Here, an improved hydrothermal synthesis for shape-controlled, size-controlled 60 nm SrTiO 3 nanocuboid (STO NC) supports, which facilitates the scalable creation of platinum nanoparticles catalyst supported on STO (Pt/STO) for the chemical conversion of waste polyolefins, is reported herein. This synthetic method: 1) produces STO NC supports with average sizes ranging from 25 – 80 nm with narrow size distributions 2) demonstrates how SrCO 3 formation and variation in solution pH prevent the formation of STO NCs, and 3) establishes that STO nucleation prior to the hydrothermal treatment favors nanocuboid formation. The updated hydrothermal synthesis was scaled-up and conducted in a 4L batch reactor, resulting in STO NCs of comparable size and morphology (m = 22.5 g, d avg = 58.6 ± 16.2 nm) to those synthesized under standard hydrothermal conditions in a lab-scale 125 mL autoclave reactor. Size-controlled STO NCs, ranging in roughly 10 nm increments from the 25 nm to 80 nm, were used to support Pt deposited through strong electrostatic adsorption (SEA), a practical and scalable solution-based method. Using SEA techniques and a STO support with an average size of 39.3 ± 6.3 nm, a Pt/STO catalyst with 3.6 wt% Pt was produced and used for high-density polyethylene hydrogenolysis under previously-reported conditions (170 psi H 2 , 300°C, 96h; final product: M w = 2400, Ð = 1.03). As a well-established model system for studying the behavior of heterogeneous catalysts and their supports in reactions, the Pt/STO system detailed in this work presents a unique opportunity to simultaneously convert waste plastic into commercially-viable products while gaining fundamental insight into the mechanism of polyethylene hydrogenolysis.
37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗