3.1Ni-1.2Mn wt% alloy was evaluated at 350 °C. The measured fatigue strength of 50 MPa at this temperature is comparable to the most fatigue resistant wrought Al alloys (2618-T6 and 7079-T6) at 315 °C. Refinement of pore populations through advanced AM processing in the examined alloy led to oxide inclusions becoming dominant fatigue crack initiation sites. The distribution of microstructural features that determine crack initiation was measured by X-ray computed tomography and served as input to make fatigue strength model predictions with various methodologies. A Monte-Carlo based approach that was previously applied to predict the fatigue strength of cast aluminum alloys through pore size distributions yielded accurate predictions for the fatigue strength of this AM alloy. Given the tunability of defect distributions in AM alloys, the sensitivity of the Al-Ce-Ni-Mn alloy fatigue behavior to defect distributions and outstanding elevated-temperature fatigue resistance of this alloy; the results together suggest the possibility of a new generation of fatigue-resistant alloys produced by the additive manufacturing route.

36 MATERIALS SCIENCE↗

Fiber reinforced superalloys for rocket engines

High-pressure turbopumps for advanced reusable liquid-propellant rocket engines such as that for the Space Shuttle Main Engine (SSME) require turbine blade materials that operate under extreme conditions of temperature, hydrogen environment, high-cycle fatigue loading, thermal fatigue and thermal shock. Such requirements tax the capabilities of current blade materials. Based on projections of properties for tungsten fiber reinforced superalloy (FRS) composites, it was concluded that FRS turbine blades offer the potential of a several-fold increase in life and over a 200C increase in temperature capability over current SSME blade material. FRS composites were evaluated with respect to mechanical property requirements for SSME blade applications. Compared to the current blade material, the thermal shock resistance of FRS materials is excellent, two to nine times better, and their thermal fatigue resistance is equal to or higher than the current blade material. FRS materials had excellent low and high-cycle fatigue strengths, and thermal shock-induced surface microcracks had no influence on their fatigue strength. The material also exhibited negligible embrittlement when exposed to a hydrogen environment.

Petrasek, Donald W.↗

Fiber reinforced superalloys for rocket engines

High pressure turbopumps for advanced reusable liquid propellant rocket engines such as that for the Space Shuttle Main Engine (SSME) require turbine blade materials that operate under extreme conditions of temperature, hydrogen environment, high-cycle fatigue loading, thermal fatigue and thermal shock. Such requirements tax the capabilities of current blade materials. Based on projections of properties for tungsten fiber reinforced superalloy (FRS) composites, it was concluded that FRS turbine blades offer the potential of a several fold increase in life and over a 200 C increase in temperature capability over the current SSME blade material. FRS composites were evaluated with respect to mechanical property requirements for SSME blade applications. Compared to the current blade material, the thermal shock resistance of FRS materials is excellent, two to nine times better, and their thermal fatigue resistance is equal to or higher than the current blade material. FRS materials had excellent low and high-cycle fatigue strengths, and thermal shock-induced surface microcracks had no influence on their fatigue strength. The material also exhibited negligible embrittlement when exposed to a hydrogen environment.

Petrasek, Donald W.↗

Successful Solutions to SSME/AT Development Turbine Blade Distress

As part of the High-Pressure Fuel Turbopump/Alternate Turbopump (HPFTP/AT) turbine blade development program, unique turbine blade design features were implemented to address 2nd stage turbine blade high cycle fatigue distress and improve turbine robustness. Features included the addition of platform featherseal dampers, asymmetric blade tip seal segments, gold plating of the blade attachments, and airfoil tip trailing edge modifications. Development testing shows these features have eliminated turbine blade high cycle fatigue distress and consequently these features are currently planned for incorporation to the flight configuration. Certification testing will begin in 1999. This presentation summarizes these features.

Montgomery, Stuart K.↗

Forced Response Aeromechanics Analysis in MATLAB®-Based Environment Code With Application to Distortion-Tolerant Fan R24 Blade Geometry

Researchers at the NASA Glenn Research Center have developed a research-level code for forced response analysis for turbomachinery that provides a streamlined framework for aeromechanics analysis, as well as for generating Goodman diagrams. The Forced Response Aeromechanics Analysis in a MATLAB-Based Environment (FRAAME, Version 1) code is designed to accept blade surface unsteady pressure time histories generated by three-dimensional (3D) Unsteady Reynolds-Averaged Navier-Stokes (URANS) code TURBO and modal displacements, modal stresses, and static stresses generated via expanded ANSYS® (Ansys, Inc.) cyclic symmetry analysis. The code’s looping structure allows for largescale analyses, including many blade surface pressure files, modal displacements, and modal stress files for full annulus forced response analysis, including a modal summation method for multiple engine orders and modes. This code is applied to the R24 fan geometry for the Boundary Layer Ingesting Inlet/Distortion-Tolerant Fan (BLI2DTF) project, a propulsion system being developed to increase the fuel efficiency of future aircraft, to serve as validation of experimental data as well as external simulation results. This tool’s functional, modular form is intended to allow users to make modifications easily. Those modifications can include requests for information for any step in the analysis process, as well as adding various functions to compute additional information of interest. It is also written, given sufficient input information, as a general blade geometry forced response solver that is not necessarily specific to the R24 geometry but is used here for verification of code functionality and accuracy. Although forced response analysis tools are also available in commercially available code packages, the post-processing FRAAME code offers reliable, fast, and scalable forced response analysis and Goodman diagram generation for large cases utilizing, specifically, TURBO and ANSYS® results information in an effort to streamline forced response and high cycle fatigue analyses.

Aeromechanics↗

Program for development of strain tolerant thermal barrier coating system

The results of thermal conductivity, thermal expansion and high cycle fatigue tests conducted on coating systems are presented. These results show that the thermal conductivity of coating system 8 at approximately 982 C (1800 F) is substantially higher than system 3 while no significant differences were observed in the thermal expansion measurements up to approximately 1316 C (2400 F). High cycle fatigue (HCF) testing, which was conducted at room temperature and several stress levels, showed both coatings to be extremely resistant to spallation in HCF.

Anderson, N. P.↗

The Grid Density Dependence of the Unsteady Pressures of the J-2X Turbines

The J-2X engine was originally designed for the upper stage of the cancelled Crew Launch Vehicle. Although the Crew Launch Vehicle was cancelled the J-2X engine, which is currently undergoing hot-fire testing, may be used on future programs. The J-2X engine is a direct descendent of the J-2 engine which powered the upper stage during the Apollo program. Many changes including a thrust increase from 230K to 294K lbf have been implemented in this engine. As part of the design requirements, the turbine blades must meet minimum high cycle fatigue factors of safety for various vibrational modes that have resonant frequencies in the engine's operating range. The unsteady blade loading is calculated directly from CFD simulations. A grid density study was performed to understand the sensitivity of the spatial loading and the magnitude of the on blade loading due to changes in grid density. Given that the unsteady blade loading has a first order effect on the high cycle fatigue factors of safety, it is important to understand the level of convergence when applying the unsteady loads. The convergence of the unsteady pressures of several grid densities will be presented for various frequencies in the engine's operating range.

Schmauch, Preston B.↗

Exploring the Role of Type-II Residual Stresses in A Laser Powder Bed Fusion Nickel-Based Superalloy Using Measurement and Modeling

Far-field high-energy X-ray diffraction microscopy (ff-HEDM) and the crystal plasticity finite element method (CPFEM) are used to investigate the role of grain-scale (Type-II) residual stresses on the fatigue life of additively manufactured (AM) Inconel alloy 625 (IN-625). Grain-averaged orientations, centroids, and residual elastic strain tensors from ff-HEDM data are used to instantiate a crystal plasticity model to simulate the effect of residual stresses at the grain scale. Simulation results indicate that the presence of tensile residual strains increase stress localization and heterogeneity within grains, triggering an earlier onset of plasticity. A microscale fatigue indicator parameter (FIP) is computed to model the impact of these residual strains on the cycles to fatigue crack nucleation. The crack nucleation model, based on the computed FIPs, predicts a significant reduction in the number of cycles for fatigue crack nucleation for mid- and high-cycle fatigue due to the residual strain induced localization, while the residual strains have minimal impact on low-cycle fatigue life.

Inconel↗

Unsteady Flow Interactions Between the LH2 Feed Line and SSME LPFP Inducer

An extensive computational effort has been performed in order to investigate the nature of unsteady flow in the fuel line supplying the three Space Shuttle Main Engines during flight. Evidence of high cycle fatigue (HCF) in the flow liner one diameter upstream of the Low Pressure Fuel Pump inducer has been observed in several locations. The analysis presented in this report has the objective of determining the driving mechanisms inducing HCF and the associated fluid flow phenomena. The simulations have been performed using two different computational codes, the NASA MSFC PHANTOM code and the Pratt and Whitney Rocketdyne ENIGMA code. The fuel flow through the flow liner and the pump inducer have been modeled in full three-dimensional geometry, and the results of the computations compared with test data taken during hot fire tests at NASA Stennis Space Center, and cold-flow water flow test data obtained at NASA MSFC. The numerical results indicate that unsteady pressure fluctuations at specific frequencies develop in the duct at the flow-liner location. Detailed frequency analysis of the flow disturbances is presented. The unsteadiness is believed to be an important source for fluctuating pressures generating high cycle fatigue.

Dorney, Dan↗

Fatigue performance of laser powder bed fusion hydride-dehydride Ti-6Al-4V powder

We report hydride-dehydride (HDH) Ti-6Al-4V alloy with particle size distribution of 50–120 µm is laser powder bed fusion (L-PBF) processed using optimum processing parameters and a near-fully dense structure with a density of 99.9 % is achieved. Microstructural observations and phase analyses indicate formation of columnar β grains with acicular α/α' phases in as-built condition. The roughness of the as-fabricated samples is significant with an average roughness of R a = 15.71 ± 3.96 µm and a root mean square roughness of R rms = 108.4 ± 24.9 µm, however, both values are reduced to R a = 0.19 ± 0.04 µm and R rms = 4.9 ± 0.6 µm after mechanical grinding. Mechanical tests are carried out on as-fabricated specimens followed by stress relief treatment. All samples are tested to failure in fatigue, under fully-reversed tension-compression conditions of R = –1. The as-built samples failed from the surface with crack initiation mainly at micro-notches, whereas after mechanically grinding, crack initiation changed to subsurface defects such as pores. Minimizing surface roughness by mechanically grinding eliminates surface micro-notches which improves fatigue strength in the high cycle fatigue region. Fatigue notch factor calculations showed that the effect of surface roughness was significantly lower when HDH powder is used compared to standard spherical powder. X-ray diffraction analysis revealed an in-plane compressive stress, micro-strain and grain refinement on the surface of the mechanically ground samples. Fractography observations (macroscale) revealed a fully brittle fracture in the first stage of crack growth with a transition to a dominantly ductile fracture in the third stage of crack growth. On the other hand, at the micro scale, even the brittle fracture regions showed evidence of ductile fracture within the α' martensite laths.