Changes in dislocation punching behavior due to hydrogen-seeded helium bubble growth in tungsten
The accumulation of gas atoms in tungsten is a topic of long-standing interest to the plasma-facing materials community due the metal's use as a divertor material in some tokamak fusion reactors. The nucleation and growth of He/H gas bubbles (along with their isotopes) can result from impinging fluxes of these gases which give rise to damage at the W divertor surface. The inclusion of He or H in W has been studied extensively by the community, finding that He bubbles modify the surface through periodic dislocation punching and bursting mechanisms while H bubbles impact the metal through plastic-strain induced material failure. However, the mechanisms which are present during the combined flux of both He and H is not well-studied atomistically. Motivated by this, an atomistic modeling study is conducted using molecular dynamics to assess the behavior of mixed concentration He:H bubbles in W. Here we find that the introduction of H into a growing He bubble results in a dramatic change in the nature and presence of dislocation loops which are typically generated via dislocation punching in over-pressurized He bubbles. Most notably, at high H concentrations, there is a switchover in energetic favorability from glissile 1/2<111> dislocations to sessile <100> dislocations. This thermodynamic crossover could imply a significant reduction in W surface morphology changes than with pure He bubbles and, additionally, we show this to have implications on the trapping of H in the bubbles and their associated dislocations.