Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

At least 667 records · Page 37
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

Drying and Analysis of Aluminum (Oxy)hydroxide Films for Dry Storage of Aluminum-Clad Spent Nuclear Fuels

In aluminum-clad spent nuclear fuels, an (oxy)hydroxide layer on the surface of the cladding hosts chemisorbed water formed during reactor and post-discharge exposure to water. Any residual water is susceptible to generating hydrogen via radiolysis, which can be a risk associated with dry fuel storage. Engineering-scale forced helium dehydration (FHD) and vacuum drying tests were conducted on mock-up fuel assemblies that included corroded aluminum surrogate plates to assess the removal of bulk and chemisorbed water. Thermogravimetric analysis was performed on samples of the surrogate plates, both undried control samples used to determine onset temperatures associated with a phase change occurring in the oxide layer and samples from drying tests used to determine the effectiveness of each drying method. Both vacuum drying and FHD processes were capable of removing bulk water. However, FHD was determined to provide additional drying capabilities, including partial removal of chemisorbed water from bayerite due to the higher temperatures during drying. In conclusion, the temperature threshold for partial dehydroxylation of the oxide layer was determined to be around 220°C, meaning any drying methods attempting to remove chemisorbed water must exceed 220°C.

chemisorbed water↗
NASA NTRSDate not supplied

Foreign Object Damage in Ytterbium Disilicate Based Environmental Barrier Coatings Modified for Oxidation Resistance

Environmental barrier coatings (EBCs) have been developed as an enabling technology for silicon carbide based ceramic matrix composites (CMCs) in gas turbine engines. Two of the key failure mechanisms identified in EBC systems are foreign object damage (FOD) and the oxidative growth of a SiO 2 thermally grown oxide (TGO) layer that can lead to premature coating spallation. Previously the effects of FOD on NASA’s ytterbium disilicate based EBC were studied and recently it was shown that the addition of oxide modifiers resulted in improved oxidation resistance in the EBC. This work will compare FOD of the baseline ytterbium disilicate EBC to that of the modified EBC. FOD was performed at room temperature using a 1.59 mm hardened steel ball with projectile velocities of 50-300 m/s. Additionally, the effects of oxidation via cyclic steam exposure prior to impact were investigated.

foreign object damage (FOD)↗
NASA NTRS1981

Creep and residual mechanical properties of cast superalloys and oxide dispersion strengthened alloys

Tensile, stress-rupture, creep, and residual tensile properties after creep testing were determined for two typical cast superalloys and four advanced oxide dispersion strengthened (ODS) alloys. The superalloys examined included the nickel-base alloy B-1900 and the cobalt-base alloy MAR-M509. The nickel-base ODS MA-757 (Ni-16CR-4Al-0.6Y2O3 and the iron-base ODS alloy MA-956 (Fe-20Cr-5Al-0.8Y2O3) were extensively studied, while limited testing was conducted on the ODS nickel-base alloys STCA (Ni-16Cr-4.5Al-2Y2O3) with a without Ta and YD-NiCrAl (Ni-16Cr-5Al-2Y2O3). Elevated temperature testing was conducted from 114 to 1477 K except for STCA and YD-NiCrAl alloys, which were only tested at 1366 K. The residual tensile properties of B-1900 and MAR-M509 are not reduced by prior creep testing (strains at least up to 1 percent), while the room temperature tensile properties of ODS nickel-base alloys can be reduced by small amounts of prior creep strain (less than 0.5 percent). The iron-base ODS alloy MA-956 does not appear to be susceptible to creep degradation at least up to strains of about 0.25 percent. However, MA-956 exhibits unusual creep behavior which apparently involves crack nucleation and growth.

Whittenberger, J. D.↗
NASA NTRSDate not supplied

Hybrid Suitcase Demonstrator

The need for a small, transportable hybrid motor used to demonstrate and test various hybrid propulsion concepts was identified. Demonstrations would be for public audiences to explain basic hybrid rocket concepts. Tests would be for scientific purposes and hands-on training of engineers. Funded by Technical Excellence and NESC, the system as a whole has served as a learning tool for the NASA project cycle. Coming out of the Preliminary Design Review (PDR), the project was split into two separate configurations, one for demonstrations and one for tests; each would have its own oxidizer feed system. The Demonstration system will be a simple, low pressure system with the ability to recycle for multiple motor firings. The grain design will be a fixed configuration for all firings and utilize a clear material such that the combustion process is visible. The Test Readiness Review has been held and final actions are being pursued before the initial firing.

hybrid rocket↗
NASA NTRS1990

Test Results of the Modified Space Shuttle Main Engine at the Marshall Space Flight Center Technology Test Bed Facility

A modified space shuttle main engine (SSME), which primarily includes an enlarged throat main combustion chamber with the acoustic cavities removed and a main injector with the stability control baffles removed, was tested. This one-of-a-kind engine's design changes are being evaluated for potential incorporation in the shuttle flight program in the mid-1990's. Engine testing was initiated on September 15, 1988 and has accumulated 1,915 seconds and 19 starts. Testing is being conducted to characterize the engine system performance, combustion stability with the baffle-less injector, and both low pressure oxidizer turbopump (LPOTP) and high pressure oxidizer turbopump (HPOTP) for suction performance. These test results are summarized and compared with the SSME flight configuration data base. Testing of this new generation SSME is the first product from the technology test bed (TTB). Figure test plans for the TTB include the highly instrumented flight configuration SSME and advanced liquid propulsion technology items.

Cook, J.↗
DOE OSTI2023

Oxidative instability of ionomers in hydroxide-exchange-membrane water electrolyzers

Hydroxide-exchange membrane (HEM) electrolyzers can produce green H 2 with only earth-abundant catalysts and electrolyte-free (nominally pure) water feed, significantly decreasing system cost and complexity. However, HEM technology suffers from short lifetimes, attributed in part to poor stability of anion-exchange polymers used in the membrane and catalyst layers. We use electrochemical analysis and ex situ characterization techniques to study anion-exchange-polymer degradation in electrolyzers. Using multiple ionomers, catalyst-layer additives, and electrolyte feed, we show how anode-ionomer oxidation is the dominant degradation mechanism for all HEM-based electrolyzer cells tested. Here, we find improved device stability using oxidation-resistant catalyst-layer binders and propose new design strategies for advanced ionomer and catalyst-layer development.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
NASA NTRS1995

Metallized Gelled Propellants: Oxygen/RP-1/aluminum Rocket Combustion Experiments

A series of combustion experiments were conducted to measure the specific impulse, Cstar-, and specific-impulse efficiencies of a rocket engine using metallized gelled liquid propellants. These experiments used a small 20- to 40-1bf (89- to 178-N) thrust, modular engine consisting of an injector, igniter, chamber and nozzle. The fuels used were traditional liquid RP-1 and gelled RP-1 with 0-, 5-, and 55-wt% loadings of aluminum and gaseous oxygen was the oxidizer. Ten different injectors were used during the testing: 6 for the baseline 02/RP-1 tests and 4 for the gelled fuel tests which covered a wide range of mixture ratios. At the peak of the Isp versus oxidizer-to-fuel ratio (O/F) data, a range of 93 to 99% Cstar efficiency was reached with ungelled 02/RP-1. A Cstar efficiency range of 75 to 99% was obtained with gelled RP-l (0-wt% RP-1/Al) while the metallized 5-wt% RP-1/Al delivered a Cstar efficiency of 94 to 99% at the peak Isp in the O/F range tested. An 88 to 99% Cstar efficiency was obtained at the peak Isp of the gelled RP1/Al with 55-wt% Al. Specific impulse efficiencies for the 55-wt% RP-1/Al of 67%-83% were obtained at a 2.4:1 expansion ratio. Injector erosion was evident with the 55-wt% testing, while there was little or no erosion seen with the gelled RP-1 with 0- and 5-wt% Al. A protective layer of gelled fuel formed in the firings that minimized the damage to the rocket injector face. This effect may provide a useful technique for engine cooling. These experiments represent a first step in characterizing the performance of and operational issues with gelled RP-1 fuels.

Palaszewski, Bryan↗
DOE OSTI2024

Summary of Gas Generation Behavior Observed in 3013 Surveillance and Monitoring Program Shelf-Life Experiments

Gas generation experiments have been conducted in small- and full-scale test containers at Los Alamos National Laboratory on samples of plutonium oxide material collected from plutonium processes across the DOE complex and tested at the bounding conditions for the Department of Energy 3013 Standard. The gas composition and pressures in the sealed experimental containers were measured over periods of months to years. These experiments have provided results for the formation and consumption of hydrogen and other gases. The conditions supporting the formation of flammable gas mixtures of hydrogen and oxygen in flammable gas mixtures were also determined. Different behaviors were observed between the materials tested based on their compositions, the stabilization performed on the material, and the post stabilization handling of the material. Many of the experiments are still ongoing. This report summarizes the results obtained for the gas generation behavior for high-purity plutonium oxides and salt-bearing impure plutonium oxides in sealed containers.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗
NASA NTRS1989

Carbon dioxide and water vapor high temperature electrolysis

The design, fabrication, breadboard testing, and the data base obtained for solid oxide electrolysis systems that have applications for planetary manned missions and habitats are reviewed. The breadboard tested contains sixteen tubular cells in a closely packed bundle for the electrolysis of carbon dioxide and water vapor. The discussion covers energy requirements, volume, weight, and operational characteristics related to the measurement of the reactant and product gas compositions, temperature distribution along the electrolyzer tubular cells and through the bundle, and thermal energy losses. The reliability of individual cell performance in the bundle configuration is assessed.

Isenberg, Arnold O.↗
NASA NTRS1989

Product assurance technology for procuring reliable, radiation-hard, custom LSI/VLSI electronics

Advanced measurement methods using microelectronic test chips are described. These chips are intended to be used in acquiring the data needed to qualify Application Specific Integrated Circuits (ASIC's) for space use. Efforts were focused on developing the technology for obtaining custom IC's from CMOS/bulk silicon foundries. A series of test chips were developed: a parametric test strip, a fault chip, a set of reliability chips, and the CRRES (Combined Release and Radiation Effects Satellite) chip, a test circuit for monitoring space radiation effects. The technical accomplishments of the effort include: (1) development of a fault chip that contains a set of test structures used to evaluate the density of various process-induced defects; (2) development of new test structures and testing techniques for measuring gate-oxide capacitance, gate-overlap capacitance, and propagation delay; (3) development of a set of reliability chips that are used to evaluate failure mechanisms in CMOS/bulk: interconnect and contact electromigration and time-dependent dielectric breakdown; (4) development of MOSFET parameter extraction procedures for evaluating subthreshold characteristics; (5) evaluation of test chips and test strips on the second CRRES wafer run; (6) two dedicated fabrication runs for the CRRES chip flight parts; and (7) publication of two papers: one on the split-cross bridge resistor and another on asymmetrical SRAM (static random access memory) cells for single-event upset analysis.

Buehler, M. G.↗
NASA NTRS1978

Static and dynamic cyclic oxidation of 12 nickel-, cobalt-, and iron-base high-temperature alloys

Twelve typical high-temperature nickel-, cobalt-, and iron-base alloys were tested by 1 hr cyclic exposures at 1038, 1093, and 1149 C and 0.05 hr exposures at 1093 C. The alloys were tested in both a dynamic burner rig at Mach 0.3 gas flow and in static air furnace for times up to 100 hr. The alloys were evaluated in terms of specific weight loss as a function of time, and X-ray diffraction analysis and metallographic examination of the posttest specimens. A method previously developed was used to estimate specific metal weight loss from the specific weight change of the sample. The alloys were then ranked on this basis. The burner-rig test was more severe than a comparable furnace test and resulted in an increased tendency for oxide spalling due to volatility of Cr in the protective scale and the more drastic cooling due to the air-blast quench of the samples. Increased cycle frequency also increased the tendency to spall for a given test exposure. The behavior of the alloys in both types of tests was related to their composition and their tendency to form scales. The alloys with the best overall behavior formed alpha-Al2O3 aluminate spinels.

Barrett, C. A.↗
DOE OSTI2025

Metal-Insulation REBCO Pancake Coil With Solder Surface Shunt: Testing and Modeling

Rare-earth barium copper oxide (REBCO) high-temperature superconducting (HTS) magnets can generate very high magnetic fields with superior engineering current density and robust mechanical integrity. The no-insulation (NI) winding technique, including its metal-insulation (MI) variant, enables “self-protection” against localized overheating through inter-turn current sharing, improving defect tolerance and allowing temporary current overloads. In REBCO pancake coils, the current-sharing path is predominantly confined to the edges of the REBCO tapes due to insulating buffer layers. Applying a surface shunt using solder can effectively enhance current sharing in NI/MI coils via the REBCO tape edges. Here, in this paper, we present both experimental and numerical research on the current distribution in surface-shunt metal-insulation (SSMI) REBCO pancake coils. We tested a stainless steel co-wound MI REBCO double-pancake coil, before and after applying a soldered surface shunt, in a saturated liquid nitrogen bath. The SSMI coil was modeled using the H-formulation and rotated anisotropic resistivity to study its dynamic behavior, including inter-turn current sharing and intra-turn screening currents. Benchmarked by experimental data, the numerical model is able to study the defect tolerance of the SSMI coil during energization.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗
NASA NTRS2009

Lightning Pin Injection Testing on MOSFETS

Lightning transients were pin-injected into metal-oxide-semiconductor field-effect transistors (MOSFETs) to induce fault modes. This report documents the test process and results, and provides a basis for subsequent lightning tests. MOSFETs may be present in DC-DC power supplies and electromechanical actuator circuits that may be used on board aircraft. Results show that unprotected MOSFET Gates are susceptible to failure, even when installed in systems in well-shielded and partial-shielded locations. MOSFET Drains and Sources are significantly less susceptible. Device impedance decreased (current increased) after every failure. Such a failure mode may lead to cascading failures, as the damaged MOSFET may allow excessive current to flow through other circuitry. Preliminary assessments on a MOSFET subjected to 20-stroke pin-injection testing demonstrate that Breakdown Voltage, Leakage Current and Threshold Voltage characteristics show damage, while the device continues to meet manufacturer performance specifications. The purpose of this research is to develop validated tools, technologies, and techniques for automated detection, diagnosis and prognosis that enable mitigation of adverse events during flight, such as from lightning transients; and to understand the interplay between lightning-induced surges and aging (i.e. humidity, vibration thermal stress, etc.) on component degradation.

Ely, Jay J.↗
NASA NTRS1974

Nuclear weapons tests and short-term effects on atmospheric ozone

Observations made when Nimbus 4 passed over a nuclear cloud about three hours after the bomb exploded are presented. Infrared and BUV measurements indicated that the atmospheric ozone level in the area of cloud was significantly less than in areas directly north and south of the cloud. It is noted, however, that it is not possible to state definitively that the ozone depletion was caused by nitrogen oxides released in the nuclear weapons test, and that further observations must be made to clarify the situation.

Miller, A. J.↗
NASA NTRSDate not supplied

Atomic Oxygen Environment and Effects Overview

Atomic oxygen is the most predominant constituent in the low Earth orbital environment between the altitudes of 180 and 650 km. It is also a major constituent of the Mars orbital environment. It is very chemically reactive and can oxidize many spacecraft surfaces to form volatile reaction products. The importance of understanding atomic oxygen reactions with materials has led to both flight experiments in low Earth orbit and ground-based testing in vacuum chambers containing atomic oxygen to study its’ effect on materials. Testing has been performed in order to determine the extent of the atomic oxygen reaction and assess material and component durability. In addition, the effectiveness of mitigation techniques such as application of a protective coating, adding fillers, or using shielding and getter materials has also been studied both in flight and ground-based experiments. This presentation will focus on defining atomic oxygen environments, discussing its effect on spacecraft materials, and describing some of the testing and mitigation techniques that have been investigated.

Atomic Oxygen, Low Earth Orbit, Low Mars Orbit, ox↗
NASA NTRS1993

Thermal coatings for titanium-aluminum alloys

Titanium aluminides and titanium alloys are candidate materials for use in hot structure and heat-shield components of hypersonic vehicles because of their good strength-to-weight characteristics at elevated temperature. However, in order to utilize their maximum temperature capability, they must be coated to resist oxidation and to have a high total remittance. Also, surface catalysis for recombination of dissociated species in the aerodynamic boundary layer must be minimized. Very thin chemical vapor deposition (CVD) coatings are attractive candidates for this application because of durability and very light weight. To demonstrate this concept, coatings of boron-silicon and aluminum-boron-silicon compositions were applied to the titanium-aluminides alpha2 (Ti-14Al-21Nb), super-alpha2 (Ti-14Al-23-Nb-2V), and gamma (Ti-33Al-6Nb-1Ta) and to the titanium alloy beta-21S (Ti-15Mo-3Al-3Nb-0.2Si). Coated specimens of each alloy were subjected to a set of simulated hypersonic vehicle environmental tests to determine their properties of oxidation resistance, surface catalysis, radiative emittance, and thermal shock resistance. Surface catalysis results should be viewed as relative performance only of the several coating-alloy combinations tested under the specific environmental conditions of the LaRC Hypersonic Materials Environmental Test System (HYMETS) arc-plasma-heated hypersonic wind tunnel. Tests were also conducted to evaluate the hydrogen transport properties of the coatings and any effects of the coating processing itself on fatigue life of the base alloys. Results are presented for three types of coatings, which are as follows: (1) a single layer boron silicon coating, (2) a single layer aluminum-boron-silicon coating, and (3) a multilayer coating consisting of an aluminum-boron-silicon sublayer with a boron-silicon outer layer.

Cunnington, George R.↗
NASA NTRS1997

10,000-Hour Cyclic Oxidation Behavior at 982 C (1800 F) of 68 High-Temperature Co-, Fe-, and Ni-Base Alloys

Sixty-eight high temperature Co-, Fe-, and Ni-base alloys were tested for 10-one thousand hour cycles in static air at 982 C (1800 F). The oxidation behavior of the test samples was evaluated by specific weight change/time data, x-ray diffraction of the post-test samples, and their final appearance. The gravimetric and appearance data were combined into a single modified oxidation parameter, KB4 to rank the cyclic oxidation resistance from excellent to catastrophic. The alloys showing the 'best' resistance with no significant oxidation attack were the alumina/aluminate spinel forming Ni-base turbine alloys: U-700, NASA-VIA and B-1900; the Fe-base ferritic alloys with Al: TRW-Valve, HOS-875, NASA-18T, Thermenol and 18SR; and the Ni-base superalloy IN-702.

Barrett, Charles A.↗