Results for “H2 production” — Page 35

DOE OSTI2025

A dual promotional effect of doping tantalum (Ta) in atomically dispersed Ru/CeO 2 catalyst toward CO 2 methanation: Enhanced associative adsorption of CO 2 and activation of H 2

Precisely controlling the product selectivity in CO 2 hydrogenation through rational catalyst design presents a promising approach to mitigate environmental and energy-related challenges, though it remains a significant scientific hurdle. Herein, the CH 4 selectivity of 0.5 wt% Ru loaded catalysts at 250 °C was effectively shifted from approximately 35 % to 100 % through the incorporation of Ta dopant into the CeO 2 support. The EXAFS spectra in conjunction with CO DRIFTS experiment indicated the presence of atomically dispersed Ru particles anchored on the Ta-doped CeO 2 surface. A higher oxidized CeO 2 surface was evidenced in the presence of Ta dopant. The presence of Ta dopant also improved the dispersion of Ru species and their interaction with the support. Most importantly, the Ru/Ta-CeO 2 catalyst exhibited a pronounced capacity for associative CO 2 -adsorption under atmospheric pressure at 50 °C. An improved H 2 activation was also observed under CO 2 hydrogenation conditions. This novel finding of the dual promotional effect of Ta carries a significant impact in the field of CO 2 capture and utilization.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2025

Nanoscopic Plugs Block Hydrogen Crossover in Submicron Thick Proton-Conducting SiO 2 Membranes for Water Electrolysis

Zero-gap electrolyzers based on submicron thick proton-conducting oxide membranes (POMs) represent a promising approach to increasing the efficiency of H 2 production from water electrolysis while moving away from conventional perfluorosulfonic acid (PFSA) membranes. A critical barrier to the commercialization of such electrolyzers is that the ultrathin nature of POMs, which is necessary to achieve low cell resistance, makes them more susceptible to defects that can lead to unacceptably high rates of H 2 crossover. Herein, we demonstrate an approach to mitigate this problem through selective deposition of carbon-containing silicon oxide (SiO x C y ) “nanoplugs” into the defects of submicron thick SiO 2 membranes using a facile electrochemically mediated deposition process. Selective deposition of nanoplugs within the defects was verified by multiple characterization techniques, while scanning electrochemical microscopy (SECM) was used to confirm selective plugging of H 2 -crossover hotspots associated with defects at identical locations. Thanks to the use of nanoplugs, the H 2 permeance of 250 nm thick SiO 2 membranes was reduced by 5 to 6 orders of magnitude compared to the unmodified atomic layer deposition (ALD) SiO 2 membranes while having negligible impact on the ionic resistance of the membrane. These plug-modified membranes also enabled safe and stable operation of a zero-gap full cell electrolysis cell, in contrast to cells lacking nanoplugs that produced anode effluent streams having H 2 concentrations near or exceeding the lower flammability limit (LFL) of H 2 . Furthermore, beyond water electrolysis, this defect-sealing strategy has the potential to be broadly implemented in other applications, such as fuel cells and flow batteries, offering a versatile solution to mitigate crossover-related performance losses.

ALD SiO2↗