Tailoring Carbide Dispersed Steels: A Path to Increased Strength and Hydrogen Tolerance
The use of transition metal carbides is reported for use as a hydrogen trapping mechanism for ferritic and austenitic steel materials. The program combined computational modeling and simulations to guide experiments towards candidate metal carbide traps, both for interfacial and interior trapping. It was found that interfacial trapping is less effective than interior trapping, with the group IVB transition metal carbides being the most effect internal traps with a loss of carbon. The sub-stoichiometric rocksalt structure accommodate the hydrogen atoms in its octahedral interstices. Using percolation theory, carbon loss of approximately 25% or more was sufficient to ensure an interconnected network of vacancies for such trapping from the surface to the internal sites within the carbide. Using this as a guide, the program developed a means to provide a uniform dispersion of ZrC nanoparticles with either Fe or 304L micron-scale powders which was then consolidated by direct current sintering. Electrolytic hydrogen diffusivity studies confirmed the reduction of hydrogen diffusion in the matrix with increasing ZrC content, which was a linear response over the sample range studied (0.01 to 1.0 wt.%). The consolidated material was micro-tensile tested in either a non-hydrogen or hydrogen charge condition and compared to a control with no carbides. Additions up to 0.05 wt.% ZrC increased the yield strength with no loss in ductility in either the non-hydrogen or hydrogen tested condition. ZrC concentrations above this amount further increased the yield strength at the expense of ductility. While these samples had a lower absolute ductility value prior to failure, the relative change in ductility between the non-hydrogen and hydrogen charge states was less for the carbides than that of the control. Metal-rich ZrC nanoparticles were fabricated through a conformal coating process yielding ZrC0.66 particles that were then incorporated into a metal matrix. Notch fatigue testing in a hydrogen environment was conducted where the number of cycles to failure was found to be less in the control than that of the carbide addition. However, the spread in experimental data and the number of samples tested limits a conclusive outcome based on defects noticed in the gauge section of all the powder processed samples. The collective outcomes of this report provide further insight into the mechanisms by which carbides act as hydrogen traps; a means to process such carbides through powder metallurgy; and their associated mechanical performance in either a non-hydrogen or hydrogen-charged condition.