DOE OSTI2020

Microstructural characterization of cold-worked 316 stainless steel flux thimble tubes irradiated up to 100 dpa in a commercial Pressurized Water Reactor

Two flux thimble tubes (FTT) made of 15% cold-worked 316 stainless steel (SS) were harvested from Ringhals Pressurized Water Reactor (PWR) Unit 2, with peak damages of 76 and 100 displacements per atom (dpa) after 29 and 34 years’ service, respectively. Specimens sectioned from parent tubes were comprehensively characterized with nominal damage levels of ~0, ~41, ~74, 76, and 100 dpa at a nominal temperature range of 285-323 °C. Both FTTs contained helium and hydrogen gases as transmutation products. The helium follows a production rate of ~9.8 appm/dpa, while environmental factors complicate hydrogen production obscuring an exact H/dpa ratio. Irradiation-induced dislocation loops, nano-cavities, solute clusters, and microsegregation were all observed. The dislocation loops and nano-cavities indicated saturation at 41 dpa. The solute clusters continued to evolve with Ni-Si clusters formed at 41 dpa, and Ni-Si-Mn-P clusters formed at 74 and 100 dpa, but neither clusters exhibited distinct diffraction patterns at any damage levels. Solute clusters were observed to frequently be co-located with dislocation loops, but fully decorated loops were rarely detected. Significant radiation-induced segregation (RIS) was observed around grain boundaries at all damage levels. The modified inverse Kirkendall (MIK) model captured the RIS behavior of major elements. Large cavities within or around an Mn-S rich region were observed for the first time. Through all the damage levels, void swelling is always below 0.05%, making significant dimensional change unlikely in core internals when used at similar conditions. Meanwhile, the role of overwhelming nanocavities, presumably helium bubbles, should be considered in other potential degradation mechanisms, including irradiation-assisted stress corrosion cracking, embrittlement, and loss of fracture toughness, which remain the concerns for extended operation of nuclear power plants.

Post Irradiation Examination, Isotope Dilution Mas↗
DOE OSTI2020

Microstructure, hardness and cavitation erosion resistance of different cold spray coatings on stainless steel 316 for hydropower applications

There is an urgent need for repair of hydropower components that have undergone damage due to cavitation. Conventional repair methods involve melting of materials and can deteriorate material properties and cause distortion. This study investigated the relevant properties of different materials using solid phase processing—cold spray technology. Stainless steel (SS) 316, Inconel 625 and CrC-NiCr materials were cold spray deposited onto base metal SS 316, respectively. Cold spray achieved dense uniform deposits with low level porosity, and intimate contact between the deposit and the base metal was observed. Severe plastic deformation imparted during the cold spray process resulted in significant grain size refinement, nanostructured regions were observed in the deposits across the interfacial area. Cold sprayed deposits exhibited elevated hardness in contrast to that of the base metal SS 316. The cavitation erosion resistance of the deposits was evaluated with a cavitation erosion jet adhering to ASTM G134. Both SS 316 and Inconel 625 achieved better cavitation erosion resistance when compared to that of the SS 316 base metal, with the former exhibiting close to a 4 times improvement.

Jiang, Xiujuan↗
DOE OSTI2020

Fractal breakage of porous carbonate sand particles: Microstructures and mechanisms

In situ, three-dimensional (3D) characterizations of particle breakage in porous carbonate sands are presented, for the first time, with synchrotron-based micro computed tomography. Evolution of grain-scale characteristics are identified and quantified via elaborate image processing and topology analyses. The sequential 3D images reveal distinctly different fracture mechanisms for carbonate sands from silica sands. The angular shape of carbonate sand particles facilitates bending fracture, and particles with a lower sphericity and a higher porosity are more prone to break. 3D crack networks extracted from fractured particles imply considerable cleavage along initial pores. The fractal dimension of crack networks increases with external loading due to crack branching via cleavage. The resultant fragment size distribution also appears fractal and the fractal feature is valid down to the breakage limit of calcium carbonate. Crack propagation along the initial pores reduces the energy barrier for particle breakage and thus fracture strength of particles

Carbonate sands↗