DOE OSTI2018

Tensile, Creep, and Fatigue Behaviors of 3D-Printed Acrylonitrile Butadiene Styrene

Acrylonitrile butadiene styrene (ABS) is a widely used thermoplastics in 3D printing. However, there is a lack of thorough investigation of the mechanical properties of 3D-printed ABS components, including orientation-dependent tensile strength and creep fatigue properties. In this work, a systematic characterization is conducted on the mechanical properties of 3D-printed ABS components. Specifically, the effect of printing orientation on the tensile and creep properties is investigated. The results show that, in tensile tests, the 0° printing orientation has the highest Young’s modulus of 1.81 GPa, and ultimate strength of 224 MPa. In the creep test, the 90° printing orientation has the lowest k value of 0.2 in the plastics creep model, suggesting 90° is the most creep resistant direction. In the fatigue test, the average cycle number under load of 30 N is 3796 cycles. The average cycle number decreases to 128 cycles when the load is 60 N. Using the Paris law, with an estimated crack size of 0.75 mm, and stress intensity factor is varied from 352 to 700 N√m, the derived fatigue crack growth rate is 0.0341 mm/cycle. This study provides important mechanical property data that is useful for applying 3D-printed ABS in engineering applications.

36 MATERIALS SCIENCE↗
DOE OSTI2019

Effect of Vertical Strut Arrangements on Compression Characteristics of 3D Printed Polymer Lattice Structures: Experimental and Computational Study

This paper discusses the behavior of the three-dimensional (3D) printed polymer lattice core structures during compressive deformation, by both physical testing and computer modeling. Four lattice configurations based on the body-centered cubic (BCC) unit cell were selected to investigate the effect of vertical strut arrangements on stiffness, failure load, and energy absorption per unit mass or the specific energy absorption (SEA). The basic BCC unit cell consists of struts connecting the body center to the corners of the cube. Three variations in the BCC configuration considered in this study are (1) BCCV, with vertical members connecting all nodes of the lattice, (2) BCCA, with vertical members in alternating layers of the lattice, and (3) BCCG, with a gradient in the number of vertical members increasing from none at the top layer to all vertical members at the bottom layer. The unit cell dimensions were 5 mm × 5 mm × 5 mm with strut diameter of 1 mm. The lattice was assembled with 5 cells in the x and y directions and 4 cells in the z direction. Specimens were first made by 3D printing by using a fused deposition modeling printer with acrylonitrile–butadiene–styrene thermoplastic. Specimens were then tested under compression in the z direction under quasi-static conditions. Finite element analysis was used to model the compressive behavior of the different lattice structures. Results from both experiments and finite element models show that the strength of the lattice structures is greater when vertical members are present, and the SEA depends on the lattice geometry and not its mass.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Mechanical Performance and Mesostructure Analysis of Proton-Irradiated Fused Filament Fabrication Acrylonitrile Butadiene Styrene Material

The use of fused filament fabrication (FFF) acrylonitrile butadiene styrene (ABS) and other thermoplastics in radiation environments is beginning to be studied as possible replacements for traditionally manufactured parts and tools. Interlayer adhesion within the mesostructure has been shown in published literature to be an integral component in the strength of FFF ABS. Research of irradiated 3D printed polymers has primarily focused on the influence of gamma irradiation on the mechanical properties of FFF ABS samples, without evaluating its impact on the mesostructure of the samples. The purpose of this paper is to understand the mechanical damage caused by proton radiation on FFF ABS samples through the evaluation of the mesostructure of the ABS samples. To achieve this objective, proton radiation at 40 MeV was applied to FFF ABS samples at radiation doses up to 1.0 MGy at a dose rate of 1 MGy/hr. Following the irradiation, tensile testing was performed on the samples. Here, the fractured surfaces of the tested samples were subsequently observed using a scanning electron microscope. The mechanical test results show an increase in the ultimate tensile strength (UTS) and a decrease in the ductility of the irradiated samples. Statistical analysis on the results shows that there is a statistically significant difference in the UTS and the ductility of unirradiated and 1.0 MGy irradiated samples and between irradiated samples and 1.0 MGy samples. In addition, the percentage elongation at break has statistically significant differences in the means between irradiated samples and 1.0 MGy samples. The UTS has statistically significant differences in the means between 0.1 MGy and 1.0 MGy. The difference in the means between the unirradiated and the 1.0 MGy samples is the most significant for both the UTS and elongation at break. The scanning electron microscopy (SEM) results indicated that interlayer adhesion improved as a function of radiation dose corresponding to the increase in tensile strength. The SEM results also showed that crazing and plastic deformation were reduced; aligning with the loss in ductility observed in the tensile tests results. The proton radiation is causing these mechanical and physical changes through two mechanisms: (1) dose rate effects on ionizing radiation-induced oxidative degradation; and (2) radiation heating effects of high energy (>1 MeV) charged particles.

electron microscopy↗
DOE OSTI2026

Design, characterization and shape recovery behavior of 3D/4D printed shape memory polymers (SMPs)

Shape memory polymers (SMPs) represent a paradigm shift in material science, uniquely capable of undergoing reversible shape transformations triggered by external stimuli, positioning them as pivotal in developing next-generation biomedical devices, aerospace components, and adaptive structures. Extensive research has been done on SMPs with a major focus on high-temperature programming methods, which can limit energy efficiency and applicability with temperature-sensitive materials. Additionally, while various SMP blends have demonstrated great potential, limited work has been done on the suitability for 3D printing these materials, particularly under high-strain and ambient temperature programming conditions. In this study, a three-component optimized SMP composition was evaluated by 3D printing via the Material Extrusion (MEX) technique and investigating its ambient temperature-programming behavior at high strains. The SMP formulation studied was a tailored blend of thermoplastic polyurethane (TPU), polycaprolactone (PCL), and an octadecane diol-based copolymer (OBC) that exhibits robust shape memory behavior, high strain tolerance, and efficient force generation. Rigorous thermal, mechanical, and shape recovery analyses, along with optimized printing parameters and consistent shape recovery rates of up to 90%, were achieved under dynamic mechanical analysis (DMA), even under ambient programming conditions. This work demonstrates the SMP composition’s potential for adaptive, self-deployable systems with 4D printing characteristics ideal for bio-inspired structures and artificial muscle fibers.

Sudan, Kavish [University of Louisville, KY]↗
DOE OSTI2020

High-performance molded composites using additively manufactured preforms with controlled fiber and pore morphology

Here, large-scale multimaterial preforms produced by additive manufacturing (AM) underwent compression molding (CM) to produce high-performance thermoplastic composites reinforced with short carbon fibers. AM and CM techniques were integrated to control the fiber orientation (microstructure) and to reduce void content for the improved mechanical performance of the composite. The new integrated manufacturing technique is termed “additive manufacturing-compression molding” (AM-CM). For the present study, the most common materials were used for large-scale printing, i.e., acrylonitrile butadiene styrene (ABS), carbon fiber (CF)–filled ABS (CF/ABS) and glass fiber (GF)–filled ABS (GF/ABS). Three different manufacturing processes; (a) AM (b) extrusion compression molding (ECM), and (c) AM-CM were used to prepare four different panel configurations: (1) neat ABS, (2) CF/ABS, (3) overmold (CF/ABS over neat ABS), and (4) sandwich (neat ABS between two CF/ABS layers). The mechanical properties (tensile and flexural strength and modulus, and Izod impact energy) of samples prepared via all three manufacturing processes were compared. X-ray microcomputer tomography was employed to evaluate the fiber orientation distribution and the volumetric porosity content. The preform maintained high fiber alignment (≈ 82% of fibers within the range of 0–20° in the deposition direction), and the volumetric porosity was reduced by 50% from 3.79% to 1.91% after compression. The alignment of long pores along the deposition direction was also observed. The mechanical properties are discussed with correlation to the fiber alignment and void content in the samples. CF/ABS samples prepared by AM-CM showed significant improvement of 11.15%, 35.27%, 28.6%, and 74.3% in the tensile strength, tensile modulus, flexural strength, and flexural modulus, respectively, when compared with samples prepared by ECM. Unique aspects of this study are the demonstration of large-scale multimaterial AM and the use of multimaterials as preforms to make high-performance composites.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Mica filled polyetherketoneketones for material extrusion 3D printing

Polyetherketoneketone (PEKK) has superior physical properties to most available thermoplastics compatible with material extrusion-based 3D printing, including analogs in the polyaryletherketone (PAEK) family. To date, the performance of fused filament fabrication (FFF) compatible PEKK has been detailed primarily as a function of varying the isomer ratios composing the co-polymer structure. The strategy to form blends or composites with PEKK for FFF is attractive for further tailoring of performance in application, yet has received limited attention. Here, we report the integration of three grades of mica platelets into PEKK at 10% and 30% mass loadings to generate an array of filament feedstocks that were then used to print objects with a simple FFF machine. The effects of mica coating chemistry and surface treatment on the compatibility with PEKK and resulting properties are described. Mica fillers at both loadings have only subtle influence on the FFF relevant melt rheological properties inherent to PEKK. Pigment micas at high loadings can lower the melting temperature of PEKK (up to 19 ºC) without shifting its glass transition temperature and inhibit much of the undesirable crystallization occurring during processing with unfilled PEKK. The printed composites were effectively cold crystallized post-printing, affording crystalline fractions up to 90% relative to unfilled PEKK with increased dimensional stabilities. All micas, when used as fillers in low and high relative PEKK crystallinities, significantly increased the tensile modulus (as high as 126% or to 7.31 GPa) of parts in correlation to the loading. Furthermore, the underlying microstructural features of a printed composite were compared to unfilled PEKK by use of a high-resolution helical micro-computed tomography instrument. Practically, pigment micas can confer a wide range of rich colors to 3D-printed PEKK.

36 MATERIALS SCIENCE↗
DOE OSTI2023

A framework for forming thermoset polymer networks during laser powder bed fusion additive manufacturing

It is commonly reported that the limited availability of material types is a major barrier to widespread adoption for polymer laser powder bed fusion (PBF/L) additive manufacturing (AM). A deeper understanding of the physico-chemical relationships between AM process stimuli and polymer responsive behavior is needed to make data-driven decisions for PBF/L specific material development and formulation. Many researchers have cumulatively built the current state of PBF/L “science-based manufacturing” framework where an initial guess for process parameter values can be determined from measured polymer properties and the first-principles of physics. However, published literature has focused on developing this framework for thermoplastic processing of polymers omitting many specific concerns unique to processing thermosetting materials. The authors consider in the present work the implications of many specific aspects unique to thermosetting polymers during PBF/L manufacturing. These aspects are contextually discussed according to the five sub-functions of PBF/L and are described mathematically where appropriate alongside example data from thermosetting materials commercially available in powder form. Further, this expansion of the prevailing material development framework to include thermosetting polymers paves the way for the unique performance properties offered by that class to be manifest through AM’s geometric freedom.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Carbon fibers derived from commodity polymers: A review

Carbon fiber composites are prohibitively expensive for a wide array of applications that would greatly benefit from their superior specific strength and specific stiffness. Replacing the market-dominant carbon fiber precursor material, polyacrylonitrile, with a low-cost alternative would significantly reduce the cost of carbon fiber production. Commodity polymers may provide such an alternative thanks to their abundance and ease of production into fibers. Furthermore, this review presents state-of-the-art carbon fiber production from polyacrylonitrile, an overview of melt-spinnable alternative precursors broadly, and an in-depth review of the latest advances in the synthesis of carbon fibers from low-cost, commodity thermoplastics such as polyethylene, polyamide, polystyrene, polyester, and poly(vinyl chloride).

36 MATERIALS SCIENCE↗
DOE OSTI2023

A systematic multicriteria-based approach to support product portfolio selection in microalgae biorefineries

Here this work proposes and applies a sequential approach of objective methods to aid the decision-making process for the deployment of microalgae biorefineries. The strategy combines Multicriteria Decision Analysis (MCDA) and weight assignment methods to simultaneously consider technical, economic, and environmental criteria to (1) outrank the best bioproduct options from different biomass fractions present in microalgae biomass at different ratios (namely carbohydrates, lipids, and protein) and (2) define the most suitable biorefining pathways associated with specific pairings of microalgae strains and cultivation conditions. The first part of the assessment identified succinic acid, acrylic acid, and citric acid as the top-ranked bioproducts from carbohydrates, polyurethane from lipids, and thermoplastic extrusion co-feed from protein. The second step of the analysis determined that, when production of a hydrocarbon fuel is desired, the compositional profile of a strain is paramount in defining the biorefining setup that should be pursued. In summary, microalgae lipids should be sent to the production of hydrocarbon fuels if the ratio between neutral lipids and fermentable carbohydrates is higher than roughly 1, with carbohydrates and protein being converted to the higher-value products noted above. Finally, this result was corroborated through process simulations, which indicated superior economic and environmental metrics when strains are paired with suitable conversion pathways identified through MCDA based on their compositional profiles. The outcomes of this work provide clear, objective, guidelines for establishing the best biorefining approach for a large suite of biochemical compositions as a screening method prior to employing detailed process simulations alongside rigorous techno-economic and life-cycle assessments.

09 BIOMASS FUELS↗
DOE OSTI2016

Modeling the measured effect of a nitroplasticizer (BDNPA/F) on cookoff of a plastic bonded explosive (PBX 9501)

Here, we have used a modified version of the Sandia Instrumented Thermal Ignition (SITI) experiment to develop a pressure-dependent, five-step ignition model for a plastic bonded explosive (PBX 9501) consisting of 95 wt% octahydro-1,3,5,7-tetranitro-1,3,5,7-tetrazoncine (HMX), 2.5 wt% Estane® 5703 (a polyurethane thermoplastic), and 2.5 wt% of a nitroplasticizer (NP): BDNPA/F, a 50/50 wt% eutectic mixture bis(2,2-dinitropropyl)-acetal (BDNPA) and bis(2,2-dinitropropyl)-formal (BDNPF). The five steps include desorption of water, decomposition of the NP to form NO2, reaction of the NO2 with Estane® and HMX, and decomposition of HMX. The model was fit using our experiments and successfully validated with experiments from five other laboratories with scales ranging from about 2 g to more than 2.5 kg of PBX. Our experimental variables included density, confinement, free gas volume, and temperature. We measured internal temperatures, confinement pressure, and ignition time. In some of our experiments, we used a borescope to visually observe the decomposing PBX. Our observations included the endothermic β–δ phase change of the HMX, a small exothermic temperature excursion in low-density unconfined experiments, and runaway ignition. We hypothesize that the temperature excursion in these low density experiments was associated with the NP decomposing exothermically within the PBX sample. This reactant-limited temperature excursion was not observed with our thermocouples in the high-density experiments. For these experiments, we believe the binder diffused to the edges of our high density samples and decomposed next to the highly conductive wall as confirmed by our borescope images.

42 ENGINEERING↗
DOE OSTI2020

A numerical study of the meso-structure variability in the compaction process of prepreg platelet molded composites

Compaction deformations in a thermoplastic composite system molded from chopped prepreg platelets were analyzed to obtain statistical distributions of local distortions that define the final consolidated meso-structure. This study provides an insight into and allows quantification of the intrinsic geometric variability of the composite meso-structure that controls the variability of the effective composite mechanical properties. A two-phase viscoelastic finite element model was utilized to treat the behavior of molten prepreg platelets, which were assumed to be incompressible and inextensible in the fiber direction during processing. A two-step simulation procedure with discretely modeled platelets and platelet-to-platelet contacts is proposed. The analysis begins with a drop simulation of the uncontrolled material deposition followed by a 3D finite element analysis of the preform compaction and bulk material flow. The proposed model provides a method for generating a composite meso-structure ab initio starting from a statistical sampling of the initial conditions for platelet deposition. The predicted platelet thickness distribution, intra-platelet fiber waviness and out-of-plane platelet undulations were found to be in good agreement with experimental measurements. An estimate of the volume of resin pockets was inferred from the compaction simulation.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Investigation of the notch sensitivity of tailorable long fiber discontinuous prepreg composite laminates

Tailorable discontinuous fiber composite laminates provide relative formability beyond that of continuous fiber laminates, while achieving improved mechanical performance over comparable stochastic systems. Here, in this work, the notch sensitivity of engineered prepreg platelet molded composite (PPMC) laminates is investigated using the open-hole tension (OHT) test and compared to available data for stochastic PPMCs and continuous fiber laminates made with the same material. The press-formed thermoplastic composites (AS4/PEKK) were molded with a quasi-isotropic stacking sequence. The discontinuous PPMC laminate was found to be notch insensitive with OHT strengths ranging from 145.4 MPa (CV $=$ 7%) for d/w $=$ 0.5 to 229.3 MPa (CV $=$ 9%) for d/w $=$ 0.25. The highly ordered meso-structure of the engineered PPMC laminate yields comparatively excellent mechanical properties for relatively thin laminates in contrast to stochastic systems. Both net- and gross-section failures were observed for d/w $=$ 0.25, which suggests that the engineered PPMC laminates studied here maintain a degree of inherent, internal stress concentrations that compete with those caused by geometric features such as a circular hole. Computational simulations of the OHT tests with explicitly represented platelets were found to be in good agreement with experimental measurements. The progressive failure analysis was used to conduct a numerical investigation of the stacking sequence and platelet meso-morphology.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Effect of plasma treatment on LMPAEK/CF tape and composites manufactured by automated tape placement (ATP)

Automated tape placement (ATP) process is widely used in aerospace for its advanced process control and multi-axis capabilities but faces issues like limited choice of materials and suboptimal tape consolidation. This study investigates air plasma treatment on ATP carbon fiber thermoplastic feedstock tape to address these challenges. The effects on low melt Polyaryletherketone/carbon fiber unidirectional tape (LMPAEK/CF UD tape) were analyzed. Treated and untreated tapes were used to fabricate composites and evaluated for physical, thermal, mechanical, and interfacial properties. Atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS) and Fourier transform infrared (FTIR) analyses revealed surface roughness changes (on LMPAEK), extent of oxidation, and the presence of hydroxyl/carboxyl groups. Composites from plasma-treated tapes showed a 7.6% increase in tensile strength, 8% in tensile modulus, 18% in flexural strength, and 8.3% in flexural modulus. Further, the interlaminar shear strength improved by 18.7%. Failure analysis showed untreated composites failed via inter-ply and fiber-matrix delamination, while treated composites experienced matrix cracking and fiber breakage. This study highlights atmospheric plasma treatment as a solution to ATP’s limitations, significantly enhancing LMPAEK/CF UD tape composites’ properties.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Fiber orientation and porosity in large-format extrusion process: The role of processing parameters

Controlling fiber orientation and porosity in short-fiber thermoplastic composites is important for enhancing mechanical, electrical and thermal properties in large-format additive manufacturing. This study employs a factorial design of experiments (DoE) to assess the effects of nozzle diameter (5.08 mm–10.16 mm), temperature (230–250 °C), and extruder screw speed (150–280 rpm) on flow rate, shear rate, porosity, fiber orientation, fiber length and tensile strength in 20 % carbon fiber-filled acrylonitrile butadiene styrene. ANOVA results show that screw speed significantly impacts flow rate, while nozzle diameter and temperature have lesser effects. Shear rate increases with smaller nozzles and higher speeds. Porosity decreases from 5.58 % with a 10.16 mm nozzle to 3.11 % with a 5.08 mm nozzle at 150 rpm due to increased shear rates, which induce shear thinning, reducing viscosity and facilitating gas escape. Larger nozzles (10.16 mm) produce larger, more heterogeneous pores, while smaller nozzles (5.08 mm) yield smaller, uniform pores. Beads produced with the 5.08 mm nozzle exhibit longer fiber lengths due to reduced residence time, lower shear stress, and better alignment. Fiber orientation improves with smaller nozzles due to higher shear rates but decreases with higher screw speeds (280 rpm) due to shorter residence times. The highest fiber alignment (A xx ∼ 0.65) and low porosity (∼3%) were achieved with a 5.08 mm nozzle at 150 rpm, while equivalent additive manufacturing-compression molding samples exhibited better tensile strength (∼93 MPa) under these conditions. In conclusion, these findings emphasize the importance of optimizing processing parameters to enhance fiber alignment and reduce porosity for improved mechanical performance.

Design of experiments↗
DOE OSTI2025

Sizing comingled CF/PA 6 fibers with cellulose nanofibrils for enhanced performance properties

Compatibility between the reinforcing phase and the polymer matrix is critical to achieving the desired mechanical and thermal performance of composite materials. Several mechanisms can enhance this interfacial interaction, including surface treatments (e.g., oxidation, plasma, or irradiation), in-situ nanoparticle deposition, and fiber sizing. Here, in this study, cellulose nanofibrils (CNF) were employed as a sustainable sizing agent to modify the interface in commingled carbon fiber (CF)/polyamide 6 (PA 6) yarns, in which CF and PA6 filaments are intimately blended to enable simultaneous consolidation. A 0.25 wt% CNF aqueous suspension was applied under bath sonication to ensure uniform dispersion and minimize agglomeration. CNF-sized and unsized yarns were used to fabricate unidirectional composite plates via filament winding on a flat mandrel, followed by compression molding. Scanning electron microscopy confirmed CNF presence on both CF and PA6 filaments. CNF-sized composites exhibited increments in interlaminar shear strength (ILSS) by 50%, flexural strength by 11%, and tensile strength by 2.5% compared to unsized composites. Thermal analysis showed minimal changes in degradation temperature and crystallinity. These findings demonstrate that CNF sizing enhances interfacial bonding and mechanical performance, offering a scalable and environmentally friendly strategy for thermoplastic composite manufacturing along with yarn/tow handleability.

Cellulose nanofibrils (CNF)↗
DOE OSTI2024

Recycling of CF-ABS machining waste for large format additive manufacturing

Large format additive manufacturing (LFAM) necessitates the use of short fiber thermoplastic composites, such as carbon fiber filled acrylonitrile butadiene styrene, to enable printing. Currently, when LFAM parts are machined into their final shape, the machining scrap (i.e., small flake like particles and offcuts) is landfilled. Previous studies have demonstrated the viability of recycling end-of-life LFAM parts by shredding and optionally re-compounding the material back into pellets. However, there is little understanding of the value and performance of recycled material made from LFAM machining scrap, which if pursued could motivate more broad recycling of this waste stream. In this study, recycled in-process machining scrap is explored as an LFAM feedstock source. Herein, it is found that the primary degradation mechanism of the recycled material is significant fiber length attrition during surface machining. While this fiber attrition negatively impacts the mechanical performance of the material in the print direction, it seems that the changes in processing behaviors and print quality, namely the surface roughness of the printed structure associated with shorter fiber lengths, is beneficial to interlayer adhesion. The tensile strength and elastic modulus of the recycled material, in the print direction, decreased 11% and 31% respectively compared to the pristine material. However, in the layer-wise direction it was found that the recycled material exhibited no significant change in elastic modulus and a significant 21% increase in tensile strength – a surprising result. In conclusion, this work indicates that machining waste could be a viable material stream for recycled LFAM feedstock materials.

42 ENGINEERING↗
DOE OSTI2026

Engineering mechanical and thermomechanical performance in additive manufacturing–Compression molded composites through multiplexed extrusion

Traditional extrusion-based additive manufacturing is limited to single material systems, restricting the multifunctional properties of composites. For this work to overcome this limitation, multiplexed additive manufacturing–compression molding (AM-CM) was employed to fabricate multi-material thermoplastic composites with spatially tailored architectures. Neat acrylonitrile butadiene styrene (ABS) and 20 wt% carbon-fiber reinforced ABS (CF-ABS) were co-extruded through a core–sheath nozzle to produce hybrid composites with neat ABS as sheath (30-50 wt%) and CF-ABS as core (50 – 70 wt%). The results show that the hybrid composites have balance of mechanical and thermomechanical performance. The tensile strength and modulus of hybrid composites exhibited a 61–95% and 173–473% increase compared to neat ABS with increases in CF-ABS content whereas the impact resistance improved by 41% compared to CF-ABS at 50 wt% ABS. Additionally, hybrid composites showed significant reduction (54 - 70%) in creep strain at 100 °C compared to neat ABS. These findings demonstrate that multiplexed AM-CM enables tunable structure–property relationships, reducing CF-ABS usage up to 50 wt% while maintaining balanced stiffness, toughness, and creep resistance.

Additive manufacturing↗
DOE OSTI2022

Plasma surface modification coupled with thermal and step-over distance effects on significant fracture improvement of adhesively-bonded metal-$\mathrm{CFRTP}$ dissimilar materials

Here, this work proposes an approach to improve the interfacial bonding between carbon-fiber-reinforced thermoplastic polymers (CFRTP) and thermoset adhesive by using the surface modification with the combination of air plasma, thermal, and step-over effects. Thanks to the proper heating which causes the exposure of carbon fibers on the CFRTP surface, both polymer matrix and these exposed carbon fibers can have improved bonding with adhesive due to air plasma treatment. By conducting the Double Cantilever Beam (DCB) tests performed on adhesively-bonded AA5052/CFRP-PA66 dissimilar joints, it was shown in this work that the average Mode I specific fracture energy can be improved up to about 180% compared to non-treated counterparts. The foregoing improvement can be further increased by considering the step-over distance of the surface treatment, which triggers the tortuous damage path in the failure process of adhesively-bonded structures. By manipulating this treatment parameter, often overlooked in the literature, and other parameters (i.e., treatment speed, nozzle tip-to-surface distance, etc.) investigated in this study, the average Mode I specific fracture energy of adhesively-bonded AA5052/CFRP-PA66 dissimilar joints can be improved reaching up to about 410% compared to non-treatment counterparts.