Phase stability, mechanical properties, and ion irradiation effects in face-centered cubic CrFeMnNi compositionally complex solid-solution alloys at high temperatures
We report two CrFeMnNi face-centered cubic complex concentrated solid-solution alloys (CSA) have been evaluated for phase stability, mechanical properties, and radiation damage effects from heavy ions. Cr 18 Fe 27 Mn 27 Ni 28 and Cr 15 Fe 35 Mn 15 Ni 35 were predicted by thermodynamic calculations to phase separate and maintain a single phase at 700 °C, respectively. Aging experiments at this temperature confirmed varying degrees of precipitation of a body-centered cubic phase in both Cr 18 Fe 27 Mn 27 Ni 28 and Cr 15 Fe 35 Mn 15 Ni 35 . The alloys showed promising strength in tensile deformation at room temperature, with yield strengths of 155 MPa and 151 MPa for Cr 18 Fe 27 Mn 27 Ni 28 and Cr 15 Fe3 5 Mn 15 Ni 35 , respectively. At 500 °C, the yield strength of Cr 18 Fe 27 Mn 27 Ni 28 fell to 93 MPa, and to 100 MPa in Cr 15 Fe3 5 Mn 15 Ni 35 . Unlike Cr 18 Fe 27 Mn 27 Ni 28 , Cr 15 Fe 35 Mn 15 Ni 35 gained some ductility at 500 °C compared to room temperature. The two CSAs were irradiated to 75 dpa at 500 °C in the plateau region of the displacement curve using 3.7 MeV Ni 2+ ions, alongside model alloy 709 as a reference. Irradiation results produced similar densities and sizes of dislocations loops in the two CSAs compared to the reference. However, while large voids form in the plateau region of Cr 18 Fe 27 Mn 27 Ni 28 , small voids form just beyond the displacement peak of Cr 15 Fe 35 Mn 15 Ni 35 . Atom probe tomography and energy dispersive X-ray spectroscopy-equipped scanning transmission electron microscopes were used to characterize the alloys for changes in chemical distribution.