NASA NTRS1984

Polyimide characterization studies - Effect of pendant alkyl groups

The effect on selected polyimide properties when pendant alkyl groups were attached to the polymer backbone was investigated. A series of polymers were prepared using benzophenone tetracarboxylic acid dianhydride (BTDA) and seven different p-alkyl-m,p'-diaminobenzophenone monomers. The alkyl groups varied in length from C(1) (methyl) to C(9) (nonyl). The polyimide prepared from BTDA and m,p'-diaminobenzophenone was included as a control. All polymers were characterized by various chromatographic, spectroscopic, thermal, and mechanical techniques. Increasing the length of the pendant alkyl group resulted in a systematic decrease in glass transition temperature (Tg) for vacuum cured films. A 70 C decrease in Tg to 193 C was observed for the nonyl polymer compared to the Tg for the control. A corresponding systematic increase in Tg indicative of crosslinking, was observed for air cured films. Thermogravimetric analysis revealed a slight sacrifice in thermal stability with increasing alkyl length. No improvement in film toughness was observed.

Jensen, B. J.↗
NASA NTRS1984

Phosphorus-containing imide resins - Modification by elastomers

The syntheses and general features of addition-type maleimide resins based on bis(m-aminophenyl)phosphine oxide and tris(m-aminophenyl)phosphine oxide have been reported previously. These resins have been used to fabricate graphite cloth laminates having excellent flame resistance. These composites did not burn even in pure oxygen. However, these resins were somewhat brittle. This paper reports the modification of these phosphorus-containing resins by an amine-terminated butadiene-acrylonitrile copolymer (ATBN) and a perfluoroalkylene diaromatic amine elastomer (3F). An approximately two-fold increase in short beam shear strength and flexural strength was observed at 7 percent ATBN concentration. The tensile, flexural, and shear strengths were reduced when 18 percent ATBN was used. Anaerobic char yields of the resins at 800 C and the limiting oxygen indexes of the laminates decreased with increasing ATBN concentration. The perfluorodiamine (3F) was used with both imide resins at 6.4 percent concentration. The shear strength was doubled in the case of the bisimide with no loss of flammability characteristics. The modified trisimide laminate also had improved properties over the unmodified one. The dynamic mechanical analysis of a four-ply laminate indicated a glass transition temperature above 300 C. Scanning electron micrographs of the ATBN modified imide resins were also recorded.

Varma, I. K.↗
NASA NTRS1984

Polyimides containing oxyethylene units. II - Polymerization of 3.3', 4.4'-benzophenonetetra carboxylic dianhydride and pyromellitic dianhydride

The study is concerned with the polymerization of diamines 2a-d with readily available dianhydrides, i.e., 3,3',4,4'-benzophenonetetracarboxylic dianhydride (BTDA) and pyromellitic dianhydride (PMDA). The synthesis and polymerization of asymmetric diamines containing substituted alkylene ether linkages are also investigated. It is assumed that the flexibility introduced into the polymer chain through the use of such diamines would result in moderate glass transition temperatures that would allow the systems to be melt processed. Mixtures of diamines are also copolymerized so as to further disrupt the polymer's symmetry and recurrence regularity. The properties of the resulting polymers are briefly discussed.

Harris, F. W.↗
NASA NTRS1984

Ethynyl-terminated polyarylates - Synthesis and characterization

Hydroxy-terminated polyarylates (HTPA) with number-average molecular weights of approximately 2500, 5000, 7500, and 10,000 were synthesized and converted to corresponding 4-ethynylbenzoyloxy-terminated polyarylates (ETPA) by reaction with 4-ethynylbenzoyl chloride. The terminal ethynyl groups were thermally reacted to provide chain extension and crosslinking. The cured ETPA exhibited higher glass transition temperatures (Tg) and better solvent resistance than a high molecular weight linear polyarylate. Solvent resistance was further improved by curing 2,2-bis(4-ethynylbenzoyloxy-4-prime-phenyl) propane, a coreactant, with ETPA at concentrations of approximately 10 percent (w/w).

Havens, S. J.↗
NASA NTRS1985

Polyfunctional epoxies. I - Rubber-toughened brominated and nonbrominated formulations for graphite composites. II - Nonrubber versus rubber-toughened brominated formulations for graphite composites

A new trifunctional epoxy resin, Tris-(hydroxyphenyl) methane triglycidyl ether, is compared to a state-of-the-art tetraglycidyl 4,4'-diaminodiphenyl methane (TGDDM), in graphite composites. Rubber-toughened brominated formulations of the epoxy resin are compared to nonbrominated ones in terms of their mechanical performance, environmental stability, thermochemical behavior, and flame retardancy. It is shown that the new resin performs almost the same way as the TGDDM does, but has improved glass transition temperature and environmental properties. Brominated polymeric additives (BPA) of different molecular weights are tested as a Br source to flame retardant graphite epoxy composites. The optimal molecular weight of the BPA and its polymeric backbone length are derived and compared with a 10 percent rubber-toughened formulation of the epoxy resin. Results indicate that when the Br content in the graphite composite is increased without the use of rubber, the mechanical properties improved. The use of BPAs as tougheners for graphite composites is also considered.

Nir, Z.↗
NASA NTRS1985

Semi-2-interpenetrating polymer networks of high temperature systems

A semi-interpenetrating (semi-IPN) polymer system of the semi-2-IPN type is described in which a polymer of acetylene-terminated imidesulfone (ATPISO2) is cross linked in the presence of polyimidesulfone (PISO2). Six different formulations obtained by mixing of either ATPISO2-1n or ATPISO2-3n with PISO2 in three different proportions were characterized in terms of glass transition temperature, thermooxidative stability, inherent viscosity, and dynamic mechanical properties. Adhesive (lap shear) strength was tested at elevated temperatures on aged samples of adhesive scrim cloth prepared from each resin. Woven graphite (Celion 1000)/polyimide composites were tested for flexural strength, flexural modulus, and shear strength. The network polymers have properties intermediate between those of the component polymers alone, have greatly improved processability over either polyimide, and are able to form good adhesive bonds and composites, making the semi-2-IPN systems superior materials for aerospace structures.

Hanky, A. O.↗
NASA NTRS1985

Fractography of the interlaminar fracture of carbon-fibre epoxy composites

The failed surfaces of interlaminar fracture (mode I) specimens of AS4/3501-6 were examined using scanning electron microscopy. The principal fracture features were fiber pull-out (bundles and single fibers), hackle markings, and regions of smooth resin fracture. Considerable (30 to 50 percent) relaxation of the deformed resin occurred when the specimens were heated above the matrix glass transition temperature. This relaxation was taken as evidence of extensive shear yielding of the resin during the fracture process. Some of the fractography features are discussed in terms of transverse tensile stresses and peeling stresses acting on the fibers. In some instances these localized stresses focus failure close to the resin-fiber interface, which can be mistakenly interpreted as interfacial failure and low fiber-resin adhesion.

Bascom, W. D.↗
NASA NTRS1985

PMR polyimides from solutions containing mixed endcaps

Previous studies have shown that partial substitution of p-aminostyrene (PAS) for the monomethylester of endo-5-norbornene-2, 3-dicarboxylic acid (NE) lowered the cure temperature of PMR polyimides from 316 to 260 C, but the modified PMR polyimides required higher compression-molding pressures than state-of-the-art PMR-15. In this study PMR polyimides are prepared employing three encaps: NE, PAS, and endo-N-phenyl-5-norbornene-2,3-dicarboximide (PN). The effect of PN addition on the processing characteristics and glass transition temperatures of graphite fiber-reinforced PMR composites is studied. The room temperature and short-time 316 C mechanical properties of the composites are determined. The weight loss and mechanical property retention characteristics of the composites after exposure in air at 316 C are also determined.

Delvigs, P.↗
NASA NTRS1985

Rheological, processing, and 371 deg C mechanical properties of Celion 6000/N-phenylnadimide modified PMR composites

The rheology, processing, and chemistry of newly developed N-phenylnadimide modified PMR (PMR-PN) polyimide resins are reviewed. The 371 C performance of their composites reinforced with Celion 6000 graphite fibers is also reviewed, along with the state of the art Celion 6000/PMR-15 composite. The effects of the 371 C exposure in air for up to 300 hr on the composite glass transition temperature, weight loss characteristics, and dimensional stability are presented. The changes in the composite 371 C interlaminar shear and flexural properties are also presented. In addition, composite interfacial degradation at a function of exposure time at 371 C was followed by scanning electron microscopy. The results suggest that the composite materials can be used at 371 C for at least 100 hr.

Pater, R. H.↗
NASA NTRS1985

The 371 deg C mechanical properties of graphite/polyimide composites

A series of condensation polyimides based on pyromellitic dianhydride is synthesized and evaluated for potential application at 371 C. Several three-and four-ring benzenoid diamine systems containing oxygen bridging groups are investigated. Thermomechanical analysis of neat resin specimens indicate that the polyimide prepared from the dimethyl ester of pyrometallitic acid (PMDE) and 2,2-bis4-(4'-aminophenoxy) phenyl]-1,1,1,3,3,3- hexafluoropropane (BDAF) is the only resin system which has a glass transition temperature (Tg) above 371 C. The Tg of the PMDE/BDAF polyimide is found to be 390 C after a postcure air at 371 C for 24 hr. Unidirectional composites are fabricated from the PMDE/BDAF system and unsized Celion 6000 graphite fibers. Final cure temperatures in the range of 371 to 427 C with an applied pressure of 10.34 to 13.78 MPa are investigated. The void content of the composites ranges from 4.6 to 8.6 percent. Composites cured at 399 C under a pressure of 10.34 MPa and postcured in air at 371 C for 24 hr exhibit the highest 371 C interlaminar shear strength (ILSS, 40.7 MPa) and flexural strength (758 MPa). The thermo-oxidative stability of the composites is determined by subjecting specimens to isothermal exposure at 371 C in air at atmospheric pressure, as well as a pressure of 0.52 MPa. Specimens exposed at atmospheric pressure exhibit a weight loss of 12 percent after 200 hr of exposure and 88 percent retention of its original 371 C ILSS. In contrast, the specimens exposed at 0.52 MPa pressure exhibit a comparable weight loss after only 72 hr, and a 71 percent retention of its original 371 C ILSS.

Delvigs, P.↗
NASA NTRS1985

Optically transparent/colorless polyimides

Several series of linear aromatic polyimide films have been synthesized and characterized with the objective of obtaining maximum optical transparency. Two approaches have been used as part of this structure-property relationship study. The first approach is to vary the molecular structure so as to separate chromophoric centers and reduce electronic interactions between polymer chains to lower the intensity of color in the resulting polymer films. A second and concurrent approach is to perform polymerizations with highly purified monomers. Glass transition temperatures of thermally cured polyimide films are obtained by thermomechanical analysis and thermal decomposition temperatures are determined by thermogravimetric analysis. Transmittance UV-visible spectra of the polyimide films are compared to that of a commercial polyimide film. Fully imidized films are tested for solubility in common organic solvents. The more transparent films prepared in this study are evaluated for use on second-surface mirror thermal control coating systems. Lightly colored to colorless films are characterized by UV-visible spectroscopy before and after exposure to 300 equivalent solar hours UV irradiation and varying doses of 1 MeV electron irradiation. The effects of monomer purity, casting solvent and cure atmosphere on polyimide film transparency are also investigated.

Stclair, A. K.↗
NASA NTRS1986

Adhesive evaluation of thin films of LARC-TPI and LARC-TPI with 5 mol % ODA

A commercially available LARC-TPI film and an experimentally prepared film of LARC-TPI with 5 mol % of 4,4'-oxydianiline (ODA), designated as LARC-TPI/ODA in the report, supplied by Mitsui Toatsu Chemicals, Incorporated (MTCI), Japan, were evaluated as thermoplastic adhesive films for bonding Ti-6Al-4V. The LARC-TPI/ODA had been shown by MTCI to possess more flow than thermoplastic LARC-TPI and was, therefore, evaluated and compared to the LARC-TPI. Lap shear strength was used to evaluate the materials as adhesives. They were characterized after fracture by determining the glass transition temperature, Tg. The mode of failure was also reported. Thermal exposure at 204C for 500 and 1000 hrs and a 72-hour water-boil were conducted on lap shear specimens prepared with the two adhesive films. Lap shear tests were conducted at RT, 177C, 204C, and 232C before and after exposures.

Progar, D. J.↗
NASA NTRS1986

Effect of annealing history on free volume in thermoplastics

Two different types of thermoplastic glassy polymers have been investigated for the effects of thermal annealing on their free volumes. It has been observed that free volumes in glassy polymers decrease asymptotically to a steady level after about four thermal anneals lasting for 24 hours at a temperature about 50 C below their glass transition temperatures. These results indicate that composites incorporating properly annealed thermoplastic matrices may not experience any additional internal stresses due to subsequent thermal excursions experienced while in service.

Singh, J. J.↗
NASA NTRS1986

Structure-to-property Relationships in Addition Cured Polymers 2: Resin Tg Composite Initial Mechanical Properties of Norbornenyl Cured Polyimide Resins

PRM (polymerization of monomeric reactants) methodology was used to prepare thirty different polyimide oligomeric resins. Monomeric composition as well as chain length between sites of crosslinks were varied to examine their effects on glass transition temperature (Tg) of the cured/postcured resins. An almost linear correlation of Tg versus molecular distance between the crosslinks was observed. An attempt was made to correlate Tg with initial mechanical properties (flexural strength and interlaminar shear strength) of unidirectional graphite fiber composites prepared with these resins. However, the scatter in mechanical strength data prevented obtaining as clear a correlation as was observed for the structural modification/crosslink distance versus Tg. Instead, only a range of composite mechanical properties was obtained at the test temperatures studied (room temperature, 288 and 316 C). Perhaps more importantly, what did become apparent during the attempted correlation study was: (1) that PMR methodology could be used to prepare composites from resins that contain a wide variety of monomer modifications, and (2) that these composites almost invariably provided satisfactory initial mechanical properties as long as the resins selected were melt processable.

Alston, W. B.↗
NASA NTRS1985

Effect of substituted phenylnadimides on processing and properties of PMR polyimide composites

Three nitrophenylnadimide cure initiators and two phenylnadimides (without nitros) were evaluated as additives to PMR-15 resins and Celion 6000 graphite fiber composites. The results of a resin screening study eliminated all of the additives except 3-nitrophenylnadimide (NO2PN) for use as a low temperature curing additive for PMR-15. Thus, NO2PN and the two control additives were investigated in PMR-15 formulations from which Celion 6000 graphite fiber/PMR-15 composites were processed both with low temperature (274 C) and normal (316 C) cure cycles. Comparisons of the two processing cycles, the resultant glass transition temperatures (Tg), the ambient, 274 and 316 C composite mechanical properties determined before and after 316 C postcure, the 316 C thermo-oxidative weight losses and the retention of 316 C composite mechanical properties are presented. Empirical correlations of the type and amount of nadimide additives with processing parameters, Tg, composite mechanical properties, composite thermo-oxidative stability and long term retention of 316 C composite mechanical properties are also presented.

Alston, W. B.↗
NASA NTRS1986

Adhesive evaluation of LARC-TPI and a water-soluble version of LARC-TPI

The results of a study to evaluate two Langley Research Center thermoplastic polimide (TPI) materials, identified as TPI/MTC for the material from Mitsui Toatsu Chemicals Inc. and TPI/H2O for the material from United Technologies Research Center, as high temperature thermoplastic adhesives and primers for bonding titanium (6AL-4V) adherends are discussed. A limited characterization of the materials was performed using a Diffuse Reflectance-Fourier Transform Infrared Spectroscopy (DR-FTIR) technique. Thermomechanical Analysis (TMA) and torsional braid techniques were used to determine glass transition temperature. The adhesive's strength, as determined by simple lap shear tests, was used to evaluate the effects of long term thermal exposure (up to 1000 hrs) at 204 deg C and a 72-hour water-boil.

Progar, D. J.↗
NASA NTRS1986

Tetraglycidyl epoxy resins and graphite fiber composites cured with flexibilized aromatic diamines

Studies were performed to synthesize new ether modified, flexibilized aromatic diamine hardeners for curing epoxy resins. The effect of moisture absorption on the glass transition temperatures of a tetraglycidyl epoxy, MY 720, cured with flexibilized hardeners and a conventional aromatic diamine was studied. Unidirectional composites, using epoxy-sized Celion 6000 graphite fiber as the reinforcement, were fabricated. The room temperature and 300 F mechanical properties of the composites, before and after moisture exposure, were determined. The Mode I interlaminar fracture toughness of the composites was characterized using a double cantilever beam technique to calculate the critical strain energy release rate.

Delvigs, P.↗
NASA NTRS1987

Thermomechanical Properties Indicate Degree of Epoxy Cure

Glass-transition temperature and density increase as reaction proceeds. Cured epoxy resin found to be related to extent of cure. In addition to providing insight into chemical reactions of curing, relationships show potential for process monitoring and control in fabrication of strong, lightweight composite parts.

Cizmecioglu, Muzaffer↗