Engineering Papers⌕ Search

SEARCH · Engineering Papers

Results for “Stress testing”

Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

At least 73 records · Page 4
All sourcesNASA NTRSDOE OSTI
NASA NTRS1982

An accelerated stress testing program for determining the reliability sensitivity of silicon solar cells to encapsulation and metallization systems

The use of accelerated testing methods in a program to determine the reliability attributes of terrestrial silicon solar cells is discussed. Different failure modes are to be expected when cells with and without encapsulation are subjected to accelerated testing and separate test schedules for each are described. Unencapsulated test cells having slight variations in metallization are used to illustrate how accelerated testing can highlight different diffusion related failure mechanisms. The usefulness of accelerated testing when applied to encapsulated cells is illustrated by results showing that moisture related degradation may be many times worse with some forms of encapsulation than with no encapsulation at all.

Lathrop, J. W.↗
NASA NTRS1983

Stress testing of digital flight-control system software

A technique for dynamically testing digital flight-control system software on a module-by-module basis is described. Each test module is repetitively executed faster than real-time with an exhaustive input sequence. Outputs of the test module are compared with outputs generated by an alternate, simpler implementation for the same input data. Discrepancies between the two sets of output indicate the possible presence of a software error. The results of an implementation of this technique in the Digital Flight-Control System Software Verification Laboratory are discussed.

Rajan, N.↗
NASA NTRS1985

Assessing corrosion problems in photovoltaic cells via electrochemical stress testing

A series of accelerated electrochemical experiments to study the degradation properties of polyvinylbutyral-encapsulated silicon solar cells has been carried out. The cells' electrical performance with silk screen-silver and nickel-solder contacts was evaluated. The degradation mechanism was shown to be electrochemical corrosion of the cell contacts; metallization elements migrate into the encapsulating material, which acts as an ionic conducting medium. The corrosion products form a conductive path which results in a gradual loss of the insulation characteristics of the encapsulant. The precipitation of corrosion products in the encapsulant also contributes to its discoloration which in turn leads to a reduction in its transparency and the consequent optical loss. Delamination of the encapsulating layers could be attributed to electrochemical gas evolution reactions. The usefulness of the testing technique in qualitatively establishing a reliability difference between metallizations and antireflection coating types is demonstrated.

Shalaby, H.↗
NASA NTRS2000

Failure Engineering Study and Accelerated Stress Test Results for the Mars Global Surveyor Spacecraft's Power Shunt Assemblies

An Engineering-of-Failure approach to designing and executing an accelerated product qualification test was performed to support a risk assessment of a "work-around" necessitated by an on-orbit failure of another piece of hardware on the Mars Global Surveyor spacecraft. The proposed work-around involved exceeding the previous qualification experience both in terms of extreme cold exposure level and in terms of demonstrated low cycle fatigue life for the power shunt assemblies. An analysis was performed to identify potential failure sites, modes and associated failure mechanisms consistent with the new use conditions. A test was then designed and executed which accelerated the failure mechanisms identified by analysis. Verification of the resulting failure mechanism concluded the effort.

Gibbel, Mark↗
NASA NTRS1999

Failure Engineering Study and Accelerated Stress Test Results for the Mars Global Surveyor Spacecraft's Power Shunt Assemblies

Due to a post launch failure of a part a new plan for the Mars Global Surveyor was developed. This new plan involved the addition of many deep thermal cycles to the Power Shunt Assemblies (PSA's). This new plan exceeds the previous acceptance cold level, and fatigue life on packaging design. This presentation reviews the experiments that were used to test the capabilities of the PSA to function in the new situation. It also reviews the analyses preformed to verify the most likely failure mechanism, and the likelihood that these failures would impact the new mission requirements.

Gibbel, Mark↗
NASA NTRS2010

Environmental Stress Testing of the Single Sample Cylinder: A Proven Consensus Standard for Internal Gas Analysis (IGA) or Residual Gas Analysis (RGA)

In August 2008, Schuessler Consulting was contracted by NASA GSFC in support of the NASA Electronic Parts and Packaging (NEPP) program to perform two separate studies on moisture laden air in a stainless steel cylinder that had been designed to become a consensus standard for Test Method 1018. This Test Method was originally released for hybrids under Mil. Std. 883 but was quickly utilized on other microelectronic devices under the auspice of Mil. Std. 750. The cylinder had subsequently been fabricated for the 750 community. It was back-filled with moist air and subsequently analyzed over a period of time under a previous NASA contract. It had been shown that moisture in the 4000 - 5000 ppm range could be analyzed rather precisely with a mass spectrometer, commonly referred to as a Residual Gas Analyzer (RGA). The scope of this study was to ascertain if the composition and precision varied as a function of thermal shock at sub-zero temperatures and whether there was consensus when the standard was submitted to other RGA units. It was demonstrated and published that the consensus standard would yield precise RGA data for moisture within +/- 1% when optimized for a given RGA unit. It has been subsequently shown in this study at Oneida Research Services, that sub-zero storage did not affect that precision when a well-defined protocol for the analysis was followed. The consensus standard was taken to a second facility for analysis where it was found that moisture adsorption on the transfer lines caused precision to drop to +/- 12%. The Single Sample Cylinder (SSC) is a one liter stainless steel cylinder with associated sampling valves and has considerable weight and volume. But this considerable size allows for approximately 300 gas samples of the same composition to be delivered to any RGA unit. Lastly, a smaller cylinder, approximately 75 cc, of a second consensus standard was fabricated and tested with a different mix of fixed gases where moisture was kept in the 100 ppm range. This second standard has the potential of providing 30 gaseous samples and can be readily shipped to any analytical facility that desires to generate comparison RGA data. A series of comparison residual gas analyses was performed at the Honeywell Federal Manufacturing & Technologies facility in the National Nuclear Facility Administration s plant in Kansas City to complete this project. It was shown that improvements in the precision of a given RGA unit can be done by controlling the cycle time for each analysis and increasing analysis temperatures to minimize moisture adsorption. It was also found that a "one time event" in the subzero storage of the large SSC did not effect the units ability to continuously supply precise samples of the same chemistry, however the "event" caused a permanent +8% shift in the reported value of the moisture content. Lastly, a set of SSC RGA results was plotted on a common graph with DSCC "correlation study" RGA data. The result demonstrates the ability of the SSC to remove many of the individual variances that single, individual samples introduce. The consensus standards are now in storage at Oneida Research Services, one of the DSCC certified houses that does RGA to Military Standards, where they await future studies. The analytical data and the operational parameters of the instruments used are provided in the following discussion. Limitations and suggested means for improvement of both precision and accuracy are provided.

Schuessler, Philipp WH↗
NASA NTRS1985

Critical assessment of precracked specimen configuration and experimental test variables for stress corrosion testing of 7075-T6 aluminum alloy plate

A research program was conducted to critically assess the effects of precracked specimen configuration, stress intensity solutions, compliance relationships and other experimental test variables for stress corrosion testing of 7075-T6 aluminum alloy plate. Modified compact and double beam wedge-loaded specimens were tested and analyzed to determine the threshold stress intensity factor and stress corrosion crack growth rate. Stress intensity solutions and experimentally determined compliance relationships were developed and compared with other solutions available in the literature. Crack growth data suggests that more effective crack length measurement techniques are necessary to better characterize stress corrosion crack growth. Final load determined by specimen reloading and by compliance did not correlate well, and was considered a major source of interlaboratory variability. Test duration must be determined systematically, accounting for crack length measurement resolution, time for crack arrest, and experimental interferences. This work was conducted as part of a round robin program sponsored by ASTM committees G1.06 and E24.04 to develop a standard test method for stress corrosion testing using precracked specimens.

Domack, M. S.↗
NASA NTRS2001

Accelerated Testing Methodology in Constant Stress-Rate Testing for Advanced Structural Ceramics: A Preloading Technique

Preloading technique was used as a means of an accelerated testing methodology in constant stress-rate ('dynamic fatigue') testing for two different brittle materials. The theory developed previously for fatigue strength as a function of preload was further verified through extensive constant stress-rate testing for glass-ceramic and CRT glass in room temperature distilled water. The preloading technique was also used in this study to identify the prevailing failure mechanisms at elevated temperatures, particularly at lower test rate in which a series of mechanisms would be associated simultaneously with material failure, resulting in significant strength increase or decrease. Two different advanced ceramics including SiC whisker-reinforced composite silicon nitride and 96 wt% alumina were used at elevated temperatures. It was found that the preloading technique can be used as an additional tool to pinpoint the dominant failure mechanism that is associated with such a phenomenon of considerable strength increase or decrease.

Choi, Sung R.↗
NASA NTRS2001

Accelerated Testing Methodology in Constant Stress-Rate Testing for Advanced Structural Ceramics: A Preloading Technique

Preloading technique was used as a means of an accelerated testing methodology in constant stress-rate (dynamic fatigue) testing for two different brittle materials. The theory developed previously for fatigue strength as a function of preload was further verified through extensive constant stress-rate testing for glass-ceramic and CRT glass in room temperature distilled water. The preloading technique was also used in this study to identify the prevailing failure mechanisms at elevated temperatures, particularly at lower test rates in which a series of mechanisms would be associated simultaneously with material failure, resulting in significant strength increase or decrease. Two different advanced ceramics including SiC whisker-reinforced composite silicon nitride and 96 wt% alumina were used at elevated temperatures. It was found that the preloading technique can be used as an additional tool to pinpoint the dominant failure mechanism that is associated with such a phenomenon of considerable strength increase or decrease.

Choi, Sung R.↗
NASA NTRS2010

Composite Overwrapped Pressure Vessel (COPV) Stress Rupture Testing

This paper reports stress rupture testing of Kevlar(TradeMark) composite overwrapped pressure vessels (COPVs) at NASA White Sands Test Facility. This 6-year test program was part of the larger effort to predict and extend the lifetime of flight vessels. Tests were performed to characterize control parameters for stress rupture testing, and vessel life was predicted by statistical modeling. One highly instrumented 102-cm (40-in.) diameter Kevlar(TradeMark) COPV was tested to failure (burst) as a single-point model verification. Significant data were generated that will enhance development of improved NDE methods and predictive modeling techniques, and thus better address stress rupture and other composite durability concerns that affect pressure vessel safety, reliability and mission assurance.

Greene, Nathanael J.↗
NASA NTRS1998

Comparative Stress Corrosion Cracking and General Corrosion Resistance of Annealed and Hardened 440 C Stainless Steel - New Techniques in Stress Corrosion Testing

The corrosion and stress corrosion cracking (SCC) characteristics of annealed and hardened 440C stainless steel were evaluated in high humidity and 3.5-percent NaCl solution. Corrosion testing consisted of an evaluation of flat plates, with and without grease, in high humidity, as well as electrochemical testing in 3.5-percent NaCl. Stress corrosion testing consisted of conventional, constant strain, smooth bar testing in high humidity in addition to two relatively new techniques under evaluation at MSFC. These techniques involve either incremental or constant rate increases in the load applied to a precracked SE(B) specimen, monitoring the crack-opening-displacement response for indications of crack growth. The electrochemical corrosion testing demonstrated an order of magnitude greater general corrosion rate in the annealed 440C. All techniques for stress corrosion testing showed substantially better SCC resistance in the annealed material. The efficacy of the new techniques for stress corrosion testing was demonstrated both by the savings in time and the ability to better quantify SCC data.

Mendreck, M. J.↗
NASA NTRS2012

Stress Free Temperature Testing and Residual Stress Calculations on Out-of-Autoclave Composites

Future launch vehicles will require the incorporation large composite parts that will make up primary and secondary components of the vehicle. NASA has explored the feasibility of manufacturing these large components using Out-of-Autoclave impregnated carbon fiber composite systems through many composites development projects. Most recently, the Composites for Exploration Project has been looking at the development of a 10 meter diameter fairing structure, similar in size to what will be required for a heavy launch vehicle. The development of new material systems requires the investigation of the material properties and the stress in the parts. Residual stress is an important factor to incorporate when modeling the stresses that a part is undergoing. Testing was performed to verify the stress free temperature with two-ply asymmetric panels. A comparison was done between three newly developed out of autoclave IM7 /Bismalieimide (BMI) systems. This paper presents the testing results and the analysis performed to determine the residual stress of the materials.

Cox, Sarah↗
NASA NTRS1968

A rapid stress-corrosion test for aluminum alloys

Stressed alloy specimens are immersed in a salt-dichromate solution at 60 degrees C. Because of the minimal general corrosion of these alloys in this solution, stress corrosion failures are detected by low-power microscopic examination.

Helfrich, W. J.↗