NASA NTRS1974

Effect of volatile removal during molding on the properties of two phenolic-fiber composites

A comparison has been made of the effect of three volatile-removing techniques during molding on the properties of phenolic-fiber composites. The first technique involved heating the molding compound from one side, initiating the volatile-producing reactions, and driving these volatiles through the compound toward the cooler side. The second technique involved the application of a vacuum to the molding cavity before and during the cure cycle. The third technique was a combination of the first two. These techniques were used in the compression molding of phenolic-asbestos and phenolic-glass composites. The effects of both the individual and combined techniques on the mechanical, thermal, and sorption properties of the composites are reported.

Price, H. L.↗
NASA NTRS1975

Long-distance recording of the humidity over the sea

A procedure is developed for long distance recording of humidity over the sea that uses humidity detectors of the sorption type, whose electrical properties depend on the relative humidity of the air. The moisture sensitive material of the hygristor is the organic polymer polyacrylonitryl, deposited on silver electrodes and thermally treated. In the measurements of the relative humidity from 60% to 95%, the resistance of the hygristor varies from several hundred kiloohms to a few kiloohms, and is an essentially nonlinear function of the humidity.

Buklanov, V. V.↗
NASA NTRS1977

Measuring trace dispersants in gas streams

Detection system uses phase shift of acoustic waves to measure amount of gaseous substances on sorption sensor. Three-part device optimizes stability and assists in achieving low-phase-noise levels.

Updike, O. L.↗
NASA NTRS1975

Specific surface area as a maturity index of lunar fines

Mature surface fines have an equilibrium specific surface area of about 0.6 sq m/g the equivalent mean particle size being about 3 microns. The adsorption behavior of inert gases (reversible isotherms) indicates that the particles are also nonporous in the size range of pores from 10 to 3000 A. Apparently, in mature soils there is a balance in the forces which cause fining, attrition, pore filling, and growth of lunar dust grains. Immature, lightly irradiated soils usually have coarser grains which reduce in size as aging proceeds. The specific surface area, determined by nitrogen or krypton sorption at 77 K, is a valuable index of soil maturity.

Gammage, R. B.↗
NASA NTRS1977

Two pumps reduce maser weight

Weight and cost of conventional hydrogen maser is reduced significantly by replacing large ion pump with hydrogen sorption pump and miniature ion pump for scavenging hydrogen and residual gases.

Source record↗
NASA NTRS1976

Electrolytic pretreatment unit gaseous effluent conditioning

The electrolytic pretreatment of urine is an advanced process that eliminates the need for handling and storing the highly corrosive chemicals that are normally used in water reclamation systems. The electrolytic pretreatment process also converts the organic materials in urine to gases (N2 and O2) that can be used to replenish those lost to space by leakage, venting, and air lock operations. The electrolytic process is more than a pretreatment, since it decreases the urine solids content by approximately one third, thus reducing the load and eventual solids storage requirements of the urine processing system. The evolved gases from the pretreatment step cannot, however, be returned directly to the atmosphere of a spacecraft without first removing several impurities including hydrogen, chlorine, and certain organic compounds. A treatment concept was developed that would decrease the impurities in the gas stream that emanates from an electrolysis unit to levels sufficiently low to allow the conditioned gas stream to be safely discharged to a spacecraft atmosphere. Two methods were experimentally demonstrated that can accomplish the desired cleanup. The bases of the two methods are, repectively: (1) raw urine scrubbing and (2) silica gel sorption.

Colombo, G. V.↗
NASA NTRS1977

A model to investigate the influence of suspended sediment on the mass transport of a pollutant in open channel flow

An explicit two-dimensional finite difference model, designed to investigate the influence of suspended sediment on the pollutant transport process, is presented. Specific attention is directed toward examining the role of suspended sediment in: (1) the turbulent vertical transport mechanism in a stratified flow, and (2) pollutant uptake due to sorption. Results presented indicate that suspended sediment plays a major role in the pollutant transport process, and subsequently, any meaningful attempt to model the fate of a pollutant in an alluvial channel must account for the presence of a suspended sediment concentration profile. Similarly, the vertical and longitudinal pollutant concentration distributions provided by the model may be utilized to improve upon the predictive capacities of existing water quality models.

Chapman, R. S.↗
NASA NTRS1977

Properties and applications of a pitch carbon microsphere composite

Some properties and applications of a pitch carbon microsphere composite are described. The small hollow microspheres are made from the pitch which is usually a wasted by-product of petroleum refining. In contrast to high density composites or syntactic foams in which microspheres are inclusions within a continuous matrix, this composite is an aggregate of microspheres bonded together by a small amount of thermosetting polymer which does not form a continuous matrix. The result is a composite with low density and thermal expansion, modest strength and rigidity, and high porosity and carbon content. Mechanical, thermal, and sorption properties have been measured. Applications of the composite include honeycomb filler for high temperature or ionizing radiation fields and a wicking absorber for solar-powered stills.

Price, H. L.↗
NASA NTRS1977

Removal of contaminant gases from an electrolytic urine pretreatment process

The effluent gas stream from an electrolytic urine pretreatment process was analyzed by gas chromatography-mass spectroscopy and wet chemical methods to determine its composition. The major constituents were identified as: hydrogen, carbon dioxide, oxygen, nitrogen, water vapor, and chlorine. The trace impurities were chlorinated light hydrocarbons, and a number of other organic impurities in the low ppm range. Several methods of removing all of the undesirable gases to levels acceptable for return to a space cabin atmosphere were investigated experimentally. A subsystem concept comprised of the following sequential unit processes and operations was successfully demonstrated: (1) raw urine scrubbing, (2) silica gel sorption, (3) dilution with cabin air, and (4) catalytic oxidation.

Colombo, G. V.↗
NASA NTRS1977

Pitch carbon microsphere composite

Petroleum pitch carbon microspheres were prepared by flash heating emulsified pitch and carbonizing the resulting microspheres in an inert atmosphere. Microsphere composites were obtained from a mixture of microspheres and tetraester precursor pyrrone powder. Scanning electron micrographs of the composite showed that it was an aggregate of microspheres bonded together by the pyrrone at the sphere contact points, with voids in and among the microspheres. Physical, thermal, and sorption properties of the composite are described. Composite applications could include use as a honeycomb filler in elevated-temperature load-bearing sandwich boards or in patient-treatment tables for radiation treatment of tumors.

Price, H. L.↗
NASA NTRS1979

Hygrothermal damage mechanisms in graphite-epoxy composites

T300/5209 and T300/5208 graphite epoxy laminates were studied experimentally and analytically in order to: (1) determine the coupling between applied stress, internal residual stress, and moisture sorption kinetics; (2) examine the microscopic damage mechanisms due to hygrothermal cycling; (3) evaluate the effect of absorbed moisture and hygrothermal cycling on inplane shear response; (4) determine the permanent loss of interfacial bond strength after moisture absorption and drying; and (5) evaluate the three dimensional stress state in laminates under a combination of hygroscopic, thermal, and mechanical loads. Specimens were conditioned to equilibrium moisture content under steady exposure to 55% or 95% RH at 70 C or 93 C. Some specimens were tested subsequent to moisture conditioning and 100 cycles between -54 C and either 70 C or 93 C.

Crossman, F. W.↗
NASA NTRS1981

Study of the dissociation of molecular hydrogen

Dissociators used to obtain an RF plasma discharge for hydrogen masers and the test system used for operation and evaluation of the dissociators are described. A compact sorption cartridge using a graphite matrix is tested as part of a hydrogen scavenging system. Testing of a vacuum enclosed hydrogen dissociator suitable for long term operation in space is described.

Vessot, R. F. C.↗
NASA NTRS1969

Aqueous alkali metal hydroxide insoluble cellulose ether membrane

A membrane that is insoluble in an aqueous alkali metal hydroxide medium is described. The membrane is a resin which is a water-soluble C2-C4 hydroxyalkyl cellulose ether polymer and an insolubilizing agent for controlled water sorption, a dialytic and electrodialytic membrane. It is particularly useful as a separator between electrodes or plates in an alkaline storage battery.

Hoyt, H. E.↗
NASA NTRS1981

Physical aging of linear and network epoxy resins

Network and linear epoxy resins principally based on the diglycidyl ether of bisphenol-A and its oligomers are prepared and studied using diamine and anhydride crosslinking agents. Rubber modified epoxies and a carbon fiber reinforced composite are also investigated. All materials display time-dependent changes when stored at temperatures below the glass transition temperature after quenching (sub-T/g/ annealing). Solvent sorption experiments initiated after different sub-T(g) annealing times demonstrate that the rate of solvent uptake can be indirectly related to the free volume of the epoxy resins. Residual thermal stresses and water are found to have little effect on the physical aging process, which affects the sub-T(g) properties of uniaxial carbon fiber reinforced epoxy material. Finally, the importance of the recovery phenomenon which affects the durability of epoxy glasses is considered.

Kong, E. S.-W.↗
NASA NTRS1982

Adsorption and excess fission xenon

The adsorption of Xe and Kr on lunar soil 10084 was measured by a method that employs only very low fractions of monolayer coverage. Results are presented as parameters for calculation of the Henry constant for adsorption as a function of temperature. The adsorption potentials are about 3 kcal/mole for Kr and 5 kcal/mole for Xe; heating the sample in vacuum increased the Xe potential to nearly 7 kcal/mole. Henry constants at the characteristic lunar temperature are about 0.3 cu cm STP/g-atm. These data were applied to consider whether adsorption is important in producing the excess fission Xe effect characteristic of highland breccias. Sorption equilibrium with a transient lunar atmosphere vented fission Xe produces concentrations seven orders of magnitude lower than observed concentrations. Higher concentrations result because of the resistance of the regolith to upward diffusion of Xe. A diffusion coefficient of 0.26 sq cm/sec is estimated for this process.

Podosek, F. A.↗
NASA NTRS1984

A research program in determination of heavy metals in sediments and benthic species in relation to nuclear power plant operation

Heavy metals in the estuarine environment can be toxic to fish and shellfish early life history stages and concentrations build up to levels of concern in marketable shellfish. The present survey was begun just before startup in 1974 of the 1900 megawatt Calvert Cliffs Nuclear Power Plant on the Chesapeake Bay in order to assess and understand factors relating to heavy metal accumulation in estuarine biota. Oysters were collected in large numbers at test and reference sites in June 1974 to 77 and individually analyzed for copper and zinc. Oyster copper and zinc concentrations were correlated with salinity read at time of collection. The relationship of oyster age to metal concentration was examined with two sets of oysters of known age and genetic origin (laboratory spawned). Copper sorption by typical mid Bay sediments, and field studies on cadmium concentrations in sediments were examined.

Phelps, H. L.↗
NASA NTRS1985

Hydride absorption refrigerator system for ten Kelvin and below

A very long-life, lightweight and efficient hydride absorption refrigerator system was built to operate at ten Kelvin and below. The system consists of four basic stages of refrigeration. The first stage is accomplished by an active refrigeration system. The second stage is operated by a hydride absorption system, wherein a heated hydride powder drives off high pressure hydrogen through a Joule-Thomson/heat exchanger expansion loop such that the hydrogen is partially liquefied. In the third stage, the vapor pressure over the collected liquid hydrogen is lowered by absorbing the hydrogen vapor onto a different low pressure, worn hydride. With a 1.7 torr partial pressure of hydrogen gas in the hydride, liquid hydrogen is solidified and sublimes at 10 K. Long-life adiabatic demagnetization refrigerators, helium desorption, or helium diaphragm compressors are used to cool to 4 K or below. It is shown that the hydride concepts provide an extremely efficient means of refrigeration to 10 K, and that an entire sorption refrigeration process can be accomplished solely by using low grade heat energy at about 150 C.

Jones, J. A.↗
NASA NTRS1985

Crystalline-silicon reliability lessons for thin-film modules

The reliability of crystalline silicon modules has been brought to a high level with lifetimes approaching 20 years, and excellent industry credibility and user satisfaction. The transition from crystalline modules to thin film modules is comparable to the transition from discrete transistors to integrated circuits. New cell materials and monolithic structures will require new device processing techniques, but the package function and design will evolve to a lesser extent. Although there will be new encapsulants optimized to take advantage of the mechanical flexibility and low temperature processing features of thin films, the reliability and life degradation stresses and mechanisms will remain mostly unchanged. Key reliability technologies in common between crystalline and thin film modules include hot spot heating, galvanic and electrochemical corrosion, hail impact stresses, glass breakage, mechanical fatigue, photothermal degradation of encapsulants, operating temperature, moisture sorption, circuit design strategies, product safety issues, and the process required to achieve a reliable product from a laboratory prototype.

Ross, R. G., Jr.↗