An extensive characterization of Bi-Sr-Ca-Cu-O (BSCCO) thin films deposited by co-evaporation on LaAlO3 and SrTiO3 substrates was performed. The films had a T(sub c) (R = O) of approximately 78 K, and were predominantly c-axis oriented, with critical current densities (J(sub c)) at 4.5 K of 1.6 x 10(exp 6) and 1.1 x 10(exp 6) A cm(sup -2), for the samples on SrTiO3 and LaAlO3, respectively. The microwave properties of the films were examined by three techniques. The complex conductivity sigma(sub *) = sigma(sub 1) - j(sigma(sub 2)) and the magnetic penetration depth (A) were measured by power transmission at 30.6 GHz; the surface resistance (R(sub s)) was measured using a cavity resonator at 58.9 GHz, and the transmission line losses were determined by measuring the quality factor (Q) of a linear microstrip resonator at 10.4 and 20.2 GHz. The complex conductivity for the film on LaAlO3 was determined to be (2.0-j10) x 10(exp 5) S/m at 77 K. It was observed that in the superconducting state sigma(sub 1) deviates from both the Bardeen-Cooper-Schrieffer (BCS) theory and the two-fluid model. Values of lambda were found to be approximately 2.0 and 1.1 microns at 77 K and 20 K respectively, and were obtained for the film on LaAlO3. The value of lambda at 20 K was approximately three times larger than that of BSCCO single crystals. R(sub s) values of 865 and 1391 mOmega were obtained for the films on SrTiO3 and LaAlO3, respectively, at 77 K and 58.9 GHz. Unloaded Q factors at 20 K of approximately 1100 and 800 at 10.4 and 20.2 GHz respectively, were measured for the BSCCO resonator. Unloaded Q values of 290 and 405 at 20 K were obtained at 10.4 GHz and 20.2 GHz respectively, for an all gold (Au) resonator.