An electrochromic device comprising a counter electrode layer comprised of lithium metal oxide which provides a high transmission in the fully intercalated state and which is capable of long-term stability, is disclosed. Methods of making an electrochromic device comprising such a counter electrode are also disclosed.
Composite silicon based materials are described that are effective active materials for lithium ion batteries. The composite materials comprise processed, e.g., high energy mechanically milled, silicon suboxide and graphitic carbon in which at least a portion of the graphitic carbon is exfoliated into graphene sheets. The composite materials have a relatively large surface area, a high specific capacity against lithium, and good cycling with lithium metal oxide cathode materials. The composite materials can be effectively formed with a two-step high energy mechanical milling process. In the first milling process, silicon suboxide can be milled to form processed silicon suboxide, which may or may not exhibit crystalline silicon x-ray diffraction. In the second milling step, the processed silicon suboxide is milled with graphitic carbon. Composite materials with a high specific capacity and good cycling can be obtained in particular with balancing of the processing conditions.
Solid tritium breeder materials must first and foremost have sufficiently high concentrations of lithium to enable a plant-scale tritium breeding ratio greater than 1:1. However, in addition to lithium content, such breeder materials must also meet other performance metrics including high tritium release rates, thermal conductivities, and irradiation damage tolerance. Perhaps most importantly, tritium breeders must maintain their mechanical integrity during reactor operation so as to avoid degradation which can jeopardize the functionality of the tritium breeder blanket module, which in most designs takes the form of a pebble bed geometry. Unfortunately, the mechanical robustness of most lithium-bearing ceramics under investigation for fusion applications is often inversely related to the lithium atom density. For example, a material such as lithium oxide (Li2O), which has one of the highest lithium atom densities, has a much lower mechanical splitting strength than lithium metatitanate (Li2TiO3), though Li2TiO3 has less than half the lithium atom density of Li2O. This work seeks to provide an alternative to monolithic ceramic tritium breeders, in the form of metal-reinforced composite tritium breeders. Specifically, composite tritium breeders have been synthesized combining Li2O with various ferrous metal reinforcements via electric field assisted sintering (EFAS), also known as spark plasma sintering (SPS). As the metal reinforcement content is increased, metallic networks are observed, via electron microscopy and X-ray computed tomography, to form throughout the composite material. Through destructive mechanical testing, even dilute metal reinforcement loading enables drastic mechanical strength improvements over pure Li2O while higher loadings give rise to quasi-ductile behavior and higher ultimate strengths than Li2TiO3 – while still maintaining a higher density of lithium atoms than Li2TiO3 and many other breeder candidates. In addition to microstructural characterization and mechanical testing, thermal property measurements and hydrogen permeability testing are underway to further assess the suitability of such composites for fusion reactor applications.
Despite the high energy density of lithium-rich layered-oxide electrodes, their real-world implementation in batteries is hindered by the substantial voltage decay on cycling. This voltage decay is widely accepted to mainly originate from progressive structural rearrangements involving irreversible transition-metal migration. As prevention of this spontaneous cation migration has proven difficult, a paradigm shift toward management of its reversibility is needed. Herein, we demonstrate that the reversibility of the cation migration of lithium-rich nickel manganese oxides can be remarkably improved by altering the oxygen stacking sequences in the layered structure and thereby dramatically reducing the voltage decay. The preeminent intra-cycle reversibility of the cation migration is experimentally visualized, and first-principles calculations reveal that an O2-type structure restricts the movements of transition metals within the Li layer, which effectively streamlines the returning migration path of the transition metals. Furthermore, we propose that the enhanced reversibility mitigates the asymmetry of the anionic redox in conventional lithium-rich electrodes, promoting the high-potential anionic reduction, thereby reducing the subsequent voltage hysteresis. Our findings demonstrate that regulating the reversibility of the cation migration is a practical strategy to reduce voltage decay and hysteresis in lithium-rich layered materials.
Lithium- and manganese-rich oxides are of interest as lithium-ion battery cathode materials as Mn is earth abundant, low cost, and can deliver high capacity. Herein, a high entropy strategy was used to prepare Mn rich high entropy oxide (HEO) materials by including four additional metals (Ni, Co, Fe and Al) in the compositions using a mild co-precipitation method. Two HEOs (Li x Ni 0.1 Mn 0.6 Co 0.1 Al 0.1 Fe 0.1 O y , where x = 1.5 for HEO-L and x = 0.5 for HEO-H) with layered and spinel-layered hybrid structures were investigated where the morphology, elemental composition, structure, atomic level phase distribution, and electrochemistry were determined. The HEO-L samples involve a Li 2 TMO 3 layered structure with ~39% stacking faults. HEO-H is a hybrid structure comprised of 80 wt% spinel and 20 wt% LiMO 2 layered structure. The high entropy manganese-rich HEO-L showed higher capacity and 93% retention of the average voltage after 100 cycles while HEO-H showed higher capacity retention and near 100% average voltage retention. Finally, operando X-ray absorption spectroscopy revealed that the Ni, Co, and Mn are redox active in both materials while the Fe center remains at the Fe 3+ oxidation state throughout cycling, where the changes in the oxidation states for both materials during discharge were consistent with the delivered electrochemical capacity rationalizing the observed electrochemistry.
Nickel-rich layered lithium transition metal oxides (LiNi 1–x–y Co x Mn y O 2 and LiNi 1–x–y Co x Al y O 2 , x + y ≤ 0.2) are the most attractive cathode materials for the next generation lithium-ion batteries for automotive application. However, they suffer from structural/interfacial instability during repeated charge/discharge, resulting in severe performance degradation and serious safety concerns. Here we provide a comprehensive review about challenges and strategies to advance nickel-rich layered cathodes specifically for harsh (high-voltage, high-temperature, and fast charging) operations. Firstly, the degradation pathways of nickel-rich cathodes including surface/interface degradation, undesired cathode–electrolytes parasitic reactions, gas evolution, inter/intragranular cracking, and electrical/ionic isolation are discussed. Then, recent achievements in stabilizing the structure/interface of nickel-rich cathodes via surface coating, cation/anion doping, composition tailoring, morphology engineering, and electrolytes optimization are summarized. Moreover, challenges and strategies to improve the performance of Ni-rich cathodes at the electrode level are discussed. Outlook and perspectives to promote the practical application of nickel-rich layered cathodes toward automotive application are provided as well.
Rechargeable hydrogen gas batteries show promises for the integration of renewable yet intermittent solar and wind electricity into the grid energy storage. Here, we describe a rechargeable, high-rate, and long-life hydrogen gas battery that exploits a nanostructured lithium manganese oxide cathode and a hydrogen gas anode in an aqueous electrolyte. The proposed lithium manganese oxide-hydrogen battery shows a discharge potential of ~1.3 V, a remarkable rate of 50 C with Coulombic efficiency of ~99.8%, and a robust cycle life. A systematic electrochemical study demonstrates the significance of the electrocatalytic hydrogen gas anode and reveals the charge storage mechanism of the lithium manganese oxide-hydrogen battery. This work provides opportunities for the development of new rechargeable hydrogen batteries for the future grid-scale energy storage.
Studies have shown fluorinated electrolyte solvents can form desirable solid electrolyte interphase (SEI) in lithium metal batteries. In this study, we develop a detailed mechanistic understanding of two high performing electrolytes, Fluoroethylene Carbonate (FEC) and Difluoroethylene Carbonate (DFEC) to demonstrate minimal structural variations can lead to different decomposition products, and thereby the nature of the SEI. Using density functional theory (DFT) calculations, we find different initial bond-breaking mechanisms between FEC and DFEC. We develop free energy diagrams for the decomposition pathways including both electrochemical and chemical steps. Using the computational Li electrode, we identify the largest limiting potential of 1.77 V for FEC decomposition, associated with the formation of lithium fluoride, lithium oxide and FEC oligomers, and 1.53 V for DFEC, which correspond to the formation of polymerized vinylene carbonate and lithium fluoride. We suggest the formation of oligomers in the case of FEC instead of long polymers may lead to better SEI compactness. We also demonstrate the SEI components of FEC and DFEC are not stable on typical cathode voltage (3.87 V). This study presents a unified electrocatalytic perspective on SEI formation and decomposition.
A rational compositional design of high-nickel, cobalt-free layered oxide materials for high-energy and low-cost lithium-ion batteries would be expected to further propel the widespread adoption of electric vehicles (EVs), yet a composition with satisfactory electrochemical properties has yet to emerge. The previous work has demonstrated a promising LiNi 0.883 Mn 0.056 Al 0.061 O 2 (NMA-89) composition that outperformed high-nickel, cobalt-containing analogs in cycling stability and maintained a comparable rate performance and thermal stability. Herein, the capacity fading mechanism of NMA-89 in a pouch full cell with a 4.2 V cutoff is compared to that of its cobalt-containing analogs. The results reveal that particle cracking in LiNi 0.89 Mn 0.055 Co 0.055 O 2 (NMC-89) and LiNi 0.883 Co 0.053 Al 0.064 O 2 (NCA-89) leads to a loss of active material and an increase in surface area, thereby exacerbating structural and surface instabilities, accelerating impedance and polarization growth, and ultimately reducing their capacity retentions. LiNi 0.89 Mn 0.044 Co 0.042 Al 0.013 Mg 0.011 O 2 (NMCAM-89) and NMA-89 experience subdued surface reactions and maintain spherical particle structures, both of which are conducive to their capacity retentions during long-term cycling. Furthermore, this investigation offers insights into how specific transition-metal ions dictate the electrochemical stability of high-Ni layered oxide cathode materials, highlights the benefit of Mn-Al combination in NMA-89, and presents potential strategies to further enhance the performance of this novel class of cathode materials.
We observed enhanced net lithium deposition and lithium erosion, possibly dominated by physical sputtering of lithium by lithium-ion bombardment, on the outer plasma-facing surface in the Lithium Tokamak eXperiment-β (LTX-β) during liquid lithium wall operations. Silicon crystal samples with micro-trenches (30 μm × 30 μm × 2–7 μm deep) were exposed to hydrogen plasmas in LTX-β for solid and liquid lithium wall operations. Post-mortem analysis using X-ray photoelectron spectroscopy combined with argon ion sputtering measured net lithium deposition of 8.2 or 21 nm on the silicon crystal surface exposed for ~ 50 repeated shots of ~ 50-ms hydrogen plasma discharges during the liquid lithium wall operations at a vessel temperature of 475 K. Energy dispersive X-ray spectroscopy measured oxygen concentration patterns on the micro-trench floors, which were due to oxidized lithium deposition. Using the inhomogeneous oxygen concentration pattern caused by an ion-shadowing effect associated with the micro-trench’s geometric structure, we determined a polar incident ion direction of 68.4 ± 1.6° referenced to the surface normal direction. This observation was well-explained by the hypothesis that self-sputtering of Li was a dominant lithium erosion source in addition to lithium sputtering by hydrogen bombardment.
Efforts have been underway for some time at Argonne National Laboratory to design structurally integrated and stabilized lithium-manganese-nickel-oxide cathode materials. The goal has been to find a cobalt-free, high-capacity cathode for a Li-ion battery that is competitive, both cost- and energy-wise, with lithium-nickel-manganese-cobalt-oxide (NMC) and lithium-iron-phosphate (LFP) products. This brief synopsis highlights the remarkable alchemy of LiMn 0.5 Ni 0.5 O 2 resulting from its well-known, slightly disordered layered structure and the recently discovered lithiated spinel phase and totally disordered rock-salt configurations. All three arrangements share a structurally compatible cubic-close-packed oxygen array. The lithiated spinel and layered components provide an intersecting network of two- and three-dimensional channels that facilitate Li + -ion transport, while a minor amount of an extensively disordered rock-salt component likely serves to enhance the structural and electrochemical stability of the electrode. The synopsis also encompasses the historical development of lithiated spinel electrode materials and structurally integrated systems.
A common kinetic feature for oxide reduction chemical/electrochemical processes is oxygen transport via a porous metallic layer, which has been considered as a rate-determining step for reducing uranium oxides to metallic uranium. Accounting this kinetic behavior must involve the resolution of the moving reactive interface between shrinking oxide and expanding metal phases. This study presents a numerical model using smoothed particles hydrodynamics (SPH) to effectively deal with the evolution of the shrinking core reaction interface and oxygen transport via mass transfer of lithium oxide (Li 2 O) species in multiple mass transfer domains. We successfully validated the proposed model against a theoretical derivation for the oxide reduction process handling a shrinking oxide core with molten salt and metal ash medium on a simple planar geometry. Armed with successful validation results, the model examined a realistic reactant geometry to extend the arguments beyond the one-dimensional analyses, allowing the proposed model to apply to general application scenarios with multi-dimensional geometry. Here, this study demonstrated that the proposed model could simulate and evaluate an arbitrary reaction basket design without iterative experimental trials, which is prohibitive for a scaled high-temperature molten salt study in an inert environment. The construct potentially provides not only deep insights on multiphysics behaviors governing the process dynamics but also a robust framework for evaluating and screening candidate basket designs in the most cost-effective manner.
Global Nuclear Fuel – Americas LLC (GNF) has partnered with Argonne National Laboratory to demonstrate electroreduction of uranium oxides produced by deconversion of UF 6 to uranium metal through the Gateway for Accelerated Innovation in Nuclear (GAIN) program under the U.S. Department of Energy to accelerate the domestic production of metallic advanced reactor fuels. Electroreduction of uranium oxide was first demonstrated and patented by Argonne in the early 2000s as a technology to convert used oxide nuclear fuel from light water reactors to metal for further fuel reprocessing. More recently, electroreduction has been proposed as a front-end technology for metallization of uranium oxides produced by deconversion of UF 6 and for scrap recovery of oxide materials. During the electroreduction process, UO 2 powder is contained in a stainless-steel mesh basket with a cathode lead located in the center of the UO 2 bed. The basket is immersed in lithium chloride molten salt electrolyte containing 1 wt% lithium oxide along with a platinum anode and a nickel/nickel oxide (Ni/NiO) reference electrode. Current is applied to the cell between the cathode and anode to reduce the UO 2 to metallic uranium via a solid-state reduction reaction. Oxide ions released from the UO 2 during reduction are transported through the salt to the anode where oxygen gas is evolved. Once reduction is complete, the basket containing the metallicized uranium is removed from the salt and can be processed to remove the salt and consolidate the uranium into an ingot for use in metallic fuel fabrication. This project was performed to provide evidence of the electroreduction technology readiness level for metallization of UO 2 powder, identify and retire technical risks for industrialization of electroreduction, and accelerate the path to commercialization for metallic fast reactor fuel production. To that end, five electroreduction tests were performed with UO 2 provided by GNF and the resulting product was analyzed for the extent of conversion to metal and for impurity contents of the metal product to verify that electroreduction does not introduce impurities that would prevent use of the product in metallic fuel fabrication.
The use of lithium peroxide (Li2O2) as a cost-effective low-weight prelithiation cathode additive was successfully demonstrated. Through a series of studies on the chemical stability of Li2O2 and the activation process of Li2O2 on the cathode, we revealed that Li2O2 is more compatible with conventional electrolyte and cathode laminate slurry than lithium oxide. Due to the significantlysmaller size of commercial Li2O2, it can beused directly as a cathode additive. Moreover, the activation of Li2O2 on the cathode leads to the impedance growthof the cathode possibly resulting from the release of dioxygen andevacuation of Li2O2 inside the cathode. Withthe introduction of a new Li2O2 spread-coatingtechnique on the cathode, the capacity loss was suppressed. Si||NMCfull cells using Li2O2 spread-coated cathodedemonstrated a highly promising activation rate of Li2O2 and significantly enhanced specific capacity and cyclingstability compared to the uncoated full cells.
Efficient operation of battery energy storage systems requires that battery temperature remains within a specific range. Current techno-economic models neglect the parasitic loads heating and cooling operations have on these devices, assuming they operate at constant temperature. In this work, these effects are investigated considering the optimal sizing of battery energy storage systems when deployed in cold environments. Here, a peak shaving application is presented as a linear programming problem which is then formulated in the PYOMO optimization programming language. The building energy simulation software EnergyPlus is used to model the heating, ventilation, and air conditioning load of the battery energy storage system enclosure. Case studies are conducted for eight locations in the United States considering a nickel manganese cobalt oxide lithium ion battery type and whether the power conversion system is inside or outside the enclosure. The results show an increase of 42% to 300% in energy capacity size, 43% to 217% in power rating, and 43% to 296% increase in capital cost dependent on location. This analysis shows that the heating, ventilation, and air conditioning load can have a large impact on the optimal sizes and cost of a battery energy storage system and merit consideration in techno-economic studies.
Solid-state electrolytes (SSEs) are challenged by complex interfacial chemistry and poor ion transport through the interfaces they form with battery electrodes. Here, we investigate a class of SSE composed of micrometer-sized lithium oxide (Li 2 O) particles dispersed in a polymerizable 1,3-dioxolane (DOL) liquid. Ring-opening polymerization (ROP) of the DOL by Lewis acid salts inside a battery cell produces polymer-inorganic hybrid electrolytes with gradient properties on both the particle and battery cell length scales. These electrolytes sustain stable charge-discharge behavior in Li||NCM811 and anode-free Cu||NCM811 electrochemical cells. On the particle length scale, Li 2 O retards ROP, facilitating efficient ion transport in a fluid-like region near the particle surface. On battery cell length scales, gravity-assisted settling creates physical and electrochemical gradients in the hybrid electrolytes. By means of electrochemical and spectroscopic analyses, we find that Li 2 O particles participate in a reversible redox reaction that increases the effective CE in anode-free cells to values approaching 100%, enhancing battery cycle life.
Here, we advance electrode-omics to identify evolutionary bursts by which ethereal locally superconcentrated electrolytes (LSCEs) mitigate silicon anode degradation through its epochs of electrochemical and chemical reactions. Anode composites form initially at high potential from ethereal solvent and anion [bis(fluorosulfonyl)imide (FSI − )] redox. A first evolutionary burst at lower potential enriches composites with lithium alkoxides (LiO–R) and lithium oxide (Li 2 O) and depletes sulfur oxides (SO x ) species. As the cells are cycled, a second evolutionary burst takes place, where previously extinct SO x species reemerge concurrently with a loss of LiO–R and Li 2 O. This identifies reactions rooted in “SuFEx” chemistry, where oxoanionic LiO–R and Li 2 O species, electrochemically generated in the solid-electrolyte interphase, chemically react with FSI − in the electrolyte to form emergent species. This sequence of evolutionary bursts produces a mechanically resilient composite that reduces silicon anode cracking over hundreds of cycles, leading to overpotential increase of only ~0.01 volts after 200 cycles.