Electrochemical Reactions Under Reverse Bias Create Additional Mobile Ions That Enable Hole Tunneling in Metal Halide Perovskite Diodes
Gradual reverse-bias breakdown in metal-halide perovskite diodes and solar cells is thought to originate from hole tunneling through steep bands in an ionic depletion region near the electron-transport layer after positively charged iodine vacancies accumulate near the hole-transport layer (HTL). However, typical reported mobile-ion concentrations near 1 x 10^17 cm-3 are too small to quantitatively explain significant tunneling-current densities and (Zener) breakdown observed near -5 V. Here, we show that inferred mobile-ion concentrations increase by more than 100x, to over 1 x 10^18cm-3 , within just 3 min of reverse bias at -6.0 V in p-i-n perovskite diodes. We attribute this increase to iodide oxidation and coupled iodine vacancy creation that must be balanced by reduction reactions near the HTL. Sub-optimal HTL coverage leads to direct contact between the transparent conducting electrode and perovskite, facilitates reduction events, enables the creation of even larger inferred mobile-ion concentrations (~1 x 10^19cm-3 ), and leads to faster degradation under reverse bias. This explains previous work that showed increased breakdown voltages and improved reverse-bias stability by implementing thick, uniform HTLs.