SEARCH · Engineering Papers

Results for “Cracking resistance”

Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

SourceResearch connectionFrom yearThrough year

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

At least 91 records · Page 5

All sources NASA NTRS DOE OSTI

NASA NTRS1988

Application of the V(R) resistance curve method to fracture of various crack configurations

The fracture resistance curve method of Newman (1985), based on the crack-tip-opening displacement, V(R), for a 'stationary' crack, was applied to various crack configurations in 2024-T351 and 7075-T651 aluminum alloys tested at room temperature. Using a stationary crack solution, the crack-tip-displacement was calculated at the current crack length for the crack configurations which included compact, middle-crack, single-edge-crack, and three-hole-crack tension specimens. The results showed that the V(R) resistance curves are insensitive to crack length, specimen width, and specimen type up to maximum load. After the maximum load is reached, the V(R) remains nearly constant; this constant depends only on specimen type, specimen width, and crack length. The V(R) resistance curve method can be used with the strip-yield analyses to accurately predict stable crack growth and instability of cracked metallic materials.

Newman, J. C., Jr.↗

NASA NTRS1982

Solute transport during the cyclic oxidation of Ni-Cr-Al alloys

Important requirements for protective coatings of Ni-Cr-Al alloys for gas turbine superalloys are resistance to oxidation accompanied by thermal cycling, resistance to thermal fatigue cracking. The resistance to oxidation accompanied by thermal cycling is discussed. The resistance to thermal fatigue cracking is also considered.

Nesbitt, J. A.↗

NASA NTRS2016

Absorption Voltages and Insulation Resistance in Ceramic Capacitors with Cracks

Time dependence of absorption voltages (Vabs) in different types of low-voltage X5R and X7R ceramic capacitors was monitored for a maximum duration of hundred hours after polarization. To evaluate the effect of mechanical defects on Vabs, cracks in the dielectric were introduced either mechanically or by thermal shock. The maximum absorption voltage, time to roll-off, and the rate of voltage decrease are shown to depend on the crack-related leakage currents and insulation resistance in the parts. A simple model that is based on the Dow equivalent circuit for capacitors with absorption has been developed to assess the insulation resistance of capacitors. Standard measurements of the insulation resistance, contrary to the measurements based on Vabs, are not sensitive to the presence of mechanical defects and fail to reveal capacitors with cracks. Index Terms: Ceramic capacitor, insulation resistance, dielectric absorption, cracking.

cracking↗

DOE OSTI2026

Evaluating Fracture Behavior of Bioinspired Alumina-YSZ Composites through Static and Dynamic Mechanical Testing

Ceramic materials are known for their high hardness and strength but are limited by low toughness and sudden failure. Inspired by the microstructure of dental enamel, which features undulating rods that promote crack deflection and energy absorption, architected specimens were designed and manufactured. A bespoke ball-on-ring (BoR) testing apparatus measured the static biaxial rupture strength of these bioinspired materials. Additionally, impact testing with spherical steel projectiles assessed their behavior under dynamic conditions. Monolithic alumina specimens were compared to architected alumina reinforced with yttria-stabilized zirconia (YSZ) rods produced via direct ink write 3D printing. BoR tests revealed that monolithic alumina had a Weibull modulus of 10.53 and a characteristic strength of 372.3 MPa, while the composite specimens showed a Weibull modulus of 5.46 and a characteristic strength of 213.3 MPa. Although the composite failed at lower stresses and projectile velocities, it exhibited notable crack deflection and fracture resistance, with cracks being effectively interrupted by the rod inclusions. The composite specimens also resulted in fewer and larger fragments upon impact. Finite element simulations confirmed the effectiveness of the rod structures in enhancing fracture resistance.

Bioinspired materials↗

NASA NTRS2018

Applying ASTM International C1421 to Glasses and Optical Ceramics

Fracture toughness is a critical structural design parameter and an excellent metric to rank structural materials. It determines fracture strength by way of the flaws, both inherent and induced, and defines the endpoint of the slow crack growth curve. The fracture toughness of glasses and structural and optical ceramics as measured by several techniques is compared. When good metrology is employed, the results are very comparable with two exceptions: materials exhibiting crack growth resistance and those with low SCG exponents. For materials exhibiting crack growth resistance (R-curve), the result is a function of extension and can be minimized with short cracks. For materials with low SCG exponents, such as glasses, elimination of the corrosive media and/or increasing the stress intensity rate minimizes effects. A summary of values is given for optical materials and glasses.

fracture toughness↗

NASA NTRS2014

Absorption Voltages and Insulation Resistance in Ceramic Capacitors with Cracks

Time dependence of absorption voltages (V(sub abs)) in different types of low-voltage X5R and X7R ceramic capacitors was monitored for a maximum duration of hundred hours after polarization. To evaluate the effect of mechanical defects on V(sub abs)), cracks in the dielectric were introduced either mechanically or by thermal shock. The maximum absorption voltage, time to roll-off, and the rate of voltage decrease are shown to depend on the crack-related leakage currents and insulation resistance in the parts. A simple model that is based on the Dow equivalent circuit for capacitors with absorption has been developed to assess the insulation resistance of capacitors. Standard measurements of the insulation resistance, contrary to the measurements based on V(sub abs)), are not sensitive to the presence of mechanical defects and fail to reveal capacitors with cracks.

ceramic capacitor↗

NASA NTRS2001

High Temperature Fatigue Crack Growth Behavior of Alloy 10

Methods to improve the high temperature, dwell crack growth resistance of Alloy 10, a high strength, nickel-base disk alloy, were studied. Two approaches, heat treat variations and composition modifications, were investigated. Under the heat treat approach, solution temperature, cooling rates, and stabilization, were studied. It was found that higher solution temperatures, which promote coarser grain sizes, coupled with a 1550 F stabilization treatment were found to significantly reduce dwell crack growth rates at 1300 F Changes in the niobium and tantalum content were found to have a much smaller impact on crack growth behavior. Lowering the niobium:tantalum ratio did improve crack growth resistance and this effect was most pronounced for coarse grain microstructures. Based on these findings, a coarse grain microstructure for Alloy 10 appears to be the best option for improving dwell crack growth resistance, especially in the rim of a disk where temperatures can reach or exceed 1300 T. Further, the use of advanced processing technologies, which can produce a coarse grain rim and fine grain bore, would be the preferred option for Alloy 10 to obtain the optimal balance between tensile, creep, and crack growth requirements for small gas turbine engines.

Gayda, John↗

NASA NTRS1998

Comparative Stress Corrosion Cracking and General Corrosion Resistance of Annealed and Hardened 440 C Stainless Steel - New Techniques in Stress Corrosion Testing

The corrosion and stress corrosion cracking (SCC) characteristics of annealed and hardened 440C stainless steel were evaluated in high humidity and 3.5-percent NaCl solution. Corrosion testing consisted of an evaluation of flat plates, with and without grease, in high humidity, as well as electrochemical testing in 3.5-percent NaCl. Stress corrosion testing consisted of conventional, constant strain, smooth bar testing in high humidity in addition to two relatively new techniques under evaluation at MSFC. These techniques involve either incremental or constant rate increases in the load applied to a precracked SE(B) specimen, monitoring the crack-opening-displacement response for indications of crack growth. The electrochemical corrosion testing demonstrated an order of magnitude greater general corrosion rate in the annealed 440C. All techniques for stress corrosion testing showed substantially better SCC resistance in the annealed material. The efficacy of the new techniques for stress corrosion testing was demonstrated both by the savings in time and the ability to better quantify SCC data.

Mendreck, M. J.↗

NASA NTRS1975

On fracture toughness evaluation for semi-brittle fracture

The existing methods of assessing the fracture toughness of materials exhibiting semi-brittle fracture are critically reviewed. The methods concern the Crack Growth Resistance (R-curve), the Crack Opening Displacement (COD), and the J-integral. An analysis of the shortcomings of the methods described makes it possible to formulate a new definition of fracture toughness appropriate to semi-brittle fracture. An improved simple experimental method for measuring fracture toughness for semi-brittle fracture is proposed which takes into account both crack growth and plastic nonlinear effects at crack front. The proposed method is shown to be free of the theoretical and experimental discrepancies encountered in the R-curve, COD, and J-integral methods.

Eftis, J.↗

NASA NTRS1990

Micromechanical model of crack growth in fiber reinforced ceramics

A model based on the micromechanical mechanism of crack growth resistance in fiber reinforced ceramics is presented. The formulation of the model is based on a small scale geometry of a macrocrack with a bridging zone, the process zone, which governs the resistance mechanism. The effect of high toughness of the fibers in retardation of the crack advance, and the significance of the fiber pullout mechanism on the crack growth resistance, are reflected in this model. The model allows one to address issues such as influence of fiber spacing, fiber flexibility, and fiber matrix friction. Two approaches were used. One represents the fracture initiation and concentrated on the development of the first microcracks between fibers. An exact closed form solution was obtained for this case. The second case deals with the development of an array of microcracks between fibers forming the bridging zone. An implicit exact solution is formed for this case. In both cases, a discrete fiber distribution is incorporated into the solution.

Rubinstein, Asher A.↗

NASA NTRS1990

Micromechanical model of crack growth in fiber reinforced brittle materials

Rubinstein, Asher A.↗

NASA NTRS2006

Fracture Toughness of Thin Plates by the Double-Torsion Test Method

Double torsion testing can produce fracture toughness values without crack length measurement that are comparable to those measured via standardized techniques such as the chevron-notch, surface-crack-in-flexure and precracked beam if the appropriate geometry is employed, and the material does not exhibit increasing crack growth resistance. Results to date indicate that 8 < W/d < 80 and L/W > 2 are required if crack length is not considered in stress intensity calculations. At L/W = 2, the normalized crack length should be 0.35 < a/L < 0.65; whereas for L/W = 3, 0.2 < a/L < 0.75 is acceptable. In addition, the load-points need to roll to reduce friction. For an alumina exhibiting increasing crack growth resistance, values corresponding to the plateau of the R-curve were measured. For very thin plates (W/d > 80) nonlinear effects were encountered.

Salem, Jonathan A.↗

NASA NTRS2003

Creep Resistance of Disk Alloy CH98 with Tungsten and Niobium Additions

Gas turbine engines for future subsonic transports will likely have higher pressure ratios which will require nickel-base superalloy disks with temperature capability up to 1400 F, an increase of about 200 F over current engines. Several advanced disk alloys are being developed to fill this need. One of these, CH98, is a promising candidate for gas turbine engines and is being studied in NASA's AST Program. Additions of the refractory elements tungsten and niobium have been shown to improve tensile and creep properties while maintaining good high temperature fatigue crack growth resistance. Further improvements in creep and crack growth resistance can be achieved with a coarse grain microstructure. The purpose of the present study is aimed at providing a detailed assessment of 0.2 percent creep rates for coarse grain CH98 with tungsten and niobium additions over a range of temperatures and stresses of interest to disk applications.

Gayda, John↗

NASA NTRS2014

Slow Strain Rate Tensile Testing to Assess the Ability of Superalloys to Resist Environment-Assisted Intergranular Cracking

Intergranular fatigue crack initiation and growth due to environmental degradation, especially at notched features, can often limit the fatigue life of disk superalloys at high temperatures. For clear comparisons, the effects of alloy composition on cracking in air needs to be understood and compared separately from variables associated with notches and cracks such as effective stress concentration, plastic flow, stress relaxation, and stress redistribution. The objective of this study was to attempt using simple tensile tests of specimens with uniform gage sections to compare the effects of varied alloy composition on environment-assisted cracking of several powder metal and cast and wrought superalloys including ME3, LSHR, Udimet 720, ATI 718Plus alloy, Haynes 282, and Inconel 740. Slow and fast strain-rate tensile tests were found to be a useful tool to compare propensities for intergranular surface crack initiation and growth. The effects of composition and heat treatment on tensile fracture strain and associated failure modes were compared. Environment interactions were determined to often limit ductility, by promoting intergranular surface cracking. The response of various superalloys and heat treatments to slow strain rate tensile testing varied substantially, showing that composition and microstructure can significantly influence environmental resistance to cracking.

Heat resistant alloys↗

NASA NTRS2014

Use of Slow Strain Rate Tensile Testing to Assess the Ability of Several Superalloys to Resist Environmentally-Assisted Intergranular Cracking

Intergranular fatigue crack initiation and growth due to environmental degradation, especially at notched features, can often limit the fatigue life of disk superalloys at high temperatures. For clear comparisons, the effects of alloy composition on cracking in air needs to be understood and compared separately from variables associated with notches and cracks such as effective stress concentration, plastic flow, stress relaxation, and stress redistribution. The objective of this study was to attempt using simple tensile tests of specimens with uniform gage sections to compare the effects of varied alloy composition on environment-assisted cracking of several powder metal and cast and wrought superalloys including ME3, LSHR, Udimet 720(TradeMark) ATI 718Plus(Registered TradeMark) alloy, Haynes 282(Trademark), and Inconel 740(TradeMark) Slow and fast strain-rate tensile tests were found to be a useful tool to compare propensities for intergranular surface crack initiation and growth. The effects of composition and heat treatment on tensile fracture strain and associated failure modes were compared. Environment interactions were determined to often limit ductility, by promoting intergranular surface cracking. The response of various superalloys and heat treatments to slow strain rate tensile testing varied substantially, showing that composition and microstructure can significantly influence environmental resistance to cracking.

fatigue(materials)↗

NASA NTRS2003

Versatile Turbine Disk Alloy Designed and Processed for Higher Temperature Applications

Advanced turbine engine configurations using higher temperature combustor and airfoil concepts require compressor and turbine disks that can withstand temperatures higher than the 650 C typical of current engines. This requires disk alloy and processing improvements. A versatile disk alloy was needed that could be given either fine grain heat treatments for high strength and fatigue and creep resistance up to 704 C or given coarse grain heat treatments for high strength and creep and dwell crack-growth resistance at higher temperatures. This alloy could produce disks with uniform microstructures and properties, as well as with varied, optimized microstructures at disk bore and rim sections. A series of experimental disk alloys were designed and processed to give subscale disks about 13 cm in diameter and 4 cm thick. These alloys had varying levels of key elements to affect mechanical properties and change the "solvus" solution heat-treatment temperature necessary to produce coarse grain microstructures. Disks were given coarse grain heat treatments followed by rapid oil quenching and slower fan air quenching. These heat treatments were intended to simulate the cooling paths of rapidly cooled full-scale disks at the outermost rim and interior bore locations, respectively. Preliminary quench tests of tensile specimens and coin-size minidisks had indicated that alloys having high solvus temperatures were more prone to cracking during rapid quenching from coarse grain heat treatments. These findings were confirmed in the subscale disks, where such alloys did form undesirable quench cracks. Mechanical tests were performed on specimens from subscale disks given these coarse grain heat treatments, as well as on specimens given a fine grain heat treatment. Tensile, creep, and crack growth tests were performed at 704 C and higher temperatures. A versatile alloy was identified that had a low solvus temperature for resistance to quench cracking as well as an optimal combination of high levels of strengthening refractory elements that produced balanced high mechanical properties for both fine grain and coarse grain microstructures. This low-solvus, high-refractory (LSHR) alloy has been scaled-up to produce prototype full-scale turbine disks typical of regional jet turbofan engines. Disks were successfully heat treated to give uniform coarse grain and uniform fine grain microstructures. Additional disks were given a NASA dual microstructure heat treatment (DMHT) that intentionally varied the solution heat-treatment temperatures between the disk rim and bore (re f. 1). The disk rim was heated to a high enough temperature to produce a coarse grain microstructure, while the bore was maintained at a lower temperature to produce a fine grain microstructure (see the figure). This DMHT can produce optimal high strength, fatigue, and creep resistance up to 704 C in the cooler running disk bore, and high strength, creep resistance, and dwell crack growth resistance at higher temperatures for the hotter disk rim. Extensive mechanical testing is being initiated to compare the mechanical properties of the uniform and DMHT disks.

Gabb, TImothy P.↗

NASA NTRS1991

Elevated temperature mechanical behavior of monolithic and SiC whisker-reinforced silicon nitrides

The mechanical behavior of a 30 volume percent SiC whisker reinforced silicon nitride and a similar monolithic silicon nitride were measured at several temperatures. Measurements included strength, fracture toughness, crack growth resistance, dynamic fatigue susceptibility, post oxidation strength, and creep rate. Strength controlling defects were determined with fractographic analysis. The addition of SiC whiskers to silicon nitride did not substantially improve the strength, fracture toughness, or crack growth resistance. However, the fatigue resistance, post oxidation strength, and creep resistance were diminished by the whisker addition.

Salem, Jonathan A.↗

NASA NTRS1990

Mechanical behavior and failure phenomenon of an in situ-toughened silicon nitride

The Weibull modulus, fracture toughness and crack growth resistance of an in-situ toughened, silicon nitride material used to manufacture a turbine combustor were determined from room temperature to 1371 C. The material exhibited an elongated grain structure that resulted in improved fracture toughness, nonlinear crack growth resistance, and good elevated temperature strength. However, low temperature strength was limited by grains of excessive length (30 to 100 microns). These excessively long grains were surrounded by regions rich in sintering additives.

Salem, Jonathan A.↗