Samples harvested from an HT-9 fuel test assembly (ACO-3) irradiated for six years in the Fast Flux Test Facility (FFTF) reaching 2–147 dpa at 382–504°C were deformed in-situ while collecting high-energy X-ray diffraction data to monitor microstructure evolution. With the initiation of plastic deformation, all samples exhibited a clear load transfer from the ferrite matrix to carbide particulate. This behavior was confirmed by modeling of the control material. The evolution of dislocation density in the material as a result of deformation was characterized through full pattern line profile analysis. The dislocation densities increased substantially after deformation, the level of dislocation evolution observed was highly dependent upon the irradiation temperature of the sample. The differences in both the yield and hardening behavior between samples irradiated at higher and lower temperatures suggest the existence of a transition in tensile behavior at an irradiation temperature near 420°C dividing regions of distinct damage effects.
Not provided.
Not Available
Not Available
Not Available
Highlights: • Al-containing Zn coating improved Mg–steel interfacial wettability during friction stir spot welding (FSSW). • Pre-existing Al{sub 5}Fe{sub 2} phase in coating on steel surface promoted Mg–steel metallurgical bonding. • A high tensile-shear load of 4.3 kN was obtained in FSSW AZ31–steel joint. - Abstract: 2.4 mm thick AZ31 Mg alloy sheet and 1.5 mm Q234 steel sheet with a hot-dipped Al-containing Zn coating were friction stir spot welded (FSSW) using a pinless tool. It was shown that the Al-containing Zn coating played a crucial role in joining the Mg alloy and steel during FSSW. The Zn coating observably improved the Mg–steel interfacial wettability during FSSW, and the Al{sub 5}Fe{sub 2} phase in the Zn coating on the steel substrate surface promoted the metallurgical bonding of Mg alloy and steel. It was confirmed that the Al{sub 5}Fe{sub 2} phase on the steel surface resulted from the reaction between the steel substrate and the Al in the Zn coating during hot-dipping, and was not related to the Al-containing Mg alloy substrate. The tensile-shear load of the FSSW Mg–steel joint reached 4.3 kN. The fracture of the joint occurred along the interface on the steel substrate side. The interface between the Al{sub 5}Fe{sub 2} layer and Mg alloy substrate was the weakest region of the Mg–steel joint.
Microstructural analyses and micro-pillar compression were conducted on 14YWT nanostructured ferritic alloy (NFA) to compare different processing pathways: hydrostatic extrusion and Pilger processing with varying annealing temperatures into thin walled tubing, and after hot extrusion and cross-rolling into a plate. Hydrostatic extrusion at 815 °C resulted in the smallest grain sizes and highest yield strength of 1.20 GPa. Pilger processing with annealing at 800 °C had fine grained regions and bands of coarse grains, leading to a large variation in yield strength of 0.9–1.40 GPa. Higher annealing temperatures of 1200 °C after pilger processing significantly increased the grain size and lowered the yield strength to 1.01 GPa. These tubes showed a stronger (111) crystallographic texture in the normal direction and elongated grains in the extrusion direction. Characterization of the nano-oxides using TEM reveals more numerous, smaller oxides present in tubing processed at lower temperatures. Overall, this work shows NFA tubing after hydrostatic extrusion and pilger processing can lead to fine grained microstructures and texturing leading to higher yield strengths at lower annealing temperatures (e.g. 800 °C).