Scalable High-H 2 Flux, Robust Thin Film Solid Oxide Electrolyzer
This project was aimed at the development of proton-conducting SOEC (P-SOEC) technology that has the potential to meet key DOE H 2 production targets. A decreased proton resistance of the electrolyte and Faradaic efficiency improvements were sought to increase the fraction of consumed electrolysis power that is used to actually generate H 2 , while simultaneously decreasing cost dramatically. Moreover, the development project was intended to yield maximum durability through the use of a steam protective layer. Furthermore, sputtering was used to overcome processing challenges that have hampered P-SOEC development, while the low-temperature operation goal of 500 °C was expected to aid in mitigating thermally activated long-term degradation. The approach to high-performance, lower-temperature SOECs leveraged our existing SOFC Ni-cermet anode support and extensive thin-film sputtering layer-deposition experience. Rather than an all-in-one, reversible fuel cell approach which has many unacceptable tradeoffs, we focused on the many benefits to hydrogen generating SOECs, including the existence of synergies for reduced manufacturing costs (e.g., SOECs and SOFCs share supporting layers and overall manufacturing processing). The end result of this project was expected to increase current performance at 500 °C from approximately 0.8 A/cm 2 (at 60% Faradaic efficiency) at 1.4 V to > 1 A/cm 2 (at > 95% Faradaic efficiency) with a > 40% reduction in system cost and to enable operation of P-SOECs in steam contents >> 20% for a goal of a > 40,000 hours lifetime. To enable 500 °C operation in a very high steam atmosphere (> 20%), we proposed the use of a sputtered dense thin film (~0.1-1 µm thick) of high-stability Ba(Zr,Y)O 3 (BZY) to protect the Ba(Ce,Zr,Y,Yb)O 3 (BCZYYb) electrolyte. The BZCYYb, in turn, blocks the hole conductivity of the BZY to boost Faradaic efficiency. As FE increases, more of the consumed electricity is used in electrolysis to generate H 2 , rather than being shunted. Additionally, as cell resistance decreases, the voltage required to maintain current decreases, as well as the power required to generate the same amount of H 2 . With the proposed enhancements, these two factors result in the final 46% decrease in power needed to run the system. Likewise, a production rate of 50,000 kg H 2 /day will require 55% less active area, such that a system will need only 650 cells for an 80 cm 2 active area instead of ~1,440. Taking the 2016 DOE projected current cost and modifying the electricity cost and linearly scaling the other costs (except thermal feedstock) based on the cell area improvement, results in a 44% decrease in lifetime system cost, or a decrease from $\$$4.95/kg H 2 to $\$$2.75/kg H 2 . This is well below the 2018 DOE target of $\$$4/kg H 2 . The results from this project showed that we can create a P-SOEC with enhanced steam stability using two different electrolytes (i.e., one on top of the other) and achieve sufficiently low area specific resistance (ASR) to achieve the target performance. Unfortunately, due to extended delays at the beginning of the project and related supply chain and equipment access issues, we were not able to completely show increased Faradaic efficiency for the P-SOEC and therefore were unable to demonstrate the full proof of concept within the first budget period budget. While there are still challenges that remain to be solved, significant progress was made during this project and the concept still has merit that warrants further development.