DOE OSTI2023

Highly Reversible Lithiation of Additive Free T‐Nb 2 O 5 for a Quarter of a Million Cycles

Abstract Fast energy storage via intercalation requires quick ionic diffusion and often results in pseudocapacitive behavior. The cycling stability of such energy storage materials remains understudied despite the relevance to lifetime cost. Orthorhombic niobium oxide (T‐Nb 2 O 5 ) is a rapid ion intercalation material with a theoretical capacity of 201.7 mAh g −1 (Li 2 Nb 2 O 5 ) and good cycling stability due to the minimal unit cell strain during (de)intercalation. Prior reports of T‐Nb 2 O 5 cycling between 1.3–3.1 V versus Li/Li + noted a 50% loss in capacity after 10 000 cycles. Here, cyclic voltammetry is used to identify the role of the voltage window, state of charge, and potentiostatic holds on the cycling stability of mesoporous T‐Nb 2 O 5 thin films. Films cycled between 1.2–3.0 V versus Li/Li + without voltage holds (Li 1.1 Nb 2 O 5 ) exhibited extreme cycling stability with 90.8% capacity retention after 0.25 million cycles without detectable morphological/crystallographic changes. In contrast, the inclusion of 60 s voltage holds (Li 2.18 Nb 2 O 5 ) led to rapid capacity loss with 61.6% retention after 10 000 cycles with corresponding X‐ray diffraction evidence of amorphization. Cycling with other limited voltage windows identifies that most crystallographic degradation occurs at higher extents of lithiation. These results reveal remarkable stability over limited conditions and suggest that T‐Nb 2 O 5 amorphization is associated with high extents of lithiation.

25 ENERGY STORAGE↗

DOE OSTI2021

Structure and reactive properties of Nb-impregnated two-dimensional pillared MWW zeolites for total oxidation of volatile organic compounds

In this work, the structure and reactive properties of niobium (Nb)-impregnated MWW-type materials were evaluated for gas-phase total oxidation of volatile organic compounds, including BTX (benzene, toluene and o -xylene). The role of the type of structure (two or three-dimensional) and the loading of Nb were considered. The results indicated most Nb species with a tetrahedral coordination on the external surfaces of both two- and three-dimensional zeolites, together with a minimal contribution of octahedral extra-framework Nb 2 O 5 species. The texture and Nb content played a key role in the gas-phase total oxidation of BTX. With the same Nb content (5 wt%), the pillared zeolite exhibited a higher specific surface, larger pore volume and mesopores between the MWW nanosheets when compared to the MCM-22 zeolites, which resulted in high accessibility of the reactant molecules to the active sites, reflected in higher BTX conversion at lower and higher temperatures (50–300 °C). The best performance was achieved with the pillared zeolite (10 wt% Nb), reaching a BTX conversion at 300 °C of 92%, 69% and 58%, respectively. Here, the catalyst was stable for up to 30 h of reaction.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Erosion and cathodic arc plasma of Nb–Al cathodes: composite versus intermetallic

Many properties of cathodic arcs from single-element cathodes show a correlation to the cohesive energy of the cathode material. For example, the burning voltage, the erosion rate, or, to a lesser extent, plasma properties like electron temperatures or average ion energy and charge states. For multi-element cathodes, various phases with different cohesive energies can initially be present in the cathode, or form due to arc exposure, complicating the evaluation of such correlations. To test the influence of morphology and phase composition of multi-element cathodes on cathodic arc properties, a Nb–Al cathode model system was used that includes: pure Nb and Al cathodes; intermetallic Nb 3 Al, Nb 2 Al and NbAl 3 cathodes; and three composite Nb–Al cathodes with atomic ratios corresponding to the stoichiometric ratios of the intermetallic phases. Pulsed cathodic arc plasmas from these cathodes were examined using a mass-per-charge and energy-per-charge analyzer, showing that charge-state-resolved ion energy distributions of plasmas from the intermetallic and corresponding composite cathodes are nearly identical. An examination of converted layers of eroded cathodes using x-ray diffraction and scanning electron microscopy indicates the formation of a surface layer with similar phase composition for intermetallic and their corresponding composite cathode types. The average arc voltages do not follow the trend of cohesive energies of Nb, Al and intermetallic Nb–Al phases, which have been calculated using density functional theory. Possible reasons for this effect are discussed based on the current knowledge of multi-element arc cathodes and their arc plasma available in literature.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Analysis of thermal grooving effects on vortex penetration in vapor-diffused Nb 3 Sn

While Nb 3 Sn theoretically offers better superconducting radio-frequency (RF) cavity performance (Q 0 and E acc ) to Nb at any given temperature, peak RF magnetic fields consistently fall short of the ~400 mT prediction. The relatively rough topography of vapor-diffused Nb 3 Sn is widely conjectured to be one of the factors that limit the attainable performance of Nb 3 Sn-coated Nb cavities prepared via Sn vapor diffusion. Here we investigate the effect of coating duration on the topography of vapor-diffused Nb 3 Sn on Nb and calculate the associated magnetic field enhancement and superheating field suppression factors using atomic force microscopy topographies. It is shown that the thermally grooved grain boundaries are major defects which may contribute to a substantial decrease in the achievable accelerating field. Further, the severity of these grooves increases with total coating duration due to the deepening of thermal grooves during the coating process.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗

DOE OSTI2025

Effects of Grain Size and Interstitial Content on Recrystallization in Nb after Cold Rolling

A fully recrystallized microstructure with a fine grain size can improve the performance of superconducting radio-frequency (SRF) cavities produced from high-purity Nb (ASTM B393–18 Type 5 Nb) while providing mechanical strength. Recrystallization depends on impurity content, initial microstructure, deformation state, and annealing conditions. To better understand how fine-grained, fully recrystallized microstructures may be produced, the recrystallization behaviors of Type 5 and Type 2 Nb materials were studied. Type 5 Nb specimens were produced with both fine and coarse initial grain sizes. All were cold rolled and then annealed under vacuum for one hour to determine the rolling reductions and temperatures required for recrystallization. The recrystallized fraction exceeded 95% in fine-grained Type 5 Nb rolled to a 30% or greater thickness reduction and then annealed at 800 °C or higher. The coarse grained Type 5 Nb required greater rolling reductions to produce any recrystallized grains at 800 °C. The higher interstitial content of the Type 2 Nb required a temperature of 1000 °C or higher to reach a recrystallized fraction greater than 95% in specimens rolled to a 60% reduction. Recrystallization is more easily achieved during annealing at a given temperature for a set time by increasing rolling reduction, decreasing interstitial content, and decreasing initial grain size prior to cold rolling. In conclusion, to avoid grain growth following recrystallization, which increases grain size, the minimum time and temperature necessary for complete recrystallization should be applied.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗

DOE OSTI2025

Microstructure, mechanical, and thermal properties of compositionally complex (Hf,Zr,Nb,Ti)B 2 ‒LaB 6 ceramics

Novel compositionally complex borides, (Hf,Zr,Nb,Ti)B 2 and (Hf,Zr,Nb,Ti)B 2 ‒LaB 6 , were fabricated using spark plasma sintering process. (Hf,Zr,Nb,Ti)B 2 ‒LaB 6 exhibits a dual-phase microstructure, in which (Hf,Zr,Nb,Ti)B 2 is a primary phase with the hexagonal structure and LaB 6 is a secondary phase with a cubic structure. The mechanical properties of both (Hf,Zr,Nb,Ti)B 2 and (Hf,Zr,Nb,Ti)B 2 ‒LaB 6 are comparable, with a combination of high hardness and moderate fracture toughness. Thermal diffusivity and conductivity of (Hf,Zr,Nb,Ti)B 2 are much lower than the individual transition metal borides but are significantly increased by the addition of LaB 6 . Herein, it is implied that the thermal properties of boride ceramics can be controlled through the appropriate design of principal metal element compositions.

borides↗

DOE OSTI2022

Nb3Sn Coating of Twin Axis Cavity for SRF Applications

The twin axis cavity with two identical accelerating beams has been proposed for Energy recovery linac (ERL) applications. Nb3Sn is a superconducting material with a higher critical temperature and a higher critical field as compared to Nb, which promises a lower operating cost due to higher quality factors. Two niobium twin axis cavities fabricated at JLab and were proposed to be coated with Nb3Sn. Due to their more complex geometry, the typical coating process used for basic elliptical cavities needs to be improved to coat these cavities. This devel-opment advances the current coating system at JLab for coating complex cavities. Two twin axis cavities were coated recently for the first time. This contribution dis-cusses initial results from coating of twin axis cavities, RF testing and witness sample analysis with an overview of the current challenges towards high performance Nb3Sn coated twin axis cavities.

Tiskumara, J.↗

DOE OSTI2023

FIRST RESULTS FROM Nb3Sn COATINGS OF 2.6 GHz Nb SRF CAVITIES USING DC CYLINDRICAL MAGNETRON SPUTTERING SYSTEM

A DC cylindrical magnetron sputtering system has been commissioned and operated to deposit Nb3Sn onto 2.6 GHz Nb SRF cavities. After optimizing the deposition conditions in a mock-up cavity, Nb-Sn films are deposited first on flat samples by multilayer sequential sputtering of Nb and Sn, and later annealed at 950 °C for 3 hours. X-ray diffraction of the films showed multiple peaks for the Nb3Sn phase and Nb (substrate). No peaks from any Nb-Sn compound other than Nb3Sn were detected. Later three 2.6 GHz Nb SRF cavities are coated with ~1 µm thick Nb3Sn. The first Nb3Sn coated cavity reached close to Eacc = 8 MV/m, demonstrating a quality factor Q0 of 3.2 × 108 at Tbath = 4.4 K and Eacc = 5 MV/m, about a factor of three higher than that of Nb at this temperature. Q0 was close to 1.1 × 109, dominated by the residual resistance, at 2 K and Eacc = 5 MV/m. The Nb3Sn coated cavities demonstrated Tc in the range of 17.9 ? 18 K. Here, we present the commissioning experience, system optimization, and the first results from the Nb3Sn fabrication on flat samples and SRF cavities.

Shakel, M.S.↗

DOE OSTI2023

First Results From Nb3Sn Coatings of 2.6 GHz Nb SRF Cavities Using DC Cylindrical Magnetron Sputtering System

A DC cylindrical magnetron sputtering system has been commissioned and operated to deposit Nb3Sn onto 2.6 GHz Nb SRF cavities. After optimizing the deposition conditions in a mock-up cavity, Nb-Sn films are deposited first on flat samples by multilayer sequential sputtering of Nb and Sn, and later annealed at 950 °C for 3 hours. X-ray diffraction of the films showed multiple peaks for the Nb3Sn phase and Nb (substrate). No peaks from any Nb- Sn compound other than Nb3Sn were detected. Later three 2.6 GHz Nb SRF cavities are coated with ~1 μm thick Nb3Sn. The first Nb3Sn coated cavity reached close to Eacc = 8 MV/m, demonstrating a quality factor Q0 of 3.2 × 108 at Tbath = 4.4 K and Eacc = 5 MV/m, about a factor of three higher than that of Nb at this temperature. Q0 was close to 1.1 × 109, dominated by the residual resistance, at 2 K and Eacc = 5 MV/m. The Nb3Sn coated cavities demonstrated Tc in the range of 17.9 – 18 K. Here we present the commissioning experience, s ystem optimization, and the first results from the Nb3Sn fabrication on flat samples and SRF cavities.

72 PHYSICS OF ELEMENTARY PARTICLES AND FIELDS↗

DOE OSTI2023

FIRST RESULTS FROM Nb3Sn COATINGS OF 2.6 GHz Nb SRF CAVITIES USING DC CYLINDRICAL MAGNETRON SPUTTERING SYSTEM

Shakel, M. S.↗

NASA NTRS1995

A study of the superconducting properties of YBa2Cu(9-x)Nb(x)O(y) thin films

Effect of Niobium substitution at the copper site in YBa2Cu3O(7-x) was studied in thin film form. The films were deposited by laser ablation technique using the targets of the YBa2Cu(3-x)Nb(x)O(y) where x = 0.0, 0.025, 0.05, 0.1, 0.2, 0.4, 0.8 and 1.0 under identical deposition conditions on SrTiO3 (100) substrates. Films were characterized by XRD, resistivity, I-V and J(sub c) measurements. Films made from x = 0.025 and 0.05 concentrations of Nb substituted targets showed relatively improved superconducting properties compared to that of undoped films. the best J(sub c) realized for x - 0.025 Nb concentration was 1.8 x 10(exp 6) A/sq cm and for 0.05 Nb concentration it was 3.2 x 10(exp 6) A/sq cm at 77 K. However, degradation of the superconducting properties, with the increase of x is greater than or equal to 0.1 Nb concentration and drastic suppression and complete loss of superconductivity was noticed for x is greater than or equal to 0.4. The growth of impurity phase YBa2NbO6 for x = 0.1 and above of Nb concentration was noted from XRD (X-Ray Diffraction) patterns. However, the site occupancy of Nb could not be confirmed from these studies.

Srinivas, S.↗

DOE OSTI2023

First Results From Nb3Sn Coatings of 2.6 GHz Nb SRF Cavities Using DC Cylindrical Magnetron Sputtering System

A DC cylindrical magnetron sputtering system has been commissioned and operated to deposit Nb3Sn onto 2.6 GHz Nb SRF cavities. After optimizing the deposition conditions in a mock-up cavity, Nb-Sn films are deposited first on flat samples by multilayer sequential sputtering of Nb and Sn, and later annealed at 950°C for 3 hours. X-ray diffraction of the films showed multiple peaks for the Nb3Sn phase and Nb (substrate). No peaks from any Nb- Sn compound other than Nb3Sn were detected. Later three 2.6 GHz Nb SRF cavities are coated with ~1 μm thick Nb3Sn. The first Nb3Sn coated cavity reached close to Eacc = 8 MV/m, demonstrating a quality factor Q0 of $3.2 \times 108$ at Tbath = 4.4 K and Eacc = 5 MV/m, about a factor of three higher than that of Nb at this temperature. Q0 was close to $1.1 \times 109$, dominated by the residual resistance, at 2 K and Eacc = 5 MV/m. The Nb3Sn coated cavities demonstrated Tc in the range of $17.9 -- 18$ K. Here we present the commissioning experience, system optimization, and the first results from the Nb3Sn fabrication on flat samples and SRF cavities.

72 PHYSICS OF ELEMENTARY PARTICLES AND FIELDS↗

DOE OSTI2024

Nb 3 Sn Superconducting Cavities by Bronze Routes for Accelerator Stewardship

This project explored the challenges of making Nb 3 Sn superconducting radio-frequency (SRF) cavities by bronze routes. The SRF research community has prioritized Nb 3 Sn for many reasons, including the possibility to operate linacs for stewardship applications in continuous-wave mode with compact cryogenic systems. Existing Nb 3 Sn approaches use a cavity body made of niobium and apply tin to the polished cavity interior, a starting point that contains the main costs of present niobium cavity technology. Further complexity is then added because a high vacuum and temperature >1100 °C must be used to prevent formation of undesirable Nb-Sn phases, de-gas interstitial contaminants, and maintain the high purity of the Nb body. The project sought a more cost-effective solution for the same performance opportunities by exploiting the Cu-Sn-Nb diffusion reactions used to make Nb 3 Sn superconducting wires for magnets, which can be carried out at ~700 °C and are compatible with much cheaper copper cavity bodies. The project also sought understanding of the materials science and factors that affect superconducting properties. The project has impacted SRF cavity technology by demonstrating feasibility of alternative routes that enable compact, high-power electron accelerators for energy, security, environment, medical, and commercial applications.

43 PARTICLE ACCELERATORS↗

DOE OSTI2020

Materials Data on Nb(ZnGa)3 by Materials Project

Nb(ZnGa)3 crystallizes in the trigonal R-3m space group. The structure is three-dimensional. Nb is bonded to six equivalent Zn and six equivalent Ga atoms to form corner-sharing NbZn6Ga6 cuboctahedra. All Nb–Zn bond lengths are 2.82 Å. All Nb–Ga bond lengths are 2.74 Å. Zn is bonded in a distorted q6 geometry to two equivalent Nb, four equivalent Zn, and four equivalent Ga atoms. All Zn–Zn bond lengths are 2.74 Å. All Zn–Ga bond lengths are 2.82 Å. Ga is bonded in a distorted q6 geometry to two equivalent Nb, four equivalent Zn, and four equivalent Ga atoms. All Ga–Ga bond lengths are 2.74 Å.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Dissolution of Nb(C,N) During Post-weld Heat-Treatment of Electric Resistance Welded X70 Line Pipe

The effect of peak temperature for post-weld heat treatment (PWHT) on the dissolution of Nb-rich carbonitrides, Nb(C,N), in the weldline of an electric resistance welded (ERW) X70 grade pipeline steel was investigated. Selected-area electron diffraction patterns and corresponding electron energy loss spectroscopy mappings revealed both Nb-rich carbonitrides and Ti-rich nitrides, (Ti,Nb)N, in the sample heat-treated to 1080 °C peak temperature. However, only Ti-rich nitrides were revealed in the sample heat-treated to 1220 °C peak temperature. During continuous heating to higher than the Ac3 temperature, i.e., near 1100 °C temperature, the dissolution of Nb(C,N) was observed in dilation and derivative of dilation. Notably, this experimental result agreed with the predictions by a DICTRA model. Furthermore, a phenomenological model was developed to explain the volume shrinkage during the dissolution of Nb(C,N) precipitates.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Electrical and Elastic Properties of Individual Single-Layer Nb 4 C 3 T x MXene Flakes

2D carbides and nitrides (MXenes) are widely recognized for their exceptional promise for numerous applications. However, physical property measurements of their individual monolayers remain very limited despite their importance for revealing the intrinsic physical properties of MXenes. The first mechanical and electrical measurements of individual single-layer flakes of Nb 4 C 3 T x MXene, which are prepared via an improved synthetic method are reported. Characterization of field-effect transistor devices based on individual single-layer Nb 4 C 3 T x flakes shows an electrical conductivity of 1024 ± 165 S cm -1 , which is two orders of magnitude higher than the previously reported values for bulk Nb 4 C 3 T x assemblies, and an electron mobility of 0.41 ± 0.27 cm 2 V -1 s -1 . Atomic force microscopy nanoindentation measurements of monolayer Nb 4 C 3 T x membranes yield an effective Young's modulus of 386 ± 13 GPa, assuming a membrane thickness of 1.26 nm. This is the highest value reported for nanoindentation measurements of solution-processable 2D materials, revealing the potential of Nb 4 C 3 T x as a primary component for various mechanical applications. In conclusion, the agreement between the mechanical properties of 2D Nb 4 C 3 T x MXene and cubic NbC suggests that the extensive experimental data on bulk carbides could be useful for identifying new MXenes with improved functional characteristics.

36 MATERIALS SCIENCE↗

DOE OSTI2026

Understanding the high-temperature behavior and corrosion resistance of Cr-Nb coated cladding for BWRs

While Cr-coated Accident Tolerant Fuel has proven successful in Pressurized Water Reactors, its dissolution in high dissolved oxygen Boiling Water Reactor environments represents a major technological barrier. Here, this study presents a comprehensive evaluation of novel Cr-Nb alloys as a coating breakthrough solution for Accident Tolerant Fuel cladding in Boiling Water Reactors. We systematically investigated Physical Vapor Deposited Cr-Nb coatings with 13% and 24 at% Nb content on commercial Zr-based cladding through rigorous testing under both normal and accident conditions. Our results demonstrate Cr-Nb coatings remained completely intact during extended Boiling Water Reactor autoclave testing, while pure Cr coatings failed catastrophically due to oxide dissolution. Under Loss-of-Coolant Accident conditions at 1100°C, Cr-Nb coatings maintained protective capability for 45 min. At 800°C, the alloy coatings matched pure Cr's excellent corrosion resistance. Despite microstructural changes during prolonged high-temperature exposure, no coating delamination occurred, ensuring continued protection of the underlying Zr substrate. These findings establish Cr-Nb coatings as a viable Accident Tolerant Fuel solution for Boiling Water Reactors.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2020

Creating Brønsted acidity at the SiO 2 -Nb 2 O 5 interface

Catalytically active acid sites associated with the silica-niobia interface were probed with a series of overcoated SiO 2 on Nb 2 O 5 (SiO 2 /Nb 2 O 5 ) mixed oxide materials prepared by deposition of tetraethyl orthosilicate onto niobic acid (Nb 2 O 5 nH 2 O) or calcined niobia (Nb 2 O 5 ). NH 3 TPD and pyridine DRIFTS studies indicated that the speciation of acid sites in the materials evolved as a function of SiO 2 loading, impacting the quantity and stability of Brønsted sites. Catalyst activity was highly dependent on SiO 2 loading in the liquid phase hydroalkoxylation of dihydropyran with n-octanol. At SiO 2 surface densities corresponding to approximately 1 Si per 2 surface Nb, the activity of these catalysts passed through a maximum approximately 20 times higher than the activity of calcined Nb 2 O 5 . We found that apparent reaction barriers measured over the most active SiO 2 /Nb 2 O 5 catalysts were 10 kJ/mol lower than those measured over niobic acid, suggesting that the OH features unique to the SiO 2 -Nb 2 O 5 interface were slightly more reactive than those on niobic acid.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗