Process for preparing polyimide adhesives

High bonding strengths are obtained for metals and fiber-reinforced organic resin composites with no significant loss in thermo-oxidative stability of the adhesive resin.

Progar, D. J.↗

Development of autoclavable polyimides

A poly(Diels-Alder) (PDA) resin approach was investigated as a means to achieve autoclavability of high temperature resistant resin/fiber composites under mild fabrication procedures. Low void content Type A-S graphite reinforced composites were autoclave fabricated from a PDA resin/fiber prepared from an acetone:methanol:dioxane varnish. Autoclave conditions were 477K (400F) and 0.7 MN/sq m (100 psi) for up to two hours duration. After postcure at temperatures up to 589K (600F), the composites demonstrated high initial mechanical properties at temperatures up to 561K (550F). The results from isothermal aging studies in air for 1000 hours indicated potential for long-term ( 1000 hours) use at 533K (500F) and shorter-term (up to 1000 hours) at 561K (550F).

Orell, M. K.↗

Weld bonding of titanium with polyimide adhesives

A conductive adhesive primer and a capillary flow adhesive were developed for weld bonding titanium alloy joints. Both formulations contained ingredients considered to be non-carcinogenic. Lap-shear joint test specimens and stringer-stiffened panels were weld bonded using a capillary flow process to apply the adhesive. Static property information was generated for weld bonded joints over the temperature range of 219K (-65 F) to 561K (550 F). The capillary flow process was demonstrated to produce weld bonded joints of equal strength to the weld through weld bonding process developed previously.

Vaughan, R. W.↗

Polyimide adhesives for weld-bonding titanium

Two weld bonding processes were developed for joining titanium alloy; one process utilizes a weld-through technique and the other a capillary-flow technique. The adhesive used for the weld-through process is similar to the P4/A5F system and a new adhesive system, CP/CFA, was used in the capillary-flow process. Static property information was generated for weld-bonded joints over the temperature range of 219K (-65 F) to 561K (550 F) and fatigue strength information was generated at room temperature. Significant improvement in fatigue strength was demonstrated for weld-bonded joints over spot-welded joints. A demonstration was made of the applicability of weld-bonding for fabricating stringer stiffened skin panels.

Vaughan, R. W.↗

Effects of graphite fiber stability on the properties of PMR polyimide composites

The effect of the stability of graphite fibers on composite properties after exposure in air at 600 F was investigated. Composites were fabricated from PMR-15 and PMR-2 monomer solutions, using HTS-2 and Celion 6000 graphite fibers as the reinforcement. The effect of long-term exposure in air at 600 F on composite weight loss and mechanical properties was determined. These composites exhibited a significantly increased lifetime at that temperature compared to composites fabricated from HTS fiber sold prior to 1975. The effect of the PMR-15 and PMR-II resin compositions on long-term composite performance at 600 F is also discussed.

Delvigs, P.↗

Effects of graphite fiber stability on the properties of PMR polyimide composites

Studies were performed to investigate the effect of the stability of graphite fibers on composite properties after exposure in air at 600 F. Composites were fabricated from PMR-15 and PMR-II monomer solutions, using HTS-2 and Celion 6000 graphite fibers as the reinforcement. The effect of long-term exposure in air at 600 F on composite weight loss and mechanical properties was determined. These composites exhibited a significantly increased lifetime at 600 F compared to composites fabricated from HTS fiber sold prior to 1975. The effect of the PMR-15 and PMR-II resin compositions on long-term composite performance at 600 F is also discussed.

Delvigs, P.↗

Quality control developments for graphite/PMR15 polyimide composites materials

The problem of lot-to-lot and within-lot variability of graphite/PMR-15 prepreg was investigated. The PMR-15 chemical characterization data were evaluated along with the processing conditions controlling the manufacture of PMR-15 resin and monomers. Manufacturing procedures were selected to yield a consistently reproducible graphite prepreg that could be processed into acceptable structural elements.

Sheppard, C. H.↗

Development of LaRC 160/NR150B2 polyimide graphite hybrid composites

A method for co-curing NR150B2 and LaRC 160 prepregs into hybrid composites was developed. The processing characteristics and the properties of the hybrid composites were compared with those of laminates fabricated from the individual component prepregs. Resin forms were selected and optimized and a new NR150 formulation was investigated. The new formulation greatly facilitated the processing and the performance of this system. Quality control techniques were evaluated and developed, high quality laminates were fabricated from both individual resin systems, and hybrid laminates were successfully co-cured. Optimum hybrid forms were investigated and several novel approaches were explored. An optimum hybrid system was developed that utilizes a LaRC curing schedule but shows no degradation of mechanical properties after aging 500 hr in air at 260 C.

Maximovich, M. G.↗

Environmental effects on graphite fiber reinforced PMR-15 polyimide

Studies were conducted to establish the effects of thermo-oxidative and hydrothermal exposure on the mechanical properties of T300 graphite fabric reinforced PMR-15 composites. The effects of hydrothermal exposure on the mechanical properties of HTS-2 continuous graphite fiber composites were also investigated. The thermo-oxidative stability characteristics of T300 fabric and T300 fabric/PMR-15 composites were determined. Flexural strengths of specimens were determined. The useful lifetime of T300 fabric/PMR-15 composites in air at 316 C was found to be about 100 hours. The useful lifetimes in air at 228 and 260 C were determined to be 500 and 1000 hours, respectively. Absorbed moisture was found to reduce the elevated temperature properties of both the T300 fabricate and HTS-2 continuous fiber composites. The moisture effect was found to be reversible.

Serafini, T. T.↗

Influence of excess diamine on properties of PMR polyimide resins and composites

This preliminary study explores the influence of 1-10 percent molar excess MDA on the molecular weight distribution and rheological properties of an imidized PMR system. Molecular weight distribution is characterized by gel permeation chromatography of the imidized molding compound; shear viscosity is related to changes in average molecular weight. The thermo-oxidative stability at 600 F glass transition temperature, flexural and interlaminar shear properties of PMR polyimide/Celion 6000 graphite fiber composites are compared as a function of the percent excess MDA in the monomer reactant mixture.

Hurwitz, F. I.↗