Assessing High Burnup U-19Pu-10Zr Fuel Performance against Historical and Modeled Behavior
Advancing the deployment of sodium-cooled fast reactors (SFRs) requires thorough testing of metallic fuel pins under accident conditions to establish safe operational limits of high burnup fuel. To conduct transient testing, a comprehensive understanding of steady-state fuel behavior obtained through both experimental characterization and accurate predictive capabilities is needed. This study comparatively assesses the steady-state irradiation performance of two high burnup U-19Pu-10Zr fuel pins, DP-36 and DP-40, irradiated under prototypic fast reactor conditions in preparation for planned safety testing at the Transient Reactor Test Facility. Since DP-40 was designated for use in the test and DP-36 serves as its sibling pin, non-destructive, engineering-scale post-irradiation examinations (PIE) were conducted on both pins while destructive examinations were performed exclusively on DP-36. The results were then assessed against historical performance data from similar fuel pins irradiated in the Experimental Breeder Reactor-II. Additionally, the steady-state irradiation of each pin was modeled using the BISON fuel performance code to assess the accuracy of current modeling capabilities in predicting the baseline irradiation behavior. Non-destructive examinations included neutron radiography to measure fuel column elongation, gamma scanning to verify pin integrity and fission product migration, and profilometry to assess dimensional changes. Benchmarking against existing PIE data revealed consistent patterns in axial fuel column growth and cladding diametral strain, though both pins exhibited longer low-density “fluff” structures, which can have implications for core reactivity and source term calculations. Destructive examinations on DP-36 included fission gas release analysis and sectioning for optical microscopy, which showed more complex constituent redistribution patterns than the traditionally accepted 3-ring model. The axial evolution of fractional areas and porosities of each of the redistributed zones were quantified and presented. Modeling comparisons showed agreement in fractional fission gas release but consistently overestimated axial and radial swelling and disagreed with measured axial porosity patterns. These conservative overpredictions suggested that the pins would appear closer to failure or operational limits at the start of transient tests, potentially leading to higher strain accumulation during the transient. While conservative estimates provide safety margins, they can negatively impact fuel economics. A review of the swelling models identified areas for improvement in the gaseous swelling, solid swelling, and fuel hot-pressing models when applied to ternary fuel. The results of this study highlight the critical importance of conducting pre-test characterization on both test and sibling pins to accurately capture steady-state fuel behavior, providing a precise baseline for post-test evaluations and essential inputs for transient modeling of the planned experiments. The analysis also revealed significant data gaps that require further investigation to enhance the understanding and prediction of fuel swelling and pore dynamics. Collecting comprehensive data across different irradiation conditions, burnup levels, and fuel compositions are essential for refining existing models and developing mechanistic models for both binary and ternary metallic fuels, ultimately improving the integration of modeling and experimental approaches in accident testing.