Energetics of Ag Adsorption on and Adhesion to Rutile TiO 2 (100) Studied by Microcalorimetry
The adsorption and adhesion energies of vapor-deposited Ag on rutile TiO 2 (100) films have been measured using single crystal adsorption calorimetry (SCAC) and He + low energy ion scattering spectroscopy (LEIS). Ag grows as three-dimensional (3D) nanoparticles at 300 and 100 K. The saturation particle density is 8 × 10 16 particles/m 2 at 300 K and 2.5 × 10 17 particles/m 2 at 100 K. The differential heat of adsorption starts low, increases with Ag coverage, and finally approaches the sublimation enthalpy of Ag at both 300 and 100 K. At 300 K, the differential heat of adsorption starts from 208 kJ/mol and rises rapidly to 265 kJ/mol by 1 ML. At 100 K, Ag grows nanoparticles with smaller particle size on the terraces, while at 300 K, the Ag nanoparticles have bigger particle size and grow on step edges with stronger binding strength to the nanoparticles. Thus, the heat of Ag adsorption at 100 K starts at 141 kJ/mol (near the monomer size limit on terrace sites) and remains lower than that at 300 K until 1.5 ML. Here, the adhesion energy of Ag(solid) to rutile TiO 2 (100) is found to be large (~2.44 J/m 2 ), supporting a trend of decreasing adhesion energy with the enthalpy of oxide reduction.