DOE OSTI2023

Investigating the failure behavior of cast Al-11Ce-0.4Mg alloys using in-situ scanning electron microscopy tensile testing

Within the last decade, research on Al-Ce-Mg alloys has reported promising results for use in cast part applications. In this paper, the failure behavior of cast Al-11Ce-0.4Mg (wt%) was investigated experimentally with focus on the effect the matrix and intermetallic phases have on the fracture propagation behavior at failure. For the first time, in-situ SEM tensile testing was used to study the failure behavior of cast Al-Ce alloys, reporting results for uniaxial, DIC, and single edge notch tensile tests. The results of the in-situ SEM tensile testing were compared with the materials characterization experiments, which included serial sectioning, EBSD, EDS, and fractography. Analysis of EBSD and EDS mapping of cast Al-11Ce-0.4Mg showed that the cast microstructure was a hypereutectic two phase Al-Ce alloy with grains encompassing large complex colonies of laminar eutectic Al 11 Ce 3 intermetallic. The uniaxial tensile results reported the effect casting defects have on the strength and ductility of the alloy, and DIC in-situ testing showed that the eutectic colonies plastically deform less than the matrix phase. In-situ SEM single edge notch tensile testing displayed how the strength of an individual phase affected the crack propagation direction in the alloy. The results of both the materials characterization and in-situ tensile testing experiments on the failure of this alloy revealed further directions for future alloy development that can improve both the strength and fracture toughness of Al-Ce-Mg alloys.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Molecular Dynamics Simulations of Calcite Fracture in Water

Calcite (CaCO 3 ) is one of the most common minerals in geologic and engineered systems. It is often in contact with aqueous solutions, causing chemically assisted fracture that is critical to understanding the stability of subsurface systems and manmade structures. Calcite fracture was evaluated with reactive molecular dynamics simulations, including the impacts of crack tip geometry (notch), the presence of water, and surface hydroxyl groups. Chemo-mechanical weakening was assessed by comparing the loads where fracture began to propagate. Our analyses show that in the presence of a notch, the load at which crack growth begins is lower, compared to the effect of water or surface hydroxyls. Additionally, the breaking of two adjacent Ca–O bonds is the kinetic limitation for crack initiation, since transiently broken bonds can reform, not resulting in crack growth. In aqueous environments, fresh (not hydroxylated) calcite surfaces exhibited water strengthening. Manual addition of H + and/or OH – species on the (104) calcite surface resulted in chemo-mechanical weakening of calcite by 9%. Achieving full hydroxylation of the calcite surface was thermodynamically and kinetically limited, with only 0.17–0.01 OH/nm 2 surface hydroxylation observed on the (104) surface at the end of the simulations. In conclusion, the limited reactivity of pure water with the calcite surface restricts the chemo-mechanical effects and suggests that reactions between physiosorbed water and localized structural defects may be dominating the chemo-mechanical process in the studies where water weakening has been reported.

Calcite↗
DOE OSTI2020

Structure and Dynamics of Aqueous Electrolytes Confined in 2D-TiO 2 /Ti 3 C 2 T 2 MXene Heterostructures

The synthesis of heterostructures of different two-dimensional (2D) materials offers an approach to combine advantages of different materials constituting the heterostructure and ultimately enhance their performance for applications such as electrochemical energy storage, achieving high energy, and high-power densities. Understanding the behavior of ions and solvents in confinement between these dissimilar layers is critical to understand their performance and control. Considering aqueous electrolytes, we explore the heterostructure of 2D lepidocrocite-type TiO 2 (2D-TiO 2 ) and hydroxylated or O-terminated Ti 3 C 2 MXene using ReaxFF molecular dynamics simulations and elastic/quasielastic neutron scattering techniques. Simulating a bilayer water intercalation, we find that the extent of interlayer hydration is impacted most by the surface terminations on the MXene and is marginally affected by 2D-TiO 2 . However, the introduction of 2D-TiO 2 decreases the water self-diffusion due to the notch sites (i.e., surface oxygen ridges) entrapping water molecules. Intercalating alkali cations into the heterostructures, we find that Li + is predominantly adsorbed at the 2D-TiO 2 surface instead of the MXenes with the preferential occupation of the notch sites. In contrast, Na+ forms a planar solvation with water, while K + is adsorbed both at the O-terminated MXene and 2D-TiO 2 . This behavior is altered when OH-terminated MXene is involved—the repulsion from the protons on the MXene surface forces the K + ions to be adsorbed exclusively to 2D-TiO 2 , while Na + retains some of its solvation in the water layer due to its smaller size. In OH-terminated MXenes, we see a consistent transfer of protons from the MXene surface toward 2D-TiO 2 , implying a greater capacity to store protons in the heterostructures. Of the three cations simulated, Na + hinders the proton migration the least and Li + the most because of its position near the 2D-TiO 2 surface. Furthermore, 2D-TiO 2 /MXene heterostructures are likely to exhibit a higher energy density but lower power density, especially with Na + intercalation.

25 ENERGY STORAGE↗
DOE OSTI2021

Molecular bridge-mediated ultralow-power gas sensing

Abstract We report the electrical detection of captured gases through measurement of the quantum tunneling characteristics of gas-mediated molecular junctions formed across nanogaps. The gas-sensing nanogap device consists of a pair of vertically stacked gold electrodes separated by an insulating 6 nm spacer (~1.5 nm of sputtered α-Si and ~4.5 nm ALD SiO 2 ), which is notched ~10 nm into the stack between the gold electrodes. The exposed gold surface is functionalized with a self-assembled monolayer (SAM) of conjugated thiol linker molecules. When the device is exposed to a target gas (1,5-diaminopentane), the SAM layer electrostatically captures the target gas molecules, forming a molecular bridge across the nanogap. The gas capture lowers the barrier potential for electron tunneling across the notched edge region, from ~5 eV to ~0.9 eV and establishes additional conducting paths for charge transport between the gold electrodes, leading to a substantial decrease in junction resistance. We demonstrated an output resistance change of >10 8 times upon exposure to 80 ppm diamine target gas as well as ultralow standby power consumption of <15 pW, confirming electron tunneling through molecular bridges for ultralow-power gas sensing.

77 NANOSCIENCE AND NANOTECHNOLOGY↗
DOE OSTI2024

Simulations of nozzle gas flow and gas-puff Z-pinch implosions on the Weizmann Z-pinch

We present simulations of an oxygen gas puff Z-pinch on a University scale generator at the Weizmann Institute of Science. The work accounts for the detailed geometry of the nozzle, the initial neutral gas density distribution, and the subsequent implosion. The modeling results show significant improvement with data for the current at the time of stagnation in comparison with a previous effort [Rosenzweig et al., Phys. Plasmas 27, 022705 (2020)]. As a first step, we performed simulations of the flow of neutral diatomic oxygen from a plenum through a nozzle within a recessed cathode, across a gap, and into the anode with a recessed grounded honeycomb. These simulations show an agreement with the measured initial gas density profiles within the region not blocked by the recesses and accessible to visible measurements. The computed neutral gas flow profile serves as the initial condition for a radiation magnetohydrodynamic simulation of the implosion using the MACH2-TCRE code. By considering the specific details of the nozzle and chamber geometry, we find agreement with the measured current profile, including the inductive notch. The simulations predict that the plasma undergoes a strong pinch within the hidden anode recess. The simulations also predict the strongest radiation pulse occurs within the anode recess and at the time of the observed inductive notch.

Physics↗
DOE OSTI2026

DLK1 is a GATA1s-driven dependency and therapeutic target in Down syndrome–associated myeloid leukemia

Children with Down syndrome have a markedly increased risk of developing myeloid leukemia. Although having an excellent prognosis, 10% to 20% develop relapsed or refractory disease with poor survival, highlighting the need for new targeted approaches. The pathogenesis of myeloid leukemia of Down syndrome (ML-DS) is tightly linked to fetal hematopoiesis and mutations in GATA1, generating the truncated GATA1 short (GATA1s) isoform. We identified Delta-like noncanonical Notch ligand 1 (DLK1) as a direct GATA1s target. DLK1, a paternally imprinted transmembrane protein, is highly expressed in fetal liver CD34 + cells but absent in adult hematopoiesis, making it an attractive immunotherapeutic target. Chromatin profiling revealed GATA1s occupancy at a distal enhancer within the DLK1-DIO3 locus, driving aberrant DLK1 upregulation in ML-DS. Functional studies demonstrated that DLK1 is a leukemia dependency, as its genetic ablation impaired proliferation and engraftment, induced apoptosis, and altered Notch and β-catenin signaling. Therapeutically, a DLK1-directed antibody-drug conjugate–induced selective cytotoxicity, abrogated colony formation, and significantly prolonged survival in refractory ML-DS patient-derived xenograft (PDX) models, achieving durable remissions at higher doses. These findings establish DLK1 as a leukemia-specific vulnerability and provide preclinical proof-of-concept for DLK1-targeted therapies in ML-DS and other leukemias with fetal-like expression programs.

Biological and medical sciences↗
DOE OSTI2022

Assessment of four strain energy decomposition methods for phase field fracture models using quasi-static and dynamic benchmark cases

Abstract Strain energy decomposition methods in phase field fracture models separate strain energy that contributes to fracture from that which does not. However, various decomposition methods have been proposed in the literature, and it can be difficult to determine an appropriate method for a given problem. The goal of this work is to facilitate the choice of strain decomposition method by assessing the performance of three existing methods (spectral decomposition of the stress or the strain and deviatoric decomposition of the strain) and one new method (deviatoric decomposition of the stress) with several benchmark problems. In each benchmark problem, we compare the performance of the four methods using both qualitative and quantitative metrics. In the first benchmark, we compare the predicted mechanical behavior of cracked material. We then use four quasi-static benchmark cases: a single edge notched tension test, a single edge notched shear test, a three-point bending test, and a L-shaped panel test. Finally, we use two dynamic benchmark cases: a dynamic tensile fracture test and a dynamic shear fracture test. All four methods perform well in tension, the two spectral methods perform better in compression and with mixed mode (though the stress spectral method performs the best), and all the methods show minor issues in at least one of the shear cases. In general, whether the strain or the stress is decomposed does not have a significant impact on the predicted behavior.

Zhang, Shuaifang↗
DOE OSTI2023

An investigation of fracture behaviors of NBG-18 nuclear graphite using in situ mechanical testing coupled with micro-CT

Nuclear graphite contains defects spanning from nanoscale basal cracks to sub-mm scale voids. This study aims to establish an experimental method to investigate pre-existing defects and 3-D crack growth inside nuclear graphite, NBG-18. Three-point bending tests were performed on single-edge notched beam specimens with and without coupling with micro-CT. The fracture toughness was measured to be 1.17 ± 0.06 MPa $\sqrt{{m}}$. Cracks were observed to initiate from the pores and thermal cracks on the edge of the notch and then defect or twist to grow along the pre-existing defects. Crack bridging, defection, and twisting were the primary toughening mechanisms. The crack resistance curve exhibited a trend of rising-plateau-rising that can be related to the interaction of crack front and the pre-existing defects. In conclusion, the results highlight the capability of laboratory micro-CT-based experimental method for the visualization of multi-scale defect interactions, which remains to be a challenge in the characterization of nuclear graphite.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Thermal-Mechanical Elastic-Plastic and Ductile Failure Model Calibrations for 6061-T651 Aluminum Alloy from Plate

Numerical simulations of metallic structures undergoing rapid loading into the plastic range require material models that accurately represent the response. In general, the material response can be seen as having four interrelated parts: the baseline response under slow loading, the effect of strain rate, the conversion of plastic work into heat and the effect of temperature. In essence, the material behaves in a thermal-mechanical manner if the loading is fast enough so when heat is generated by plastic deformation it raises the temperature and therefore influences the mechanical response. In these cases, appropriate models that can capture the aspects listed above are necessary. The matters of interest here are the elastic-plastic response and ductile failure behavior of 6061-T651 aluminum alloy under the conditions described above. The work was accomplished by first designing and conducting a material test program to provide data for the calibration of a modular $J_2$ plasticity model with isotropic hardening as well as a ductile failure model. Both included modules that accounted for temperature and strain rate dependence. The models were coupled with an adiabatic heating module to calculate the temperature rise due to the conversion of plastic work to heat. The test program included uniaxial tension tests conducted at room temperature, 150 and 300 C and at strain rates between 10 –4 and 10 3 1/s as well as four geometries of notched tension specimens and two tests on specimens with shear-dominated deformations. The test data collected allowed the calibration of both the plasticity and the ductile failure models. Most test specimens were extracted from a single piece of plate to maintain consistency. Notched tension tests came from a possibly different plate, but from the same lot. When using the model in structural finite element calculations, element formulations and sizes different from those used to model the test specimens in the calibration are likely to be used. A brief investigation demonstrated that the failure model can be particularly sensitive to the element selection and provided an initial guide to compensate in a specific example.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Fracture toughness evaluations for spent nuclear fuel dry storage canister welds and spent nuclear fuel clad-pellet structures

Integrity of spent nuclear fuel (SNF) interim storage canisters is very important to the safety of the back-end nuclear fuel cycle. Stress corrosion cracking (SCC) potential of interim storage canister has been considered as a high priority. Because no post-weld heat treatment was required for forming these canisters, the high tensile residual stress existed within these canister welds. This can change the fracture resistance capacity significantly as well as increase SCC potential. Due to relative thin shell thickness of a canister weldment, the spiral notch torsion test (SNTT) method was used to estimate the canister weldment fracture toughness. SNTT was developed to measure the intrinsic fracture toughness of structural materials using small specimens. The SNTT method has been applied to a wide variety of structural materials, such as low-alloy steels, stainless steel, aluminum alloy, ceramics, concrete, and composites. The SNTT system operates by applying pure torsion to cylindrical specimens with a notch line that spirals around the specimen at a 45° pitch. In order to carry out pure torsion load mode, biaxial tension/torsion tester was developed accordingly to perform SNTT protocol. Moreover, applying fracture mechanics approach to SNF system reliability investigation is warranted due to the inherent flaws and hydride structures existed in a SNF system after nuclear reactor operation. However, none of the existing fracture toughness data deal with fuel cladding specific geometry or spent fuel material conditions, such as cladding structure with the pellet-inserts and the associated pellet clad mechanical interactions induced mixed-mode damage mechanisms. Thus, the development of an intrinsic fracture mechanics approach that is suitable for SNF materials is needed. Furthermore, due to thin wall and small dimension of clad tubing structure, the SNTT method was used to estimate the clad tubing structure fracture toughness. Fracture testing were performed on the received stainless steel canister weldment, most SNTT weld samples fracture initiation sites are at heat-affected zone (HAZ) regions. The estimated fracture toughness J Q ’ for the baseline SS304 steel is at 283 kJ/m². The estimated JQ’ for the SS304/308 weld and baseline metals are 148 kJ/m 2 and 459 kJ/m 2 , respectively. Out of cell fracture testing for spent fuel structure were carried out on the surrogate rods made of Zr-4 clad and alumina inserts, the estimated fracture toughness values for baseline Zr-4 cladding with alumina-pellet inserts are: (1) For SNTT samples with a short or medium crack length, between 5.4-mm and 8-mm, the estimate J IQ upon fracture initiation for the baseline Zr-4 cladding is at 50 kJ/m 2 with 2-sigma uncertainty of 3.26 kJ/m 2 , and the associated K IQ is at 67.46 MPa$\sqrt{m}$; and (2) For SNTT samples with a long crack length, around 13-mm, the crack initialization is deviated from that of the Mode-I tensile fracture and appears to be a mixed-mode fracture of Mode I - tensile stress and Mode III - out of plane shear stress; the estimated J MQ is at 18.9 kJ/m 2 , the associated K MQ is at 41.4 MPa$\sqrt{m}$.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2021

Replaceable Paddle Tip Fabrication and Testing for Saltstone Production Facility (SPF) Mixer (FY2020 Update)

Details of the operations and issues related to the paddles used in the Saltstone Production Facility (SPF) employing the 10-inch READCO ™ -Kurimoto co-rotating dual shaft continuous mixer are provided in SRNL-ST1-2019-00142, Based on a recent effort performed by the Savannah River National Laboratory (SRNL) and funded by Savannah River Remediation (SRR), eight different replaceable paddle designs were proposed and the angled notched design was selected for this study. This design was selected over the other designs due to its simplicity and its ability to meet the fitness of duty requirements. There are two types of angled notched replaceable tip designs, one being flat and the other helical. Either of these designs can be used for blending the premix with the salt solution. Stress calculations performed on this design (the use of the bolts and connections) are documented in M-CLC-Z-00137 showing it was suitable for use.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗
DOE OSTI2024

Testing Protocol Development for the Fracture Toughness of Parts Built with Big Area Additive Manufacturing

The mechanical testing of additively manufactured parts has largely relied on the existing standards developed for traditional manufacturing. While this approach leverages the investment made in current standards development, it inaccurately assumes that the mechanical response of additive manufacturing (AM) parts is identical to that of parts manufactured through traditional processes. When considering thermoplastic, material extrusion AM, the differences in response can be attributed to an AM part’s inherent inhomogeneity caused by porosity, interlayer zones, and surface texture. Additionally, the interlayer bonding of parts printed with large-scale AM is difficult to adequately assess, as much testing is performed such that stress is distributed across many layer interfaces; therefore, the lack of AM-specific standards to assess interlayer bonding is a significant research gap. To quantify interlayer bonding via fracture toughness, double cantilever beam (DCB) testing has been used for some AM materials, and DCB has been generally used for a variety of materials including metal, wood, and laminates. Mode I DCB testing was performed on thermoplastic matrix composites printed with Big Area Additive Manufacturing (BAAM). Of particular interest was the notch shape and deflection speed during testing. The results examine the differences when using two notch types and three deflection speeds. The testing method introduced by the following paper differentiates itself from the ones described in the standards used by modernizing the methodology. This was conducted with the introduction of Digital Image Correlation (DIC) to gather displacement and load data simultaneously without human intervention.

Polymer Science↗
DOE OSTI2022

Damage Evolution of Double-Sided Copper Conductor on Multi-layer Flexible Substrate Under Bending

Abstract—Thin-film conductors continue to play an important role in flexible electronics, and thus, the performance and reliability of such conductors under mechanical loading such as stretch, bend, and twist need to be studied through experiments as well as simulations. This paper focuses on the damage evolution of the thin-film conductors under cyclic bending. Four types of double-sided copper conductors: straight trace without coverlay, straight trace with coverlay, notched trace without coverlay, and notched trace with coverlay on multi-layer substrates were studied in this work. The adaptive curvature flexure test method, which is suitable for thin-film bending, was employed in this work. Adaptive curvature flexure test is one where the flexible substrate with its conductor is positioned between two parallel plates, and the parallel plates are moved relative to each other such that the gap distance between the parallel plates changes in one of the configurations of the adaptive curvature flexure test. Different strain levels can be achieved easily in such an adaptive curvature flexure test by controlling the gap distance between the parallel plates. By subjecting flexible substrates with thin conductors to such bend tests, the fatigue life of the specimen was determined for different magnitudes of strain ranges. The results were then compared among the four types of conductors. Specimens were designed such that the conductors were placed on both sides of the substrate so that the one of the conductors would undergo tensile straining, while the other one would undergo compressive straining. It was shown that the fatigue life was highly dependent on the magnitude of strain range, and that the conductor on the compressive side failed sooner than that on the tensile side. The failed specimens were examined in a microscope at different number of cycles. Also, the resistance of the conductors, which is directly related to the reliability of thin-film conductors, was monitored in-situ during bending. The resistance change with the strain range change as well as the resistance progression with the number of cycles in tensile as well as compressive mode were determined, and such information is then used to create failure prediction models for thin-film conductors on flexible substrates.

damage evolution, flexible conductor, multi-layer ↗
DOE OSTI2022

Electromagnetic propulsion system

An electromagnetic propulsion system comprises a plurality of stator coils wound about a first axis, a plurality of support structures, a coupler that surrounds a portion of the stator coils, and a plurality of rotor coils wound about an axis that is parallel to the first axis. The stator coils are configured to receive electric current to induce a first magnetic field. The support structures support the stator coils. The coupler includes a notch oriented so that one of the support structures can pass through the notch when the coupler moves along the stator coils. The rotor coils are attached to the coupler and are configured to receive electric current to induce a magnetic field that interacts with the first magnetic field so that a magnetic force is applied to the rotor coils, thereby propelling the coupler and the rotor coils along the stator coils.

Hartman, Seth↗
DOE OSTI2025

KIPM Detector Characterization in QUIET

Kinetic Inductance Phonon‑Mediated (KIPM) detectors are superconducting microwave resonators that sense energy depositions in the substrate through a transient shift in their resonant frequency. In this work, I installed new devices in the QUIET cryogenic facility and used a network analyzer to drive them across a range of power levels. At each setting, I measured the transmitted signal and fit it to a simple notch‑filter model, allowing us to extract key performance metrics. Despite the increased noise at low power, the model consistently captured the resonance behavior. I first measured the resonance parameters as a function of RF drive power, then repeated the measurement across a range of temperatures to test whether the device behaved like an MKID. While the notch-filter fits captured the resonance reliably, the observed temperature dependence did not match the expected MKID signature — indicating that these first in-house fabricated chips are not yet functioning as true MKIDs. Overall, this reframes our work as a study of resonance parameter extraction and identification, pointing towards future iterations of device design and fabrication to get the true MKID response.

Savitala, Akash [U. Washington, Seattle (main); Fe↗
DOE OSTI2024

Effects of hydrogen partial pressure on crack initiation and growth rate in vintage X52 steel

There is an increasing interest in ensuring compatibility of existing natural gas infrastructure with conveyance of hydrogen, especially for vintage (pre-1970s) pipeline steels. While hydrogen is known to affect the fatigue and fracture resistance of these materials, there is a lack of data on its effects on crack initiation at low hydrogen partial pressure. To address this gap, the current work presents a series of fatigue tests on vintage API Grade X52 steel in pure nitrogen, air and gaseous hydrogen at partial pressures of 1 and 207 bar. Circumferential notch tension (CNT) specimens with direct current potential difference (DCPD) measurements are used to get S–N curves for crack initiation and failure, and compact tension (CT) tests to assess crack growth rates. Results indicate that air accelerates crack initiation, low hydrogen partial pressure affects the crack growth rate, and higher pressures have the largest impact on both. Surprisingly, crack initiation is faster in air than at 1 bar hydrogen partial pressure. The CNT tests also reveal that the orientation of the banded microstructure has no effect on the crack initiation site, but it influences its growth behavior. Moreover, fractography shows that hydrogen also promotes instances of quasi-cleavage and intergranular fracture, linked to embrittlement of the material. Here, these results demonstrate that, while hydrogen may impact the entirety of the fatigue process, its effects on the early stages of damage accumulation become relevant only at larger pressures. More comprehensive studies of crack initiation in hydrogen atmospheres will be critical to future codes and standards for hydrogen infrastructure.

Circumferential notch tension↗
DOE OSTI2025

Fracture toughness measurement of ceramics with fuel pellet geometry

The crack initiation of nuclear fuel pellets, driven by extreme temperature gradients, is a critical factor impacting reactor performance. Although this fact is widely acknowledged, there is limited fracture toughness data for specimens with representative geometry and fabricated using relevant processing methods. Here, to address this, a new chevron-notched short-rod specimen configuration with diameter and length both equal to 10 mm, representative of a conventional fuel pellet and tested in tension, was developed in an attempt to validly measure Mode I fracture toughness, K Ic . Test calibration was carried out by testing polycrystalline ZrO 2 , SiC, and Si 3 N 4 ceramics fabricated with conventional fuel pellet geometry and known fracture toughnesses. The results suggest that the method described in this paper produces valid K Ic measurements using conventional ceramic fuel pellets.

Ceramics↗
DOE OSTI2022

Update on the Current R&D Activity in the U.S.

An NRC-sponsored assessment of a previous version of Section III, Division 5 of the ASME BPVC identified an inadequate understanding of the impact of a multiaxial stress, structural discontinuities, and notch effects.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗