SEARCH · Engineering Papers

Results for “Damage models”

Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

SourceResearch connectionFrom yearThrough year

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

At least 73 records · Page 4

All sources NASA NTRS DOE OSTI

NASA NTRS2011

Numerical Implementation of a Multiple-ISV Thermodynamically-Based Work Potential Theory for Modeling Progressive Damage and Failure in Fiber-Reinforced Laminates

A thermodynamically-based work potential theory for modeling progressive damage and failure in fiber-reinforced laminates is presented. The current, multiple-internal state variable (ISV) formulation, enhanced Schapery theory (EST), utilizes separate ISVs for modeling the effects of damage and failure. Damage is considered to be the effect of any structural changes in a material that manifest as pre-peak non-linearity in the stress versus strain response. Conversely, failure is taken to be the effect of the evolution of any mechanisms that results in post-peak strain softening. It is assumed that matrix microdamage is the dominant damage mechanism in continuous fiber-reinforced polymer matrix laminates, and its evolution is controlled with a single ISV. Three additional ISVs are introduced to account for failure due to mode I transverse cracking, mode II transverse cracking, and mode I axial failure. Typically, failure evolution (i.e., post-peak strain softening) results in pathologically mesh dependent solutions within a finite element method (FEM) setting. Therefore, consistent character element lengths are introduced into the formulation of the evolution of the three failure ISVs. Using the stationarity of the total work potential with respect to each ISV, a set of thermodynamically consistent evolution equations for the ISVs is derived. The theory is implemented into commercial FEM software. Objectivity of total energy dissipated during the failure process, with regards to refinements in the FEM mesh, is demonstrated. The model is also verified against experimental results from two laminated, T800/3900-2 panels containing a central notch and different fiber-orientation stacking sequences. Global load versus displacement, global load versus local strain gage data, and macroscopic failure paths obtained from the models are compared to the experiments.

Pineda, Evan J.↗

NASA NTRS2024

Characterization of Low-Velocity Impact Damage in Toughened Non-Crimp Fabric Laminates

The damage response of resin-infused composites was investigated using quasi-static indentation (QSI) and instrumented drop-weight impact testing. The test specimens were composed of six layers of non-crimp fabrics where each layer contained +45°, 90°, −45°, and 0° plies. The goals of the testing were to identify damage responses that may differ from traditional thermoset materials and provide damage characterization data to evaluate current damage prediction analyses and aid improvements to current damage models. The damage was characterized using X-ray computed tomography (CT) and ultrasonic testing (UT). Incremental QSI loading was used on a single specimen to investigate damage growth in nine steps at progressively higher loads. Realtime acoustic emission data were used to determine the unloading points. Unlike typical thermoset composites, the force-displacement was smooth and showed no obvious indications of damage. The primary damage consisted of large lines of fiber fracture on the plies near the impact surface and delaminations through the thickness. Nine specimens were impacted at nominal impact energies of 25 ft-lbs, 30 ft-lbs, and 35 ft-lbs. The force histories at each energy followed nearly identical paths. Again, no obvious signs of damage were observed in any of the force histories. The general damage response in the dynamic tests was similar to the QSI-loaded specimens. However, repeat specimens impacted with a given impact energy showed variations in the damage. Some characteristics of the damage response were different than those typically observed in thermoset composites and will need to be evaluated using current analysis methods.

Composite Materials↗

NASA NTRSDate not supplied

Characterization of Low-Velocity Impact Damage in Toughened Non-Crimp Fabric Laminates

Composite Materials↗

NASA NTRS2013

Automated 3D Damaged Cavity Model Builder for Lower Surface Acreage Tile on Orbiter

The 3D Automated Thermal Tool for Damaged Acreage Tile Math Model builder was developed to perform quickly and accurately 3D thermal analyses on damaged lower surface acreage tiles and structures beneath the damaged locations on a Space Shuttle Orbiter. The 3D model builder created both TRASYS geometric math models (GMMs) and SINDA thermal math models (TMMs) to simulate an idealized damaged cavity in the damaged tile(s). The GMMs are processed in TRASYS to generate radiation conductors between the surfaces in the cavity. The radiation conductors are inserted into the TMMs, which are processed in SINDA to generate temperature histories for all of the nodes on each layer of the TMM. The invention allows a thermal analyst to create quickly and accurately a 3D model of a damaged lower surface tile on the orbiter. The 3D model builder can generate a GMM and the correspond ing TMM in one or two minutes, with the damaged cavity included in the tile material. A separate program creates a configuration file, which would take a couple of minutes to edit. This configuration file is read by the model builder program to determine the location of the damage, the correct tile type, tile thickness, structure thickness, and SIP thickness of the damage, so that the model builder program can build an accurate model at the specified location. Once the models are built, they are processed by the TRASYS and SINDA.

Belknap, Shannon↗

NASA NTRS2017

Fracture-Based Mesh Size Requirements for Matrix Cracks in Continuum Damage Mechanics Models

This paper evaluates the ability of progressive damage analysis (PDA) finite element (FE) models to predict transverse matrix cracks in unidirectional composites. The results of the analyses are compared to closed-form linear elastic fracture mechanics (LEFM) solutions. Matrix cracks in fiber-reinforced composite materials subjected to mode I and mode II loading are studied using continuum damage mechanics and zero-thickness cohesive zone modeling approaches. The FE models used in this study are built parametrically so as to investigate several model input variables and the limits associated with matching the upper-bound LEFM solutions. Specifically, the sensitivity of the PDA FE model results to changes in strength and element size are investigated.

Leone, Frank A.↗

NASA NTRS2018

Implementation of a Matrix Crack Spacing Parameter in a Continuum Damage Mechanics Finite Element Model

Continuum Damage Mechanics (CDM) based progressive damage and failure analysis (PDFA) methods have demonstrated success in a variety of finite element analysis (FEA) implementations. However, the technical maturity of CDM codes has not yet been proven for the full design space of composite materials in aerospace applications. CDM-based approaches represent the presence of damage by changing the local material stiffness definitions and without updating the original mesh or element integration schemes. Without discretely representing cracks and their paths through the mesh, damage in models with CDM-based materials is often distributed in a region of partially damaged elements ahead of stress concentrations. Having a series of discrete matrix cracks represented by a softened region may affect predictions of damage propagation and, thus, structural failure. This issue can be mitigated by restricting matrix damage development to discrete, fiber-aligned rows of elements; hence CDM-based matrix cracks can be implemented to be more representative of discrete matrix cracks. This paper evaluates the effect of restricting CDM matrix crack development to discrete, fiber-aligned rows where the spacing of these rows is controlled by a user-defined crack spacing parameter. Initially, the effect of incrementally increasing matrix crack spacing in a unidirectional center notch coupon is evaluated. Then, the lessons learned from the center notch specimen are applied to open-hole compression finite element models. Results are compared to test data, and the limitations, successes, and potential of the matrix crack spacing approach are discussed.

Hyder, Imran↗

NASA NTRS2008

Damage Propagation Modeling for Aircraft Engine Prognostics

This paper describes how damage propagation can be modeled within the modules of aircraft gas turbine engines. To that end, response surfaces of all sensors are generated via a thermo-dynamical simulation model for the engine as a function of variations of flow and efficiency of the modules of interest. An exponential rate of change for flow and efficiency loss was imposed for each data set, starting at a randomly chosen initial deterioration set point. The rate of change of the flow and efficiency denotes an otherwise unspecified fault with increasingly worsening effect. The rates of change of the faults were constrained to an upper threshold but were otherwise chosen randomly. Damage propagation was allowed to continue until a failure criterion was reached. A health index was defined as the minimum of several superimposed operational margins at any given time instant and the failure criterion is reached when health index reaches zero. Output of the model was the time series (cycles) of sensed measurements typically available from aircraft gas turbine engines. The data generated were used as challenge data for the Prognostics and Health Management (PHM) data competition at PHM 08.

Saxena, Abhinav↗

NASA NTRS2007

Prediction of Size Effects in Notched Laminates Using Continuum Damage Mechanics

This paper examines the use of a continuum damage model to predict strength and size effects in notched carbon-epoxy laminates. The effects of size and the development of a fracture process zone before final failure are identified in an experimental program. The continuum damage model is described and the resulting predictions of size effects are compared with alternative approaches: the point stress and the inherent flaw models, the Linear-Elastic Fracture Mechanics approach, and the strength of materials approach. The results indicate that the continuum damage model is the most accurate technique to predict size effects in composites. Furthermore, the continuum damage model does not require any calibration and it is applicable to general geometries and boundary conditions.

Camanho, D. P.↗

NASA NTRS2001

Evaluation of a Linear Cumulative Damage Failure Model for Epoxy Adhesive

Recently a significant amount of work has been conducted to provide more complex and accurate material models for use in the evaluation of adhesive bondlines. Some of this has been prompted by recent studies into the effects of residual stresses on the integrity of bondlines. Several techniques have been developed for the analysis of bondline residual stresses. Key to these analyses is the criterion that is used for predicting failure. Residual stress loading of an adhesive bondline can occur over the life of the component. For many bonded systems, this can be several years. It is impractical to directly characterize failure of adhesive bondlines under a constant load for several years. Therefore, alternative approaches for predictions of bondline failures are required. In the past, cumulative damage failure models have been developed. These models have ranged from very simple to very complex. This paper documents the generation and evaluation of some of the most simple linear damage accumulation tensile failure models for an epoxy adhesive. This paper shows how several variations on the failure model were generated and presents an evaluation of the accuracy of these failure models in predicting creep failure of the adhesive. The paper shows that a simple failure model can be generated from short-term failure data for accurate predictions of long-term adhesive performance.

Richardson, David E.↗

NASA NTRS2013

Micromechanics Fatigue Damage Analysis Modeling for Fabric Reinforced Ceramic Matrix Composites

A micromechanics analysis modeling method was developed to analyze the damage progression and fatigue failure of fabric reinforced composite structures, especially for the brittle ceramic matrix material composites. A repeating unit cell concept of fabric reinforced composites was used to represent the global composite structure. The thermal and mechanical properties of the repeating unit cell were considered as the same as those of the global composite structure. The three-phase micromechanics, the shear-lag, and the continuum fracture mechanics models were integrated with a statistical model in the repeating unit cell to predict the progressive damages and fatigue life of the composite structures. The global structure failure was defined as the loss of loading capability of the repeating unit cell, which depends on the stiffness reduction due to material slice failures and nonlinear material properties in the repeating unit cell. The present methodology is demonstrated with the analysis results evaluated through the experimental test performed with carbon fiber reinforced silicon carbide matrix plain weave composite specimens.

Min, J. B.↗

NASA NTRS2012

Progressive Damage Analysis of Bonded Composite Joints

The present work is related to the development and application of progressive damage modeling techniques to bonded joint technology. The joint designs studied in this work include a conventional composite splice joint and a NASA-patented durable redundant joint. Both designs involve honeycomb sandwich structures with carbon/epoxy facesheets joined using adhesively bonded doublers.Progressive damage modeling allows for the prediction of the initiation and evolution of damage within a structure. For structures that include multiple material systems, such as the joint designs under consideration, the number of potential failure mechanisms that must be accounted for drastically increases the complexity of the analyses. Potential failure mechanisms include fiber fracture, intraply matrix cracking, delamination, core crushing, adhesive failure, and their interactions. The bonded joints were modeled using highly parametric, explicitly solved finite element models, with damage modeling implemented via custom user-written subroutines. Each ply was discretely meshed using three-dimensional solid elements. Layers of cohesive elements were included between each ply to account for the possibility of delaminations and were used to model the adhesive layers forming the joint. Good correlation with experimental results was achieved both in terms of load-displacement history and the predicted failure mechanism(s).

Leone, Frank A., Jr.↗

NASA NTRS2017

Multiscale Fiber Kinking: Computational Micromechanics and a Mesoscale Continuum Damage Mechanics Models

In this work, the fiber kinking phenomenon, which is known as the failure mechanism that takes place when a fiber reinforced polymer is loaded under longitudinal compression, is studied. A computational micromechanics model is employed to interrogate the assumptions of a recently developed mesoscale continuum damage mechanics (CDM) model for fiber kinking based on the deformation gradient decomposition (DGD) and the LaRC04 failure criteria.

Herraez, Miguel↗

NASA NTRS1991

Constitutive and damage material modeling in a high pressure hydrogen environment

Numerous components in reusable space propulsion systems such as the SSME are exposed to high pressure gaseous hydrogen environments. Flow areas and passages in the fuel turbopump, fuel and oxidizer preburners, main combustion chamber, and injector assembly contain high pressure hydrogen either high in purity or as hydrogen rich steam. Accurate constitutive and damage material models applicable to high pressure hydrogen environments are therefore needed for engine design and analysis. Existing constitutive and cyclic crack initiation models were evaluated only for conditions of oxidizing environments. The main objective is to evaluate these models for applicability to high pressure hydrogen environments.

Russell, D. A.↗

NASA NTRS2008

Aerodynamic Effects and Modeling of Damage to Transport Aircraft

A wind tunnel investigation was conducted to measure the aerodynamic effects of damage to lifting and stability/control surfaces of a commercial transport aircraft configuration. The modeling of such effects is necessary for the development of flight control systems to recover aircraft from adverse, damage-related loss-of-control events, as well as for the estimation of aerodynamic characteristics from flight data under such conditions. Damage in the form of partial or total loss of area was applied to the wing, horizontal tail, and vertical tail. Aerodynamic stability and control implications of damage to each surface are presented, to aid in the identification of potential boundaries in recoverable stability or control degradation. The aerodynamic modeling issues raised by the wind tunnel results are discussed, particularly the additional modeling requirements necessitated by asymmetries due to damage, and the potential benefits of such expanded modeling.

Shah, Gautam H.↗

NASA NTRS2016

A Continuum Damage Mechanics Model to Predict Kink-Band Propagation Using Deformation Gradient Tensor Decomposition

A new model is proposed that represents the kinematics of kink-band formation and propagation within the framework of a mesoscale continuum damage mechanics (CDM) model. The model uses the recently proposed deformation gradient decomposition approach to represent a kink band as a displacement jump via a cohesive interface that is embedded in an elastic bulk material. The model is capable of representing the combination of matrix failure in the frame of a misaligned fiber and instability due to shear nonlinearity. In contrast to conventional linear or bilinear strain softening laws used in most mesoscale CDM models for longitudinal compression, the constitutive response of the proposed model includes features predicted by detailed micromechanical models. These features include: 1) the rotational kinematics of the kink band, 2) an instability when the peak load is reached, and 3) a nonzero plateau stress under large strains.

Bergan, Andrew C.↗

NASA NTRS2002

Life-Extending Control for Aircraft Engines Studied

Current aircraft engine controllers are designed and operated to provide both performance and stability margins. However, the standard method of operation results in significant wear and tear on the engine and negatively affects the on-wing life--the time between cycles when the engine must be physically removed from the aircraft for maintenance. The NASA Glenn Research Center and its industrial and academic partners have been working together toward a new control concept that will include engine life usage as part of the control function. The resulting controller will be able to significantly extend the engine's on-wing life with little or no impact on engine performance and operability. The new controller design will utilize damage models to estimate and mitigate the rate and overall accumulation of damage to critical engine parts. The control methods will also provide a means to assess tradeoffs between performance and structural durability on the basis of mission requirements and remaining engine life. Two life-extending control methodologies were studied to reduce the overall life-cycle cost of aircraft engines. The first methodology is to modify the baseline control logic to reduce the thermomechanical fatigue (TMF) damage of cooled stators during acceleration. To accomplish this, an innovative algorithm limits the low-speed rotor acceleration command when the engine has reached a threshold close to the requested thrust. This algorithm allows a significant reduction in TMF damage with only a very small increase in the rise time to reach the commanded rotor speed. The second methodology is to reduce stress rupture/creep damage to turbine blades and uncooled stators by incorporating an engine damage model into the flight mission. Overall operation cost is reduced by an optimization among the flight time, fuel consumption, and component damages. Recent efforts have focused on applying life-extending control technology to an existing commercial turbine engine, and doing so without modifying the hardware or adding sensors. This approach makes it possible to retrofit existing engines with life-extending control technology by changing only the control software in the full-authority digital engine controller (FADEC). The significant results include demonstrating a 20- to 30-percent reduction in TMF damage to the hot section by developing and implementing smart acceleration logic during takeoff. The tradeoff is an increase, from 5.0 to 5.2 sec, in the time required to reach maximum power from ground idle. On a typical flight profile of a cruise at Mach 0.8 at an altitude of 41,000 ft, and cruise time of 104 min, the optimized system showed that a reduction in cruise speed from Mach 0.8 to 0.79 can achieve an estimated 25-to 35-percent creep/rupture damage reduction in the engine's hot section and a fuel savings of 2.1 percent. The tradeoff is an increase in flight time of 1.3 percent (1.4 min).

Guo, Te-Huei↗

NASA NTRS2020

Evaluation of Fatigue Damage Accumulation Functions for Delamination Initiation and Propagation

The present report follows on the cohesive fatigue damage model methodology proposed in NASA-TP-2018-219838. In that report, an empirical function describing the incremental damage due to cyclic loading was used to calculate fatigue damage within a cohesive formulation. The form of the function was developed such that, when integrated at a constant stress amplitude from no damage to failure, it produces a life versus load response that is consistent with an S-N diagram. Therefore, the parameters of the damage model could be obtained by fitting the model predictions to an S-N diagram. The finite element analyses performed demonstrate that the cohesive fatigue accumulation function provides a link between the S-N diagram that describes crack initiation, and the Paris law that characterizes the rate of crack propagation. However, when the model was proposed, it was not known whether the form of the damage accumulation function associated with a desired S-N diagram is unique and, if not, if the link between S-N and the Paris law is unique and independent of the fatigue function selected. In the effort described herein, several alternative forms of the damage function that reproduce the desired features of S-N diagrams were found and evaluated. The effects of each of these functions on the predicted parameters of the Paris law and the propagation threshold are discussed. The results indicate that the predicted exponent m of the Paris law is indeed independent of the damage accumulation function. However, different functions predict different values for the pre-factor C of the Paris law. Therefore, the proper damage accumulation function must be selected by comparison with experiments. One of the new damage accumulation functions proposed herein was found to be particularly useful for analysis because of the ease with which the model parameters can be determined with a minimal amount of experimental information. The effectiveness of the proposed methodology and damage function was demonstrated by conducting analyses of a double cantilever beam test, a mixed-mode bending test, and a three-point bending test of a skin/doubler specimen. The results indicate that the same set of model parameters can provide accurate predictions of the rate of fatigue crack propagation for a variety of material interfaces, mode mixities, load levels, and stress ratios.

Cohesive elements↗

NASA NTRS2015

Investigation of Micro-Scale Architectural Effects on Damage of Composites

This paper presents a three-dimensional, energy based, anisotropic, stiffness reduction, progressive damage model for composite materials and composite material constituents. The model has been implemented as a user-defined constitutive model within the Abaqus finite element software package and applied to simulate the nonlinear behavior of a damaging epoxy matrix within a unidirectional composite material. Three different composite microstructures were considered as finite element repeating unit cells, with appropriate periodicity conditions applied at the boundaries. Results representing predicted transverse tensile, longitudinal shear, and transverse shear stress-strain curves are presented, along with plots of the local fields indicating the damage progression within the microstructure. It is demonstrated that the damage model functions appropriately at the matrix scale, enabling localization of the damage to simulate failure of the composite material. The influence of the repeating unit cell geometry and the effect of the directionality of the applied loading are investigated and discussed.

damage↗