Highly Responsive Near-Infrared Photodetector Based on Contactless PdSe 2 Integration with a Few-Layered MoSe 2 Field-Effect Transistor
Two-dimensional (2D) semiconductors with narrow bandgaps are promising candidates for near- and far-infrared (IR) photodetection, particularly in the telecommunication spectral window. However, current low-bandgap IR photodetectors face significant challenges due to their high dark current, increased carrier recombination, and thermally generated noise. Here, in this work, a hybrid phototransistor is demonstrated by integrating direct, contact-free palladium diselenide (PdSe 2 ) as a highly responsive IR detection layer with a non-IR-absorbing molybdenum diselenide (MoSe 2 ) field-effect transistor (FET), using a near-IR source at a wavelength of λ = 1650 nm. Exfoliated PdSe 2 flakes integrated into a back-gated FET architecture exhibit ambipolar transport behavior, with extracted hole and electron mobilities of 24.8 cm 2 V –1 s –1 and 58.4 cm 2 V –1 s –1 , respectively. The devices show a clear photocurrent generation under the illumination of a λ = 1650 nm laser source, achieving a notable responsivity of ∼300 mA W -1 at an applied gate voltage of 15 V, which highlights the suitability of PdSe 2 as a narrow-bandgap material for photodetection. Photoresponsivity saturates and does not have any effect above an applied gate voltage of 15 V. To further tune the photoresponsivity performance continuously with the applied gate voltage, we construct a van der Waals heterostructure phototransistor, where few layers of PdSe 2 are directly transferred onto the 2D channel region of a MoSe 2 FET, while avoiding any contact with the metal electrodes. In this heterostructure, PdSe 2 works as the primary active IR-absorbing layer, while MoSe 2 provides high-performance FET characteristics. This spatial separation of absorption and transport facilitates efficient interlayer charge transfer and charge separation, resulting in high responsivities of up to 972 mA W –1 at near-IR wavelengths and a low power density of 1.5 mW/mm 2 . The responsivity of our photodetector is comparable to that of some state-of-the-art commercially available NIR photodetectors, highlighting the potential of PdSe 2 -based heterostructures as scalable, CMOS-compatible platforms for high-performance near-IR detection.