SEARCH · Engineering Papers

Results for “crack damage”

Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

SourceResearch connectionFrom yearThrough year

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

At least 721 records · Page 40

All sources NASA NTRS DOE OSTI

NASA NTRS2011

Surrogate Modeling of High-Fidelity Fracture Simulations for Real-Time Residual Strength Predictions

A surrogate model methodology is described for predicting, during flight, the residual strength of aircraft structures that sustain discrete-source damage. Starting with design of experiment, an artificial neural network is developed that takes as input discrete-source damage parameters and outputs a prediction of the structural residual strength. Target residual strength values used to train the artificial neural network are derived from 3D finite element-based fracture simulations. Two ductile fracture simulations are presented to show that crack growth and residual strength are determined more accurately in discrete-source damage cases by using an elastic-plastic fracture framework rather than a linear-elastic fracture mechanics-based method. Improving accuracy of the residual strength training data does, in turn, improve accuracy of the surrogate model. When combined, the surrogate model methodology and high fidelity fracture simulation framework provide useful tools for adaptive flight technology.

Spear, Ashley D.↗

DOE OSTI2023

Hydrologic Impacts of a Strike-Slip Fault Zone: Insights from Joint 3D Body-Wave Tomography of Rock Valley

The Rock Valley fault zone (RVFZ), an intraplate strike-slip fault zone in the southern Nevada National Security Site (NNSS), hosted a series of very shallow (<3 km) earthquakes in 1993. The RVFZ may also have hydrological significance within the NNSS, potentially playing a role in regional groundwater flow, but there is a lack of local hydrological data. In the Spring of 2021, we collected active-source accelerated weight drop seismic data over part of the RVFZ to better characterize the shallow subsurface. Here, we manually picked ~17,000 P-wave travel times and over 14,000 S-wave travel times, which were inverted for P-wave velocity (V P ), S-wave velocity (V S ), and V P /V S ratio in a 3D joint tomographic inversion scheme. Seismic velocities are imaged as deep as ~700 m in areas and generally align with geologic and structural expectations. V P and V S are relatively reduced near mapped and inferred faults, with the most prominent lower V P and V S zone around the densest collection of faults. We image V P /V S ratios ranging from ~1.5 to ~2.4, the extremes of which occur at a depth of ~100 m and are juxtaposed across a fault. One possible interpretation of the imaged seismic velocities is enhanced fault damage near the densest collection of faults with relatively higher porosity and/or crack density at ~100 m depth, with patches of semiperched groundwater present in the sedimentary rock in higher V P /V S areas and drier rock in lower V P /V S areas. A relatively higher V P /V S area beneath the densest faults persists at depth, which suggests percolation of groundwater via the fault damage zone to the regionally connected lower carbonate aquifer. Potentially, the presence and movement of groundwater may have played a role in the 1993 earthquake aftershocks.

58 GEOSCIENCES↗

NASA NTRS1996

Structural Durability of Damaged Metallic Panel Repaired with Composite Patches

Structural durability/damage tolerance characteristics of an aluminum tension specimen possessing a short crack and repaired by applying a fiber composite surface patch is investigated via computational simulation. The composite patch is made of graphite/epoxy plies with various layups. An integrated computer code that accounts for all possible failure modes is used for the simulation of combined fiber-composite/aluminum structural degradation under loading. Damage initiation, growth, accumulation, and propagation to structural fracture are included in the simulation. Results show the structural degradation stages due to tensile loading and illustrate the use of computational simulation for the investigation of a composite patch repaired cracked metallic panel.

Chamis, Christos C.↗

NASA NTRS1997

Structural Durability of Damaged Metallic Panel Repaired with Composite Patches

Structural durability/damage tolerance characteristics of an aluminum tension specimen possessing a short crack and repaired by applying a fiber composite surface patch is investigated via computational simulation. The composite patch is made of graphite/epoxy plies with various layups. An integrated computer code that accounts for all possible failure modes is utilized for the simulation of combined fiber-composite/aluminum structural degradation under loading. Damage initiation, growth, accumulation, and propagation to structural fracture are included in the simulation. Results show the structural degradation stages due to tensile loading and illustrate the use of computational simulation for the investigation of a composite patch repaired cracked metallic panel.

Minnetyan, Levon↗

NASA NTRS2003

Fracture Evaluation of In-Situ Sensors for High Temperature Applications

The feasibility of fabricating an in-situ crack sensor for real-time detection of surface cracks propagating in engine components was evaluated using a computational fracture mechanics model. The in-situ sensor system would be required to: (1) Be capable of sustaining normal function in a severe environment; (2) Transmit a signal if a detected crack in the component was above a predetermined length, but below a critical length that would lead to failure; (3) Act neutrally upon the overall performance of the engine system and not interfere with the engine maintenance operations. In this work, fracture mechanics methodologies are used to identify the requirements for an in-situ sensor system that could withstand the engine operating environment, foreign object damage, and minimally degrade engine performance. A computational fracture mechanics model was developed to evaluate the feasibility of fabricating an in-situ crack sensor for real-time damage propagation detection in engine components.

Forth, Scott C.↗

NASA NTRS2002

Failure Analysis of a Helicopter External Fuel-Tank Pylon

An eight-inch-long (0.2 m) crack was found in an external fuel-tank pylon of a U.S. Coast Guard HH-60 helicopter. The damaged pylon was removed from service and destructively examined at NASA Langley Research Center (LaRC) to determine the cause of the crack. Results of the analysis revealed that crack initiation occurred at corrosion pits in a fastener hole and crack propagation was a result of cyclic loading.

Newman, John A.↗

DOE OSTI2023

A phase-field model for hydraulic fracture nucleation and propagation in porous media

Many geo-engineering applications, for example, enhanced geothermal systems, rely on hydraulic fracturing to enhance the permeability of natural formations and allow for sufficient fluid circulation. Over the past few decades, the phase-field method has grown in popularity as a valid approach to modeling hydraulic fracturing because of the ease of handling complex fracture propagation geometries. However, existing phase-field methods cannot appropriately capture nucleation of hydraulic fractures because their formulations are solely energy-based and do not explicitly take into account the strength of the material. Thus, in this work, we propose a novel phase-field formulation for hydraulic fracturing with the main goal of modeling fracture nucleation in porous media, for example, rocks. Built on the variational formulation of previous phase-field methods, the proposed model incorporates the material strength envelope for hydraulic fracture nucleation through two important steps: (i) an external driving force term, included in the damage evolution equation, that accounts for the material strength; (ii) a properly designed damage function that defines the fluid pressure contribution on the crack driving force. In conclusion, the comparison of numerical results for two-dimensional test cases with existing analytical solutions demonstrates that the proposed phase-field model can accurately model both nucleation and propagation of hydraulic fractures. Additionally, we present the simulation of hydraulic fracturing in a three-dimensional domain with various stress conditions to demonstrate the applicability of the method to realistic scenarios.

15 GEOTHERMAL ENERGY↗

DOE OSTI2023

Irradiation-assisted cracking of SA508-304L weldments with 308L groove filler and 309L butter in hot water immersion constant rate extension tests

Low alloy SA508 bainitic steel is often welded to 300 series austenitic stainless steel in nuclear power plants. These dissimilar metal weldments use 309L butter applied to the low alloy steel and 308L groove filler material to join the 309L to austenite. High alloy steels (such as the 308L and 309L material used here) have been identified as having greater susceptibility to irradiation-assisted stress corrosion cracking (IASCC). Evidence is presented here of cracking under tensile loads in 309L weldment butter in LWR hydrothermal conditions that correlates irradiation induced changes at δ ferrite–γ austenite phase boundaries and γ–γ grain boundaries; specifically intergranular Cr 23 C 6 precipitates. Cracking is not observed in irradiated 308L groove filler under the same conditions. Both the 309L butter and 308L filler material have a duplex or mixed δ–γ phase microstructure due to solidification during the welding procedure. We have performed constant extension rate autoclave immersion tests in BWR normal water chemistry hot water (288 °C, 10 MPa, 2000 wt. ppb dissolved oxygen, <100 nS/cm conductivity, neutral pH) of proton irradiated (2 MeV, approximately 3 displacements per atom at a depth of 10 μm) tensile specimens. Proton irradiation to the dpa levels used here induced Cr 23 C 6 carbide precipitation at γ–γ grain boundaries and δ–γ phase boundaries in the 309L butter but not the 308L filler. Cracking was observed in the proton-irradiated volume of 309L at these interfaces in the vicinity of the Cr 23 C 6 precipitates. We hypothesis the SA508 is the source of carbon in the 309L butter. Cr depletion at γ–γ grain boundaries was also observed and may also be a root cause of cracking. Furthermore, the 309L butter is under significant tensile residual stress in the weldment that adds to applied tensile loads and this too may be a contributing factor.

309L weld butter↗

DOE OSTI2023

Machine Learning for Processing Ultrasonic Data from Long-Term Monitoring of Concrete with Alkali-Silica Reaction (ASR)

The alkali–silica reaction (ASR) is a phenomenon that leads to material degradation in concrete, resulting in the formation of microcracks and cracks. This deterioration causes a loss of mechanical properties, concrete damage, and even corrosion. To address this issue, ultrasonic nondestructive evaluation can be employed as a technique for long-term monitoring of ASR development and condition assessment of concrete subjected to ASR. However, traditional approaches typically utilize only a few wave parameters, such as wave velocity or amplitude, to characterize ASR-induced concrete damage while disregarding the majority of information present in the ultrasonic signals.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Testing Various Cement Formulations under Temperature Cycles and Drying Shrinkage for Low-Temperature Geothermal Wells

Low-enthalpy geothermal wells are considered a sustainable energy source, particularly for district heating in the Netherlands. The cement sheath in these wells experiences thermal cycles. The stability of cement recipes under such conditions is not well understood. In this work, thermal cycling experiments for intermediate- and low-temperature geothermal well cements have been conducted. The samples were cured either under ambient conditions or under realistic pressure and temperature for 7 days. The samples did not show any signs of failure after performing 10 cycles of thermal treatment between 100 °C and 18 °C. We also tested cement formulations under drying conditions. Drying shrinkage is caused by a reduction in the water content of cement, which leads to capillary forces that can damage cement. Such circumstances lead to tensile stresses causing radial cracks. Most samples exhibited cracks under low humidity conditions (drying). Fiber reinforcement, especially using short PP fibers, improved the cement’s resilience to temperature and humidity changes. Such additives can improve the longevity of cement sheaths in geothermal wells.

36 MATERIALS SCIENCE↗

NASA NTRS1979

The erosion/corrosion of small superalloy turbine rotors operating in the effluent of a PFB coal combustor

The operation of a turbine in the effluent of a pressurized fluidized bed (PFB) coal combustor presents serious materials problems. Synergistic erosion/corrosion and deposition/corrosion interactions may favor the growth of erosion-resistant oxides on blade surfaces, but brittle cracking of these oxides may be an important source of damage along heavy particle paths. Integrally cast alloy 713LC and IN792 + Hf superalloy turbine rotors in a single-stage turbine with 6% partial admittance have been operated in the effluent of a PFB coal combustor for up to 164 hr. The rotor erosion pattern exhibits heavy particle separation with severe erosion at the leading edge, pressure side center, and suction side trailing edge at the tip. The erosion distribution pattern gives a spectrum of erosion/oxidation/deposition as a function of blade position. The data suggest that preferential degradation paths may exist even under the targeted lower loadings (less than 20 ppm).

Zellars, G. R.↗

NASA NTRS1985

On the use of crack-tip-opening displacement to predict the fracture strength of notched graphite/epoxy laminates

Using the center-cracked tension specimen geometry, the fracture strength of notched graphite/epoxy laminates is measured experimentally. Four replicate tests are conducted for a variety of laminate-stacking sequences, thicknesses, and notch lengths. Extensive notch-tip damage prior to fracture is characteristic of most laminates. The values of critical crack-tip-opening displacement (CTOD) are calculated from values of crack-opening displacement measured at the notch center line at failure and are found to be independent of notch size for the laminates studied. A Dugdale (1950) model is used along with the estimated CTOD to predict notched laminate strength.

Harris, C. E.↗

NASA NTRS1986

Further observations of SCC in alpha-beta brass Considerations regarding the appearance of crack arrest markings during SCC

A series of constant displacement and constant extension rate stress corrosion cracking (SCC) tests was performed on an alpha-beta brass alloy in 1 N Na2SO4 solutions. The chosen mechanical and electrochemical conditions resulted in predominantly transgranular, cleavage-like failure at high (about 8 to 50 microns/s) average crack propagation rates. Crack arrest markings were observed on selected transgranular facets, which almost exclusively bordered regions of ductile overload failure. It is proposed that the observed crack velocities and the specific nature of the arrest mark appearance are most consistent with a cracking mechanism involving adsorption or some other interaction with a damaging environmental species.

Hintz, M. B.↗

NASA NTRS1988

Automated design of composite plates for improved damage tolerance

The present effort toward design automation for local damage tolerance in composite plates under compressive loading, simulating the local damage condition by a central, through-the-thickness crack-like notch, uses a micromechanical failure model for the fiber kink formation in the load-carrying layers. This accounts for the combined effects of compressive and shearing stresses around the notch. For stiffened plates, minimum-weight configurations are obtained where the crack is isolated in low stiffness plate regions.

Gurdal, Zafer↗

NASA NTRS1992

Linear elastic fracture mechanics primer

This primer is intended to remove the blackbox perception of fracture mechanics computer software by structural engineers. The fundamental concepts of linear elastic fracture mechanics are presented with emphasis on the practical application of fracture mechanics to real problems. Numerous rules of thumb are provided. Recommended texts for additional reading, and a discussion of the significance of fracture mechanics in structural design are given. Griffith's criterion for crack extension, Irwin's elastic stress field near the crack tip, and the influence of small-scale plasticity are discussed. Common stress intensities factor solutions and methods for determining them are included. Fracture toughness and subcritical crack growth are discussed. The application of fracture mechanics to damage tolerance and fracture control is discussed. Several example problems and a practice set of problems are given.

Wilson, Christopher D.↗

NASA NTRS1993

Effects of thermal and mechanical fatigue on the flexural strength of G40-600/PMR-15 cross-ply laminates

The effects of thermal and mechanical fatigue on the flexural strength of G40-600/PMR-15 cross-ply laminates with ply orientation of (0(2),90(2))2S and (90(2),0(2))2S are examined. The relative importance of shear and tensile stresses is examined by varying the span-to-depth ratios of flexural test specimens from 8 to 45. Acoustic emission signals are measured during the flexural tests in order to monitor the initiation and growth of damage. Optical microscopy is used to examine specimens for resin cracking, delamination, and fiber breaks after testing. Transverse matrix cracks and delaminations occur in all specimens, regardless of ply orientation, span-to-depth ratio, or previous exposure of specimens to thermal and mechanical fatigue. A small amount of fiber tensile fracture occurs in the outer 0 deg ply of specimens with high span-to-depth ratios. Because of the complex failure modes, the flexural test results represent the 'apparent' strengths rather than the true flexural or shear strengths for these cross-ply laminates. Thermal cycling of specimens prior to flexural testing does not reduce the apparent flexural strength or change the mode of failure. However, fewer acoustic events are recorded at all strains during flexural testing of specimens exposed to prior thermal cycling. High temperature thermal cycling (32 to 260 C, 100 cycles) causes a greater reduction in acoustic events than low temperature thermal cycling (-85 to +85 C, 500 cycles). Mechanical cycling (0 to 50 percent of the flexural strength, 100 cycles) has a similar effect, except that acoustic events are reduced only at strains less than the maximum strain applied during flexural fatigue.

Roberts, Gary D.↗

NASA NTRS1996

Improved Damage Resistant Composite Materials Incorporating Shape Memory Alloys

Metallic shape memory alloys (SMA) such as nitinol have unique shape recovery behavior and mechanical properties associated with a material phase change that have been used in a variety of sensing and actuation applications. Recent studies have shown that integrating nitinol-SMA actuators into composite materials increases the composite material's functionality. Hybrid composites of conventional graphite/epoxy or glass/epoxy and nitinol-SMA elements can perform functions in applications where monolithic composites perform inadequately. One such application is the use of hybrid composites to function both in load bearing and armor capacities. While monolithic composites with high strength-to-weight ratios function efficiently as loadbearing structures, because of their brittle nature, impact loading can cause significant catastrophic damage. Initial composite failure modes such as delamination and matrix cracking dissipate some impact energy, but when stress exceeds the composite's ultimate strength, fiber fracture and material perforation become dominant. One of the few methods that has been developed to reduce material perforation is hybridizing polymer matrix composites with tough kevlar or high modulus polyethynylene plies. The tough fibers increase the impact resistance and the stiffer and stronger graphite fibers carry the majority of the load. Similarly, by adding nitinol-SMA elements that absorb impact energy through the stress-induced martensitic phase transformation, the composites' impact perforation resistance can be greatly enhanced. The results of drop-weight and high velocity gas-gun impact testing of various composite materials will be presented. The results demonstrate that hybridizing composites with nitinol-SMA elements significantly increases perforation resistance compared to other traditional toughening elements. Inspection of the composite specimens at various stages of perforation by optical microscope illustrates the mechanisms by which perforation is initiated. Results suggest that the out-of-plane transverse shear properties of the composite and nitinol elements have a significant effect on the perforation resistance. Applications that can utilize the hybrid composites effectively will also be presented with the experimental studies.

Paine, Jeffrey S. N.↗

NASA NTRS1999

Effects of Fiber/Matrix Interface and its Composition on Mechanical Properties of Hi-Nicalon/Celsian Composites

To evaluate the effects of fiber coatings on composite mechanical properties. unidirectional celsian matrix composites reinforced with uncoated Hi-Nicalon fibers and those precoated with a dual BN/SiC layer in two separate batches (batch 1 and batch 2) were tested in three-point flexure. The uncoated-fiber reinforced composites showed catastrophic failure with strength of 210+/-35 MPa and a flat fracture surface. In contrast, composites reinforced with coated fibers exhibited graceful failure with extensive fiber pullout and showed significantly higher ultimate strengths, 904 and 759 MPa for the batch 1 and 2 coatings. respectively. Fiber push-in tests and microscopic examination indicated no chemical reaction at the uncoated or coated fiber-matrix interfaces that might be responsible for fiber strength degradation. Instead, the low strength of composite with uncoated fibers was due to degradation of the fiber strength from mechanical damage during composite processing. Despite identical processing, the first matrix cracking stresses (Sigma(sub mc)) of the composites reinforced with fibers coated in batch 1 and batch 2 were quite different, 436 and 122 MPa, respectively. The large difference in Sigma(sub mc) of the coated-fiber composites was attributed to differences in fiber sliding stresses (Tau(sub friction)), 121.2+/-48.7 and 10.4+/-3.1 MPa, respectively. for the two composites as determined by the fiber push-in method. Such a large difference in Tau(sub friction). for the two composites was found to be due to the difference in the compositions of the interface coatings. Scanning Auger microprobe analysis revealed the presence of carbon layers between the fiber and BN. and also between the BN and SiC coatings in the composite showing lower Tau(sub friction). This resulted in lower Sigma(sub mc) in agreement with the ACK theory. The ultimate strengths of the two composites depended mainly on the fiber volume fraction and were not significantly effected by Tau(sub friction) values, as expected. The poor reproducibility of the fiber coating composition between the two batches was judged to be the primary source of the large differences in performance of the two composites.

Bansal, Narottam P.↗